CN103333515B - A kind of resin tempering raised table and production technique thereof - Google Patents
A kind of resin tempering raised table and production technique thereof Download PDFInfo
- Publication number
- CN103333515B CN103333515B CN201310281337.XA CN201310281337A CN103333515B CN 103333515 B CN103333515 B CN 103333515B CN 201310281337 A CN201310281337 A CN 201310281337A CN 103333515 B CN103333515 B CN 103333515B
- Authority
- CN
- China
- Prior art keywords
- expects
- stir
- mould
- expect
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of resin tempering raised table and production technique thereof, comprise the raw material of following weight part: A expects: unsaturated polyester 100 parts; B expects: silica powder 50-70 part; C expects: concentration is 2000pg/ml promotor 8-15 part; D expects: solidifying agent 3-8 part; E expects: 04# glasscloth; F expects: refractory fiber cotton.First A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould molding to be implanted; Before injection bottom mould, add D material, become mixture G, the G of 50% is injected mould and spread and expect the first layer into E, spread again into F material, repave and expect into second layer E, reinject 50% G, use upper strata mold clamp.Deburring, cleaning are carried out in rear taking-up of having shaped, and pack after the assay was approved.The present invention is inexpensive, manufactures and does not limit by type shape, thickness and style, and color is random, high temperature resistant less than 100 DEG C, low temperature resistant less than-50 DEG C not modification, do not break, do not contain any nuisance, clean Environmental Safety.
Description
Technical field
The invention belongs to chemical technology field, particularly relate to a kind of resin tempering raised table, relate to the making method of this resin tempering raised table simultaneously.
Background technology
Raised table, as the term suggests there is the sheet material of embossment or openwork carving on surface exactly.Have a variety of material, general have plasterboard, ceramic plate, plank, glass, high-grade any have grouan, marmorean, more high-grade is exactly copper, surface gold-plating etc.
Raised table is applicable to high-rise building balcony protective grating, corridor protective grating, passage protective grating, channel protection hurdle, common bridge guardrail, isolated column, mountain pass path protective grating, garden protective grating, pond, Hua Chi, garden, lawn protective grating.But due to the difference of raised table material and purposes, people, when choice for use raised table, always cannot accomplish both to have ensured at a low price, to ensure high-quality again.
No. 196 lower shrinkage unsaturated polyesters, it is a kind of thermosetting resin, when its heat or initiator effect under, curablely become a kind of insoluble polymer network polymer do not melted, but this polymer machinery epistasis is very low, the requirement that major part uses can not be met, when becoming a kind of matrix material with during glass fiber reinforcement, outward appearance opaque white color thick liquid, viscosity is 0.4-0.8pa.s, and acid number is 8-14min, and solid content is 63%-65%, characteristic is thousand classification lower shrinkage, and its linear shrinkage is 7 ‰.
Ultrafine quartz powder is mainly used in the industries such as chemical industry, electronics, coating, resin, rubber, pottery, glue paste.For in modified resin based composites, its performance can be improved comprehensively, improve intensity, toughness, unit elongation, smooth finish, anti-aging.
Glass fibre woven roving is when reasonable selection resin and model formula, there is withstand voltage, corrosion-resistant, anti-aging, long service life, lightweight, intensity is high, antiseepage, the feature such as heat insulation, nontoxic and smooth surface, can oil be widely used in, chemical industry, weaving, printing and dyeing, electric power, food, brewage, synthetic, plumbing, sea water desaltination, the industry such as water conservancy irrigation.Be easy to be infiltrated for resin, and ply adhesion is good, can be applicable to various curved surface, operating efficiency is high, acid and alkali-resistance, resistance to chemical attack.
Summary of the invention
The object of the invention is to overcome above-mentioned shortcoming and a kind of resin tempering raised table of both having ensured the quality of products cheap provided.
Another object of the present invention is to the making method that this resin tempering raised table is provided.
Object of the present invention and solve its technical problem underlying and realize by the following technical solutions:
A kind of resin tempering raised table of the present invention, comprises the raw material of following weight part:
A expects: unsaturated polyester 100 parts;
B expects: silica powder 50-70 part;
C expects: concentration is 2000pg/ml promotor 8-15 part;
D expects: solidifying agent 3-8 part;
E expects: 04# glass fibre;
F expects: refractory fiber cotton.
The making method of resin tempering raised table of the present invention, comprises the following steps:
(1) first A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould to be implanted.
(2) D material stirs, and becomes mixture G, the G of 50% is injected mould and spreads and expect the first layer into E, spread again and expect one deck (thickness is 30-50 silk) into F, repave and expect into second layer E, reinject 50% G, inject and rear use upper strata mold clamp.
(3) after curing molding, deburring, cleaning are carried out in taking-up, pack after the assay was approved.
Above-mentioned whole shot process must complete at 3-5 minutes.
The present invention compared with prior art, there is obvious beneficial effect, as can be known from the above technical solutions: the present invention utilizes unsaturated polyester for main raw material, be used for improving the quality of raised table, rational formula and making method, make product be provided with inexpensive guarantee simultaneously.Manufacture of the present invention does not limit by type shape, thickness and style, color is random, and technique essence bears elegance, expressive force is strong, high temperature resistant less than 100 DEG C, low temperature resistant less than-50 DEG C not modification, do not break, cause damage under by powerful surging force, rupture event is netted, be not separated and come off, nonflammable, do not soak, in the same industry, never someone attempts in the present invention, not containing any nuisance, and clean Environmental Safety.
Embodiment
Below in conjunction with preferred embodiment, to a kind of resin tempering raised table proposed according to the present invention and production technique embodiment, feature and effect thereof, be described in detail as follows.
Embodiment 1:
The formula of resin tempering raised table and a making method, comprise following:
(1) A material: unsaturated polyester 100 parts; B expects: silica powder 50 parts; C expects: the promotor of concentration 2000pg/ml 8 parts; D expects: 3 parts, solidifying agent; E expects: 04# glasscloth; F expects: refractory fiber cotton.
(2) first A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould to be implanted, D expects to stir, become mixture G, the G of 50% is injected mould and spread into E material the first layer, spread again into F material (thickness is 30-50 silk), repave and expect into second layer E, reinject 50% G, inject after uses upper strata mold clamp.
(3) after curing molding, deburring, cleaning are carried out in taking-up, pack after the assay was approved.
Note: whole shot process completed at 3-5 minutes.
Embodiment 2:
The formula of resin tempering raised table and a making method, comprise following:
(1) A material: unsaturated polyester 100 parts; B expects: silica powder 60 parts; C expects: the promotor of concentration 2000pg/ml 11 parts; D expects: 5 parts, solidifying agent; E expects: 04# glasscloth; F expects: refractory fiber cotton.
(2) first A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould to be implanted.Before injection bottom mould, add D material stir, become mixture G, the G of 50% is injected mould and spread and expect the first layer into E, spread again into F material (thickness is 30-50 silk), repave and expect into second layer E, reinject 50% G, inject and use upper strata mold clamp afterwards.
(3) after curing molding, deburring, cleaning are carried out in taking-up, pack after the assay was approved.
Note: whole shot process completed at 3-5 minutes.
Embodiment 3:
The formula of resin tempering raised table and a making method, comprise following:
(1) A material: unsaturated polyester 100 parts; B expects: silica powder 70 parts; C expects: concentration is 2000pg/ml promotor 15 parts; D expects: 8 parts, solidifying agent; E expects: 04# glasscloth; F expects: refractory fiber cotton.。
(2) first A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould to be implanted.D expects, becomes mixture G, the G of 50% is injected mould and spreads and expect the first layer into E, spread again into F material (thickness is 30-50 silk), repave and expect into second layer E, reinject 50% G, inject and rear use upper strata mold clamp.
(3) after curing molding, deburring, cleaning are carried out in taking-up, pack after the assay was approved.
Note: whole shot process completed at 3-5 minutes.
The present invention utilizes unsaturated polyester for main raw material, is used for improving the quality of raised table, and reasonably formula and making method, make product be provided with inexpensive guarantee simultaneously.Manufacture of the present invention does not limit by type shape, thickness and style, color is random, and technique essence bears elegance, expressive force is strong, high temperature resistant less than 100 DEG C, low temperature resistant less than-50 DEG C not modification, do not break, cause damage under by powerful surging force, rupture event is netted, be not separated and come off, nonflammable, do not soak, in the same industry, never someone attempts in the present invention, not containing any nuisance, and clean Environmental Safety.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, anyly do not depart from technical solution of the present invention content, the any simple modification done above embodiment according to technical spirit of the present invention, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (1)
1. a resin tempering raised table, is characterized in that: its material prescription weight proportion is as follows:
A expects: unsaturated polyester 100 parts;
B expects: silica powder 50-70 part;
C expects: concentration is 2000pg/ml promotor 8-15 part;
D expects: solidifying agent 3-8 part;
E expects: 04# glass fibre;
F expects: refractory fiber cotton;
Its production technique, comprises the following steps:
(1) first A material is expected to carry out mixing and stirring with B, limit edged to stir; Then add C material, stir simultaneously, wait mould to be implanted;
(2) before injection bottom mould, add D material to stir, become mixture G, the G of 50% is injected mould and spread and expect the first layer into E, spreading again into thickness is the F material of 30-50 silk, repaves and expect into second layer E, reinject 50% G, inject and use upper strata mold clamp afterwards;
(3) after curing molding, deburring, cleaning are carried out in taking-up, pack after the assay was approved;
Whole shot process must complete at 3-5 minutes above.