CN103360967A - Aluminum-foil adhesive tape special for refrigerator and manufacturing process thereof - Google Patents
Aluminum-foil adhesive tape special for refrigerator and manufacturing process thereof Download PDFInfo
- Publication number
- CN103360967A CN103360967A CN2012101024733A CN201210102473A CN103360967A CN 103360967 A CN103360967 A CN 103360967A CN 2012101024733 A CN2012101024733 A CN 2012101024733A CN 201210102473 A CN201210102473 A CN 201210102473A CN 103360967 A CN103360967 A CN 103360967A
- Authority
- CN
- China
- Prior art keywords
- film
- aluminium foil
- adhesive tape
- conjunction
- foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an aluminum-foil adhesive tape special for a refrigerator and a manufacturing process thereof. The aluminum-foil adhesive tape is composed of a foaming bonding release layer, a flexible film, an adhesive layer, an aluminium foil layer and a pressure-sensitive adhesive layer. The foaming bonding release layer is 0.3-1 micron and mainly formed from silicon rubber with a foaming material compatibly; the flexible film is 6-30 microns thick, and formed from a polyester (PET) film, a polyethylene (PE) film, a polypropylene (PP) film, a BOPP (Biaxially-oriented Polypropylene) film or a polyvinyl chloride (PVC) film; the adhesive layer is 8-20 microns thick, and formed from rubber, polyurethane, acrylic acid and an adhesive; the aluminium foil layer is 10-30 microns thick, and formed from a calendered aluminium foil having the purity in the range from 80% to 99.99%. Compared with the traditional aluminum-foil adhesive tape, the aluminum-foil adhesive tape provided by the invention is capable of improving the overall quality of the refrigerator, and further is flat to fit, soft, strong in metallic luster and excellent in foaming bonding effect. Furthermore, the operating time of workers in a refrigerator factory is saved; the aluminum-foil adhesive tape is low in cost and more friendly to environment; in addition, resource waste is reduced.
Description
Technical field:
The present invention relates to refrigerator aluminum foil special adhesive tape and manufacturing process
Background technology:
Aluminum foil and adhesive tape kind on the market is tired many, aluminum foil and adhesive tape with separate-type paper is arranged, not with the aluminum foil and adhesive tape of separate-type paper, mould again in addition the use of aluminum foil and adhesive tape in the refrigeration for refrigerator industry, all exist and use inconvenience, the fixed effect of refrigerator inner capillary tube is bad, is combined insecure with whipping agent, manufacturing cost is high, the problems such as waste resource.
Summary of the invention:
Purpose of the present invention will provide a kind of refrigerator aluminum foil special adhesive tape and manufacturing process exactly, and it can overcome the existing existing above problem of aluminum foil and adhesive tape.The object of the present invention is achieved like this, and refrigerator aluminum foil special adhesive tape and manufacturing process is characterized in that: aluminum foil and adhesive tape is comprised of in conjunction with release layer, flexible membrane layer, adhesive layer, aluminium foil layer, pressure-sensitive adhesive layer foaming; Described foaming is 0.3-1 μ m in conjunction with release layer thickness, adopts mainly that silicon rubber and foamed material are compatible to be made; Described flexible membrane layer thickness is 6-30 μ m, selects polyester PET film, polythene PE film, polypropylene PP, BOPP film, polyvinylchloride film to make; Described adhesive layer thickness is 8-20 μ m, selects rubber, Polyurethane, vinylformic acid to add tackiness agent and makes; Described aluminium foil layer thickness 10-30 μ m, the rolling aluminum foil of purity 80%-99.99% is made; Manufacturing process is to adopt fexible film thickness at poly-hydro carbons film or the polyester film of 6 μ m-30 μ m, processes; On the fexible film surface, be coated with foaming in conjunction with parting agent; Between another surface of fexible film and aluminium foil surface, adopt dry adhered technique, make between fexible film and aluminium foil in conjunction with close and firm, make external force can't separate aluminium foil; Described aluminium foil is rolling aluminum foil, and thickness is at 8 μ m-75 μ m; Pressure-sensitive adhesive layer at another surface-coated thickness 15 μ m-50 μ m of aluminium foil; Described pressure sensitive adhesive comprises water-based acryl glue system, oiliness acryl glue system, rubber-type glue system, silica gel system; When being coated with foaming in conjunction with parting agent on the flexible membrane surface, adopt parting agent on the intaglio plate coating method, by the 12m-32m drying tunnel, drying tunnel temperature is controlled at 120 ℃-180 ℃, baking and curing, speed 60-160 m/min, rolling namely forms foaming in conjunction with release film, adopts intaglio plate dispense tip coated with adhesive by the 12m-20m drying tunnel with the another side that foams in conjunction with release film, and drying tunnel temperature is controlled at 60 ℃ of-120 ℃ of oven dry, fit through applying rolling position and aluminium foil, binding temperature is controlled at 100 ℃-160 ℃
,Speed 60-160 m/min namely form and mould again aluminium foil, adopt glue directly to scrape the formula dispense tip at the aluminium foil surface of moulding again aluminium foil, are coated with pressure sensitive adhesive; By the oven dry of 24m-32m drying tunnel, speed 120-160m/ min, rolling namely forms refrigerator aluminum foil special adhesive tape.The present invention compares with traditional aluminum foil and adhesive tape, has the refrigerator of lifting total quality, and it is smooth to fit, softness, and the metal sense is strong, and well foaming is in conjunction with effect.Saved refrigerator factory employee's operating time, cost is low, and more environmental protection has reduced the wasting of resources.
Description of drawings:
Fig. 1 is structural representation of the present invention;
1. foam in conjunction with release layer, 2. flexible membrane layer, 3. adhesive layer, 4. aluminium foil layer, 5. pressure-sensitive adhesive layer.
Embodiment: the invention will be further described below in conjunction with accompanying drawing;
Refrigerator aluminum foil special adhesive tape and manufacturing process is characterized in that: aluminum foil and adhesive tape is comprised of in conjunction with release layer, flexible membrane layer, adhesive layer, aluminium foil layer, pressure-sensitive adhesive layer foaming; Described foaming is 0.3-1 μ m in conjunction with release layer thickness, adopts mainly that silicon rubber and foamed material are compatible to be made; Described flexible membrane layer thickness is 6-30 μ m, selects polyester PET film, polythene PE film, polypropylene PP, BOPP film, polyvinylchloride film to make; Described adhesive layer thickness is 8-20 μ m, selects rubber, Polyurethane, vinylformic acid to add tackiness agent and makes; Described aluminium foil layer thickness 10-30 μ m, the rolling aluminum foil of purity 80%-99.99% is made; Manufacturing process is to adopt fexible film thickness at poly-hydro carbons film or the polyester film of 6 μ m-30 μ m, processes; On the fexible film surface, be coated with foaming in conjunction with parting agent; Between another surface of fexible film and aluminium foil surface, adopt dry adhered technique, make between fexible film and aluminium foil in conjunction with close and firm, make external force can't separate aluminium foil; Described aluminium foil is rolling aluminum foil, and thickness is at 8 μ m-75 μ m; Pressure-sensitive adhesive layer at another surface-coated thickness 15 μ m-50 μ m of aluminium foil; Described pressure sensitive adhesive comprises water-based acryl glue system, oiliness acryl glue system, rubber-type glue system, silica gel system; When being coated with foaming in conjunction with parting agent on the flexible membrane surface, adopt parting agent on the intaglio plate coating method, by the 12m-32m drying tunnel, drying tunnel temperature is controlled at 120 ℃-180 ℃, baking and curing, speed 60-160 m/min, rolling namely forms foaming in conjunction with release film, adopts intaglio plate dispense tip coated with adhesive by the 12m-20m drying tunnel with the another side that foams in conjunction with release film, and drying tunnel temperature is controlled at 60 ℃ of-120 ℃ of oven dry, fit through applying rolling position and aluminium foil, binding temperature is controlled at 100 ℃-160 ℃
,Speed 60-160 m/min namely form and mould again aluminium foil, adopt glue directly to scrape the formula dispense tip at the aluminium foil surface of moulding again aluminium foil, are coated with pressure sensitive adhesive; By the oven dry of 24m-32m drying tunnel, speed 120-160m/ min, rolling namely forms refrigerator aluminum foil special adhesive tape.
Embodiment 1
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 24m drying tunnel with the coating of 80 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 120 ℃, speed 80 m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 6 μ m, tackiness agent bed thickness 15 μ m, aluminium foil bed thickness 15 μ m, the thick 20 μ m of inferior quick glue-line in conjunction with parting agent 80 order glue spreads.
Embodiment 2
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 26m drying tunnel with the coating of 90 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 110 ℃, speed 90m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 7 μ m, tackiness agent bed thickness 17 μ m, aluminium foil bed thickness 16 μ m, the thick 22 μ m of inferior quick glue-line in conjunction with parting agent 90 order glue spreads.
Embodiment 3
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 28m drying tunnel with the coating of 100 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 100 ℃, speed 120m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 8 μ m, tackiness agent bed thickness 18 μ m, aluminium foil bed thickness 18 μ m, the thick 23 μ m of inferior quick glue-line in conjunction with parting agent 100 order glue spreads.
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane 2, to foam in conjunction with parting agent through the 29m drying tunnel with the coating of 110 order intaglio plates on the flexible membrane surface, 90 ℃ of drying tunnel control temperature, speed 110m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 9 μ m, tackiness agent bed thickness 19 μ m, aluminium foil bed thickness 19 μ m, the thick 24 μ m of inferior quick glue-line in conjunction with parting agent 110 order glue spreads.
Embodiment 5
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 30m drying tunnel with the coating of 120 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 90 ℃, speed 120m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, coats pressure sensitive adhesive with the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 10 μ m, tackiness agent bed thickness 20 μ m, aluminium foil bed thickness 20 μ m, the thick 25 μ m of inferior quick glue-line in conjunction with parting agent 120 order glue spreads.
Embodiment 6
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 31m drying tunnel with the coating of 130 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 80 ℃, speed 130m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 11 μ m, tackiness agent bed thickness 21 μ m, aluminium foil bed thickness 21 μ m, the thick 26 μ m of inferior quick glue-line in conjunction with parting agent 130 order glue spreads.
Embodiment 7
As shown in the figure, foaming of the present invention is in conjunction with release layer 1 and flexible membrane layer 2, to foam in conjunction with parting agent through the 32m drying tunnel with the coating of 140 order intaglio plates on the flexible membrane surface, drying tunnel temperature is controlled at 120 ℃, speed 80m/min producing foamed binding film, coating adhesive is combined with aluminium foil to make and is moulded again aluminium foil on the foaming binding film, is coated with pressure sensitive adhesive at the aluminium foil surface of moulding again aluminium foil again and namely makes the special-purpose film coated aluminum foil adhesive tape of refrigerator.
Described foaming is flexible membrane bed thickness 9 μ m, tackiness agent bed thickness 16 μ m, aluminium foil bed thickness 16 μ m, the thick 23 μ m of inferior quick glue-line in conjunction with parting agent 140 order glue spreads.
Claims (2)
1. refrigerator aluminum foil special adhesive tape and manufacturing process is characterized in that: aluminum foil and adhesive tape is comprised of in conjunction with release layer, flexible membrane layer, adhesive layer, aluminium foil layer, pressure-sensitive adhesive layer foaming; Its manufacturing process is to adopt fexible film thickness at poly-hydro carbons film or the polyester film of 6 μ m-30 μ m, processes; On the fexible film surface, be coated with foaming in conjunction with parting agent; Between another surface of fexible film and aluminium foil surface, adopt dry adhered technique, make between fexible film and aluminium foil in conjunction with close and firm; Another surface-coated pressure-sensitive adhesive layer at aluminium foil; When being coated with foaming in conjunction with parting agent on the flexible membrane surface, adopt parting agent on the intaglio plate coating method, by the 12m-32m drying tunnel, drying tunnel temperature is controlled at 120 ℃-180 ℃, baking and curing, speed 60-160 m/min, rolling namely forms foaming in conjunction with release film, adopts intaglio plate dispense tip coated with adhesive by the 12m-20m drying tunnel with the another side that foams in conjunction with release film, and drying tunnel temperature is controlled at 60 ℃ of-120 ℃ of oven dry, fit through applying rolling position and aluminium foil, binding temperature is controlled at 100 ℃-160 ℃
,Speed 60-160 m/min namely form and mould again aluminium foil, adopt glue directly to scrape the formula dispense tip at the aluminium foil surface of moulding again aluminium foil, are coated with pressure sensitive adhesive; By the oven dry of 24m-32m drying tunnel, speed 120-160m/ min, rolling namely forms refrigerator aluminum foil special adhesive tape.
2. refrigerator aluminum foil special adhesive tape according to claim 1 and manufacturing process, it is characterized in that: described foaming is 0.3-1 μ m in conjunction with release layer thickness, adopts mainly that silicon rubber and foamed material are compatible to be made; Described flexible membrane layer thickness is 6-30 μ m, selects polyester PET film, polythene PE film, polypropylene PP, BOPP film, polyvinylchloride film to make; Described adhesive layer thickness is 8-20 μ m, selects rubber, Polyurethane, vinylformic acid to add tackiness agent and makes; Described aluminium foil layer thickness 10-30 μ m is made by the rolling aluminum foil of purity 80%-99.99%; Described pressure-sensitive adhesive layer thickness is 15 μ m-50 μ m, selects water-based acryl glue system, oiliness acryl glue system, rubber-type glue system, silica gel system to make.