CN103351616A - 抗老化pa-pps塑料合金 - Google Patents

抗老化pa-pps塑料合金 Download PDF

Info

Publication number
CN103351616A
CN103351616A CN2013102956852A CN201310295685A CN103351616A CN 103351616 A CN103351616 A CN 103351616A CN 2013102956852 A CN2013102956852 A CN 2013102956852A CN 201310295685 A CN201310295685 A CN 201310295685A CN 103351616 A CN103351616 A CN 103351616A
Authority
CN
China
Prior art keywords
pps
aging
parts
shells
plastic alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102956852A
Other languages
English (en)
Other versions
CN103351616B (zh
Inventor
黄美蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN CITY PUBLIC A NEW MATERIAL TECHNOLOGY CO., LTD.
Original Assignee
Shanghai Qiucheng New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Qiucheng New Material Technology Co Ltd filed Critical Shanghai Qiucheng New Material Technology Co Ltd
Priority to CN201310295685.2A priority Critical patent/CN103351616B/zh
Publication of CN103351616A publication Critical patent/CN103351616A/zh
Application granted granted Critical
Publication of CN103351616B publication Critical patent/CN103351616B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗老化PA-PPS塑料合金,由下述组分按重量份组成:20-40份PA、50-70份PPS、6-14份相容剂、0.5-1.5份抗老化剂。本发明的抗老化PA-PPS塑料合金,克服聚苯硫醚冲击强度低,耐弯折性差的缺点,提高材料的冲击韧性,且具有优秀的热老化性能,适合在极端高温环境下使用。本发明的PA-PPS塑料合金可以用于:连接器、开关、定时计外壳、线轴断电器、照相机、整流器外壳等电子电器;仪表板、视镜外壳、轮圈盖、后挡风板等汽车配件;机具外壳、马达盖、水量计器等工业零件。

Description

抗老化PA-PPS塑料合金
技术领域
本发明涉及一种塑料合金,尤其涉及一种抗老化PA-PPS塑料合金。
背景技术
PPS树脂(丙烯腈-苯乙烯-丁二烯共聚物,PPS是Acrylonitrile ButadieneStyrene的首字母缩写)是一种强度高、韧性好、易于加工成型的热塑型高分子材料结构。
聚苯硫醚,全称为聚亚苯基硫醚,英文名称为Polyphenylene sulfide,简称PPS。PPS的分子结构比较简单,分子主链由苯环和硫原子交替排列,大量的苯环赋予PPS以刚性,大量的硫醚键又提供柔顺性。它具有硬而脆、结晶度高、难燃、热稳定性好、机械强度较高、电性能优良等优点。
PA-PPS塑料合金,弱酸强酸、弱碱强碱条件下都为优秀,并具良加工安定性、机械性能优异、耐热性高、具自熄性、耐水性良好、电气特性佳、成形收缩率小。
然而,目前的PA-PPS塑料合金抗老化性能并不佳。
发明内容
针对现有技术中存在的上述不足,本发明所要解决的技术问题是提供一种抗老化PA-PPS塑料合金,具有良好的抗老化性能。
本发明所要解决的技术问题是通过如下技术方案实现的:
一种抗老化PA-PPS塑料合金,由下述组分按重量份组成:20-40份PA、50-70份PPS、6-14份相容剂、0.5-1.5份抗老化剂。
所述抗老化剂,由下述组分按重量份组成:30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
4,4’-硫代双(6-叔丁基-3-甲基苯酚),CAS号:96-69-5,英文名:4,4'-Thio-bis(6-tert-butyl-m-methyl phenol)。
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷,CAS号:1843-03-4,4,4',4''-(1-methyl-1-propanyl-3-ylidene)tris[2-(1,1-dimethylethyl)-5-methyl-Phenol。
硫代二丙酸双十八醇酯,英文名:Distearyl thiodipropionate,CAS号:693-36-7。
将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯搅拌混合均匀,即可制得该抗老化剂。
所述相容剂为POE-g-MAH、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-Pa6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
可以采用本行业通用方法进行制备本发明的抗老化PA-PPS塑料合金,例如:按配比称取各组分,混合均匀后,熔融混炼、挤出造粒,即获得所述抗老化PA-PPS塑料合金。
具体的,可以为按配比称取各组分,在混合机中,室温下控制转速在300-400转/分钟,混合5-10分钟,取出后转入螺杆挤出机中,在160-220℃温度下挤出造粒,即获得所述抗老化PA-PPS塑料合金。
显然,在本发明中为提高产品的其他性能,还可以适应性地添加其他助剂,如阻燃剂、着色剂和抗静电剂等。
发明人通过大量实验得出,将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯三种抗老化剂进行合理复配使用,协同增效,抗老化效果明显。
本发明的抗老化PA-PPS塑料合金,克服聚苯硫醚冲击强度低,耐弯折性差的缺点,提高材料的冲击韧性,且具有优秀的热老化性能,适合在极端高温环境下使用。
本发明的PA-PPS塑料合金可以用于:连接器、开关、定时计外壳、线轴断电器、照相机、整流器外壳等电子电器;仪表板、视镜外壳、轮圈盖、后挡风板等汽车配件;机具外壳、马达盖、水量计器等工业零件。
具体实施方式
实施例1
按照表1中对应实施例1数据称取各原料。将各组分加入到高速混合机中,室温下控制转速在350转/分钟,混合8分钟,取出后转入螺杆挤出机中,在200℃温度下挤出造粒,获得抗老化PA-PPS塑料合金。
表1:抗老化PA-PPS塑料合金配方表  单位:公斤
实施例1 实施例2 实施例3 实施例4
PA树脂 30 30 30 30
PPS树脂 60 60 60 60
相容剂SEBS-g-MAH 10 10 10 10
4,4’-硫代双(6-叔丁基-3-甲基苯酚) 0.4 0.8 / 0.5
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷 0.4 / 0.8 0.5
硫代二丙酸双十八醇酯 0.2 0.2 0.2 /
PA树脂选用美国杜邦公司牌号101L的PA66树脂;
PPS树脂选用日本东丽公司牌号A503的PPS树脂。
实施例2-4
分别按照表1中对应实施例2-4数据称取各原料。采用实施例1所述的方法制备所述抗老化PA-PPS塑料合金。
测试例1
根据热氧老化实验标准GB/T7141-2008,对制得的塑料进行人工加速老化实验(90℃,500h),并分别测定该塑料人工加速老化前后的拉伸强度、悬臂梁缺口冲击强度。
拉伸强度保持率=(人工加速老化后的拉伸强度-人工加速老化前的拉伸强度)÷人工加速老化前的拉伸强度×100%。
冲击强度保持率=(人工加速老化后的悬臂梁缺口冲击强度-人工加速老化前的悬臂梁缺口冲击强度)÷人工加速老化前的悬臂梁缺口冲击强度×100%。
表2:塑料抗老化性能测试表(90℃,500h)
拉伸强度保持率,% 悬臂梁缺口冲击强度保持率,%
实施例1 82.4 81.8
实施例2 81.6 80.4
实施例3 81.9 80.7
实施例4 81.2 80.6

Claims (4)

1.一种抗老化PA-PPS塑料合金,其特征在于,由下述组分按重量份组成:20-40份PA、50-70份PPS、6-14份相容剂、0.5-1.5份抗老化剂。
2.如权利要求1所述的抗老化PA-PPS塑料合金,其特征在于,所述抗老化剂,由下述组分按重量份组成:30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
3.如权利要求1所述的抗老化PA-PPS塑料合金,其特征在于:所述相容剂为POE-g-MAH、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-Pa6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
4.如权利要求3所述的抗老化PA-PPS塑料合金,其特征在于:所述相容剂为SEBS-g-MAH。
CN201310295685.2A 2013-07-15 2013-07-15 抗老化pa-pps塑料合金 Expired - Fee Related CN103351616B (zh)