CN103319118B - 一种利用工业固体废料制作保温隔热板的方法 - Google Patents

一种利用工业固体废料制作保温隔热板的方法 Download PDF

Info

Publication number
CN103319118B
CN103319118B CN201310194865.1A CN201310194865A CN103319118B CN 103319118 B CN103319118 B CN 103319118B CN 201310194865 A CN201310194865 A CN 201310194865A CN 103319118 B CN103319118 B CN 103319118B
Authority
CN
China
Prior art keywords
thermal insulation
calcium silicate
industrial solid
silicate slag
insulation board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310194865.1A
Other languages
English (en)
Other versions
CN103319118A (zh
Inventor
孙俊民
曹钊
杨志杰
张金山
苗瑞平
曹永丹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia University of Science and Technology
High Aluminum Coal Resources Development and Utilization R&D Center of Datang International Power Generation Co Ltd
Original Assignee
Inner Mongolia University of Science and Technology
High Aluminum Coal Resources Development and Utilization R&D Center of Datang International Power Generation Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia University of Science and Technology, High Aluminum Coal Resources Development and Utilization R&D Center of Datang International Power Generation Co Ltd filed Critical Inner Mongolia University of Science and Technology
Priority to CN201310194865.1A priority Critical patent/CN103319118B/zh
Publication of CN103319118A publication Critical patent/CN103319118A/zh
Application granted granted Critical
Publication of CN103319118B publication Critical patent/CN103319118B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明的目的为提供一种利用工业固体废料制作保温隔热板的方法，该方法通过将硅钙渣、粉煤灰及脱硫石膏等原料，按配比经过称重计量—加水搅拌—二次逆流搅拌—制板成型—预先养护—蒸压养护—干燥的工艺流程，得到满足国家标准的各项指标要求的保温隔热板产品。该发明方法具有制作工艺简单、流程稳定、原料成本低廉的特点，同时还可以变废为宝，降低工业固体废物对环境的影响。

Description

一种利用工业固体废料制作保温隔热板的方法
技术领域
本发明涉及一种利用工业固体废料制作保温隔热板的方法，特别是利用硅钙渣、粉煤灰及脱硫石膏工业固废制作保温隔热板的方法，属于工业固体废物资源综合利用领域，尤其是对电力、煤炭及钢铁行业工业固体废物的协同利用。
背景技术
由于我国以煤为主要能源，每年电力用煤量高达4亿吨，因此粉煤灰、硅钙渣及脱硫石膏等燃煤工业固废排放量巨大，固废常年累积，占用大量土地并严重污染区域环境。目前对这些工业固体废物没有很好的综合利用方法。
保温隔热板目前生产所用的原料主要为石英粉、石灰、水泥、增强纤维和助剂等，现今保温隔热板生产企业面临问题为：石英粉、石灰和水泥原料价格高、产品销售价格低，导致企业利润被压缩，寻找价格低廉原材料是这一问题有效解决途径。
发明内容
本发明的目的为提供一种利用工业固体废料制作保温隔热板的方法，以实现工业固体废物的协同综合利用，降低制作成本。
技术方案
本发明方法步骤如下：
（1）保温隔热板原料按重量百分比计：硅钙渣45-55%，水泥10-20%，脱硫石膏7-17%，粉煤灰8-18%，石棉纤维5-15%；
（2）将步骤（1）物料混合，加入搅拌桶中加水调制至固体质量浓度为20-40%，由给料机给入逆流式搅拌机进行二次搅拌，搅拌水温22-30℃，搅拌充分后经过双幅流浆制板机进行预制板成型；
（3）预制板在50-60℃下预先养护8-12小时，之后放入高压反应釜中蒸压养护15-20小时，干燥后得到保温隔热板产品。
所述方法中要求硅钙渣原料中含碱量要小于3%。，若硅钙渣含碱量大于3%，生产出来的保温隔热板表面会产生白色碱点，碱点吸水潮解后会影响保温隔热板强度，故需要在30-40%固体质量浓度下进行水洗数次，直至硅钙渣最终含碱量低于3%。
步骤（3）蒸压养护条件为：温度170-230℃、压力1.2-1.4MPa。
本发明所用硅钙渣含碱量大于3%时，需对硅钙渣原料进行水浸脱碱，使硅钙渣含碱量小于3%。
本发明的特点是：本发明利用硅钙渣、粉煤灰及脱硫石膏等工业固废制作建筑用保温隔热板，充分发挥三种固体废物之间的协同作用，制作工艺简单、流程稳定、成本低廉，生产出来的保温隔热板满足国家标准的各项指标要求，采用本发明技术，可以减小固体废物对环境影响，还能变废为宝，降低目前保温隔热板生产成本。
附图说明
图1为本发明保温隔热板的生产流程图。
具体实施方式
实施例：
硅钙渣、粉煤灰及脱硫石膏都取自内蒙古呼和浩特地区一燃煤电厂，化学成分分别如表1、表2和表3所示。
表1  硅酸钙化学成分
硅钙渣 FeO SiO2 CaO MgO Al2O3 碱 烧减 Fe2O3 合计
含量(%) ＜0.1 22.35 55.76 1.73 3.04 4.0 9.01 1.87 97.76
表2  脱硫石膏化学成分
脱硫石膏 TFe SiO2 CaO MgO Al2O3 SO3 H2O Fe2O3 合计
含量(%) 0.40 2.59 34.30 1.55 0.88 42.31 8.7 0.48 91.21
表3  粉煤灰化学成分
粉煤灰 SiO2 A12O3 TFeO MgO CaO Na2O K2O TiO2 MnO2 P2O5 LOI Total
含量(%) 37.8 48.5 2.27 0.31 3.62 0.15 0.36 1.64 0.012 0.15 4.91 99.76
水泥为市售复合32.5级水泥。
硅钙渣原料中含碱量为4%，在30%固体质量浓度下水洗3次，每次搅拌10分钟，得到最终脱碱后硅钙渣含碱量低于3%，保温隔热板原料重量百分配比为：脱碱硅钙渣占总原料的50%，水泥占15%，脱硫石膏占12%，粉煤灰占13%，石棉纤维占10%。原料按照配方进行称重计量，加入搅拌桶中加水调制至固体浓度30%，由给料机给入逆流式搅拌机进行二次搅拌，搅拌水温24℃，搅拌充分后经过双幅流浆制板机进行预制板成型。预制板在55℃下预先养护8小时，之后放入高压反应釜中在200℃、1.3MPa下蒸压养护17小时，干燥后得到保温隔热板产品。产品性能指标检测结果如表4所示，产品所有指标都满足国家标准JC/T 564.2规定。
表4  保温隔热板产品性能指标

Claims (3)

1.一种利用工业固体废料制作保温隔热板的方法，其特征在于，所述方法步骤如下：
（1）保温隔热板原料按重量百分比计：硅钙渣45-55%，水泥10-20%，脱硫石膏7-17%，粉煤灰8-18%，石棉纤维5-15%；
（2）将步骤（1）物料混合，加入搅拌桶中加水调制至固体质量浓度为20-40%，由给料机给入逆流式搅拌机进行二次搅拌，搅拌水温22-30℃，搅拌充分后经过双幅流浆制板机进行预制板成型；
（3）成型的预制板在50-60℃下预先养护8-12小时，之后放入高压反应釜中蒸压养护15-20小时，干燥后得到保温隔热板产品。
2.根据权利要求1所述的一种利用工业固体废料制作保温隔热板的方法，其特征在于，步骤（3）蒸压养护条件为：温度170-230℃、压力1.2-1.4MPa。
3.根据权利要求1所述的一种利用工业固体废料制作保温隔热板的方法，其特征在于，所用硅钙渣含碱量大于3%时，对硅钙渣原料需进行水洗脱碱处理，使硅钙渣含碱量小于3%。
CN201310194865.1A 2013-05-21 2013-05-21 一种利用工业固体废料制作保温隔热板的方法 Active CN103319118B (zh)