CN103290518A - 有色抗菌涤丙复合超细纤维及生产方法 - Google Patents

有色抗菌涤丙复合超细纤维及生产方法 Download PDF

Info

Publication number
CN103290518A
CN103290518A CN2013101965587A CN201310196558A CN103290518A CN 103290518 A CN103290518 A CN 103290518A CN 2013101965587 A CN2013101965587 A CN 2013101965587A CN 201310196558 A CN201310196558 A CN 201310196558A CN 103290518 A CN103290518 A CN 103290518A
Authority
CN
China
Prior art keywords
parts
fiber
polyester
nickel
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101965587A
Other languages
English (en)
Other versions
CN103290518B (zh
Inventor
余三川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongxiang Laidaobao Home Textile Co., Ltd.
Original Assignee
NINGBO SANBANG HOME PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO SANBANG HOME PRODUCTS CO Ltd filed Critical NINGBO SANBANG HOME PRODUCTS CO Ltd
Priority to CN201310196558.7A priority Critical patent/CN103290518B/zh
Publication of CN103290518A publication Critical patent/CN103290518A/zh
Application granted granted Critical
Publication of CN103290518B publication Critical patent/CN103290518B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种有色抗菌涤丙复合超细纤维，它包括着色超细涤丙复合纤维，所述的超细涤丙复合纤维是以超细丙纶纤维为芯线，外包覆功能性涤纶纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述功能性涤纶是在涤纶的熔体中含有氧化铈纳米粉体材料及由锌、镍、钯组成的纳米粉体材料。本发明得到的有色抗菌涤丙复合超细纤维，既具有丙纶的良好纤维特性，又具有涤纶的良好纤维特性，并且兼具良好的抗菌功能；通过采用具有代表性的抗菌性能测试方法GB15979-2002标准测试，本发明提供的有色抗菌涤丙复合超细纤维，其抗菌率达到99%以上。同时也提高了着色强度和着色稳定性。

Description

有色抗菌涤丙复合超细纤维及生产方法
技术领域
本发明涉及一种纤维的生产技术，特别是一种有色抗菌涤丙复合超细纤维及生产方法。
背景技术
目前涤丙复合超细纤维都是采用超细丙纶纤维和超细涤纶纤维简单加捻而成，这种简单加捻的复合纤维，由于纤维性能的不同，给后处理带来了一定的难度，特别是丙纶和涤纶的着色性能完全不同，给复合纤维的染色带来的很大的难题；另外，对于抗菌纤维，通常在纺丝后的后整理工艺中再进行抗菌涂层的处理，这种抗菌纤维，抗菌时间短，效果差，经不起长期洗涤。
发明内容
本发明的目的是为了解决上述现有技术的不足而提供一种能长期具有抗菌效果，且抗菌效果好，又使着色牢度高的有色抗菌涤丙复合超细纤维及生产方法。
为了实现上述目的，本发明提供的一种有色抗菌涤丙复合超细纤维，它包括超细涤丙复合纤维，其特征是所述的超细涤丙复合纤维是以超细丙纶纤维为芯线，外包覆功能性涤纶纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述功能性涤纶是在按重量计的100份涤纶的熔体中含有氧化铈纳米粉体材料0.01份至0.1份，以对苯二甲酸丁二酯为载体的有色母粒5份至7份，由锌、镍、钯组成的纳米粉体材料0.5份至5份，其中在锌、镍、钯的组成中按重量份计算：锌60份至70份、镍25份至30份、钯5份至10份；所述的纳米粉体材料是粉体粒径达到D90＜0.1um的纳米级粉体材料。
一种有色抗菌涤丙复合超细纤维的生产方法，包括采用上述的有色抗菌涤丙复合超细纤维，其特征是所述功能性涤纶是在按重量计的100份涤纶的熔体中加入重量份的氧化铈纳米粉体材料0.01份至0.1份，以对苯二甲酸丁二酯为载体的有色母粒5份至7份，混熔后再加入重量份的由锌、镍、钯组成的纳米粉体材料0.5份至5份，其中在锌、镍、钯的组成中按重量份计算：锌60份至70份、镍25份至30份、钯5份至10份；充分分散均匀后，在235℃至250℃保持0.5小时而得到；功能性涤纶熔体与丙纶熔体共轭拉丝，并将功能性涤纶包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃, 功能性涤纶的纺丝温度控制在290℃，包覆后的复合纤维直径控制在4微米至1微米。
在此，所述的超细纤维是指纤度0.3旦（直径5微米）以下的纤维。
本发明提供的有色抗菌涤丙复合超细纤维的生产方法所得到的有色抗菌涤丙复合超细纤维，通过对内外包覆结构的设置，复合纤维既具有丙纶的良好纤维特性，又具有涤纶的良好纤维特性，并且兼具良好的抗菌功能；通过采用具有代表性的抗菌性能测试方法GB15979-2002标准测试，本发明提供的有色抗菌涤丙复合超细纤维，其抗菌率达到99%以上。 由于活性物质氧化铈纳米粉体材料的加入，极大地提高了色母粒在涤纶上的着色强度，提高了着色稳定性。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1：
本实施例提供的一种有色抗菌涤丙复合超细纤维，它包括超细涤丙复合纤维，所述的超细涤丙复合纤维是以超细丙纶纤维为芯线，外包覆功能性涤纶纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述功能性涤纶是在按重量计的100份涤纶的熔体中含有氧化铈纳米粉体材料0.01份，以对苯二甲酸丁二酯为载体的有色母粒5份，由锌、镍、钯组成的纳米粉体材料0.5份，其中在锌、镍、钯的组成中按重量份计算：锌60份、镍25份、钯5份；所述的纳米粉体材料是粉体粒径达到D90＜0.1um的纳米级粉体材料。
一种有色抗菌涤丙复合超细纤维的生产方法，包括采用上述的有色抗菌涤丙复合超细纤维，所述功能性涤纶是在按重量计的100份涤纶的熔体中加入重量份的氧化铈纳米粉体材料0.01份，以对苯二甲酸丁二酯为载体的有色母粒5份，混熔后再加入重量份的由锌、镍、钯组成的纳米粉体材料0.5份，其中在锌、镍、钯的组成中按重量份计算：锌60份、镍25份、钯5份；充分分散均匀后，在235℃至250℃保持0.5小时而得到；功能性涤纶熔体与丙纶熔体共轭拉丝，并将功能性涤纶包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃, 功能性涤纶的纺丝温度控制在290℃，包覆后的复合纤维直径控制在4微米至1微米。
本实施例提供的有色抗菌涤丙复合超细纤维通过采用抗菌性能测试方法GB15979-2002标准测试，其抗菌率达到99%以上。通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。
实施例2：
所述功能性涤纶是在按重量计的100份涤纶的熔体中含有氧化铈纳米粉体材料0.1份，以对苯二甲酸丁二酯为载体的有色母粒7份，由锌、镍、钯组成的纳米粉体材料5份，其中在锌、镍、钯的组成中按重量份计算：锌70份、镍25份、钯10份；生产方法同实施例1。
本实施例提供的有色抗菌涤丙复合超细纤维通过采用抗菌性能测试方法GB15979-2002标准测试，其抗菌率达到99.9%以上。通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。
实施例3：
本实施例提供的有色抗菌涤丙复合超细纤维，所述功能性涤纶是在按重量计的100份涤纶的熔体中含有氧化铈纳米粉体材料0.5份，有色母粒6份，由锌、镍、钯组成的纳米粉体材料3份，其中在锌、镍、钯的组成中按重量份计算是：锌70份、镍25、钯8份，生产方法同实施例1。
通过抗菌性能测试，其抗菌率达到99.5%，通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。

Claims (2)

1.一种有色抗菌涤丙复合超细纤维，它包括超细涤丙复合纤维，其特征是所述的超细涤丙复合纤维是以超细丙纶纤维为芯线，外包覆功能性涤纶纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述功能性涤纶是在按重量计的100份涤纶的熔体中含有氧化铈纳米粉体材料0.01份至0.1份，以对苯二甲酸丁二酯为载体的有色母粒5份至7份，由锌、镍、钯组成的纳米粉体材料0.5份至5份，其中在锌、镍、钯的组成中按重量份计算：锌60份至70份、镍25份至30份、钯5份至10份。
2.一种有色抗菌涤丙复合超细纤维的生产方法，包括采用如权利要求1所述的有色抗菌涤丙复合超细纤维，其特征是所述功能性涤纶是在按重量计的100份涤纶的熔体中加入重量份的氧化铈纳米粉体材料0.01份至0.1份，以对苯二甲酸丁二酯为载体的有色母粒5份至7份，混熔后再加入重量份的由锌、镍、钯组成的纳米粉体材料0.5份至5份，其中在锌、镍、钯的组成中按重量份计算：锌60份至70份、镍25份至30份、钯5份至10份；充分分散均匀后，在235℃至250℃保持0.5小时而得到；功能性涤纶熔体与丙纶熔体共轭拉丝，并将功能性涤纶包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃, 功能性涤纶的纺丝温度控制在290℃，包覆后的复合纤维直径控制在4微米至1微米。
CN201310196558.7A 2013-05-24 2013-05-24 有色抗菌涤丙复合超细纤维及生产方法 Active CN103290518B (zh)