CN103334562A - 一种应力装饰板及其制备方法 - Google Patents
一种应力装饰板及其制备方法 Download PDFInfo
- Publication number
- CN103334562A CN103334562A CN2012101570075A CN201210157007A CN103334562A CN 103334562 A CN103334562 A CN 103334562A CN 2012101570075 A CN2012101570075 A CN 2012101570075A CN 201210157007 A CN201210157007 A CN 201210157007A CN 103334562 A CN103334562 A CN 103334562A
- Authority
- CN
- China
- Prior art keywords
- long filament
- stress
- glue
- top layer
- unsaturated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种应力装饰板及其制备方法,其特征在于:一种应力装饰板由表层和底层组成,其中表层为不饱和树脂与食用明矾按重量份数比为1:0.03,底层为三层相同的材料,由不饱和树脂:云母粉:应力粉按重量份数比1:0.34:1.2真空反应后顶层覆盖侵过胶的长丝涤纶布,底层上粘一层侵过胶的长丝涤纶里子布,再粘一层侵过胶的长丝涤纶面布,在长丝涤纶面布上涂附表层。其将不饱和树脂、应力粉、云母粉与长丝涤纶布有效的结合,拥有抗冲击连导性、整体性、美观性,能取代现有市场地板、地砖、瓷砖、理石及家具所使用的材料。
Description
技术领域
本发明涉及一种应力装饰板及其制备方法,属于一种新型装潢材料技术领域。
背景技术
在传统的装饰装潢中对木制建材与石质建材过渡依赖,但这两种材料都存在缺陷,木质材料,在使用中会出现变形、开裂、膨胀、收缩等物理现象;石质材料容易存在对人体有害的元素,对人体造成危害。
发明内容
本发明的目的是提供一种应力装饰板及其制备方法,其将不饱和树脂、应力粉、云母粉与长丝涤纶布有效的结合,拥有抗冲击连导性、整体性、美观性,能取代现有市场地板、地砖、瓷砖、理石及家具所使用的材料。
本发明的技术方案是这样实现的:一种应力装饰板及其制备方法,其特征在于:一种应力装饰板由表层和底层组成,其中表层为不饱和树脂与食用明矾按重量份数比为1:0.03,底层为三层相同的材料,由不饱和树脂:云母粉:应力粉按重量份数比1: 0.34 : 1.2真空反应后顶层覆盖浸过胶的长丝涤纶布,固化后的底层上粘一层浸过胶的长丝涤纶里子布,再粘一层浸过胶的长丝涤纶面布,在长丝涤纶面布上涂附表层。
所述的一种应力装饰板的制备方法如下:1)首先将底层的原料不饱和树脂:云母粉:应力粉按重量份数比1: 0.34 : 1.2进行混合,加入促进剂二甲基苯胺4%搅拌均匀后再加入固化剂氧化乙酮2%搅拌均匀,在真空下进行固化反应,混合物由液态至固态需要的反应时间为20分钟,由固态至简单强化需要的反应时间为4小时,常温状态下强化时间需要3天;强化完成后将浸过胶的长丝涤纶布覆盖在混合物上,使其与长丝涤纶布充分结合,将三层相同的合成材料即覆有长丝涤纶布的混合物进行导制,使底层成为一体,每层的厚度为0.1公分;2)在导制好的底层上涂附一层浸过胶的长丝涤纶里子布,再粘一层浸过胶的长丝涤纶面布;3)最后在长丝涤纶面布上淋涂不饱和树脂与食用明矾按重量份数比为1:0.03混合均匀后加入促进剂二甲基苯胺4%搅拌均匀后再加入固化剂氧化乙酮2%搅拌均匀制成的表层,淋涂表层后用高压聚脂绝缘膜覆盖,排除表层内的气泡,固化后脱去高压聚脂绝缘膜。
本发明的积极效果是取代了木材、石材的大量使用,节约资源、保护环境,在为室内进行装饰美化的同时,不对环境造成破坏;其通过淋涂、绝氧、镀漆的方式,使材料的平坦度、光洁度、密度及强度均得以提高。
附图说明
图1为本发明的结构层面图。
具体实施方式
下面结合附图和实施例对本发明做进一步的描述:如图1所示,一种应力装饰板由表层1和底层2组成,其中表层1为不饱和树脂与食用明矾按重量份数比为1:0.03,底层2为三层相同的材料,由不饱和树脂:云母粉:应力粉按重量份数比1: 0.34 : 1.2真空反应后顶层覆盖浸过胶的长丝涤纶布3,底层2上粘一层浸过胶的长丝涤纶里子布4,再粘一层浸过胶的长丝涤纶面布5,在长丝涤纶面布上涂附表层1。
实施例1
首先将不饱和树脂:云母粉:应力粉按重量份数1: 0.34 : 1.2的比例混合搅拌,加入促进剂二甲基苯胺4%搅拌均匀再加入固化剂氧化乙酮2%搅拌均匀后,在真空状态下进行反应,混合物由液态至固态需要的反应时间为20分钟,由固态至简单强化需要的反应时间为4小时,常温状态下强化时间需要3天;按每米 5公斤拉平,强化完成后将浸过胶的长丝涤纶布覆盖在混合物;重复此顺序铺垫达到三层,每层的厚度为0.1公分;之后在导制好的底层上涂附一层浸过胶的长丝涤纶里子布,再粘一层浸过胶的长丝涤纶面布;最后在长丝涤纶面布上淋涂不饱和树脂与食用明矾按重量份数比为1:0.03混合均匀后,加入促进剂二甲基苯胺4%搅拌均匀再加入固化剂氧化乙酮2%搅拌均匀后制成的表层,淋涂表层后用高压聚脂绝缘膜覆盖,排除表层内的气泡,固化后脱去高压聚脂绝缘膜。
Claims (2)
1.一种应力装饰板及其制备方法,其特征在于:一种应力装饰板由表层和底层组成,其中表层为不饱和树脂与食用明矾按重量份数比为1:0.03,底层为三层相同的材料,由不饱和树脂:云母粉:应力粉按重量份数比1: 0.34 : 1.2真空反应后顶层覆盖侵过胶的长丝涤纶布,底层上粘一层侵过胶的长丝涤纶里子布,再粘一层侵过胶的长丝涤纶面布,在长丝涤纶面布上涂附表层。
2.根据权利要求1中所述的一种应力装饰板及其制备方法,其特征在于所述的一种应力装饰板的制备方法如下:1)首先将底层的原料不饱和树脂:云母粉:应力粉按重量份数比1: 0.34 : 1.2进行混合,加入促进剂二甲基苯胺4%搅拌均匀后再加入固化剂氧化乙酮2%搅拌均匀,在真空下进行固化反应,混合物由液态至固态需要的反应时间为20分钟,由固态至简单强化需要的反应时间为4小时,常温状态下强化时间需要3天;强化完成后将浸过胶的长丝涤纶布覆盖在混合物上,使其与长丝涤纶布充分结合,将三层相同的合成材料即覆有长丝涤纶布的混合物进行导制,使底层成为一体,每层的厚度为0.1公分;2)在导制好的底层上涂附一层浸过胶的长丝涤纶里子布,再粘一层浸过胶的长丝涤纶面布;3)最后在长丝涤纶面布上淋涂不饱和树脂与食用明矾按重量份数比为1:0.03混合均匀后加入促进剂二甲基苯胺4%搅拌均匀后再加入固化剂氧化乙酮2%搅拌均匀制成的表层,淋涂表层后用高压聚脂绝缘膜覆盖,排除表层内的气泡,固化后脱去高压聚脂绝缘膜。