CN105032595A - Polymer composite table concentrator face - Google Patents
Polymer composite table concentrator face Download PDFInfo
- Publication number
- CN105032595A CN105032595A CN201510361855.1A CN201510361855A CN105032595A CN 105032595 A CN105032595 A CN 105032595A CN 201510361855 A CN201510361855 A CN 201510361855A CN 105032595 A CN105032595 A CN 105032595A
- Authority
- CN
- China
- Prior art keywords
- polymer composite
- table surface
- formula
- diamond dust
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polymer composite table concentrator face, and relates to concentrating table components, in particular to the polymer composite table concentrator face and a manufacturing method thereof. The polymer composite table concentrator face can overcome defects in the prior art, and is smooth and flat and resistant to wear, and a gel coat resin layer cannot blister and fall off, so that the service life of the table concentrator face is prolonged by one to two times, and the recycling rate is improved by 10% to 20% compared with the recycling rate of a common table concentrator face. According to the formula of table concentrator face material manufacturing, the polymer composite table concentrator face comprises, by weight, 30% to 40% of unsaturated polyester resin, 2% to 3% of an accelerant, 4% to 5% of a curing agent, 15% to 20% of high impact polystyrene, 10% to 20% of polyethylene terephthalate and 22% to 29% of brown aluminum oxide silicon carbide.
Description
Technical field
The present invention relates to a kind of cleaning table assembly, shaking table surface of especially a kind of pbz polymer composite and preparation method thereof.
Background technology
The shaking table of ore dressing is mainly for the treatment of tungsten, aluminium, coloured, rare and precious metal ore.Effectively sorting particle size range is 3 ~ 0.019 millimeters, how to improve tabling efficiency and service life, be related to make full use of resource and reduce production cost, successively a lot of improvement and research were carried out to shaking table surface for a long time, include shaking table surface shape and arrangement form, existing bed surface by connector and mylar by shape, fiberglass, filler and riffling entirety connect together; The fiberglass of bed surface is composited by unsaturated-resin, glass fibre, mixed with resin inserts, through repeatedly repairing, after appearance spray paint, just need can reach bright and clean, smooth requirement.And in use, surface, under the flushing, corrosion of sludge, water, is understood large area very soon and is come off, cause the ore in sand form of precipitation to pile up, block.In order to address this problem, the steelframe layer of shaking table surface is had to be included among glass fiber resin layer, covering resin mixing inserts on the glass fiber resin layer of shaking table working face; It is coated with again and stacks gradually formed gel coat protective layer by gel coating resin, surperficial felt, glass fibre.The made disposable stripping forming of bed surface; the problem that comes off solving shaking table surface in theory; but use and find again: because gel coat protective layer contains surperficial felt and glass fibre; add in manufacture and be mixed into a small amount of air unavoidably man-hour; time has been grown gel coat protective layer and will bubble and cause coming off; mixed with resin inserts is not wear-resisting in addition, and service life is not long.
Summary of the invention
Technical problem to be solved by this invention is: provide a kind of polymer composite table surface, the deficiencies in the prior art can be overcome, bed surface not only any surface finish, smooth, and it is wear-resisting, gel coating resin layer can not bubble and come off, make to improve 1-2 the service life of bed surface doubly, the rate of recovery improves 10%-20% compared to common bed surface.
The technical solution adopted for the present invention to solve the technical problems is: a kind of polymer composite table surface, and its making the material of table formula is: unsaturated polyester resin 30%-40%, promoter 2%-3%, curing agent 4%-5%, high impact polystyrene 15%-20%, polyethylene terephthalate 10%-20%, Brown Alundum diamond dust 22%-29%
Preparation method of the present invention comprises following several step:
A, first shaking table surface die surface is coated with cured layer, be evenly coated with and stick with paste on cured layer surface, thickness is 0.2 ~ 1mm, normal temperature cure 10 ~ 30 minutes;
B, with covering on gel coating resin layer by the resin of the deployed pbz polymer composite of each component content material and diamond dust in formula;
C, put into steelframe layer concora crush reinforce, then with glass fiber resin layer covering secure, abundant normal temperature cure in more than 6 hours;
F, mould and product to be departed from, be namely made into macromolecule compound shaking table surface.
The invention has the beneficial effects as follows: gel coating resin layer of the present invention, in even, continuous print glue-line, there is the gloss on surface, simultaneously, there is good water-fast, chemically-resistant, corrosion-resistant, wear-resisting, anti-deformation, the performance such as shock-resistant, weather-proof, reach specious and practical purpose.Repairing, lacquer spraying technique can be simplified, directly reduce fiberglass cleaning table and make, repair cost, improve recovery rate in ore-dressing, extend the service life of fiberglass cleaning table.
Detailed description of the invention
Embodiment one
A kind of polymer composite table surface, its making the material of table formula is: unsaturated polyester resin 30%, promoter 3%, curing agent 4.5%, high impact polystyrene 20%, polyethylene terephthalate 13.5%, Brown Alundum diamond dust 29%
Preparation method of the present invention comprises following several step:
A, first shaking table surface die surface is coated with cured layer, be evenly coated with and stick with paste on cured layer surface, thickness is 0.2 ~ 1mm, normal temperature cure 10 ~ 30 minutes;
B, with covering on gel coating resin layer by the resin of the deployed pbz polymer composite of each component content material and diamond dust in formula;
C, put into steelframe layer concora crush reinforce, then with glass fiber resin layer covering secure, abundant normal temperature cure in more than 6 hours;
F, mould and product to be departed from, be namely made into macromolecule compound shaking table surface.
Embodiment two
A kind of polymer composite table surface, its making the material of table formula is: unsaturated polyester resin 40%, promoter 2%, curing agent 4%, high impact polystyrene 15%, polyethylene terephthalate 10%, Brown Alundum diamond dust 29%
Preparation method of the present invention comprises following several step:
A, first shaking table surface die surface is coated with cured layer, be evenly coated with and stick with paste on cured layer surface, thickness is 0.2 ~ 1mm, normal temperature cure 10 ~ 30 minutes;
B, with covering on gel coating resin layer by the resin of the deployed pbz polymer composite of each component content material and diamond dust in formula;
C, put into steelframe layer concora crush reinforce, then with glass fiber resin layer covering secure, abundant normal temperature cure in more than 6 hours;
F, mould and product to be departed from, be namely made into macromolecule compound shaking table surface.
Embodiment three
A kind of polymer composite table surface, its making the material of table formula is: unsaturated polyester resin 35%, promoter 2.3%, curing agent 5%, high impact polystyrene 15.7%, polyethylene terephthalate 20%, Brown Alundum diamond dust 22%
Preparation method of the present invention comprises following several step:
A, first shaking table surface die surface is coated with cured layer, be evenly coated with and stick with paste on cured layer surface, thickness is 0.2 ~ 1mm, normal temperature cure 10 ~ 30 minutes;
B, with covering on gel coating resin layer by the resin of the deployed pbz polymer composite of each component content material and diamond dust in formula;
C, put into steelframe layer concora crush reinforce, then with glass fiber resin layer covering secure, abundant normal temperature cure in more than 6 hours;
F, mould and product to be departed from, be namely made into macromolecule compound shaking table surface.
Claims (5)
1. a polymer composite table surface, its making the material of table formula is: unsaturated polyester resin 30%-40%, promoter 2%-3%, curing agent 4%-5%, high impact polystyrene 15%-20%, polyethylene terephthalate 10%-20%, Brown Alundum diamond dust 22%-29%.
2. polymer composite table surface according to claim 1, is characterized in that: its making the material of table formula is: unsaturated polyester resin 30%, promoter 3%, curing agent 4.5%, high impact polystyrene 20%, polyethylene terephthalate 13.5%, Brown Alundum diamond dust 29%.
3. polymer composite table surface according to claim 1, is characterized in that: its making the material of table formula is: unsaturated polyester resin 40%, promoter 2%, curing agent 4%, high impact polystyrene 15%, polyethylene terephthalate 10%, Brown Alundum diamond dust 29%.
4. polymer composite table surface according to claim 1, is characterized in that: its making the material of table formula is: unsaturated polyester resin 35%, promoter 2.3%, curing agent 5%, high impact polystyrene 15.7%, polyethylene terephthalate 20%, Brown Alundum diamond dust 22%.
5. according to the manufacture method of the polymer composite table surface one of claim 1-4 Suo Shu, it is characterized in that: preparation method comprises following several step:
A, first shaking table surface die surface is coated with cured layer, be evenly coated with and stick with paste on cured layer surface, thickness is 0.2 ~ 1mm, normal temperature cure 10 ~ 30 minutes;
B, cover on gel coating resin layer with the resin containing polymer composite and diamond dust deployed by each component content material in formula;
C, put into steelframe layer concora crush reinforce, then with glass fiber resin layer covering secure, abundant normal temperature cure in more than 6 hours;
F, mould and product to be departed from, be namely made into macromolecule compound shaking table surface.