CN103319803A - 一种高强度pvc木塑塑料 - Google Patents
一种高强度pvc木塑塑料 Download PDFInfo
- Publication number
- CN103319803A CN103319803A CN2013102444375A CN201310244437A CN103319803A CN 103319803 A CN103319803 A CN 103319803A CN 2013102444375 A CN2013102444375 A CN 2013102444375A CN 201310244437 A CN201310244437 A CN 201310244437A CN 103319803 A CN103319803 A CN 103319803A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- wood
- strength
- strength pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种塑料,具体来讲是一种高强度PVC木塑塑料;该塑料包括如下重量份的原料:PVC:80-110份,380um木粉:30-50份,96μm木粉:40-60份,氯化聚乙烯:7-9份,重钙:3-5份,丙烯酸酯类共聚物:1-3份,邻苯二甲酸二辛酯:7-9份,三碱式硫酸铅:2-4份,二碱式硫酸铅:1.0-2.0份,硬质酸铅:0.5-0.7份,硬质酸钙:0.4-0.6份,硬脂酸:0.1-0.3份,石蜡:0.0-0.2份;本发明的PVC木塑塑料采用成熟的技术工艺参数,并经过生产实践生产出了合格的试验产品,具备了产业化生产的基础条件。
Description
技术领域
本发明涉及一种塑料,具体来讲是一种高强度PVC木塑塑料。
背景技术
木塑复合材料是国内外近年蓬勃兴起的一类新型复合材料,指利用聚乙烯、聚丙烯和聚氯乙烯等代替通常的树脂胶粘剂,与超过50%以上的木粉、稻壳、秸秆等废弃的植物纤维混合成新的木质材料,再经挤压、模压、注射成型等塑料加工工艺,生产出的板材或型材。主要用于建材、家具、物流包装等行业。目前,在我国的现有技术中,该产业尚处于初级阶段,现有技术中的木塑复合材料还存在一些缺陷,如:强度不够、韧性不好以及不耐疲劳等缺点,所以如何能够提供一种由我国自主研发的高强度PVC木塑复合材料成为人们迫切的需求。
发明内容
本发明所要解决的技术问题是,克服现有技术困难,提供一种能够生产出高强度、高韧性的高强度PVC木塑塑料。
本发明解决以上技术问题的技术方案:提供一种高强度PVC木塑塑料,该塑料包括如下重量份的原料: PVC:80-110份,380um木粉:30-50份,96μm木粉:40-60份,氯化聚乙烯:7-9份,重钙:3-5份,丙烯酸酯类共聚物:1-3份,邻苯二甲酸二辛酯:7-9份,三碱式硫酸铅:2-4份,二碱式硫酸铅:1.0-2.0份,硬质酸铅:0.5-0.7份,硬质酸钙:0.4-0.6份,硬脂酸:0.1-0.3份,石蜡:0.0-0.2份。
本发明进一步限定的技术方案为:
进一步的,塑料包括如下重量份的原料:PVC:100份,380um木粉:40份,96μm木粉:50份,氯化聚乙烯:8份,重钙:4份,丙烯酸酯类共聚物:2份,邻苯二甲酸二辛酯:8份,三碱式硫酸铅:3份,二碱式硫酸铅:1.5份,硬质酸铅:0.6,硬质酸钙:0.5份,硬脂酸:0.2份,石蜡:0.1份。
进一步的,PVC为平均聚合度1000的PVC。
本发明的有益效果为:本发明的高强度PVC木塑塑料能够充分发挥材料中各组分的优势,克服现有技术中单一材料的缺点,而且成本低廉,提高了材料的附加值。本发明的高强度PVC木塑塑料具有高强度、高弹性、高韧性、耐疲劳等优点,具有优良的综合性能。采用本发明的高强度PVC木塑塑料制得的制品能够再次回收利用,可生物降解,抗冲击强度高、尺寸稳定性好、耐磨、耐火、耐化学腐蚀、不怕虫蛀,兼具木材和塑料的双重加工性。本发明可锯、刨、旋、削、敲击、粘贴和胶合,也可用于挤出、压制、注塑成型,应用范围广、产品种类多、形态结构多样。本发明的高强度PVC木塑塑料采用成熟的技术工艺参数,并经过生产实践生产出了合格的试验产品,具备了产业化生产的基础条件。
具体实施方式
实施例1
一种高强度PVC木塑塑料,包括如下重量份的原料:平均聚合度1000的PVC:100份,380um木粉:40份,96μm木粉:50份,氯化聚乙烯:8份,重钙:4份,丙烯酸酯类共聚物:2份,邻苯二甲酸二辛酯:8份,三碱式硫酸铅:3份,二碱式硫酸铅:1.5份,硬质酸铅:0.6,硬质酸钙:0.5份,硬脂酸:0.2份,石蜡:0.1份。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。
Claims (3)
1.一种高强度PVC木塑塑料,其特征在于:所述塑料包括如下重量份的原料:PVC:80-110份,380um木粉:30-50份,96μm木粉:40-60份,氯化聚乙烯:7-9份,重钙:3-5份,丙烯酸酯类共聚物:1-3份,邻苯二甲酸二辛酯:7-9份,三碱式硫酸铅:2-4份,二碱式硫酸铅:1.0-2.0份,硬质酸铅:0.5-0.7份,硬质酸钙:0.4-0.6份,硬脂酸:0.1-0.3份,石蜡:0.0-0.2份。
2.根据权利要求1所述的高强度PVC木塑塑料,其特征在于:所述塑料包括如下重量份的原料:PVC:100份,380um木粉:40份,96μm木粉:50份,氯化聚乙烯:8份,重钙:4份,丙烯酸酯类共聚物:2份,邻苯二甲酸二辛酯:8份,三碱式硫酸铅:3份,二碱式硫酸铅:1.5份,硬质酸铅:0.6,硬质酸钙:0.5份,硬脂酸:0.2份,石蜡:0.1份。
3.根据权利要求1所述的高强度PVC木塑塑料,其特征在于:所述PVC为平均聚合度1000的PVC。