CN103382367B - 一种有机硅绝缘浸渍漆及其制备方法 - Google Patents

一种有机硅绝缘浸渍漆及其制备方法 Download PDF

Info

Publication number
CN103382367B
CN103382367B CN201310261788.7A CN201310261788A CN103382367B CN 103382367 B CN103382367 B CN 103382367B CN 201310261788 A CN201310261788 A CN 201310261788A CN 103382367 B CN103382367 B CN 103382367B
Authority
CN
China
Prior art keywords
impregnating varnish
film forming
forming agent
hour
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310261788.7A
Other languages
English (en)
Other versions
CN103382367A (zh
Inventor
曹忠富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHANG CAISHIJI PAINT CO Ltd
Original Assignee
MAANSHANG CAISHIJI PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHANG CAISHIJI PAINT CO Ltd filed Critical MAANSHANG CAISHIJI PAINT CO Ltd
Priority to CN201310261788.7A priority Critical patent/CN103382367B/zh
Publication of CN103382367A publication Critical patent/CN103382367A/zh
Application granted granted Critical
Publication of CN103382367B publication Critical patent/CN103382367B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种有机硅绝缘浸渍漆及其制备方法，其特征在于由下列重量份的原料制成：聚甲基苯基乙烯基硅氧烷12-14、一缩二乙二醇苯甲酸酯4-6、柠檬酸三乙酯3-4、烯基丁二酸2-3、二烷基二硫代磷酸锌1-2、抗氧剂DSTP1-2、异丙基二硬脂酰氧基铝酸酯3-4、聚异丁烯6-8、过氧化环己酮1-2、亚甲基双环己烷胺2-3、乙烯基羧酸酯3-4、醋酸乙烯酯5-6、环烷酸钙1-2、成膜剂4-5。本发明所制得的浸渍漆固化时无低分子副产物放出,不影响绝缘材料的电气性能,而且整浸效果好、耐高温、绿色环保。

Description

一种有机硅绝缘浸渍漆及其制备方法
技术领域
本发明属于绝缘材料领域，涉及一种浸渍漆，尤其是一种有机硅绝缘浸渍漆及其制备方法。
背景技术
电机、变压器、导线等生产普遍采用压力浸渍工艺。将工件预烘去潮后冷却，置于真空环境中，排除内部的空气和挥发物，依靠真空中漆液重力、施加一定压力的作用，使漆液迅速渗透并充满绝缘结构内层。该工艺可获得连续致密、无针孔的漆膜。
现有的浸渍漆是由环氧树脂作为主体树脂、酸酐为固化剂。但是该体系固化产物的耐温等级和韧性不足，需要对环氧酸酐浸渍漆体系进行改性，是浸渍漆体系固化物同时满足耐温等级和机械性能的要求。
发明内容
本发明的目的是提供一种有机硅绝缘浸渍漆及其制备方法。
本发明的技术方案如下：
一种有机硅绝缘浸渍漆，其特征在于由下列重量份的原料制成：
聚甲基苯基乙烯基硅氧烷12-14、一缩二乙二醇苯甲酸酯4-6、柠檬酸三乙酯3-4、烯基丁二酸2-3、二烷基二硫代磷酸锌1-2、抗氧剂DSTP1-2、异丙基二硬脂酰氧基铝酸酯3-4、聚异丁烯6-8、过氧化环己酮1-2、亚甲基双环己烷胺2-3、乙烯基羧酸酯3-4、醋酸乙烯酯5-6、环烷酸钙1-2、成膜剂4-5。
所述的成膜剂由下列重量份的原料制成：硅烷偶联剂KH5502-4、582-2氨基树脂16-21、聚异丁烯3-4、环烷酸钴1-2、异丙基二硬脂酰氧基铝酸酯1-2、双十四碳醇酯4-5、氮化铝1-2、纳米凹凸棒土1-2、环氧大豆油4-5、吗啉1-2；
制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
所述的有机硅绝缘浸渍漆的制备方法，其特征在于包括以下步骤：
将一缩二乙二醇苯甲酸酯、柠檬酸三乙酯、烯基丁二酸、异丙基二硬脂酰氧基铝酸酯、聚异丁烯、醋酸乙烯酯混合，加热至80-90℃，滴加过氧化环己酮，搅拌反应1-2小时，然后，加入聚甲基苯基乙烯基硅氧烷、环烷酸钙、成膜剂，升温至115-120℃，继续搅拌2-3小时，保温，继续加入其它剩余物料，搅拌1-2小时即得。
本发明所合成的聚甲基苯基乙烯基硅氧烷以乙醇为溶剂,无毒、无害,所制得的浸渍漆固化时无低分子副产物放出,不影响绝缘材料的电气性能,而且整浸效果好、耐高温、绿色环保。
本发明浸渍漆能耐高温、高湿，电绝缘性能好，机械强度高，改善了导热性，可长期工作200℃，短期220℃，满足了设计要求。
具体实施方式
一种有机硅绝缘浸渍漆，由下列重量份的原料（公斤）制成：
聚甲基苯基乙烯基硅氧烷14、一缩二乙二醇苯甲酸酯6、柠檬酸三乙酯4、烯基丁二酸2、二烷基二硫代磷酸锌2、抗氧剂DSTP2、异丙基二硬脂酰氧基铝酸酯4、聚异丁烯6、过氧化环己酮2、亚甲基双环己烷胺3、乙烯基羧酸酯4、醋酸乙烯酯5、环烷酸钙1、成膜剂5。
所述的成膜剂由下列重量份的原料制成：硅烷偶联剂KH5504、582-2氨基树脂16、聚异丁烯4、环烷酸钴2、异丙基二硬脂酰氧基铝酸酯2、双十四碳醇酯5、氮化铝2、纳米凹凸棒土2、环氧大豆油4、吗啉2；
制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
有机硅绝缘浸渍漆的制备方法，包括以下步骤：
将一缩二乙二醇苯甲酸酯、柠檬酸三乙酯、烯基丁二酸、异丙基二硬脂酰氧基铝酸酯、聚异丁烯、醋酸乙烯酯混合，加热至80-90℃，滴加过氧化环己酮，搅拌反应1-2小时，然后，加入聚甲基苯基乙烯基硅氧烷、环烷酸钙、成膜剂，升温至115-120℃，继续搅拌2-3小时，保温，继续加入其它剩余物料，搅拌1-2小时即得。
固化工艺：在110~150℃下烘制3-5小时；
其固化后粘结强度大于25N，耐热等级为H级，体积电阻率不低于1×1014Ω·m，表面电阻不低于1×1014Ω，浸水后体积电阻率不低于1×1012Ω·m，表面电阻不低于1×1012Ω。本发明浸渍漆能耐高温、高湿，电绝缘性能好，机械强度高，改善了导热性，可长期工作200℃，短期220℃，满足了设计要求。

Claims (2)

1.一种有机硅绝缘浸渍漆，其特征在于由下列重量份的原料制成：
聚甲基苯基乙烯基硅氧烷12-14、一缩二乙二醇苯甲酸酯4-6、柠檬酸三乙酯3-4、烯基丁二酸2-3、二烷基二硫代磷酸锌1-2、抗氧剂DSTP1-2、异丙基二硬脂酰氧基铝酸酯3-4、聚异丁烯6-8、过氧化环己酮1-2、亚甲基双环己烷胺2-3、乙烯基羧酸酯3-4、醋酸乙烯酯5-6、环烷酸钙1-2、成膜剂4-5；
所述的成膜剂由下列重量份的原料制成：硅烷偶联剂KH5502-4、582-2氨基树脂16-21、聚异丁烯3-4、环烷酸钴1-2、异丙基二硬脂酰氧基铝酸酯1-2、双十四碳醇酯4-5、氮化铝1-2、纳米凹凸棒土1-2、环氧大豆油4-5、吗啉1-2；
成膜剂的制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
2.根据权利要求1所述的有机硅绝缘浸渍漆的制备方法，其特征在于包括以下步骤：将一缩二乙二醇苯甲酸酯、柠檬酸三乙酯、烯基丁二酸、异丙基二硬脂酰氧基铝酸酯、聚异丁烯、醋酸乙烯酯混合，加热至80-90℃，滴加过氧化环己酮，搅拌反应1-2小时，然后，加入聚甲基苯基乙烯基硅氧烷、环烷酸钙、成膜剂，升温至115-120℃，继续搅拌2-3小时，保温，继续加入其它剩余物料，搅拌1-2小时即得。
CN201310261788.7A 2013-06-27 2013-06-27 一种有机硅绝缘浸渍漆及其制备方法 Active CN103382367B (zh)