CN103276201A - 一种碳钢lf精炼渣的循环利用方法 - Google Patents

一种碳钢lf精炼渣的循环利用方法 Download PDF

Info

Publication number
CN103276201A
CN103276201A CN2013101974228A CN201310197422A CN103276201A CN 103276201 A CN103276201 A CN 103276201A CN 2013101974228 A CN2013101974228 A CN 2013101974228A CN 201310197422 A CN201310197422 A CN 201310197422A CN 103276201 A CN103276201 A CN 103276201A
Authority
CN
China
Prior art keywords
slag
refining
refining slag
carbon steel
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101974228A
Other languages
English (en)
Inventor
仪桂兰
史永林
王建昌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN2013101974228A priority Critical patent/CN103276201A/zh
Publication of CN103276201A publication Critical patent/CN103276201A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种碳钢LF精炼渣的循环利用方法，属于钢渣的利用领域，该方法选取78~82份LF精炼渣和18~22份糖蜜为原料，将精炼渣压球，养护后可代替预熔渣使用；在转炉出钢之前或出钢过程中，精炼渣压球通过高位料仓加入钢包中，钢水经吹氩站吹氩搅拌3~5分钟后至LF钢包精炼炉，进行脱硫、去除夹杂物精炼。本发明的有益效果：在钢包中加入精炼渣压球，能够实现提前化渣；吹氩站吹氩后能够快速熔化，达到提前脱硫的目的；LF冶炼正常，使用精炼渣压球可满足炼钢工艺要求，脱硫率大于63.23%。

Description

一种碳钢LF精炼渣的循环利用方法
技术领域
本发明涉及一种碳钢LF精炼渣的循环利用方法，属于钢渣的利用领域。
背景技术
LF钢包精炼炉从20世纪70年代出现以来，由于具有设备简单、投资费用低、操作灵活和精炼效果好的特点，在炉外精炼领域得到广泛应用。利用精炼渣对钢液进行精炼是LF钢包精炼炉的一个主要功能，LF精炼渣CaO、Al2O3含量高，其高碱度、低氧化性的特点保证了钢液低硫、低氧含量的精炼效果，但是LF炉精炼渣的产生也造成环境的严重污染和资源的浪费，因此，研究如何利用LF精炼渣就成了迫切需要解决的问题。
LF精炼渣具有较高的碱度和较强的还原性，经过对钢渣进行理化分析，这种钢渣为CaO-SiO2-Al2O3系渣， CaO含量大于52%，Al2O3含量24~29%，S含量也较低（0.15~0.51%），具有一定的脱硫能力；熔点也较低，是一种较好的造渣料，可代替预熔渣使用；但是LF精炼渣特别容易粉化，不易直接加入钢包中。
发明内容
为了克服上述不足，本发明旨在提供一种碳钢LF精炼渣的循环利用方法，本发明对LF精炼渣进行压球，然后把LF精炼渣压球加入钢包中，代替预熔渣使用，解决了LF精炼渣因粉化而不能代替预熔渣的问题。
本发明提供的一种碳钢LF精炼渣的循环利用方法，包括以下步骤：
（1）碳钢LF精炼渣压球
将废弃的碳钢LF精炼渣通过皮带输送至混碾机，然后，在混碾机中加入糖蜜，将两种原料搅拌均匀，然后经皮带机输送到对辊压球机中挤压成型；
原料的质量配比为：LF精炼渣78~82份，
                  糖蜜18~22份；
其中糖蜜为制糖工业的副产品，起粘结剂作用；
（2）再经皮带输送到仓库自然养护5~7天后，可代替预熔渣使用；
碳钢LF精炼渣压球的性能为：球团强度为1949~2780N/个球，软熔带温度区间为1318~1352.1℃，化学成份为：TFe：0.79~2.04%；FeO：1.38~2.18%；SiO2：8.52~12.1%；Al2O3：17.92~19.55%；CaO：43.34~53.17%；MgO：4.11~8.28%；P：0.02~0.08%；S：0.22~0.53%，上述百分比为质量百分比；
（3）代替预熔渣加入钢包中
在转炉出钢之前或出钢过程中，碳钢LF精炼渣压球代替预熔渣，通过高位料仓加入钢包中使用，钢水经吹氩站吹氩搅拌3~5分钟后至LF钢包精炼炉，进行脱硫、去除夹杂物精炼。
上述方案中，在步骤（3）中预熔渣加到钢包中的配加量为2.5kg/t钢。
本发明提供的碳钢LF精炼渣的循环利用方法，选取糖蜜作为LF精炼渣压球的粘结剂；在转炉出钢之前或出钢过程中，碳钢LF精炼渣压球，通过高位料仓加入钢包中，代替预熔渣使用。
本发明的有益效果：在钢包中加入精炼渣压球，能够实现提前化渣；吹氩站吹氩后能够快速熔化，达到提前脱硫的目的；LF冶炼正常，使用精炼渣压球可满足炼钢工艺要求，脱硫率大于63.23% 。
具体实施方式
    下面结合实施例详细说明本发明的具体实施方式，但不局限于下述的实施例。
实施例1：
（1）碳钢LF精炼渣压球
按下述原料质量份配比称量：
碳钢LF精炼渣79份，糖蜜21份；
糖蜜是制糖工业的副产品，是一种粘稠、黑褐色、呈半流动的物体,起粘结剂作用。直接到制糖工业购买即可；
准确计量上述各原料，首先将碳钢LF精炼渣通过皮带输送至混碾机，然后，在混碾机中加入糖蜜，将其搅拌均匀，然后经皮带输送后送到对辊压球机中挤压成型；
上述实施例中的原料每份为10kg。
(2)再经皮带输送到仓库养护7天后，碳钢LF精炼渣压球强度平均值达2220N/个，软熔区间为1322~1349.4℃，化学成份见表1：
表1   碳钢精炼渣压球的化学成份            WT%
Figure 36433DEST_PATH_IMAGE001
碳钢精炼渣压球中还含有K2O、 Na2O、ZnO、MnO等，不是主要成份，一般不做分析。
（3）代替预熔渣加入钢包
在转炉出钢过程中，这种碳钢LF精炼渣压球代替预熔渣，通过高位料仓加入钢包中使用。配加量为2.5kg/t钢，钢水经吹氩站吹氩搅拌4分钟后至LF钢包精炼炉，进行脱硫、去除夹杂物精炼。
转炉出钢过程中，通过高位料仓，在钢包中加入精炼渣压球，能够实现提前化渣；吹氩站吹氩后能够快速熔化，达到提前脱硫目的；LF冶炼正常，使用精炼渣压球可满足炼钢工艺要求，脱硫率达68.82% 。
实施例2：
（1）碳钢LF精炼渣压球
按下述原料质量份配比称量：
碳钢LF精炼渣80份，糖蜜20份；
糖蜜是制糖工业的副产品，是一种粘稠、黑褐色、呈半流动的物体,起粘结剂作用。直接到制糖工业购买即可；
准确计量上述各原料，首先将碳钢LF精炼渣通过皮带输送至混碾机，然后，在混碾机中加入糖蜜，将其搅拌均匀，然后经皮带输送后送到对辊压球机中挤压成型；
上述实施例中的原料每份为10kg。
(2)再经皮带输送到仓库养护6天后，碳钢LF精炼渣压球强度平均值达2310N/个，软熔区间为1324~1345.2℃，化学成份见表2：
表2  碳钢精炼渣压球的化学成份            WT%
。
（3）代替预熔渣加入钢包
在转炉出钢过程中，这种碳钢LF精炼渣压球代替预熔渣，通过高位料仓加入钢包中使用。配加量为2.5kg/t钢，钢水经吹氩站吹氩搅拌3分钟后至LF钢包精炼炉，进行脱硫、去除夹杂物精炼。
转炉出钢过程中，通过高位料仓，在钢包中加入精炼渣压球，能够实现提前化渣；吹氩站吹氩后能够快速熔化，达到提前脱硫目的；LF冶炼正常，使用精炼渣压球可满足炼钢工艺要求，脱硫率达65.23% 。

Claims (3)

1.一种碳钢LF精炼渣的循环利用方法，包括以下步骤：
（1）碳钢LF精炼渣压球
将废弃的碳钢LF精炼渣通过皮带输送至混碾机，然后，在混碾机中加入糖蜜，将两种原料搅拌均匀，然后经皮带机输送到对辊压球机中挤压成型，即得碳钢LF精炼渣压球；
原料的质量配比为：LF精炼渣78~82份，
                  糖蜜18~22份；
其中糖蜜为制糖工业的副产品，起粘结剂作用；
（2）再经皮带输送到仓库自然养护5~7天后，可代替预熔渣使用；
（3）代替预熔渣加入钢包中
在转炉出钢之前或出钢过程中，碳钢LF精炼渣压球代替预熔渣，通过高位料仓加入钢包中使用，钢水经吹氩站吹氩搅拌3~5分钟后至LF钢包精炼炉，进行脱硫、去除夹杂物精炼。
2.根据权利要求1所述的碳钢LF精炼渣的循环利用方法，其特征在于：所述碳钢LF精炼渣压球的性能为：球团强度为1949~2780N/个球，软熔带温度区间为1318~1352.1℃，化学成份为：TFe：0.79~2.04%；FeO：1.38~2.18%；SiO2：8.52~12.1%；Al2O3：17.92~19.55%；CaO：43.34~53.17%；MgO：4.11~8.28%；P：0.02~0.08%；S：0.22~0.53%，上述百分比为质量百分比。
3.根据权利要求1所述的碳钢LF精炼渣的循环利用方法，其特征在于：在步骤（3）中预熔渣加到钢包中的配加量为2.5kg/t钢。
CN2013101974228A 2013-05-24 2013-05-24 一种碳钢lf精炼渣的循环利用方法 Pending CN103276201A (zh)