CN103275411A - 一种超薄壁汽车电线用pvc - Google Patents

一种超薄壁汽车电线用pvc Download PDF

Info

Publication number
CN103275411A
CN103275411A CN2013100633480A CN201310063348A CN103275411A CN 103275411 A CN103275411 A CN 103275411A CN 2013100633480 A CN2013100633480 A CN 2013100633480A CN 201310063348 A CN201310063348 A CN 201310063348A CN 103275411 A CN103275411 A CN 103275411A
Authority
CN
China
Prior art keywords
percentage composition
cent
calcium carbonate
pvc
molecular weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100633480A
Other languages
English (en)
Inventor
蒋振华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO KBE ELECTRICAL TECHNOLOGY Co Ltd
Original Assignee
NINGBO KBE ELECTRICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO KBE ELECTRICAL TECHNOLOGY Co Ltd filed Critical NINGBO KBE ELECTRICAL TECHNOLOGY Co Ltd
Priority to CN2013100633480A priority Critical patent/CN103275411A/zh
Publication of CN103275411A publication Critical patent/CN103275411A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％，采用高聚合度的PVC树脂，高分子量的增塑剂和部分线性高分子量增塑剂，纳米级的碳酸钙做为填充，在保证低温性能的同时满足耐磨性能的要求。

Description

一种超薄壁汽车电线用PVC
技术领域
本发明涉及一种超薄壁汽车电线用PVC。 
背景技术
由于超薄壁汽车电线使用的PVC需要耐105摄氏度，低温-40摄氏度，耐磨性能要求较高，而厚度只有0.2mm，普通的汽车电线PVC无法满足要求。 
发明内容
针对上述技术缺陷，本发明提出一种超薄壁汽车电线用PVC。 
为了解决上述技术问题，本发明的技术方案如下： 
一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。 
进一步的，所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
进一步的，所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
进一步的，所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量 百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
本发明的有益效果在于；采用高聚合度的PVC树脂，高分子量的增塑剂和部分线性高分子量增塑剂，纳米级的碳酸钙做为填充，在保证低温性能的同时满足耐磨性能的要求。另外由于该产品中增塑剂含量较少，而且电线产品的绝缘很薄，不需要像普通PVC一样加入三氧化二锑等阻燃剂就能够使电线满足ISO6722的阻燃性能要求。这样既降低了材料的成本，又减少了重金属元素的加入。该产品完全符合RoHS指令要求。该PVC生产出的电线完全满足ISO6722标准中的超薄壁电线的绝缘要求。 
具体实施方式
下面将结合具体实施例对本发明做进一步的说明。 
一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。 
实施例一： 
所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
实施例二： 
所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
实施例三： 
所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。 
按照实施例一、二或者三任意一种比例制成汽车电线用PVC，其耐磨使用寿命一般为普通pvc的1倍以上，阻燃性能和普通pvc相同。 
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员，在不脱离本发明构思的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明保护范围内。 

Claims (4)

1.一种超薄壁汽车电线用PVC，其特征在于，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。
2.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
3.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
4.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
CN2013100633480A 2013-02-27 2013-02-27 一种超薄壁汽车电线用pvc Pending CN103275411A (zh)