CN103265809A - 尼龙66复合材料及其制备方法 - Google Patents

尼龙66复合材料及其制备方法 Download PDF

Info

Publication number
CN103265809A
CN103265809A CN2013101781117A CN201310178111A CN103265809A CN 103265809 A CN103265809 A CN 103265809A CN 2013101781117 A CN2013101781117 A CN 2013101781117A CN 201310178111 A CN201310178111 A CN 201310178111A CN 103265809 A CN103265809 A CN 103265809A
Authority
CN
China
Prior art keywords
parts
nylon
glass fibre
composite material
oxidation inhibitor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101781117A
Other languages
English (en)
Inventor
张庆文
胡爱琴
俞奇渊
吴昊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGGUO HUASHENG PLASTIC PRODUCTS CO Ltd
Original Assignee
NINGGUO HUASHENG PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGGUO HUASHENG PLASTIC PRODUCTS CO Ltd filed Critical NINGGUO HUASHENG PLASTIC PRODUCTS CO Ltd
Priority to CN2013101781117A priority Critical patent/CN103265809A/zh
Publication of CN103265809A publication Critical patent/CN103265809A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种尼龙66复合材料，其是由下述重量份的原料混合造粒而得：尼龙PA66 100、玻璃纤维80-90、无水乙醇2-3、钛白粉2-3、ABS高胶粉10-15、聚己酸内酯5-7、甲基三甲氧基硅烷7.5-9、聚乙烯蜡2-3、柠檬酸三乙酯2-3、硬脂酸锌1.5-2.2、海泡石粉5-10、氨丙基三乙氧基硅烷1-2、抗氧剂10350.3-0.5、抗氧剂168 1.5-1.8、乙撑双硬脂酰胺2.5-2.8、乌洛托品1-2、二甲基二巯基乙酸异辛酯锡0.5-0.8。本发明经过改性加工的材料拉伸强度183MPa、弯曲强度221MPa、缺口冲击强度17KJ/㎡，耐高温200度，水解密度保持率在99.9%，使用寿命长。

Description

尼龙66复合材料及其制备方法
技术领域
    本发明涉及高分子塑料材料，具体是一种尼龙66复合材料及其制备方法。
背景技术
目前市场上常规结构塑料尼龙产品机械强度（拉伸强度、弯曲强度和缺口冲击强度）低，高温老化变形，容易水解，使用寿命短的问题。
发明内容
本发明的目的是提供一种尼龙66复合材料及其制备方法，其拉伸强度、弯曲强度和缺口冲击强度高。
本发明技术方案如下：
一种尼龙66复合材料，其特征在于，其是由下述重量份的原料混合造粒而得：
尼龙PA66  100、玻璃纤维80-90、无水乙醇2-3、钛白粉2-3、ABS高胶粉 10-15、聚己酸内酯5-7、甲基三甲氧基硅烷7.5-9、聚乙烯蜡2-3、柠檬酸三乙酯2-3、硬脂酸锌1.5-2.2、海泡石粉5-10、氨丙基三乙氧基硅烷1-2、抗氧剂1035 0.3-0.5、抗氧剂168  1.5-1.8、乙撑双硬脂酰胺2.5-2.8、乌洛托品1-2、二甲基二巯基乙酸异辛酯锡0.5-0.8。
所述的尼龙66复合材料的制备方法，其特征在于包括以下步骤：
（1）、无水乙醇与甲基三甲氧基硅烷混合，喷洒到玻璃纤维上，拌匀；
（2）、主加料器加入尼龙PA66及钛白粉、ABS高胶粉 、聚己酸内酯、聚乙烯蜡、柠檬酸三乙酯、硬脂酸锌、海泡石粉、氨丙基三乙氧基硅烷、抗氧剂1035 、抗氧剂168  、乙撑双硬脂酰胺、乌洛托品、二甲基二巯基乙酸异辛酯锡，从侧向加料器加入步骤（1）所得玻璃纤维，通过同向双螺杆挤出机造粒得到，加工温度为250-300度，挤出机转速为230--250转/每秒。
所述的尼龙66复合材料，其特征在于，ABS高胶粉指的是苯乙烯、丙稀晴－丁二烯橡胶，核壳型聚合物，所述的玻璃纤维为无碱玻璃纤维。
 
本发明经过改性加工的材料拉伸强度183MPa、弯曲强度221MPa、缺口冲击强度17KJ/㎡，耐高温200度，水解密度保持率在99.9%，使用寿命长。
具体实施方式
一种尼龙66复合材料，其是由下述重量份（公斤）的原料混合造粒而得：
尼龙PA66  100、玻璃纤维90、无水乙醇3、钛白粉3、ABS高胶粉 15、聚己酸内酯7、甲基三甲氧基硅烷7.5、聚乙烯蜡2、柠檬酸三乙酯3、硬脂酸锌1.5、海泡石粉10、氨丙基三乙氧基硅烷2、抗氧剂1035 0.5、抗氧剂168  1.5、乙撑双硬脂酰胺2.5、乌洛托品2、二甲基二巯基乙酸异辛酯锡0.5。
制备方法包括以下步骤：
（1）、无水乙醇与甲基三甲氧基硅烷混合，喷洒到玻璃纤维上，拌匀；
（2）、主加料器加入尼龙PA66及钛白粉、ABS高胶粉 、聚己酸内酯、聚乙烯蜡、柠檬酸三乙酯、硬脂酸锌、海泡石粉、氨丙基三乙氧基硅烷、抗氧剂1035 、抗氧剂168  、乙撑双硬脂酰胺、乌洛托品、二甲基二巯基乙酸异辛酯锡，从侧向加料器加入步骤（1）所得玻璃纤维，通过同向双螺杆挤出机造粒得到，加工温度为250-300度，挤出机转速为230--250转/每秒。
ABS高胶粉指的是苯乙烯、丙稀晴－丁二烯橡胶，核壳型聚合物，所述的玻璃纤维为无碱玻璃纤维。
本发明经过改性加工的材料拉伸强度183MPa、弯曲强度221MPa、缺口冲击强度17KJ/㎡，耐高温200度，水解密度保持率在99.9%，使用寿命长。

Claims (3)

1.一种尼龙66复合材料，其特征在于，其是由下述重量份的原料混合造粒而得：
尼龙PA66  100、玻璃纤维80-90、无水乙醇2-3、钛白粉2-3、ABS高胶粉 10-15、聚己酸内酯5-7、甲基三甲氧基硅烷7.5-9、聚乙烯蜡2-3、柠檬酸三乙酯2-3、硬脂酸锌1.5-2.2、海泡石粉5-10、氨丙基三乙氧基硅烷1-2、抗氧剂1035 0.3-0.5、抗氧剂168  1.5-1.8、乙撑双硬脂酰胺2.5-2.8、乌洛托品1-2、二甲基二巯基乙酸异辛酯锡0.5-0.8。
2.根据权利要求1所述的尼龙66复合材料的制备方法，其特征在于包括以下步骤：
（1）、无水乙醇与甲基三甲氧基硅烷混合，喷洒到玻璃纤维上，拌匀；
（2）、主加料器加入尼龙PA66及钛白粉、ABS高胶粉 、聚己酸内酯、聚乙烯蜡、柠檬酸三乙酯、硬脂酸锌、海泡石粉、氨丙基三乙氧基硅烷、抗氧剂1035 、抗氧剂168  、乙撑双硬脂酰胺、乌洛托品、二甲基二巯基乙酸异辛酯锡，从侧向加料器加入步骤（1）所得玻璃纤维，通过同向双螺杆挤出机造粒得到，加工温度为250-300度，挤出机转速为230--250转/每秒。
3.根据权利要求1所述的尼龙66复合材料，其特征在于，ABS高胶粉指的是苯乙烯、丙稀晴－丁二烯橡胶，核壳型聚合物，所述的玻璃纤维为无碱玻璃纤维。
CN2013101781117A 2013-05-15 2013-05-15 尼龙66复合材料及其制备方法 Pending CN103265809A (zh)