CN103332956A - 发泡建筑混凝土及其生产方法 - Google Patents

发泡建筑混凝土及其生产方法 Download PDF

Info

Publication number
CN103332956A
CN103332956A CN2013102323046A CN201310232304A CN103332956A CN 103332956 A CN103332956 A CN 103332956A CN 2013102323046 A CN2013102323046 A CN 2013102323046A CN 201310232304 A CN201310232304 A CN 201310232304A CN 103332956 A CN103332956 A CN 103332956A
Authority
CN
China
Prior art keywords
concrete
cement
building concrete
kilogram
kilograms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102323046A
Other languages
English (en)
Inventor
郑先平
段祥君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhenjiang Yinxin New Building Material Technology Co Ltd
Original Assignee
Zhenjiang Yinxin New Building Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhenjiang Yinxin New Building Material Technology Co Ltd filed Critical Zhenjiang Yinxin New Building Material Technology Co Ltd
Priority to CN2013102323046A priority Critical patent/CN103332956A/zh
Publication of CN103332956A publication Critical patent/CN103332956A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种发泡建筑混凝土，包括水泥、粉煤灰、石灰和发泡剂，每100公斤水泥中还混合有10-20公斤的四氧化三铁。本发明的发泡建筑混凝土的配制方法简单，在使用时加水和掺合料混合成混凝土砂浆，加入四氧化三铁、鼓入发泡剂制成发泡混凝土砖，制成的混凝土砖根据粉煤灰和石灰的配合比其表观密度在650～800公斤/立方米，但具体较高的强度和硬度，抗压强度达到10-20MPa。

Description

发泡建筑混凝土及其生产方法
技术领域
本发明涉及建筑用材料技术领域，尤其是一种发泡建筑混凝土及其生产方法。
 
背景技术
建筑材料是建筑工程的物质基础，建筑物从主体结构到装饰装修施工中需要用到各种材料。混凝土是一种耐久性材料，其主要成分包括水泥、掺合物和骨料，加水搅拌后硬化而成，具有工艺简单、防火性能等优点。发泡混凝土又名泡沫混凝土，是通过智通发泡系统发泡，并将泡沫与水泥浆均匀混合，然后经过泵送系统进行现浇施工或模具成型，经自然养护所形成的一种含有大量封闭气孔的新型轻质保温材料。它属于气泡状绝热材料，突出特点是在混凝土内部形成封闭的气孔，成蜂窝型紧密均匀排列气孔，使混凝土轻质化和多达五倍隔热保温性能。耐火性能高，低吸水量（防潮），低导温性质及环保特性，比其它隔温材料更具优势。干体积密度为400-700kg/m3，相当于普通水泥混凝土的1/3 ～ 1/6 左右，可减轻建筑物整体荷载。减少基建成本，极大的节约了建筑费用，但是抗压强度为0.6-5.5MPa，而普通的混凝土达到40-60MPa，其抗压强度低，导致其不能用于承重位置，也就限制了发泡混凝土的运用。
 
发明内容
本发明要解决的技术问题是：克服现有技术中发泡混凝土抗压强度不高的技术问题，提供一种发泡建筑混凝土，提高混凝土的抗压强度。
本发明解决其技术问题所采用的技术方案是：一种发泡建筑混凝土，包括水泥、粉煤灰、石灰和发泡剂，每100公斤水泥中还混合有10-20公斤的四氧化三铁。四氧化三铁能提高粉煤灰、石灰与水泥之间的粘合牢度，以提高混凝土强度和硬度。
每100公斤水泥中还混合有1-2公斤甲基纤维素。甲基纤维素是一种分散剂，能使四氧化三铁分散均匀，从而更好的发挥四氧化三铁的增强、增硬作用。
一种生产上述发泡建筑混凝土的方法，具有如下步骤：将100公斤水泥投入搅拌装置中；开启搅拌装置，然后向搅拌装置中按所需配合比分批或同时投入粉煤灰和石灰；将10-20公斤的四氧化三铁投入水中搅拌均匀后溶液投入搅拌装置中；待搅拌至砂浆状后鼓入发泡剂；通过泵送装置输送至模具内；再对模具内的混凝土进行蒸气养护。
将1-2公斤甲基纤维素投入水中搅拌。
本发明的有益效果是，本发明的发泡建筑混凝土的配制方法简单，在使用时加水和掺合料混合成混凝土砂浆，加入四氧化三铁、鼓入发泡剂制成发泡混凝土砖，制成的混凝土砖根据粉煤灰和石灰的配合比其表观密度在650～800公斤/立方米，但具体较高的强度和硬度，抗压强度达到10-20MPa。
具体实施方式
本发明的：一种发泡建筑混凝土，包括水泥、粉煤灰、石灰和发泡剂，每100公斤水泥中还混合有10-20公斤的四氧化三铁。四氧化三铁能提高粉煤灰、石灰与水泥之间的粘合牢度，以提高混凝土强度和硬度。每100公斤水泥中加入10公斤四氧化三铁时抗压强度为10MPa，加入20公斤四氧化三铁时抗压强度为20MPa。
每100公斤水泥中还混合有1-2公斤甲基纤维素。甲基纤维素是一种分散剂，能使四氧化三铁分散均匀，从而更好的发挥四氧化三铁的增强、增硬作用。每10公斤四氧化三铁对应添加1公斤甲基纤维素。
一种生产上述发泡建筑混凝土的方法，具有如下步骤：将100公斤水泥投入搅拌装置中；开启搅拌装置，然后向搅拌装置中按所需配合比分批或同时投入粉煤灰和石灰；将10-20公斤的四氧化三铁投入水中搅拌均匀后溶液投入搅拌装置中；待搅拌至砂浆状后鼓入发泡剂；通过泵送装置输送至模具内；再对模具内的混凝土进行蒸气养护。
将1-2公斤甲基纤维素投入水中搅拌。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (4)

1.一种发泡建筑混凝土，包括水泥、粉煤灰、石灰和发泡剂，其特征是：每100公斤水泥中还混合有10-20公斤的四氧化三铁。
2.如权利要求1所述的发泡建筑混凝土，其特征是：每100公斤水泥中还混合有1-2公斤甲基纤维素。
3.一种生产如权利要求1或2所述的发泡建筑混凝土的方法，其特征是具有如下步骤：将100公斤水泥投入搅拌装置中；开启搅拌装置，然后向搅拌装置中按所需配合比分批或同时投入粉煤灰和石灰；将10-20公斤的四氧化三铁投入水中搅拌均匀后溶液投入搅拌装置中；待搅拌至砂浆状后鼓入发泡剂；通过泵送装置输送至模具内；再对模具内的混凝土进行蒸气养护。
4.如权利要求3所述的发泡建筑混凝土的生产方法，其特征是：将1-2公斤甲基纤维素投入水中搅拌。
CN2013102323046A 2013-06-13 2013-06-13 发泡建筑混凝土及其生产方法 Pending CN103332956A (zh)