CN103321098A - 一种新型阻燃纸蜂窝专用阻燃剂及其制备方法 - Google Patents

一种新型阻燃纸蜂窝专用阻燃剂及其制备方法 Download PDF

Info

Publication number
CN103321098A
CN103321098A CN2013101959393A CN201310195939A CN103321098A CN 103321098 A CN103321098 A CN 103321098A CN 2013101959393 A CN2013101959393 A CN 2013101959393A CN 201310195939 A CN201310195939 A CN 201310195939A CN 103321098 A CN103321098 A CN 103321098A
Authority
CN
China
Prior art keywords
fire retardant
retardant
flame
paper honeycomb
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101959393A
Other languages
English (en)
Other versions
CN103321098B (zh
Inventor
赵振宁
赵静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao yinghengda Packaging Co.,Ltd.
Original Assignee
QINGDAO CHIEFEX HONEYCOMB NEW MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO CHIEFEX HONEYCOMB NEW MATERIALS Co Ltd filed Critical QINGDAO CHIEFEX HONEYCOMB NEW MATERIALS Co Ltd
Priority to CN201310195939.3A priority Critical patent/CN103321098B/zh
Publication of CN103321098A publication Critical patent/CN103321098A/zh
Application granted granted Critical
Publication of CN103321098B publication Critical patent/CN103321098B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾K2CO3 2-8重量份,碳酸氢钠NaHCO3 1-3重量份,硅酸钠Na2SiO3 4-8重量份,硼砂Na2B4O7.10H2O1-5重量份,水50-150重量份。本发明在高温下形成二氧化碳CO2不燃性气体和形成玻璃状保护层，从而隔离纸面与火焰，阻止火焰在纸面燃烧、蔓延，窒息火焰；可增加纸的强度和刚性，不吸潮不分解，持久阻燃，性能优异，价格低；测试结果达到GB8624-2006《建筑材料及制品燃烧性能分级》中难燃材料最高级别B级，并与欧盟RoSH指令2002/95EC以及后续修正指令的要求相符，便于推广。

Description

一种新型阻燃纸蜂窝专用阻燃剂及其制备方法
技术领域
本发明涉及一种新型阻燃纸蜂窝专用阻燃剂及其制备方法，属于纸张生产用化学品领域。  
背景技术
新型阻燃纸蜂窝轻质墙材作为一种符合国家宏观政策、产业发展方向，低碳环保、循环经济、可持续发展的新型建筑材料，具有强度高，整体性好，隔音隔热，阻燃防火，抗震防震，施工便捷，缩短工期，提高工效，减小劳动强度，增大空间使用面积、提高得房率，居住环保、清洁、舒适，其优异性日益彰显，越来越被广泛采用，其所用原料是阻燃纸。
通常生产阻燃纸的阻燃剂主要是氮磷系列，卤素系列等，这类阻燃剂有良好的阻燃效果，如APP就是一种使用时间很久，阻燃效果很好，应用广泛，价格合适的一种。但是这种阻燃剂有它严重缺点，易吸潮，阻燃后的纸张变软，强度下降。在光线下或长期暴露在空气中容易分解，阻燃性大大降低，甚至完全失去阻燃性。APP等氨氮类的阻燃剂分子上都含有大量的--NH2和--CN，其化学键的不稳定，极易受到--OH的攻击断裂下来和H+结合形成毒害的NH3↑和剧毒的HCN↑,危害极大。新型阻燃纸蜂窝轻质墙材是一种新开发的建筑材料，阻燃纸在加工成纸蜂窝时使用环保的淀粉胶，配制淀粉胶须用NaOH，而NaOH会水解出--OH，这就决定了阻燃纸蜂窝轻质墙材这个行业不能使用氨氮类阻燃剂。磷系列由于分子结构决定了它严重吸潮性，卤素系列中除溴类还在使用外，由于其毒性早已被禁止使用。这就给出了阻燃纸蜂窝用阻燃纸难以逾越的难题。    
发明内容
    针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种新型阻燃纸蜂窝专用阻燃剂及其制备方法，可增加纸的强度和刚性，不吸潮，不分解，持久阻燃，性能优异，价格低廉，便于推广。
为解决上述技术问题，本发明采取的技术方案是，一种新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾 K2CO3  2-8重量份,碳酸氢钠NaHCO3   1-3重量份,硅酸钠Na2SiO3   4-8重量份,硼砂Na2B4O7.10H2O  1-5重量份, 水50-150重量份。  
优化的，上述新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾 K2CO3  5重量份,碳酸氢钠NaHCO3   2重量份,硅酸钠Na2SiO3   6重量份,硼砂Na2B4O7.10H2O  3重量份, 水100重量份。
一种权利要求1或2所述的新型阻燃纸蜂窝专用阻燃剂的制备方法，其按权利要求1或2所述的重量份配比称取各组分，向配制罐中按配比加入水升温至60-70℃，搅拌均匀配制成13.8%的水溶液即可。
权利要求1或2所述的新型阻燃纸蜂窝专用阻燃剂的应用，将其用于制备具有耐火性能的纸蜂窝。  
本发明与现有技术相比具有以下优点，在高温下并在纸燃烧时形成二氧化碳CO2不燃性气体和形成玻璃状保护层，从而隔离纸面与火焰，阻止火焰在纸面燃烧、蔓延，窒息火焰；本发明的配方可增加纸的强度和刚性，不吸潮，不分解，持久阻燃，性能优异，价格低；测试结果达到GB8624-2006《建筑材料及制品燃烧性能分级》中难燃材料最高级别B级 ，并与欧盟RoSH指令2002/95EC以及后续修正指令的要求相符，便于推广。   
具体实施方式
实施例1
本发明为一种新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾 K2CO3  2重量份,碳酸氢钠NaHCO3   1重量份,硅酸钠Na2SiO3   4重量份,硼砂Na2B4O7.10H2O  1重量份, 水50重量份。 
一种新型阻燃纸蜂窝专用阻燃剂的制备方法，按上述的重量份配比称取各组分，向配制罐中按配比加入水，升温至60-70℃，搅拌均匀，配制成13.8%的水溶液即可。
新型阻燃纸蜂窝专用阻燃剂的应用，将其用于制备具有耐火性能的纸蜂窝。
实施例2
本发明为一种新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾 K2CO3  5重量份,碳酸氢钠NaHCO3   2重量份,硅酸钠Na2SiO3   6重量份,硼砂Na2B4O7.10H2O  3重量份, 水100重量份。 
一种新型阻燃纸蜂窝专用阻燃剂的制备方法，按上述的重量份配比称取各组分，向配制罐中按配比加入水，升温至60-70℃，搅拌均匀，配制成13.8%的水溶液即可。
新型阻燃纸蜂窝专用阻燃剂的应用，将其用于制备具有耐火性能的纸蜂窝。 
实施例3
本发明为一种新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：碳酸钾 K2CO3  8重量份,碳酸氢钠NaHCO3   3重量份,硅酸钠Na2SiO3   8重量份,硼砂Na2B4O7.10H2O  5重量份, 水150重量份，配制成13.8%的水溶液即可。
一种新型阻燃纸蜂窝专用阻燃剂的制备方法，按上述的重量份配比称取各组分，向反应釜中按配比加入水，升温至60-70℃，搅拌均匀，配制成13.8%的水溶液即可。
新型阻燃纸蜂窝专用阻燃剂的应用，将其用于制备具有耐火性能的纸蜂窝。
本发明与现有技术相比具有以下优点，在高温下并在纸燃烧时形成二氧化碳CO2不燃性气体和形成玻璃状保护层，从而隔离纸面与火焰，阻止火焰在纸面燃烧、蔓延，窒息火焰；本发明的配方可增加纸的强度和刚性，不吸潮，不分解，持久阻燃，性能优异，价格低廉，测试结果与欧盟RoSH指令2002/95EC以及后续修正指令的要求相符，便于推广。  
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明的保护范围。

Claims (4)

1.一种新型阻燃纸蜂窝专用阻燃剂，其特征在于：由以下重量份数的原料制成：碳酸钾 K2CO3  2-8重量份,碳酸氢钠NaHCO3   1-3重量份,硅酸钠Na2SiO3                 4-8重量份,硼砂Na2B4O7.10H2O  1-5重量份, 水50-150重量份。
2.根据权利要求1所述的新型阻燃纸蜂窝专用阻燃剂，其特征在于：由以下重量份数的原料制成：碳酸钾 K2CO3  5重量份,碳酸氢钠NaHCO3   2重量份,硅酸钠Na2SiO3   6重量份,硼砂Na2B4O7.10H2O   3重量份, 水100重量份。
3.一种权利要求1或2所述的新型阻燃纸蜂窝专用阻燃剂的制备方法，其特征在于：按权利要求1或2所述的重量份配比称取各组分，向配制罐中按配比加入水，升温至60-70℃，搅拌均匀配制成13.8%的水溶液即可。
4.权利要求1或2所述的新型阻燃纸蜂窝专用阻燃剂的应用，将其用于制备具有耐火性能的纸蜂窝。
CN201310195939.3A 2013-05-24 2013-05-24 一种新型阻燃纸蜂窝专用阻燃剂及其制备方法 Active CN103321098B (zh)