CN103305155A - 一种裱卡胶 - Google Patents
一种裱卡胶 Download PDFInfo
- Publication number
- CN103305155A CN103305155A CN2013102880088A CN201310288008A CN103305155A CN 103305155 A CN103305155 A CN 103305155A CN 2013102880088 A CN2013102880088 A CN 2013102880088A CN 201310288008 A CN201310288008 A CN 201310288008A CN 103305155 A CN103305155 A CN 103305155A
- Authority
- CN
- China
- Prior art keywords
- parts
- attapulgite
- temperature
- borax
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种粘合剂,本发明属于裱卡用粘合剂技术领域。一种裱卡胶组成包括成分质量份:水42.9-83.35,聚乙烯醇5-12,分散剂0.1-0.5,乳化剂0.1-0.2,冰醋酸0.1-2,硼酸0.1-10,硼砂0.1-2,重铬酸钾0.05-0.2,煅烧高岭土,9-20,气相二氧化硅1-5,凹凸棒土1-5,防腐剂0.1-0.2,其制备方法:按质量配比称量水、聚乙烯醇、分散剂、乳化剂、煅烧高岭土、气相二氧化硅、凹凸棒土、硼酸、硼砂、重铬酸钾加入到反应釜中分散均匀之后缓慢升温到95℃,保温1.5小时后,之后降温到40℃用适量的冰醋酸调节pH到4-5,加入计量的防腐剂后即得裱卡胶成品。
Description
技术领域:本发明涉及一种粘合剂,具体地说是属于裱卡用粘合剂技术领域。
背景技术:目前,包装用裱卡量日趋加,越来越多的产品都需要有一个既美观又牢固的包装,但是由于生产水平有限,常用的淀粉型胶水质量参差不齐,粘结强度不高,受潮后容易变形,用这样的粘合剂粘接出来的裱卡硬而脆,而且生产和使用过程中需要工人自己调配,无形中增加了劳动量和生产成本,而且批次之间的质量因工人操作的不同有很大出入,聚乙烯醇缩甲醛胶水虽然粘接强度很好,但是甲醛残留带来的危害影响到使用工人,残留在裱卡中的甲醛还有可能给接触者带来其他的危害。
发明内容:本发明的目的在于提供一种产品质量稳定,性能优良,成本低廉的裱卡胶,从根本上解决该类产品的粘接强度不够,平整度不高,甲醛残留,按本发明生产出来的裱卡胶生产简单、原料易得、成本低廉、储存稳定、有助于我国的包装行业发展。其技术内容是,一种裱卡胶组成包括成分质量份:水42.9-83.35,聚乙烯醇5-12,分散剂0.1-0.5,乳化剂0.1-0.2,冰醋酸0.1-2,硼酸0.1-10,硼砂0.1-2,重铬酸钾0.05-0.2,煅烧高岭土,9-20,气相二氧化硅1-5,凹凸棒土1-5,防腐剂0.1-0.2,其制备方法:按质量配比称量水、聚乙烯醇、分散剂、乳化剂、煅烧高岭土、气相二氧化硅、凹凸棒土、硼酸、硼砂、重铬酸钾加入到反应釜中分散均匀之后缓慢升温到95℃,保温1.5小时后,之后降温到40℃用适量的冰醋酸调节ph到4-5,加入计量的防腐剂后即得裱卡胶成品。
本发明所用水为自来水,聚乙烯醇为PVA24-88,分散剂为5040,乳化剂为TX-10,煅烧高岭土为4000目,所用高重铬酸钾为试剂级,其他原料均为工业级。
本发明和现有技术相比其先进之处在于,该裱卡胶生产简单原料易得,成本低廉,生产设备简单,适用性强,用该裱卡胶生产的纸管具有快干粘结强度高,平整度好,零污染零排放,可在零下5℃以内使用,可以完全取代进口产品,大幅度降低成本。
具体实施方式:其制备方法,按质量配比称量水76.96-87.89,加入到反应釜内,开动搅拌分散装置60r/min,加入分散剂0.2-0.4,乳化剂0.1-0.2,煅烧高岭土9-15,气相二氧化硅1-2,凹凸棒土1-3,硼酸0.5-0.5,硼砂0.1-0.12,重铬酸钾0.01-0.02,分散并缓慢升温到95℃,保温1.5小时,之后降温到40℃用0.1-1.6的冰醋酸调节ph到4-5,加入防腐剂0.1-0.2后即得裱卡胶成品,以上便构成本发明。
Claims (1)
1.一种裱卡胶包括成分质量份:水42.9-83.35,聚乙烯醇5-12,分散剂0.1-0.5,乳化剂0.1-0.2,冰醋酸0.1-2,硼酸0.1-10,硼砂0.1-2,重铬酸钾0.05-0.2,煅烧高岭土,9-20,气相二氧化硅1-5,凹凸棒土1-5,防腐剂0.1-0.2组成,其特征在于:气相二氧化硅1-5,凹凸棒土1-5。