CN103351807B - 一种热固化导热散热涂料及其制备方法 - Google Patents

一种热固化导热散热涂料及其制备方法 Download PDF

Info

Publication number
CN103351807B
CN103351807B CN201310243293.1A CN201310243293A CN103351807B CN 103351807 B CN103351807 B CN 103351807B CN 201310243293 A CN201310243293 A CN 201310243293A CN 103351807 B CN103351807 B CN 103351807B
Authority
CN
China
Prior art keywords
minute
add
dimethylbenzene
ester
acid acyloxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310243293.1A
Other languages
English (en)
Other versions
CN103351807A (zh
Inventor
钱程
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG CHICHENG ELECTRIC TECHNOLOGY Co Ltd
Original Assignee
TIANCHANG CHICHENG ELECTRIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG CHICHENG ELECTRIC TECHNOLOGY Co Ltd filed Critical TIANCHANG CHICHENG ELECTRIC TECHNOLOGY Co Ltd
Priority to CN201310243293.1A priority Critical patent/CN103351807B/zh
Publication of CN103351807A publication Critical patent/CN103351807A/zh
Application granted granted Critical
Publication of CN103351807B publication Critical patent/CN103351807B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种热固化导热散热涂料及其制备方法，其特征在于由下列重量份的原料制成：有机硅树脂32-35、三聚氰胺甲醛树脂12-14、二甲苯21-23、乙酸乙酯24-26、丁醇8-10、氮化铝粉末26-28、二氨基二苯基甲烷2-3、二异丙基乙醇胺4-5、安息香1-2、二正辛基-4-异噻唑啉-3-酮1-2、云母粉12-15、衣康酸酯4-6、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯3-5、乙烯基三(β-甲氧基乙氧基)硅烷2-3、成膜剂4-5；本发明采用二正辛基-4-异噻唑啉-3-酮，增加了涂料的防霉性能，长期存放，不会变质产生异味。

Description

一种热固化导热散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，涉及一种散热涂料，更具体地说，是一种热固化导热散热涂料及其制备方法。
背景技术
随着LED灯使用范围的迅速扩大，延长LED灯使用寿命也已成为急需解决的问题。目前一般的LED灯并没有采用特别的散热措施，采用灯壳自然散热，这种方式使得LED灯使用一段时间后，出现灯壳老化，由于灯壳长时间高温，使得LED使用寿命下降；不能满足LED灯发展现状与要求。
发明内容
本发明的目的是提供一种热固化导热散热涂料及其制备方法，本发明涂料具有粘结力大，耐老化、散热系数大的优点。
本发明所采用的技术方案是：
一种热固化导热散热涂料，其特征在于由下列重量份的原料制成：
有机硅树脂32-35、三聚氰胺甲醛树脂12-14、二甲苯21-23、乙酸乙酯24-26、丁醇8-10、氮化铝粉末26-28、二氨基二苯基甲烷2-3、二异丙基乙醇胺4-5、安息香1-2、二正辛基-4-异噻唑啉-3-酮1-2、云母粉12-15、衣康酸酯4-6、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯3-5、乙烯基三(β-甲氧基乙氧基)硅烷2-3、成膜剂4-5；
所述的成膜剂由以下重量份的原料制得：
原料组成硼化钒2-4、交联剂TAC2-3、双十四碳醇酯4-5、过氧化环己酮1-2、苯乙烯3-4、丙烯腈1-2、二甲苯8-10、丙二醇12-13；
制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得。
所述的热固化导热散热涂料的制备方法，其特征在于包括以下步骤：将二正辛基-4-异噻唑啉-3-酮、云母粉、衣康酸酯、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯混合，加入到二甲苯与乙酸乙酯混合溶剂中，搅拌，加热至110-120℃，反应60-90分钟，然后，加入乙烯基三(β-甲氧基乙氧基)硅烷、二异丙基乙醇胺、安息香、丁醇，继续反应30-40分钟，然后，加入其它剩余成分，继续反应90-120分钟，研磨除渣即得。
本发明施工时，散热涂料喷涂施工，在180-200℃下高温烘干30-50分钟，即可成膜，得到散热涂层。
本发明采用二正辛基-4-异噻唑啉-3-酮，增加了涂料的防霉性能，长期存放，不会变质产生异味。
本发明具有耐老化，粘结力大，散热效果好，可以在200℃下长期使用，而力学性能不变的优点。
具体实施方式
一种热固化导热散热涂料，由下列重量份（公斤）的原料制成：
有机硅树脂32、三聚氰胺甲醛树脂14、二甲苯21、乙酸乙酯26、丁醇10、氮化铝粉末26、二氨基二苯基甲烷3、二异丙基乙醇胺5、安息香1、二正辛基-4-异噻唑啉-3-酮2、云母粉15、衣康酸酯4、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯3、乙烯基三(β-甲氧基乙氧基)硅烷3、成膜剂4；
所述的成膜剂由以下重量份（公斤）的原料制得：
原料组成硼化钒4、交联剂TAC2、双十四碳醇酯5、过氧化环己酮1、苯乙烯4、丙烯腈2、二甲苯10、丙二醇13；制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得。
热固化导热散热涂料的制备方法，包括以下步骤：将二正辛基-4-异噻唑啉-3-酮、云母粉、衣康酸酯、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯混合，加入到二甲苯与乙酸乙酯混合溶剂中，搅拌，加热至110-120℃，反应60-90分钟，然后，加入乙烯基三(β-甲氧基乙氧基)硅烷、二异丙基乙醇胺、安息香、丁醇，继续反应30-40分钟，然后，加入其它剩余成分，继续反应90-120分钟，研磨除渣即得。
将本发明涂料涂于LED灯壳体上，在80℃和300W紫外光辐照条件下人工加速老化试验，耐老化时间4800小时，耐温高温250℃，粘结剪切力20MPa.，导热系数280W/（m·K）。

Claims (1)

1.一种热固化导热散热涂料，其特征在于由下列重量份的原料制成：有机硅树脂32-35、三聚氰胺甲醛树脂12-14、二甲苯21-23、乙酸乙酯24-26、丁醇8-10、氮化铝粉末26-28、二氨基二苯基甲烷2-3、二异丙基乙醇胺4-5、安息香1-2、二正辛基-4-异噻唑啉-3-酮1-2、云母粉12-15、衣康酸酯4-6、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯3-5、乙烯基三(β-甲氧基乙氧基)硅烷2-3、成膜剂4-5；
所述的成膜剂由以下重量份的原料制得：原料组成硼化钒2-4、交联剂TAC2-3、双十四碳醇酯4-5、过氧化环己酮1-2、苯乙烯3-4、丙烯腈1-2、二甲苯8-10、丙二醇12-13；制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得；
　所述的热固化导热散热涂料的制备方法，包括以下步骤：将二正辛基-4-异噻唑啉-3-酮、云母粉、衣康酸酯、异丙基二油酸酰氧基（二辛基磷酸酰氧基）钛酸酯混合，加入到二甲苯与乙酸乙酯混合溶剂中，搅拌，加热至110-120℃，反应60-90分钟，然后，加入乙烯基三(β-甲氧基乙氧基)硅烷、二异丙基乙醇胺、安息香、丁醇，继续反应30-40分钟，然后，加入其它剩余成分，继续反应90-120分钟，研磨除渣即得。
CN201310243293.1A 2013-06-19 2013-06-19 一种热固化导热散热涂料及其制备方法 Expired - Fee Related CN103351807B (zh)