CN103333430A - 一种耐腐蚀的软质聚氯乙烯塑料及其制备方法 - Google Patents
一种耐腐蚀的软质聚氯乙烯塑料及其制备方法 Download PDFInfo
- Publication number
- CN103333430A CN103333430A CN2013102540122A CN201310254012A CN103333430A CN 103333430 A CN103333430 A CN 103333430A CN 2013102540122 A CN2013102540122 A CN 2013102540122A CN 201310254012 A CN201310254012 A CN 201310254012A CN 103333430 A CN103333430 A CN 103333430A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant soft
- soft pvc
- corrosion resistant
- pvc plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种耐腐蚀的软质聚氯乙烯塑料及其制备方法,包括以下重量份计的组分:聚氯乙烯25-50份、阻燃增塑剂10-12份、抗氧剂1~20份、内润滑剂0.3~1份、着色剂10~20份、阻燃剂2~8份。本发明阻燃性高、具有良好的抗氧化作用,硬度适中、外观美观,耐火性强。
Description
技术领域
本发明涉及塑胶领域,尤其涉及一种耐腐蚀的软质聚氯乙烯塑料及其制备方法。
背景技术
塑料是以合成树脂为主要成份,并加入其它的添加剂,一定温度和压力下塑化成型的高分子合成材料,经过化学反应合成,合成的塑料是由许多较小而结构简单的小分子,由共价键来组合而成的。塑料的种类繁多,一般若是以对热之变化来分类,它可以分为两大类:热固性塑料加热后,会使分子构造结合成网状型态,一但结合成网状聚合体,即使再加热也不会软化;热塑性塑料加热后会熔化,可流动至模具冷却后成型,再加热后又会熔化的塑料,即可运用加热及冷却,使其产生[可逆变化](液态←→固态),是所谓的物理变化。而热塑性塑料又可再区分为泛用塑料、泛用工程塑料、高性能工程塑料等三类。根据制成成分的调整,可以调整软硬度,本发明提供了一软质聚氯乙烯塑料。聚氯乙烯塑料是由氯乙烯单体聚合而成的,是常用的热塑性塑料之一。它的商品名称简称为“氯塑”,英文缩写为PVC。 纯聚氯乙烯树脂是坚硬的热塑性物质,其分解温度与塑化温度极为接近,而且机械强度较差。因此,无法用聚氯乙烯树脂来塑制产品,必须加入增塑剂、稳定剂、填 料等以改善性能,制成聚氯乙烯塑料,然后再加工成各类产品。聚氯乙烯,根据加入增塑剂量的多少分为硬质聚氯乙烯和软质聚氯乙烯。软质聚氯乙烯一般含增塑剂30—50%。由于质地柔软,强度较高;具有良好的气密性和不透水性;但是其耐化学腐蚀性能好。
发明内容
本发明提供了一种软质聚氯乙烯塑料及其制备方法,具有良好的耐腐蚀性能。
本发明采用以下技术方案:
一种耐腐蚀的软质聚氯乙烯塑料,包括以下重量份计的组分:
聚氯乙烯25-50份、
阻燃增塑剂10-12份、
抗氧剂1~20份、
内润滑剂0.3~1份、
着色剂10~20份、
阻燃剂2~8份、
二氯异氰尿酸钠2~5份、
三乙醇胺1~2份、
硅藻土1~2份、
二乙基二硫代氨基甲酸钠0.4~0.6份、
硬脂酸镁3~4份。
加入阻燃增塑剂的目的是为了降低软质聚氯乙烯塑料的可燃性,保证其安全,为了使软质聚氯乙烯塑料具有更好的阻燃性,阻燃增塑剂优选邻苯二甲酸酯类增塑剂或磷酸酯类增塑剂或二者的混合,邻苯二甲酸酯类增塑剂和磷酸酯类增塑剂的重量比优选1:1。阻燃增塑剂还可以是磷酸酯或氯化石蜡。
加入抗氧剂的目的是为了避免PVC在加工使用过程中,因受热、紫外线的作用发生氧化,为了使抗氧化剂与游离基结合,形成稳定的化合物,使连锁反应终止,最好选用双酚A作为抗氧剂。本发明在选用双酚A作为抗氧剂时,可以加入亚磷酸三苯酯与亚磷酸苯二异辛酯作为辅助抗氧剂,主辅抗氧剂并用可发挥协同作用。
为了减少聚合物分子链之间的摩擦力,加入了内润滑剂进行润滑,润滑剂用量太多,会起霜并影响制品的强度及高频焊接和印刷性;而润滑剂太少则会粘辊,选择0.5~0.8份的润滑剂最为适宜。内润滑剂优选单甘酯。
着色剂优选酞菁红、铬黄、镉黄、荧光黄、酞菁蓝、酞菁绿、钛白粉、碳黑的一种或多种。
掺入阻燃剂的目的是增加其耐火焰性。阻燃剂优选氯化石蜡、三氧化二锑、磷酸酯中的一种。
上述的软质聚氯乙烯塑料的制备方法:将各组分按所述比例混合均匀后,导入加热筒中,熔融完全,熔融温度是150~230℃;注入于闭合模具,固化后,再开启模具取出成品。
本发明软化点高温高达150℃,在200℃左右开始分解,而低温冲击脆化温度则零下50℃左右,具有很好的耐高温、耐低温性能,不易腐蚀,老化后的断裂伸长率在20左右,性能稳定。
具体实施方式
下面通过具体实施例进一步说明本发明。
实施例1
一种耐腐蚀的软质聚氯乙烯塑料,包括以下重量份计的组分:聚氯乙烯30份、阻燃增塑剂11份、双酚A和亚磷酸三苯酯(重量比10:1)10份、单甘酯0.8份、着色剂15份、阻燃剂5份、二氯异氰尿酸钠2份、三乙醇胺1份、硅藻土1份、二乙基二硫代氨基甲酸钠0.4份、硬脂酸镁3份。
阻燃增塑剂是重量比是1:1的邻苯二甲酸酯类增塑剂和磷酸酯类增塑剂,着色剂是酞菁红。阻燃剂是氯化石蜡。
上述的软质聚氯乙烯塑料的制备方法:将各组分按所述比例混合均匀后,导入加热筒中,熔融完全,熔融温度是150℃;注入于闭合模具,固化后,再开启模具取出成品。
实施例2
一种耐腐蚀的软质聚氯乙烯塑料,包括以下重量份计的组分:聚氯乙烯25份、阻燃增塑剂10份、双酚A1份、单甘酯0.3份、着色剂10份、阻燃剂2份、二氯异氰尿酸钠5份、三乙醇胺2份、硅藻土2份、二乙基二硫代氨基甲酸钠0.6份、硬脂酸镁4份。
阻燃增塑剂是邻苯二甲酸酯类增塑剂。着色剂铬黄和镉黄。阻燃剂是三氧化二锑。
将各组分按所述比例混合均匀后,导入加热筒中,熔融完全,熔融温度是230℃;注入于闭合模具,固化后,再开启模具取出成品。
实施例3
一种耐腐蚀的软质聚氯乙烯塑料,包括以下重量份计的组分:聚氯乙烯50份、阻燃增塑剂12份、双酚A20份、单甘酯1份、着色剂20份、阻燃剂8份、二氯异氰尿酸钠3份、三乙醇胺1.5份、硅藻土1.5份、二乙基二硫代氨基甲酸钠0.5份、硬脂酸镁3.5份。
阻燃增塑剂是磷酸酯类增塑剂。着色剂是碳黑的。阻燃剂是磷酸酯。
将各组分按所述比例混合均匀后,导入加热筒中,熔融完全,熔融温度是200℃;注入于闭合模具,固化后,再开启模具取出成品。
实施例的产品的性能参数如下:
性能 | 测试条件 | 实施例1 | 实施例2 | 实施例3 |
相对密度g/cm2 | 1.20 | 1.21 | 1.22 | |
邵氏硬度度 | 78 | 75 | 76 | |
拉伸强度Mpa | 15.0 | 16 | 17 | |
拉伸强度 | 老化后(100℃±2℃*168M) | 28 | 26 | 24 |
断裂伸长率% | 240 | 250 | 245 | |
断裂伸长率 | 老化后(100℃*168M) | 22 | 20 | 19 |
维卡软化点℃ | 150.0 | 150.5 | 151.2 | |
低温冲击脆化温度℃ | -53℃ | -56℃ | -58℃ |
Claims (8)
1.一种耐腐蚀的软质聚氯乙烯塑料,其特征在于包括以下重量份计的组分:聚氯乙烯25-50份、阻燃增塑剂10-12份、抗氧剂1~20份、内润滑剂0.3~1份、着色剂10~20份、阻燃剂2~8份、二氯异氰尿酸钠2~5份、三乙醇胺1~2份、硅藻土1~2份、二乙基二硫代氨基甲酸钠0.4~0.6份、硬脂酸镁3~4份。
2.根据权利要求1所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:所述的阻燃增塑剂是邻苯二甲酸酯类增塑剂或磷酸酯类增塑剂或二者的混合物。
3.根据权利要求1所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:所述的抗氧剂包括双酚A。
4.根据权利要求3所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:所述的抗氧剂还包括亚磷酸三苯酯与亚磷酸苯二异辛酯。
5.根据权利要求1所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:所述的内润滑剂为0.5~0.8重量份的单甘酯。
6.根据权利要求1所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:着色剂为酞菁红、铬黄、镉黄、荧光黄、酞菁蓝、酞菁绿、钛白粉、碳黑的一种或多种。
7.根据权利要求1所述的耐腐蚀的软质聚氯乙烯塑料,其特征在于:阻燃剂为氯化石蜡、三氧化二锑、磷酸酯中的一种。
8.根据权利要求1-7任一项所述的耐腐蚀的软质聚氯乙烯塑料的制备方法,其特征在于包括以下步骤:将各组分按所述比例混合均匀后,导入加热筒中,熔融完全,熔融温度是150~230℃;注入于闭合模具,固化后,再开启模具取出成品。