CN103394630A - 一种熔模铸造蜡件粘结剂及其制备方法 - Google Patents
一种熔模铸造蜡件粘结剂及其制备方法 Download PDFInfo
- Publication number
- CN103394630A CN103394630A CN2013103342468A CN201310334246A CN103394630A CN 103394630 A CN103394630 A CN 103394630A CN 2013103342468 A CN2013103342468 A CN 2013103342468A CN 201310334246 A CN201310334246 A CN 201310334246A CN 103394630 A CN103394630 A CN 103394630A
- Authority
- CN
- China
- Prior art keywords
- wax
- binder
- kerosene
- binding agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种熔模铸造蜡件粘结剂,具体包括如下重量比的原料:蜡料和煤油的重量比为1:0.8-1.3。本发明的熔模铸造蜡件粘结剂解决了常用粘结剂粘结不牢,价格昂贵,污染蜡液的问题。本发明还提供了一种制备熔模铸造蜡件粘结剂的方法,该方法原料便宜,方法简单。
Description
技术领域
本发明涉及一种粘结剂,具体涉及一种熔模铸造蜡件粘结剂及其制备方法。
背景技术
在熔模铸造行业,对内腔复杂的产品设计蜡件成型时,经常需要设计成分体结构,然后分别生产,并采取粘接的方式进行组合。拼合蜡件各部分时,一般采用的粘结剂有502胶水、凡士林和粘结蜡。其中502胶水,虽然价格便宜,采购便捷,但是不易涂抹均匀,使蜡件每个部位完全粘合,未完全粘结的位置,容易出现缝隙;502胶水干后,容易起“白皮”,增加修蜡难度和工作量,且脱蜡后污染蜡液。凡士林粘合效率高,但粘结力较小,容易造成粘合不牢;同时凡士林油性大,浆液不易涂挂。上述两种粘结剂均为一次性使用,无法回收,同时对蜡液有一定的污染。市场上销售的粘结蜡,其粘结效果最好,但价格昂贵,增加生产成本,不利于节能降耗。
有鉴于此,需要发明一种成本低廉、粘结效果好的粘结剂。
发明内容
本发明所要解决的技术问题是提供一种粘结效果好,效率高、成本低廉、制备简单的熔模铸造蜡件粘结剂及其制备方法。
为解决上述问题,本发明一方面提供了一种熔模铸造蜡件粘结剂,具体方案如下:
一种熔模铸造蜡件粘结剂,其包括以下重量比的原料:
蜡料:煤油为1:0.8-1.3。
作为本发明的进一步改进,所述蜡料:煤油为1:1。
本发明另一方面提供了一种上述熔模铸造蜡件粘结剂的制备方法,具体方案包括以下步骤:
(1)称取上述重量份蜡料及煤油;
(2)将蜡料放入锅内,进行加热,熬煮,将蜡内的水分蒸发完全,停止加热;
(3)将煤油缓缓加入熬好的蜡液中,一边加入一边进行搅拌,搅拌均匀;
(3)放凉即得。
作为本发明的进一步改进,所述煤油和蜡料的重量比为1:1。
本发明中的蜡料可以为熔模铸造常用蜡料,比如162回收蜡料。由于粘结剂与蜡模采用同种蜡料,可以避免对蜡模料的污染,并且方便回收。
本发明在制备粘结剂时,需要将蜡料中的水分蒸发干净,因此可以根据火候的不同,适当延长或减少加热时间。
本发明中的煤油是必须的,经无数次试验尝试,其他油均不能达到本发明想要的效果,例如汽油和柴油无法与蜡料互溶。
本发明中蜡料与煤油的重量比尤为重要,并不是所有比例均可以完成本发明,蜡料过多,煤油过少,会使粘结剂变硬,粘结有效性降低,起不到粘结蜡模的作用。蜡料过少,煤油过多会使粘结剂变稀,也会减弱粘结剂的粘性。经过无数次筛选,完成本发明所需的原料重量比。
本发明取得的有益效果为:
本发明所提供的熔模铸造蜡件粘结剂解决了常用粘结剂粘结不牢,价格昂贵,污染蜡液的问题。其使用方便,成本低廉,能将拼合蜡件各部位完全粘合,不出现缝隙,粘合后不开裂,蜡件脱蜡后粘结剂不污染蜡液。且本发明所提供的熔模铸造蜡件粘结剂制备方法简单。
具体实施方式
下面将结合具体实施例对本发明进行进一步详细的说明。
实施例1
称取500g的162回收蜡料,放入平底锅内,进行加热,熬煮12min,将蜡内的水分蒸发完全,然后停止加热。随后称量500g煤油,缓缓加入熬好的蜡液中,一边加入一边进行搅拌,搅拌均匀;最后,放凉即可使用。
实施例2
称取500g的162回收蜡料,放入平底锅内,进行加热,熬煮12min,将蜡内的水分蒸发完全,然后停止加热。随后称量400g煤油,缓缓加入熬好的蜡液中,一边加入一边进行搅拌,搅拌均匀;最后,放凉即可使用。
实施例3
称取500g的162回收蜡料,放入平底锅内,进行加热,熬煮12min,将蜡内的水分蒸发完全,然后停止加热。随后称量650g煤油,缓缓加入熬好的蜡液中,一边加入一边进行搅拌,搅拌均匀;最后,放凉即可使用。
对比例 1
将按照实施例1-3所制备的熔模铸造蜡件粘结剂,分别与502胶水、凡士林和粘结蜡对同一批蜡件进行分别涂抹粘结,每组粘结10个蜡模,对粘结后的各组蜡模进行统计分析,观察缝隙率、并用悬挂重物的方法进行粘结力测试、对蜡模有无污染,具体见表1:
表1 分析结果
项目 | 缝隙率 | 粘结力 | 对蜡模有无污染 |
实施例1 | 0% | 7.9kg | 无 |
实施例2 | 10% | 9.0kg | 无 |
实施例3 | 10% | 6.1kg | 无 |
502胶水 | 40% | >10.5kg | 有 |
凡士林 | 30% | 1.7kg | 有 |
粘结蜡 | 0% | >9.0kg | 无 |
结论:本发明所提供的粘结剂粘结更牢,更环保,缝隙更少,有利于提高铸件合格率,粘结蜡具有很好的兼容性,与模型蜡配合使用不会改变模型蜡的性能,同时粘结蜡也不会对下一道制壳工序产生任何不良影响。
以上所述实施例仅为本发明的优选实施例,而并非本发明可行实施的穷举。对于本领域一般技术人员而言,在不背离本发明原理和精神的前提下对其所作出的任何显而易见的改动,都应当被认为包含在本发明的权利要求保护范围之内。
Claims (4)
1.一种熔模铸造蜡件粘结剂,其特征在于其包括以下重量比的原料:
蜡料:煤油为1:0.8-1.3。
2.根据权利要求1所述的一种熔模铸造蜡件粘结剂,其特征在于,所述蜡料:煤油的重量比为1:1。
3.如权利要求1所述的一种熔模铸造蜡件粘结剂的制备方法,其特征在于具体方案包括以下步骤:
(1)称取上述重量份蜡料及煤油;
(2)将蜡料放入锅内,进行加热,熬煮,将蜡内的水分蒸发完全,停止加热;
(3)将煤油缓缓加入熬好的蜡液中,一边加入一边进行搅拌,搅拌均匀;
(4)放凉即得。
4.根据权利要求3所述的一种熔模铸造蜡件粘结剂的制备方法,其特征在于所述煤油和蜡料的重量比为1:1。