CN103352372B - 箱包用pvc合成革及其制备方法 - Google Patents

箱包用pvc合成革及其制备方法 Download PDF

Info

Publication number
CN103352372B
CN103352372B CN201310276729.7A CN201310276729A CN103352372B CN 103352372 B CN103352372 B CN 103352372B CN 201310276729 A CN201310276729 A CN 201310276729A CN 103352372 B CN103352372 B CN 103352372B
Authority
CN
China
Prior art keywords
synthetic leather
upper strata
minute
polyvinyl chloride
case
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310276729.7A
Other languages
English (en)
Other versions
CN103352372A (zh
Inventor
许月莲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Quantai Environmental Protection Technology Co., Ltd.
Original Assignee
LIUAN SANXI LEATHER PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUAN SANXI LEATHER PRODUCTS Co Ltd filed Critical LIUAN SANXI LEATHER PRODUCTS Co Ltd
Priority to CN201310276729.7A priority Critical patent/CN103352372B/zh
Publication of CN103352372A publication Critical patent/CN103352372A/zh
Application granted granted Critical
Publication of CN103352372B publication Critical patent/CN103352372B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

箱包用PVC合成革，其特征在于由二层复合构成，基材是布，上层为PVC树脂层，上层由下列重量份的原料制成：SG-3型PVC树脂60-65、二茂铁4-6、2-氨基-2-甲基-1-丙醇3-5、尼龙PA66？4-5、氰尿酸锌1-2、白云石粉12-14、铝矾土6-8、甲基三甲氧基硅烷3-4、沉淀法白炭黑12-14、硬酸酸锌3-4、甘油三醋酸酯4-6、二甲基氯化锡1-2、苯并三氮唑1-2、改性粘土粉末3-4；本发明通过配方与工艺改进，增加了合成革的防霉性能、防腐蚀性能，具有玫瑰香味，具有类似于天然皮革所具有的自然舒适手感；3-5年不容易破损或撕裂损坏，适合于作为运动鞋面料。

Description

箱包用PVC合成革及其制备方法
技术领域
本发明属于一种化学合成革面料加工技术领域，具体是一种聚氯乙烯合成革及其制备方法。
背景技术
聚氯乙烯合成革具有的耐水解、耐磨、耐刮、阻燃等优势，广泛用于高档运动鞋、箱包、沙发等方面，但其在柔软性、透气性、手感、耐曲折等诸方面仍有许多不足，需要对其配方与工艺进行改进。
发明内容
本发明的目的在于提供一种箱包用PVC合成革及其制备方法，生产的合成革产品质量好。
本发明的目的可以通过以下技术方案实现：
箱包用PVC合成革，其特征在于由二层复合构成，基材是布，上层为PVC树脂层，上层由下列重量份的原料制成：
SG-3型PVC树脂60-65、二茂铁4-6、2-氨基-2-甲基-1-丙醇3-5、尼龙PA664-5、氰尿酸锌1-2、白云石粉12-14、铝矾土6-8、甲基三甲氧基硅烷3-4、沉淀法白炭黑12-14、硬酸酸锌3-4、甘油三醋酸酯4-6、二甲基氯化锡1-2、苯并三氮唑1-2、改性粘土粉末3-4；
所述的改性粘土粉末通过以下方法制得：
将粘土放入460-480℃下煅烧3-4小时，取出，冷却，研成粉末；再加入相当于粘土粉末重量5-8%的氮化铝、3-4%的三聚磷酸钠、2-3%的玫瑰精油、2-3%的吗啉、3-4%的二正辛基-4-异噻唑啉-3-酮，混合搅拌30-40分钟，然后再喷入相当于粘土粉末重量3-5%的硅烷偶联剂KH550，在13000-16000转/分下搅拌60-70分钟，即得。
所述的箱包用PVC合成革的制备方法，其特征在于包括以下步骤：
A）将二茂铁、2-氨基-2-甲基-1-丙醇、尼龙PA66、氰尿酸锌、白云石粉、铝矾土、甲基三甲氧基硅烷、沉淀法白炭黑、硬酸酸锌，在130-150℃下搅拌10-15分钟，然后，降温100-105℃，加入其它剩余原料，高速混合8-12分钟，然后，下料到开炼机进行充分混炼后到胶布机进行贴合，将上层贴到基材上；
B）产品经表面效果处理；
C）成品检验合格，出厂。
本发明通过配方与工艺改进，增加了合成革的防霉性能、防腐蚀性能，具有玫瑰香味，具有类似于天然皮革所具有的自然舒适手感；3-5年不容易破损或撕裂损坏，适合于作为运动鞋面料。
具体实施方式
箱包用PVC合成革，由二层复合构成，基材是布，上层为PVC树脂层，上层由下列重量份（公斤）的原料制成：
SG-3型PVC树脂60、二茂铁4、2-氨基-2-甲基-1-丙醇5、尼龙PA664、氰尿酸锌1、白云石粉12、铝矾土6、甲基三甲氧基硅烷3、沉淀法白炭黑12、硬酸酸锌4、甘油三醋酸酯4、二甲基氯化锡1、苯并三氮唑1、改性粘土粉末4；
箱包用PVC合成革的制备方法，包括以下步骤：
A）将二茂铁、2-氨基-2-甲基-1-丙醇、尼龙PA66、氰尿酸锌、白云石粉、铝矾土、甲基三甲氧基硅烷、沉淀法白炭黑、硬酸酸锌，在130-150℃下搅拌10-15分钟，然后，降温100-105℃，加入其它剩余原料，高速混合8-12分钟，然后，下料到开炼机进行充分混炼后到胶布机进行贴合，将上层贴到基材上；
B）产品经表面效果处理；
C）成品检验合格，出厂。
所述的改性粘土粉末通过以下方法制得：
将粘土放入460-480℃下煅烧4小时，取出，冷却，研成粉末；再加入相当于粘土粉末重量5%的氮化铝、3%的三聚磷酸钠、2%的玫瑰精油、3%的吗啉、3%的二正辛基-4-异噻唑啉-3-酮，混合搅拌30-40分钟，然后再喷入相当于粘土粉末重量3%的硅烷偶联剂KH550，在13000-16000转/分下搅拌60-70分钟，即得。
本发明合成革检测：径向拉断强度/纬向拉断强度〉440N/3CM，径/纬向撕裂强度〉29N，-10℃低温曲挠性可达到耐曲折3万次，老化试验不开裂。

Claims (2)

1.箱包用PVC合成革，其特征在于由二层复合构成，基材是布，上层为PVC树脂层，上层由下列重量份的原料制成：SG-3型PVC树脂60-65、二茂铁4-6、2-氨基-2-甲基-1-丙醇3-5、尼龙PA664-5、氰尿酸锌1-2、白云石粉12-14、铝矾土6-8、甲基三甲氧基硅烷3-4、沉淀法白炭黑12-14、硬脂酸锌3-4、甘油三醋酸酯4-6、二甲基氯化锡1-2、苯并三氮唑1-2、改性粘土粉末3-4；所述的改性粘土粉末通过以下方法制得：将粘土放入460-480℃下煅烧3-4小时，取出，冷却，研成粉末；再加入相当于粘土粉末重量5-8%的氮化铝、3-4%的三聚磷酸钠、2-3%的玫瑰精油、2-3%的吗啉、3-4%的2-正辛基-4-异噻唑啉-3-酮，混合搅拌30-40分钟，然后再喷入相当于粘土粉末重量3-5%的硅烷偶联剂KH550，在13000-16000转/分下搅拌60-70分钟，即得。
2.根据权利要求1所述的箱包用PVC合成革的制备方法，其特征在于包括以下步骤：
A）将二茂铁、2-氨基-2-甲基-1-丙醇、尼龙PA66、氰尿酸锌、白云石粉、铝矾土、甲基三甲氧基硅烷、沉淀法白炭黑、硬脂酸锌，在130-150℃下搅拌10-15分钟，然后，降温100-105℃，加入其它剩余原料，高速混合8-12分钟，然后，下料到开炼机进行充分混炼后到胶布机进行贴合，将上层贴到基材上；
B）产品经表面效果处理；
C）成品检验合格，出厂。
CN201310276729.7A 2013-07-03 2013-07-03 箱包用pvc合成革及其制备方法 Active CN103352372B (zh)