CN103360631A - 改性乙基纤维素的配方 - Google Patents
改性乙基纤维素的配方 Download PDFInfo
- Publication number
- CN103360631A CN103360631A CN2013103298910A CN201310329891A CN103360631A CN 103360631 A CN103360631 A CN 103360631A CN 2013103298910 A CN2013103298910 A CN 2013103298910A CN 201310329891 A CN201310329891 A CN 201310329891A CN 103360631 A CN103360631 A CN 103360631A
- Authority
- CN
- China
- Prior art keywords
- ethyl cellulose
- accounts
- prescription
- modification
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性乙基纤维素的配方,所述的改性乙基纤维素的配方包括乙基纤维素及添加剂,所述的添加剂包括阻燃剂、增韧剂、抗冲击改性剂、抗氧化剂以及偶联剂,所述的阻燃剂为磷酸三苯酯,所述的增韧剂为聚醋酸乙烯,所述的抗冲击改性剂为甲基丙烯酸甲酯-丁二烯-苯乙烯,所述的抗氧化剂为对苯二胺,所述的偶联剂为氨丙基三乙氧基硅烷。本发明改性乙基纤维素的配方通过在乙基纤维素中添加多种添加剂,使得改性乙基纤维素提高了阻燃性、提高了韧性、提高了机械强度、提高了抗氧化性能、提高了产品质量以及降低了产品的生产成本。
Description
技术领域
本发明涉及塑料配方,特别是涉及一种改性乙基纤维素的配方。
背景技术
乙基纤维素是纤维素中的部分或全部羟基上的氢被乙基取代的产物。具有良好的韧性、耐寒性和成膜性。但是乙基纤维素本身的阻燃性、机械强度都存在着很大的缺陷,而且现有的改性乙基纤维素存在的质量都欠佳,成色较差,并且生产成本较高。
发明内容
本发明主要解决的技术问题是提供一种改性乙基纤维素的配方,该改性乙基纤维素的配方具有提高了阻燃性、提高了韧性、提高了机械强度、提高了抗氧化性能、提高了产品质量以及降低了产品的生产成本的特点。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种改性乙基纤维素的配方,所述的改性乙基纤维素的配方包括乙基纤维素及添加剂,所述的添加剂包括阻燃剂、增韧剂、抗冲击改性剂、抗氧化剂以及偶联剂,所述的阻燃剂为磷酸三苯酯,所述的增韧剂为聚醋酸乙烯,所述的抗冲击改性剂为甲基丙烯酸甲酯-丁二烯-苯乙烯,所述的抗氧化剂为对苯二胺,所述的偶联剂为氨丙基三乙氧基硅烷。
在本发明一个较佳实施例中,所述的改性乙基纤维素的配方各成分所占重量百分比分别为乙基纤维素占75.8%-79.4%,磷酸三苯酯占1.6%-2.3%,聚醋酸乙烯占5.3%-6.1%,甲基丙烯酸甲酯-丁二烯-苯乙烯占5.8%-6.4%,对苯二胺占3.7%-4.5%,氨丙基三乙氧基硅烷占4.2%-4.9%。
在本发明一个较佳实施例中,所述的改性乙基纤维素的配方各成分所占重量百分比具体为乙基纤维素占76.7%,磷酸三苯酯占2.1%,聚醋酸乙烯占5.9%,甲基丙烯酸甲酯-丁二烯-苯乙烯占6.2%,对苯二胺占4.3%,氨丙基三乙氧基硅烷占4.8%。
本发明的有益效果是:本发明改性乙基纤维素的配方通过在乙基纤维素中添加多种添加剂,使得改性乙基纤维素提高了阻燃性、提高了韧性、提高了机械强度、提高了抗氧化性能、提高了产品质量以及降低了产品的生产成本。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
一种改性乙基纤维素的配方,所述的改性乙基纤维素的配方包括乙基纤维素及添加剂,所述的添加剂包括阻燃剂、增韧剂、抗冲击改性剂、抗氧化剂以及偶联剂,所述的阻燃剂为磷酸三苯酯,所述的增韧剂为聚醋酸乙烯,所述的抗冲击改性剂为甲基丙烯酸甲酯-丁二烯-苯乙烯,所述的抗氧化剂为对苯二胺,所述的偶联剂为氨丙基三乙氧基硅烷。
进一步地,所述的改性乙基纤维素的配方各成分所占重量百分比分别为乙基纤维素占75.8%-79.4%,磷酸三苯酯占1.6%-2.3%,聚醋酸乙烯占5.3%-6.1%,甲基丙烯酸甲酯-丁二烯-苯乙烯占5.8%-6.4%,对苯二胺占3.7%-4.5%,氨丙基三乙氧基硅烷占4.2%-4.9%。
进一步地,所述的改性乙基纤维素的配方各成分所占重量百分比具体为乙基纤维素占76.7%,磷酸三苯酯占2.1%,聚醋酸乙烯占5.9%,甲基丙烯酸甲酯-丁二烯-苯乙烯占6.2%,对苯二胺占4.3%,氨丙基三乙氧基硅烷占4.8%。
进一步地,所述的改性乙基纤维素的配方各成分所占重量百分比分别为乙基纤维素占78.7%,磷酸三苯酯占1.7%,聚醋酸乙烯占5.5%,甲基丙烯酸甲酯-丁二烯-苯乙烯占5.9%,对苯二胺占3.8%,氨丙基三乙氧基硅烷占4.4%。
本发明改性乙基纤维素的配方的有益效果是:本发明改性乙基纤维素的配方通过在乙基纤维素中添加多种添加剂,使得改性乙基纤维素提高了阻燃性、提高了韧性、提高了机械强度、提高了抗氧化性能、提高了产品质量以及降低了产品的生产成本。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种改性乙基纤维素的配方,其特征在于:所述的改性乙基纤维素的配方包括乙基纤维素及添加剂,所述的添加剂包括阻燃剂、增韧剂、抗冲击改性剂、抗氧化剂以及偶联剂,所述的阻燃剂为磷酸三苯酯,所述的增韧剂为聚醋酸乙烯,所述的抗冲击改性剂为甲基丙烯酸甲酯-丁二烯-苯乙烯,所述的抗氧化剂为对苯二胺,所述的偶联剂为氨丙基三乙氧基硅烷。
2.根据权利要求1所述的改性乙基纤维素的配方,其特征在于,所述的改性乙基纤维素的配方各成分所占重量百分比分别为乙基纤维素占75.8%-79.4%,磷酸三苯酯占1.6%-2.3%,聚醋酸乙烯占5.3%-6.1%,甲基丙烯酸甲酯-丁二烯-苯乙烯占5.8%-6.4%,对苯二胺占3.7%-4.5%,氨丙基三乙氧基硅烷占4.2%-4.9%。
3.根据权利要求2所述的改性乙基纤维素的配方,其特征在于,所述的改性乙基纤维素的配方各成分所占重量百分比具体为乙基纤维素占76.7%,磷酸三苯酯占2.1%,聚醋酸乙烯占5.9%,甲基丙烯酸甲酯-丁二烯-苯乙烯占6.2%,对苯二胺占4.3%,氨丙基三乙氧基硅烷占4.8%。