CN103266248A - 一种碳化钒钛基硬质合金 - Google Patents

一种碳化钒钛基硬质合金 Download PDF

Info

Publication number
CN103266248A
CN103266248A CN2013101956272A CN201310195627A CN103266248A CN 103266248 A CN103266248 A CN 103266248A CN 2013101956272 A CN2013101956272 A CN 2013101956272A CN 201310195627 A CN201310195627 A CN 201310195627A CN 103266248 A CN103266248 A CN 103266248A
Authority
CN
China
Prior art keywords
cobalt
hard alloy
wimet
carbide
mass percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101956272A
Other languages
English (en)
Inventor
王静
伏思静
丁义超
罗建设
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Technological University CDTU
Chengdu Univeristy of Technology
Original Assignee
Chengdu Technological University CDTU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Technological University CDTU filed Critical Chengdu Technological University CDTU
Priority to CN2013101956272A priority Critical patent/CN103266248A/zh
Publication of CN103266248A publication Critical patent/CN103266248A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种碳化钒钛基硬质合金，在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨，得到性能更优于钴粘结碳化钨硬质合金的新型硬质合金；该硬质合金所含元素及各元素的质量百分比分别为：V，其含量为39.06-43.65％；Ti，其含量为36.75-41.08％；Fe，其含量为0.5％-5％；C，其含量为9.19-10.27％；余量是钴和杂质。本发明由于新型的硬质合金是在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨，所以碳化钒钛基硬质合金弥补了钴粘结碳化钨硬质合金的不足，在经济性上更优越。本发明提供了一种性能更优于钴粘结碳化钨硬质合金的新型硬质合金，该硬质合金在机械性能、经济性上更优越。

Description

一种碳化钒钛基硬质合金
技术领域
本发明属于硬质合金领域，尤其涉及一种碳化钒钛基硬质合金。
背景技术
钴粘结碳化钨硬质合金是以碳化钨为基体，钴为粘结相，采用粉末冶金技术制备而成。钨属于战略资源，而且我国又是一个金属钨资源缺乏的国家，这导致钴粘结碳化钨硬质合金比较昂贵。因此有必要开发新型硬质合金。
碳化钛、碳化钒是两种难熔的金属化合物，具有高的硬度、高的弹性模量、高的热稳定性以及与钴之间具有良好的润湿性等优点，并且我国具有丰富的钒钛资源。因此可以制备碳化钒钛基硬质合金。
新型的硬质合金是在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨，碳化钒钛基硬质合金弥补了钴粘结碳化钨硬质合金的不足，在经济性上更优越。
发明内容
本发明的目的在于提供一种性能更优于钴粘结碳化钨硬质合金的新型硬质合金，旨在解决钴粘结碳化钨硬质合金的不足且价格比较昂贵的问题。
本发明是这样实现的，一种碳化钒钛基硬质合金，一种在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨的技术，得到性能更优于钴粘结碳化钨硬质合金的新型硬质合金。该硬质合金所含元素及各元素的质量百分比分别为：V，其含量为39.06-43.65％；Ti，其含量为36.75-41.08％；Fe，其含量为0.5％-5％；C，其含量为9.19-10.27％。余量是钴和不可避免的杂质。
进一步，硬质合金所含元素及各元素的质量百分比
Figure BSA00000900420500021
余量是钴和不可避免的杂质；经测试其硬度为91.4HRA，抗弯强度为2580MPa。
进一步，硬质合金所含元素及各元素的质量百分比
Figure BSA00000900420500022
余量是钴和不可避免的杂质；经测试其硬度为93.8HRA，抗拉强度为2332MPa。
进一步，硬质合金所含元素及各元素的质量百分比
余量是钴和不可避免的杂质；经测试其硬度为95.2HRA，抗拉强度为2130MPa。
本发明由于新型的硬质合金是在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨，所以碳化钒钛基硬质合金弥补了钴粘结碳化钨硬质合金的不足，在经济性上更优越。本发明提供了一种性能更优于钴粘结碳化钨硬质合金的新型硬质合金，该硬质合金在机械性能、经济性上更优越。
具体实施方式
本发明是这样实现的，提供一种在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨的技术，得到性能更优于钴粘结碳化钨硬质合金的新型硬质合金。该硬质合金所含元素及各元素的质量百分比分别为：V，其含量为39.06-43.65％；Ti，其含量为36.75-41.08％；Fe，其含量为0.5％-5％；C，其含量为9.19-10.27％。余量是钴和不可避免的杂质。
实施例一：硬质合金所含元素及各元素的质量百分比
Figure BSA00000900420500031
余量是钴和不可避免的杂质
经测试其硬度为91.4HRA，抗弯强度为2580MPa。
实施例二：硬质合金所含元素及各元素的质量百分比
Figure BSA00000900420500032
余量是钴和不可避免的杂质
经测试其硬度为93.8HRA，抗拉强度为2332MPa。
实施例三：硬质合金所含元素及各元素的质量百分比
余量是钴和不可避免的杂质
经测试其硬度为95.2HRA，抗拉强度为2130MPa。
碳化钒钛基硬质合金包含V，其质量百分比为39.06-43.65％；Ti，其质量百分比为36.75-41.08％；Fe其质量百分比为0.5％-5％；C，其质量百分比为9.19-10.27％；余量是钴和不可避免的杂质。提供一种在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨的技术，得到性能更优于钴粘结碳化钨硬质合金的新型硬质合金。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种碳化钒钛基硬质合金，其特征在于，在钴粘结碳化钨硬质合金基础上以碳化钒钛代替碳化钨，得到性能更优于钴粘结碳化钨硬质合金的新型硬质合金；该硬质合金所含元素及各元素的质量百分比分别为：V，其含量为39.06-43.65％；Ti，其含量为36.75-41.08％；Fe，其含量为0.5％-5％；C，其含量为9.19-10.27％；余量是钴和杂质。
2.如权利要求1所述的碳化钒钛基硬质合金，其特征在于，硬质合金所含元素及各元素的质量百分比：
Figure FSA00000900420400011
余量是钴和不可避免的杂质；经测试其硬度为91.4HRA，抗弯强度为2580MPa。
3.如权利要求1所述的碳化钒钛基硬质合金，其特征在于，硬质合金所含元素及各元素的质量百分比：
Figure FSA00000900420400012
余量是钴和不可避免的杂质；经测试其硬度为93.8HRA，抗拉强度为2332MPa。
4.如权利要求1所述的碳化钒钛基硬质合金，其特征在于，硬质合金所含元素及各元素的质量百分比：
Figure FSA00000900420400013
Figure FSA00000900420400021
余量是钴和不可避免的杂质；经测试其硬度为95.2HRA，抗拉强度为2130MPa。
CN2013101956272A 2013-05-24 2013-05-24 一种碳化钒钛基硬质合金 Pending CN103266248A (zh)