CN103351745A - 一种外墙涂料及其制备方法 - Google Patents

一种外墙涂料及其制备方法 Download PDF

Info

Publication number
CN103351745A
CN103351745A CN2013102476126A CN201310247612A CN103351745A CN 103351745 A CN103351745 A CN 103351745A CN 2013102476126 A CN2013102476126 A CN 2013102476126A CN 201310247612 A CN201310247612 A CN 201310247612A CN 103351745 A CN103351745 A CN 103351745A
Authority
CN
China
Prior art keywords
parts
film
minute
add
rev
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102476126A
Other languages
English (en)
Inventor
魏明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Original Assignee
CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd filed Critical CHUZHOU MAISITE NEW BUILDING MATERIAL Co Ltd
Priority to CN2013102476126A priority Critical patent/CN103351745A/zh
Publication of CN103351745A publication Critical patent/CN103351745A/zh
Pending legal-status Critical Current

Abstract

一种外墙涂料，它是由下述重量份的原料组成的：水性丙烯酸乳液95-100、钛白粉30-60、苯丙乳液6-10、泡花碱2-3、一缩二丙二醇2-4、六偏磷酸钠1-2、乙二醇乙醚0.8-1、碳化钨1-2、氧化铝1-2、2-(3，4-环氧环己基)乙基三甲氧基硅烷0.8-1、二甲基硅油0.1-0.2、成膜助剂3-4、去离子水10-20；本发明生产的涂料原料损失少、凝胶生成少、工艺简单、漆膜坚硬、光泽度好、抗冲击力强，不容易开裂，质感柔和，装饰性强、有高耐侯性、耐刷洗性、附着力强，使用寿命长、无特殊气味，不含汞、铅等重金属，无甲醛挥发物，符合环保涂料的技术要求，加入的成膜助剂具有很高的稳定性、高效粘合性、成膜性，增加了涂层膜的致密度，改善了成膜质量，使得膜层具有附着力强，无空洞、裂陷，致密均匀等优点。

Description

一种外墙涂料及其制备方法
技术领域
    本发明主要涉及一种涂料，尤其涉及一种外墙涂料及其制备方法。
背景技术
近年来，随着人民生活水平的提高以及社会的不断发展，人们对建筑装饰性涂料的选择日益重视，对涂料的施工要求越简单越好，对于特别是在外墙涂料中，已不仅仅停留在最基本的对底材的保护上，对涂料的装饰效果提出了更高的要求，外墙涂料要求有抗水性能，要求有自涤性，漆膜要硬而平整，脏污一冲就掉。
但目前国内市场上投放的丙烯酸涂料存在光泽低、附着力差、耐寒性差，不耐水、水蒸气、酸碱、盐溶液以及有机极性溶剂，室温下的弹性差、耐磨性差等缺点，且高温易返粘、低温易脆裂，导致涂料容易开裂、剥落，雨水等容易渗入墙面、腐蚀墙体，这不但影响建筑物的装饰美观，而且将降低建筑物的使用寿命。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种漆膜稳定、光泽度好、耐受性强的外墙涂料及其制备方法。
本发明是通过以下技术方案实现的：
一种外墙涂料，它是由下述重量份的原料组成的：
水性丙烯酸乳液95-100、钛白粉30-60、苯丙乳液6-10、泡花碱2-3、一缩二丙二醇2-4、六偏磷酸钠1-2、乙二醇乙醚0.8-1、碳化钨1-2、氧化铝1-2、2-(3，4- 环氧环己基) 乙基三甲氧基硅烷0.8-1、二甲基硅油0.1-0.2、成膜助剂3-4、去离子水10-20；
所述的成膜助剂是由下述重量份的原料组成的：
纳米二氧化硅30-40、聚乙烯醇4-6、乙烯基三乙氧基硅烷6-10、烷基酚聚氧烯醚0.8-1、苯丙乳液3-4、纳米碳1-2；
将聚乙烯醇加入到4-5倍水中，蒸汽加热至95-100℃，搅拌溶解，加入苯丙乳液，降低温度为60-70℃，恒温搅拌3-4分钟，加入剩余各原料，低速300-400转/分分散2-3分钟，100-120℃保温静置1-2小时，冷却至常温，即得所述成膜助剂。
一种外墙涂料的制备方法，包括以下步骤：
将上述重量份的氧化铝加入到一缩二丙二醇中，在温度为80-90℃下搅拌分散3-4分钟，加入六偏磷酸钠、苯丙乳液，400-500转/分搅拌6-8分钟，升高温度至90-100℃，滴加乙二醇乙醚，边滴加边搅拌，滴加完毕后降低至常温；加入水性丙烯酸乳液、去离子水，900-1000转/分搅拌8-10分钟；再加入钛白粉、碳化钨、泡花碱，在700-800转/分搅拌15-20分钟；加入剩余各原料，在500-700转/分的速度下，充分搅拌，加入乙酸或者乙酸钠，调节PH为8-9，搅拌均匀即为所述外墙涂料。
本发明的优点是：
本发明生产的涂料原料损失少、凝胶生成少、工艺简单、漆膜坚硬、光泽度好、抗冲击力强，不容易开裂，质感柔和，装饰性强、有高耐侯性、耐刷洗性、附着力强，使用寿命长、无特殊气味，不含汞、铅等重金属，无甲醛挥发物，符合环保涂料的技术要求，加入的成膜助剂具有很高的稳定性、高效粘合性、成膜性，增加了涂层膜的致密度，改善了成膜质量，使得膜层具有附着力强，无空洞、裂陷，致密均匀等优点。
具体实施方式
实施例1
一种外墙涂料，它是由下述重量份(公斤)的原料组成的：
水性丙烯酸乳液100、钛白粉50、苯丙乳液10、泡花碱3、一缩二丙二醇4、六偏磷酸钠1、乙二醇乙醚1、碳化钨1、氧化铝2、2-(3，4- 环氧环己基) 乙基三甲氧基硅烷0.8、二甲基硅油0.2、成膜助剂4、去离子水20；
所述的成膜助剂是由下述重量份的原料组成的：
纳米二氧化硅40、聚乙烯醇6、乙烯基三乙氧基硅烷10、烷基酚聚氧烯醚0.8、苯丙乳液4、纳米碳2；
将聚乙烯醇加入到5倍水中，蒸汽加热至100℃，搅拌溶解，加入苯丙乳液，降低温度为70℃，恒温搅拌4分钟，加入剩余各原料，低速400转/分分散2分钟，120℃保温静置2小时，冷却至常温，即得所述成膜助剂。
一种外墙涂料的制备方法，包括以下步骤：
将上述重量份的氧化铝加入到一缩二丙二醇中，在温度为90℃下搅拌分散3分钟，加入六偏磷酸钠、苯丙乳液， 500转/分搅拌8分钟，升高温度至100℃，滴加乙二醇乙醚，边滴加边搅拌，滴加完毕后降低至常温；加入水性丙烯酸乳液、去离子水， 1000转/分搅拌10分钟；再加入钛白粉、碳化钨、泡花碱，在800转/分搅拌20分钟；加入剩余各原料，在700转/分的速度下，充分搅拌，加入乙酸或者乙酸钠，调节PH为9，搅拌均匀即为所述外墙涂料。
性能测试：
漆膜外观饱满、平整、无硬块、光泽度好；
耐洗刷性试验：10000 次通过，漆膜无破损；
耐人工老化性试验：2000小时不起泡、不剥落、无裂纹；
耐温变性（5次循环）：无异常；
耐碱性：200小时无异常。

Claims (2)

1.一种外墙涂料，其特征在于它是由下述重量份的原料组成的：
水性丙烯酸乳液95-100、钛白粉30-60、苯丙乳液6-10、泡花碱2-3、一缩二丙二醇2-4、六偏磷酸钠1-2、乙二醇乙醚0.8-1、碳化钨1-2、氧化铝1-2、2-(3，4- 环氧环己基) 乙基三甲氧基硅烷0.8-1、二甲基硅油0.1-0.2、成膜助剂3-4、去离子水10-20；
所述的成膜助剂是由下述重量份的原料组成的：
纳米二氧化硅30-40、聚乙烯醇4-6、乙烯基三乙氧基硅烷6-10、烷基酚聚氧烯醚0.8-1、苯丙乳液3-4、纳米碳1-2；
将聚乙烯醇加入到4-5倍水中，蒸汽加热至95-100℃，搅拌溶解，加入苯丙乳液，降低温度为60-70℃，恒温搅拌3-4分钟，加入剩余各原料，低速300-400转/分分散2-3分钟，100-120℃保温静置1-2小时，冷却至常温，即得所述成膜助剂。
2.一种如权利要求1所述的外墙涂料的制备方法，其特征在于包括以下步骤：
将上述重量份的氧化铝加入到一缩二丙二醇中，在温度为80-90℃下搅拌分散3-4分钟，加入六偏磷酸钠、苯丙乳液，400-500转/分搅拌6-8分钟，升高温度至90-100℃，滴加乙二醇乙醚，边滴加边搅拌，滴加完毕后降低至常温；加入水性丙烯酸乳液、去离子水，900-1000转/分搅拌8-10分钟；再加入钛白粉、碳化钨、泡花碱，在700-800转/分搅拌15-20分钟；加入剩余各原料，在500-700转/分的速度下，充分搅拌，加入乙酸或者乙酸钠，调节PH为8-9，搅拌均匀即为所述外墙涂料。
CN2013102476126A 2013-06-20 2013-06-20 一种外墙涂料及其制备方法 Pending CN103351745A (zh)