CN103304210B - 高强度无机保温砂浆及其制备方法 - Google Patents
高强度无机保温砂浆及其制备方法 Download PDFInfo
- Publication number
- CN103304210B CN103304210B CN201310234622.6A CN201310234622A CN103304210B CN 103304210 B CN103304210 B CN 103304210B CN 201310234622 A CN201310234622 A CN 201310234622A CN 103304210 B CN103304210 B CN 103304210B
- Authority
- CN
- China
- Prior art keywords
- mortar
- expanded
- high strength
- small ball
- vitrified small
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高强度无机保温砂浆及其制备方法。所述高强度无机保温砂浆包含的各组分及其配比含量如下:每4~8m3容重为80~110Kg/m3的膨胀玻化微珠,对应的其余组分的重量为:普通硅酸盐水泥350~450Kg,粉煤灰250~350Kg,灰钙粉86~162Kg,脱硫石膏50~150Kg,保温砂浆专用胶粉8~15Kg,羟丙基甲基纤维素醚4~7Kg,聚丙烯纤维6~12Kg。制备时,将除膨胀玻化微珠外的各组分一次投料,搅拌;将膨胀玻化微珠加入已搅拌好的粉料中,继续搅拌;包装入库,即可。与现有技术相比,本发明的无机保温砂浆具备良好的保温性能,还具有高抗压强度、高干密度,具备更广泛的市场应用前景。
Description
技术领域
本发明属于建筑保温领域,涉及一种无机保温砂浆,具体涉及一种高强度无机保温砂浆。
背景技术
由于建筑保温材料防火性能要求的升级,无机保温材料成为目前保温材料的主流材料。其中,无机保温砂浆具有A级燃烧等级,成为夏热冬暖地区建筑节能材料的主要产品之一。然而,现有的无机保温砂浆中高强度与优异的保温性能是一对矛盾体,二者往往无法兼顾,要求强度高则要牺牲保温性能;也因如此,在现有的无机砂浆应用领域,在要求无机保温砂浆达到优良的保温性能的同时,对强度的要求并不高;如,国家标准GBT26000-2010《膨胀玻化微珠保温砂浆》的性能指标要求中规定,导热系数≤0.070W/m·K,干密度≤300kg/m3,抗压强度≥0.30MPa。
经对现有技术的文献检索发现,专利号为CN101863639,专利名称为一种用于建筑外墙的无机保温砂浆及其制备方法的发明专利,其以膨胀玻化微珠为轻集料、水泥与粉煤灰为主要粘结材料,并添加一定的添加剂制备而成的无机保温砂浆,具有防火阻燃、抗老化性佳以及较高的抗压强度等优点;然而,其抗压强度为0.4~0.8Mpa,仅稍大于标准,并未真正实现无机保温砂浆的高强度与优异保温性能的统一。专利号为CN101857410,专利名称为单组份无机保温砂浆及其制备方法的发明专利,其采用单组份产品取代传统的双组份生产模式,其导热系数为0.065W/m·K,干表观密度为285kg/m3,抗压强度为0.38Mpa;可见该单组份无机保温砂浆在保温性能复合要求的同时,其强度仅仅是符合行业标准,也进一步说明了在现有的无机保温砂浆中高强度与优异的保温性能是难以兼顾的。
发明内容
本发明的目的在于克服上述现有技术存在的不足,提供一种高强度无机保温砂浆及其制备方法。本发明通过以传统的工业废弃物粉煤灰、脱硫石膏、聚丙烯纤维废料粉为原料,在实现废弃原料利用的同时,通过采取两次加料、一次搅拌的生产方式,能够生产出在既具备良好的保温性能,还具有高抗压强度、高干密度,且性能稳定的高强度无机保温砂浆。
本发明的目的是通过以下技术方案来实现的:
第一方面,本发明涉及一种高强度无机保温砂浆,所包含的各组分及其配比含量如下:
每4~8m3容重为80~110Kg/m3的膨胀玻化微珠,对应的其余组分的重量为:
优选地,所述普通硅酸盐水泥的强度等级大于或等于42.5。
优选地,所述粉煤灰等级为I级或II级。
优选地,所述脱硫石膏粉的规格为为200~325目。
优选地,所述羟丙基甲基纤维素醚的粘度为100000~200000mPa·S。
优选地,所述聚丙烯纤维为200~325目的聚丙烯纤维粉和6~10mm长的聚丙烯纤维丝。聚丙烯纤维粉为聚丙烯纤维废料粉碎后形成的。
优选地,所述膨胀玻化微珠为30~50目。
第二方面,本发明还涉及一种前述的高强度无机保温砂浆的制备方法,包括如下步骤:
第一步,投料、拌合:将所述重量的除膨胀玻化微珠外的各组分一次投料,搅拌3分钟;
第二步,继续投料:将所述膨胀玻化微珠加入第一步中已搅拌好的粉料中,继续搅拌1分钟;包装入库。
与现有技术相比,本发明具有如下有益效果:
1、本发明采用普通硅酸盐水泥为主要胶凝材料,此外还采用工业副产物粉煤灰、脱硫石膏、聚丙烯纤维废料粉等作为掺合料,未采用成本较高的原材料,成本较低;实现了成本与性能的平衡。
2、本发明的无机保温砂浆,不仅具有良好的和易性和施工性,还克服了传统的技术偏见,兼顾了无机保温砂浆优良的保温性能和干密度、抗压强度。
3、现有技术中,大剂量粉煤灰的添加将严重影响无机保温砂浆的强度;本发明通过对粉煤灰、脱硫石膏、灰钙粉和聚丙烯纤维粉等各组分的科学选择和配比,使各组分发挥良好的协效作用,在添加大剂量粉煤灰降低生产成本的同时,实现了高强、保温共存的无机保温砂浆。
具体实施方式
下面结合具体实施例对本发明进行进一步的说明;以下实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式和具体的操作过程,但本发明的保护范围不限于下述实施例。
实施例1~3
实施例1~3中各组分及其重量份如表1所示,其中羟丙基甲基纤维素醚的粘度均为200000mPa·S(也可为100000~200000mPa·S任一粘度);保温砂浆专用胶粉可为市购的保温砂浆专用胶粉,本实施例1~3中采用北京名昂瑞祥2031型保温砂浆专用胶粉;膨胀玻化微珠的容重为100kg/m3(也可为80~110Kg/m3中任一容量)、粒径为30~50目;普通硅酸盐水泥的等级为42.5(也可为大于42.5强度等级的普通硅酸盐水泥);粉煤灰的等级为II级(也可为I级)。
实施例1中脱硫石膏粉为200目,聚丙烯纤维粉为200目,聚丙烯纤维丝为6mm;
实施例2中脱硫石膏粉为250目,聚丙烯纤维粉为300目,聚丙烯纤维丝为9mm;
实施例3中脱硫石膏粉为300目,聚丙烯纤维粉为325目,聚丙烯纤维丝为10mm。
表1
由表1可知,本发明的聚丙烯纤维为200~325目的聚丙烯纤维粉和6~9mm长的聚丙烯纤维丝的组合,二者的质量比优选为2∶1。
将除膨胀玻化微珠外的各组分一次投料,搅拌3分钟;再将所述膨胀玻化微珠加入搅拌机中再次搅拌1分钟;包装入库,以待工地直接按照加水量加水搅拌以备施工;其中,水的添加量为砂浆质量的0.9~1.2倍。
对上述实施例1~3制得的高强度无机保温砂浆按照国家标准GBT26000-2010《膨胀玻化微珠保温砂浆》的要求成型试件,并测试其干密度、导热系数和抗压强度,试验结果如表2所示:
表2
项目 | 国标 | 实施例1 | 实施例2 | 实施例3 |
干密度kg/m3 | ≤300 | 350 | 450 | 550 |
导热系数,W/m·K | ≤0.070 | 0.065 | 0.075 | 0.085 |
抗压强度,MPa | ≥0.30 | 1.2 | 1.9 | 2.8 |
在现有的无机保温砂浆中要求强度高则要牺牲导热系数,而由表2可知,本发明的高强无机保温砂浆在保证了较低的导热系数的同时,具有较高的干密度和抗压强度;其性能远远高于国家标准GBT26000-2010。结合表1可知,本发明的无机保温砂浆中添加了大剂量的粉煤灰;粉煤灰主要是作为胶凝材料的掺合料,本领域公知:在无机保温砂浆中粉煤灰添加量过大影响砂浆强度,因此,在要求提高无机保温砂浆强度的应用场合,通常都是通过减少粉煤灰用量、提高水泥用量来提高强度的,然而水泥用量提高,带来的是导热系数的提高,保温性能下降。本发明采用了大剂量粉煤灰却仍具备良好的强度,其原因在于粉煤灰、脱硫石膏、灰钙粉和聚丙烯纤维粉发挥良好的协同作用,参与水泥的水化反应,提高了砂浆的抗压强度;同时,大剂量粉煤灰中的漂珠和聚丙烯纤维也为保温性能带来补充。
因此,本发明的高强度无机保温砂浆,不仅具有良好的和易性和施工性,还克服了传统的技术偏见,实现了优良的保温性能和强度的统一,具备更广泛的市场应用前景。
以上对本发明的具体实施例进行了描述。需要理解的是,本发明并不局限于上述特定实施方式,本领域技术人员可以在权利要求的范围内做出各种变形或修改,这并不影响本发明的实质内容。
Claims (4)
1.一种高强度无机保温砂浆,其特征在于,由如下配比含量的各组分组成:
每4~8m3容重为80~110Kg/m3的膨胀玻化微珠,对应的其余组分的重量为:
其中,所述聚丙烯纤维为200~325目的聚丙烯纤维粉和6~10mm长的聚丙烯纤维丝,所述羟丙基甲基纤维素醚的粘度为100000~200000mPa·S,所述粉煤灰等级为Ⅰ级或Ⅱ级,所述脱硫石膏的规格为200~325目。
2.根据权利要求1所述的高强度无机保温砂浆,其特征在于,所述普通硅酸盐水泥的强度等级大于或等于42.5。
3.根据权利要求1所述的高强度无机保温砂浆,其特征在于,所述膨胀玻化微珠的规格为30~50目。
4.一种根据权利要求1所述的高强度无机保温砂浆的制备方法,其特征在于,包括如下步骤:
第一步,投料、拌合:将所述重量的除膨胀玻化微珠外的各组分一次投料,搅拌3分钟;
第二步,继续投料:将所述膨胀玻化微珠加入第一步中已搅拌好的粉料中,继续搅拌1分钟;包装入库。