CN103272876A - 一种镍铁铬合金无缝管 - Google Patents
一种镍铁铬合金无缝管 Download PDFInfo
- Publication number
- CN103272876A CN103272876A CN2013101942994A CN201310194299A CN103272876A CN 103272876 A CN103272876 A CN 103272876A CN 2013101942994 A CN2013101942994 A CN 2013101942994A CN 201310194299 A CN201310194299 A CN 201310194299A CN 103272876 A CN103272876 A CN 103272876A
- Authority
- CN
- China
- Prior art keywords
- blank
- resisto
- seamless pipe
- carrying
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明揭示了一种镍铁铬合金无缝管,成分包括:镍,铜,铁,锰,碳,硅,硫,以及铬,制造步骤为:(1)首先对坯料进行检验,(2)然后对坯料进行热加工处理,(3)对热加工处理过程中的坯料进行穿孔处理,(4)对穿孔后的坯料进行退火处理,(5)对坯料进行酸洗,酸洗好的坯料进行润滑、去油、冷拔轧处理,(6)判断是否满足成品,如是则进行热处理、矫直、探伤处理,(7)如不是则进行热处理、矫直、探伤并重复步骤5,(8)最后成品进行检验,以及后续的标识入库处理。本发明使镍铁铬合金无缝管具有耐腐蚀、耐高温、耐强酸、耐强碱以及节约成本的功能。
Description
技术领域
本发明涉及一种无缝管的制造,具体涉及一种UNS NO6600合金制成的镍铁铬合金无缝管。
背景技术
无缝管是一种具有中空截面、周边没有接缝的圆形,方形,矩形钢材。无缝管是用钢锭或实心管坯经穿孔制成毛管,然后经热轧、冷轧或冷拨制成。无缝管具有中空截面,大量用作输送流体的管道,钢管与圆钢等实心钢材相比,在抗弯抗扭强度相同时,重量较轻,是一种经济截面钢材,广泛用于制造结构件和机械零件,如石油钻杆、汽车传动轴、自行车架以及建筑施工中用的钢脚手架等。
在一些高温、混有杂质的无机酸和有机酸(如甲酸和乙酸)、海水腐蚀环境等方面,一般管无法在该环境中广泛应用,并且维修费用比较大,无法大范围推广。
因此,研发一种耐腐蚀、耐高温、耐强酸、耐强碱、节约成本的无缝管是亟待解决的问题。
发明内容
本发明的目的在于提供一种耐腐蚀、耐高温、耐强酸、耐强碱、节约成本的镍铁铬合金无缝管。
本发明的技术方案是,一种镍铁铬合金无缝管,所述镍铁铬合金无缝管按重量百分比包括:镍为72%-78%,铜为0.3%-0.5%,铁为6%-10%,锰为0.5%-1%,碳为0.06%-0.12%,硅为0.4%-0.7%,硫为0.008%-0.015%,以及铬14%-17%,所述镍铁铬合金无缝管的制造步骤为:
(1)首先对坯料进行检验,
(2)然后对坯料进行热加工处理,
(3)对热加工处理过程中的坯料进行穿孔处理,
(4)对穿孔后的坯料进行退火处理,
(5)对坯料进行酸洗,酸洗好的坯料进行润滑、去油、冷拔轧处理,
(6)判断是否满足成品,如是则进行热处理、矫直、探伤处理,
(7)如不是则进行热处理、矫直、探伤并重复步骤5,
(8)最后成品进行检验,以及后续的标识入库处理。
在本发明一个较佳实施例中,所述热加工处理的加工温度为980℃-1210℃。
在本发明一个较佳实施例中,所述退火处理包括一次退火和二次退火。
在本发明一个较佳实施例中,所述一次退火温度范围为650℃-780℃,所述二次退火温度范围为480℃-570℃。
在本发明一个较佳实施例中,所述酸洗溶液是氢氟酸和硝酸混合溶液,所述的酸洗溶液中的酸洗液的成分包括质量百分比为10%-14%的硝酸和质量百分比为4.5%-9%的氢氟酸,酸温在40℃以下。
本发明所述为一种镍铁铬合金无缝管,使哈氏合金无缝管具有耐腐蚀、耐高温、耐强酸、耐强碱以及节约成本的功能。
附图说明
图1为本发明一较佳实施例的的工艺流程框图。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种镍铁铬合金无缝管,参见图1所示,所述镍铁铬合金无缝管按重量百分比包括:镍为72%-78%,铜为0.3%-0.5%,铁为6%-10%,锰为0.5%-1%,碳为0.06%-0.12%,硅为0.4%-0.7%,硫为0.008%-0.015%,以及铬14%-17%,所述镍铁铬合金无缝管的制造步骤为:
(1)首先对坯料进行检验,
(2)然后对坯料进行热加工处理,
(3)对热加工处理过程中的坯料进行穿孔处理,
(4)对穿孔后的坯料进行退火处理,
(5)对坯料进行酸洗,酸洗好的坯料进行润滑、去油、冷拔轧处理,
(6)判断是否满足成品,如是则进行热处理、矫直、探伤处理,
(7)如不是则进行热处理、矫直、探伤并重复步骤5,
(8)最后成品进行检验,以及后续的标识入库处理。
进一步说明,所述热加工处理的加工温度为980℃-1210℃,所述退火处理包括一次退火和二次退火,所述一次退火温度范围为650℃-780℃,所述二次退火温度范围为480℃-570℃,所述酸洗溶液是氢氟酸和硝酸混合溶液,所述的酸洗溶液中的酸洗液的成分包括质量百分比为10%-14%的硝酸和质量百分比为4.5%-9%的氢氟酸,酸温在40℃以下。
进一步说明,在热处理过程中不能接触硫、磷、铅及其它低熔点金属,否则会损害材料的性能,应注意清除诸如润滑油、燃料等污物。控制时间在30min,氢氟酸够有效快速的起到去油作用并对管子表面无任何过酸发白影响,薄壁管的材料也可采用快速空冷,以上所述目的达到理想的表面耐腐蚀性能提高,提高性能优越标准的1.1-1.2倍。
本发明的一种镍铁铬合金无缝管,使哈氏合金无缝管具有耐腐蚀、耐高温、耐强酸、耐强碱以及节约成本的功能。
以上所述仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (5)
1.一种镍铁铬合金无缝管,其特征在于:所述镍铁铬合金无缝管按重量百分比包括:镍为72%-78%,铜为0.3%-0.5%,铁为6%-10%,锰为0.5%-1%,碳为0.06%-0.12%,硅为0.4%-0.7%,硫为0.008%-0.015%,以及铬14%-17%,所述镍铁铬合金无缝管的制造步骤为:
(1)首先对坯料进行检验,
(2)然后对坯料进行热加工处理,
(3)对热加工处理过程中的坯料进行穿孔处理,
(4)对穿孔后的坯料进行退火处理,
(5)对坯料进行酸洗,酸洗好的坯料进行润滑、去油、冷拔轧处理,
(6)判断是否满足成品,如是则进行热处理、矫直、探伤处理,
(7)如不是则进行热处理、矫直、探伤并重复步骤5,
(8)最后成品进行检验,以及后续的标识入库处理。
2.根据权利要求1所述的镍铁铬合金无缝管,其特征在于:所述热加工处理的加工温度为980℃-1210℃。
3.根据权利要求1所述的镍铁铬合金无缝管,其特征在于:所述退火处理包括一次退火和二次退火。
4.根据权利要求3所述的镍铁铬合金无缝管,其特征在于:所述一次退火温度范围为650℃-780℃,所述二次退火温度范围为480℃-570℃。
5.根据权利要求1所述的镍铁铬合金无缝管,其特征在于:所述酸洗溶液是氢氟酸和硝酸混合溶液,所述的酸洗溶液中的酸洗液的成分包括质量百分比为10%-14%的硝酸和质量百分比为4.5%-9%的氢氟酸,酸温在40℃以下。