CN103319997A - 一种高阻燃全水发泡聚氨酯外墙喷涂料及其制备方法 - Google Patents
一种高阻燃全水发泡聚氨酯外墙喷涂料及其制备方法 Download PDFInfo
- Publication number
- CN103319997A CN103319997A CN2013100461893A CN201310046189A CN103319997A CN 103319997 A CN103319997 A CN 103319997A CN 2013100461893 A CN2013100461893 A CN 2013100461893A CN 201310046189 A CN201310046189 A CN 201310046189A CN 103319997 A CN103319997 A CN 103319997A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- polyether glycol
- wall spray
- spray material
- polyurethane exterior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高阻燃全水发泡聚氨酯外墙喷涂料及其制备方法，本发明所述聚氨酯外墙喷涂料的阻燃性能很高，保障了房屋外墙的防火安全性。同时本发明所述聚氨酯外墙喷涂料的防水性能很高，长期使用无渗漏现象，而且具有很好的保温隔热效果，使用寿命长。另外由于配方中采用的原料均为无毒害的材料，因而对环境环保无危害。
Description
技术领域
本发明涉及一种外墙喷涂料及其制备方法，特别涉及一种高阻燃全水发泡聚氨酯外墙喷涂料及其制备方法，属于涂料技术领域。
背景技术
当今社会经常会发生因建筑房屋的火灾事故而引发的重大安全问题，给人们的生命财产安全带来极大的危害，造成了很坏的社会影响。其中建筑外墙的防火性能是房屋建筑防火的重要方面，由于现有技术中的外墙喷涂料通常防火性能不佳，遇到火灾引发时常常没有很强的抵御能力，有的遇火反而加剧燃烧，有的涂料在燃烧过程中会产生一些有毒有害物质，这些都会对人们的生命财产造成很严重的后果。因而探索高阻燃、无毒害的建筑外墙涂料是目前涂料领域亟须解决的技术问题。
发明内容
本发明的目的在于克服现有技术中的缺陷，提供一种高阻燃全水发泡聚氨酯外墙喷涂料及其制备方法，所述聚氨酯外墙喷涂料的阻燃性能很高，防水性能优异，保温性能佳。
本发明是通过以下技术方案予以实现的。
一种高阻燃全水发泡聚氨酯外墙喷涂料，所述喷涂料由以下质量配比的组分构成：组合聚醚聚酯︰异氰酸酯=1︰1；
所述组合聚醚聚酯的构成按质量份数计如下：
上述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其中，所述的聚醚多元醇1为聚醚多元醇4110，生产厂家为石家庄亚东石油化工厂。
上述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其中，所述的聚醚多元醇2为聚醚多元醇3628，生产厂家为上海高桥化工厂有限公司。
上述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其中，所述的聚酯多元醇为聚酯多元醇400，生产厂家为张家港南光化工厂。
上述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其中，所述的聚氨酯硅油为AK-8802，生产厂家为南京德美世创化工有限公司。
上述的一种高阻燃全水发泡聚氨酯外墙喷涂料的制备方法，制备步骤如下：首先将聚醚多元醇1、聚醚多元醇2、聚酯多元醇、聚氨酯硅油和水加入反应釜中进行混合反应，搅拌速度80－150r/min，反应时间4－6h，然后再将反应后的混合料与异氰酸酯按1︰1的比例进行混合，即可制得本发明所述的外墙喷涂料。
本发明所述的高阻燃全水发泡聚氨酯外墙喷涂料的阻燃性能很高，保障了房屋外墙的防火安全性。同时本发明所述聚氨酯外墙喷涂料的防水性能很高，长期使用无渗漏现象，而且具有很好的保温隔热效果，使用寿命长。另外由于配方中采用的原料均为无毒害的材料，因而对环境环保无危害。
具体实施方式
实施例1
一种高阻燃全水发泡聚氨酯外墙喷涂料的制备方法，制备步骤如下：首先将25份的聚醚多元醇4110、10份的聚醚多元醇3628、25份的聚酯多元醇400、2份的聚氨酯硅油AK-8802和4份的水加入反应釜中进行混合反应，搅拌速度80r/min，反应时间4h，然后再将反应后的混合料与异氰酸酯按1︰1的比例进行混合，即可制得本发明所述的外墙喷涂料。
实施例2
一种高阻燃全水发泡聚氨酯外墙喷涂料的制备方法，制备步骤如下：首先将28份的聚醚多元醇4110、12份的聚醚多元醇3628、28份的聚酯多元醇400、3份的聚氨酯硅油AK-8802和4.5份的水加入反应釜中进行混合反应，搅拌速度120r/min，反应时间5h，然后再将反应后的混合料与异氰酸酯按1︰1的比例进行混合，即可制得本发明所述的外墙喷涂料。
实施例3
一种高阻燃全水发泡聚氨酯外墙喷涂料的制备方法，制备步骤如下：首先将30份的聚醚多元醇4110、15份的聚醚多元醇3628、30份的聚酯多元醇400、3.5份的聚氨酯硅油AK-8802和5份的水加入反应釜中进行混合反应，搅拌速度150r/min，反应时间6h，然后再将反应后的混合料与异氰酸酯按1︰1的比例进行混合，即可制得本发明所述的外墙喷涂料。
以下为本发明所述高阻燃全水发泡聚氨酯外墙喷涂料的阻燃性能测试结果：
检验标准要求：阻燃材料的燃烧速度应不大于100mm/min,若出现下列情况则分别按要求标识试验结果,检验结果分为A、B、C、D、E 5个等级：
A -（ 0 mm/min）：试样暴露在火焰中15s，熄灭火源试样仍未燃烧，或试样能燃烧，但火焰达到第一测量标线之前熄灭，无燃烧距离可计。
B：从试验计时开始，火焰在60s内自行熄灭，且燃烧距离不大于50mm，则认为满足标准要求。
C - 燃烧速度实测值（mm/min）
从试验计时开始，火焰在两个测量标线之间熄灭，且不满足第2条情况时，则按标准计算燃烧速度。
D - 燃烧速度实测值（mm/min）
从试验计时开始，火焰燃烧到达第二标线，或从计时开始，试样长时间缓慢燃烧，则可以在试验计时20min时终止试验，并记录燃烧时间及燃烧距离且按标准计算燃烧速度。
E：试样在火焰引燃15s内已经燃烧并到达第一标线，则认为试样不能满足燃烧速度的要求。
检验结果：A - C（mm/mi n）。
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。
Claims (6)
1.一种高阻燃全水发泡聚氨酯外墙喷涂料，其特征在于，所述喷涂料由以下质量配比的组分构成：组合聚醚聚酯︰异氰酸酯=1︰1；
所述组合聚醚聚酯的构成按质量份数计如下：
聚醚多元醇1 25－30份
聚醚多元醇2 10－15份
聚酯多元醇 25－30份
聚氨酯硅油 2－3.5份
水 4－5份。
2.如权利要求1所述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其特征在于，所述的聚醚多元醇1为聚醚多元醇4110。
3.如权利要求1所述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其特征在于，所述的聚醚多元醇2为聚醚多元醇3628。
4.如权利要求1所述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其特征在于，所述的聚酯多元醇为聚酯多元醇400。
5.如权利要求1所述的一种高阻燃全水发泡聚氨酯外墙喷涂料，其特征在于，所述的聚氨酯硅油为AK-8802。
6.如权利要求1所述的一种高阻燃全水发泡聚氨酯外墙喷涂料的制备方法，其特征在于，制备步骤如下：首先将聚醚多元醇1、聚醚多元醇2、聚酯多元醇、聚氨酯硅油和水加入反应釜中进行混合反应，搅拌速度80－150r/min，反应时间4－6h，然后再将反应后的混合料与异氰酸酯按1︰1的比例进行混合，即可制得本发明所述的外墙喷涂料。