CN103392738A - Inorganic nanometer silver-zinc composite transparent antiseptic and preparation method thereof - Google Patents
Inorganic nanometer silver-zinc composite transparent antiseptic and preparation method thereof Download PDFInfo
- Publication number
- CN103392738A CN103392738A CN2013103661177A CN201310366117A CN103392738A CN 103392738 A CN103392738 A CN 103392738A CN 2013103661177 A CN2013103661177 A CN 2013103661177A CN 201310366117 A CN201310366117 A CN 201310366117A CN 103392738 A CN103392738 A CN 103392738A
- Authority
- CN
- China
- Prior art keywords
- add
- agent
- silver
- salt
- alkaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An inorganic nanometer silver-zinc composite transparent antiseptic preferably consists of the following components in parts by mass: 800-12000 parts of water, 0.1-8 parts of an alkali inorganic salt, 1-12 parts of an acid metal-ion complexing agent, 0.01-1 part of a silver salt, 0.02-5 parts of a zinc salt, 1-16 parts of an alkali metal-ion complexing agent, 0.3-5 parts of a chelate coupling agent, 0.2-5 parts of a dispersant, and 0.5-7 parts of a heterocyclic metal-ion corrosion inhibitor. The invention also provides a preparation method of the antiseptic. The preparation method comprises: making the silver salt and the zinc salt in the solution react with the alkali metal-ion complexing agent to form a stable complex, adding into a diluents of the alkali inorganic salt and the acid metal-ion complexing agent for secondary protective complexation, then adding the chelate coupling agent and the dispersant to avoid generation of particle agglomerated precipitates, and finally adding the heterocyclic metal-ion corrosion inhibitor for resisting oxidation, resisting ultraviolet and preventing color changes, to obtain the colorless transparent silver-zinc composite antiseptic.
Description
Technical field
The invention belongs to antibiotic and technical field, especially relate to a kind of inorganic nano-silver zinc composite transparent antibacterial agent and preparation method thereof.
Background technology
Environment for human survival exists the microorganism of various harmful healths, productive life to the mankind produces many harmful effects, and particularly after SARS occurred, the mankind found simultaneously, many noxious bacterias morph, and rely on existing medical means often to be caught unprepared.The continuous renewal of antimicrobial technology is imperative.The antibacterial ability of silver is very strong and have the broad-spectrum sterilization effect, can not produce toxin in the human body accumulation again, a long time ago, just is used as the antibacterial activity material.The nanometer-level silver ion has higher surface energy and more contact area, has higher antibacterial activity, and bacterium just loses activity 6 seconds after contacting with Nano Silver.
At present, existing single nanometer silver antimicrobial technology, the antibacterial agent that this method is produced is fine to the killing effect of bacterium, but undesirable to the fungi bactericidal effect.And silver is single antibacterial agent, and yellowing resistance can be poor.As the patent No.: 201,210,553,614 1 kinds of nano silver colloidal sol antibacterial agents and preparation method thereof, the patent No.: the preparation method of 200,710,133,403 1 kinds of nano silver antimicrobials, the patent No.: 201010596742.7 1 kinds of nano silver antimicrobials and preparation method thereof, above 3 kinds is all single nanometer silver antimicrobial technology, only have the release of silver ion that anti-microbial property is just arranged, antimycotic undesirable, and along with silver ion constantly dissociates out, longer xanthochromia performance of time worse and worse on white object.
" silver and silver zinc complex antibacterial agent and application thereof " delivered in " Committee of Experts's inaugural meeting of Chinese Plastics processing industry association and plastic new material in 2005, new technology international symposium collection of thesis " for Mr. Li Bizhong, it is mainly set forth, and with zeolite, does carrier and carries out ion exchange and obtain carrier silver zinc complex antibacterial agent; " preparation of zinc-silver compounding sea afrodite antibacterial agent " is in May, 2010 Lu Yu of Chengdu University of Technology master thesis in addition, is also carrier silver zinc complex antibacterial agent.Their shortcoming is, (1) is solid powder material, and the scope of application is limited to.(2) in process of production, carry out ion exchange, heating process is arranged, cause energy loss, and increased time production cycle.
Summary of the invention
For addressing the above problem, the purpose of this invention is to provide that a kind of silver zinc complex, clear, colorless become, easy to prepare, equipment investment simple, the fluid antimicrobial agent and preparation method thereof of nanoscale fine particle.
For realizing the purpose of foregoing invention, the present invention adopts following technical scheme.
It is as follows that a kind of its material of inorganic nano-silver zinc composite transparent antibacterial agent consists of water, alkaline, inorganic salts, acid metal ionic complexing agent, silver salt, zinc salt, alkaline metal ions complexing agent, chelating titanate coupling agent, dispersant, its mass fraction of heterocyclic metal ion corrosion inhibiter:
1. water is 800 ~ 12000 parts
2. alkaline, inorganic salts is 0.1 ~ 8 part
3. the acid metal ionic complexing agent is 1 ~ 12 part
4. silver salt is 0.01 ~ 1 part
5. zinc salt is 0.02 ~ 5 part
6. the alkaline metal ions complexing agent is 1 ~ 16 part
7. the chelating type coupling agent is 0.3 ~ 5 part
8. dispersant is 0.2 ~ 5 part
9. heterocyclic metal ion corrosion inhibiter is 0.5 ~ 7 part
Its preparation method is by the alkaline metal ions complex compound of silver salt and zinc salt, again add the acid metal ionic complexing agent to add the solidity complexing, then add chelating type coupling agent and dispersant to prevent particle aggregation precipitation, add finally that heterocyclic metal ion corrosion inhibiter is anti-oxidant, uvioresistant prevents that look becomes.
Through such Ag of practice test
+The antibacterial agent of concentration 100ppm, apply or pad the textile fabric fabric to staphylococcus aureus, Escherichia coli, Candida albicans bacteriostasis rate greater than 99%, and this antibiotic facing material is through solar radiation colourless change in 48 hours.
Embodiment:
1. silver salt fully is dissolved in appropriate water, separately also fully is dissolved in appropriate water zinc salt standby
2. water-soluble solution diluted for use takes a morsel the alkaline metal ions complexing agent
3. by chelating type coupling agent and dispersant, get the little water dissolved dilution standby
4. by a little organic solvent dissolution of heterocyclic metal ion corrosion inhibiter, add a small amount of water diluted for use
5. by alkaline, inorganic salts, the acid metal ionic complexing agent successively fully is dissolved in residue water standby
6. by 2, slowly add successively in the aqueous solution of 1 silver salt and zinc salt, and constantly stir, reaction is to transparent getting final product, then two kinds of transparent liquid that will obtain add in 5 and stir together
7. secondly by 3, add in 5 and stir
8. again by 4, add in 5 and stir
This antibacterial agent is pressed Ag
+Concentration is diluted with water to 80 ~ 200ppm(and adjusts pH value to 7 with sodium silicate or citric acid) use and get final product
Embodiment 1
Water inventory is 3000g,
(1) by the silver salt 0.5g silver nitrate water-soluble solution of 300g, separately by the zinc salt 2g zinc nitrate water-soluble solution of 400g
(2) by alkaline metal ions complexing agent 12g ammoniacal liquor, with the dilution of 60g water
(3) chelating type coupling agent 2g titanate coupling agent KHT-301 and dispersant 1.5g polyoxyethylene nonylphenol ether are got to 300g water mixed diluting
(4) by heterocyclic metal ion corrosion inhibiter 3g BTA, with 20g alcohol, dissolve, add the dilution of 50g water
(5) by alkaline, inorganic salts 2g sodium silicate, acid metal ionic complexing agent 4g sodium ethylene diamine tetracetate successively fully is dissolved in remaining 1890g water
(6) (2) are slowly added in (1) successively, and constantly stir, reaction is to transparent getting final product, then two kinds of transparent liquid that will obtain add in 5 and stir together;
(7) secondly by 3, add in 5 and stir
(8) again by 4, add in 5 and stir
Obtain a kind of water white silver zinc complex antibacterial agent
Embodiment 2
Water inventory is 120kg,
(1) by the 20g silver nitrate water-soluble solution of 5kg, separately by the 80g zinc sulphate water-soluble solution of 5kg
(2) 300g ammoniacal liquor is diluted with 500g water
(3) Tween 80 of 70g bis-(diisooctyl phosphoryl) methyl oxyacetate titanate and 60g is got to 500g water mixed diluting
(4), by 150g BTA sodium, add the dilution of 1kg water
(5) by 30g sodium carbonate sodium, the 210g ethylenediamine tetra-acetic acid successively fully is dissolved in remaining 30kg water
(6) (2) are slowly added in (1) successively, and constantly stir, reaction is to transparent getting final product, then two kinds of transparent liquid that will obtain add in 5 and stir together;
(7) secondly by 3, add in 5 and stir
(8) again by 4, add in 5 and stir, finally will remain water 78kg and add
Obtain a kind of water white silver zinc complex antibacterial agent
Embodiment 3
Water inventory is 6250g,
(1) by the 1g silver nitrate water-soluble solution of 300g, separately by the 3.5g zinc nitrate water-soluble solution of 500g
(2) 25g ammoniacal liquor is diluted with 100g water
(3) 3.5g bis-(diisooctyl pyrophosphoryl base) methyl oxyacetate titanate and dispersant 3g polysorbas20 are got to 400g water mixed diluting
(4) the 5.5g methyl benzotriazazole is dissolved with 10g alcohol, add the dilution of 100g water
(5) by the 4g sodium silicate, the 10g disodium ethylene diamine tetraacetate successively fully is dissolved in remaining 4750g water
(6) (2) are slowly added in (1) successively, and constantly stir, reaction is to transparent getting final product, then two kinds of transparent liquid that will obtain add in 5 and stir together;
(7) secondly by 3, add in 5 and stir
(8) again by 4, add in 5 and stir
Obtain a kind of water white silver zinc complex antibacterial agent.
Claims (7)
1. its material of inorganic nano-silver zinc composite transparent antibacterial agent consists of water, alkaline, inorganic salts, the agent of acid metal ion network, silver salt, zinc salt, alkaline metal ions complexing agent, chelating type coupling agent, dispersant, the slow agent of heterocyclic metal ion, and their mass fractions are preferably 800 ~ 12000 parts, water, 0.1 ~ 8 part of alkaline, inorganic salts, 1 ~ 12 part of the sub-complexing agent of acid metal, 0.01 ~ 1 part of silver salt, 0.02 ~ 5 part of zinc salt, 1 ~ 16 part of alkaline metal ions complexing agent, 0.3 ~ 5 part of mould assembly coupling agent, 0.2 ~ 5 part of dispersant, 0.5 ~ 7 part of heterocyclic metal ion corrosion inhibiter; Its technical characterictic is by the alkaline metal ions complex compound of silver salt and zinc salt, again add the acid metal ionic complexing agent to add the solidity network stable, then add chelating type coupling agent and dispersant to prevent particle aggregation precipitation, add finally that heterocyclic metal sublayer corrosion inhibiter is anti-oxidant, uvioresistant prevents that look becomes.
2. according to the described a kind of inorganic nano-silver zinc composite transparent antibacterial agent its preparation method of claim 1, be characterized as the alkaline metal ions complex compound of silver salt and zinc salt, again add the acid metal ionic complexing agent to add the solidity complexing, then add chelating type coupling agent and dispersant to prevent particle aggregation precipitation, add finally that heterocyclic metal ion corrosion inhibiter is anti-oxidant, uvioresistant prevents that look becomes.
3. the mass fraction that forms according to its material of the described a kind of inorganic nano-silver zinc composite transparent antibacterial agent of claim 1 is preferably 800 ~ 12000 parts, water, 0.1 ~ 8 part of alkaline, inorganic salts, 1 ~ 12 part of acid metal ionic complexing agent, 0.01 ~ 1 part of silver salt, 0.02 ~ 5 part of zinc salt, 1 ~ 16 part of alkaline metal ions complexing agent, 0.3 ~ 5 part of chelating type coupling agent, 0.2 ~ 5 part of dispersant, 0.5 ~ 7 part of heterocyclic metal ion corrosion inhibiter.
4. according to claim 1,3 described a kind of its materials of inorganic nano-silver zinc composite transparent antibacterial agent, consist of water, alkaline, inorganic salts, acid metal ionic complexing agent, silver salt, zinc salt, alkaline metal ions complexing agent, chelating type coupling agent, dispersant, heterocyclic metal ion corrosion inhibiter.
5. according to claim 1, the 2 described complex compounds of alkaline metal ions by silver salt and zinc salt, again add the acid metal ionic complexing agent to add the solidity complexing.
6. according to claim 1, the 2 described metal ion complexs that will add after the solidity complexing, add chelating type coupling agent and dispersant to prevent the particle aggregation precipitation.
7. according to claim 1,2 described metal ion complexs by dual complexing, after stablizing mark and processing, add finally that heterocyclic metal ion corrosion inhibiter is anti-oxidant, uvioresistant prevents that look becomes.