CN103254761A - 一种耐老化防腐的聚酰亚胺涂料 - Google Patents

一种耐老化防腐的聚酰亚胺涂料 Download PDF

Info

Publication number
CN103254761A
CN103254761A CN201310208451XA CN201310208451A CN103254761A CN 103254761 A CN103254761 A CN 103254761A CN 201310208451X A CN201310208451X A CN 201310208451XA CN 201310208451 A CN201310208451 A CN 201310208451A CN 103254761 A CN103254761 A CN 103254761A
Authority
CN
China
Prior art keywords
resistant
ageing
extract
coating material
polyimide coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310208451XA
Other languages
English (en)
Other versions
CN103254761B (zh
Inventor
徐伟伟
刘战合
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU YABAO INSULATION MATERIAL CO Ltd
Original Assignee
JIANGSU YABAO INSULATION MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU YABAO INSULATION MATERIAL CO Ltd filed Critical JIANGSU YABAO INSULATION MATERIAL CO Ltd
Priority to CN201310208451.XA priority Critical patent/CN103254761B/zh
Publication of CN103254761A publication Critical patent/CN103254761A/zh
Application granted granted Critical
Publication of CN103254761B publication Critical patent/CN103254761B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了属于涂料技术领域的一种耐老化防腐的聚酰亚胺涂料。该涂料由以下重量份数的物质组成：聚酰亚胺10-50份，纳米硅3-10份，聚硅氧烷10-20份，溶剂3-10份，阻燃剂2-8份，仙人掌提取物1-5份，紫茎泽兰提取物5-10份。本发明纳米硅的加入提高了涂料的耐磨性，防止涂料久用老化，聚硅氧烷的加入提高了涂料的隔热性能，阻燃剂的加入提高了涂料的防火性能，仙人掌提取物的加入进一步提高了涂料的防辐射性能，并且推高了防污性能，紫茎泽兰提取物的应用开发了一种有害杂草的利用途径，并且增强了涂料的防污性能。

Description

一种耐老化防腐的聚酰亚胺涂料
技术领域
本发明属于涂料技术领域，具体涉及一种耐老化防腐的聚酰亚胺涂料。
背景技术
随着电气事业的发展和通信电缆技术的提高，对聚酰亚胺涂料的需求量越来越大，聚酰亚胺涂料具有耐高温、绝缘性能好等优点，被广泛应用于光导纤维、船舶壳体、通信电缆、半导体、家用电器和电力电缆等行业。
聚酰亚胺涂料虽然有耐高温和绝缘性能强的优点，但是，其容易老化，在水下容易被污染和腐化，还容易被水生动物粘附，破坏机器零件的正常使用，限制了该类涂料的应用。
仙人掌为一种在沙漠中高辐射环境下能顽强生长的植物，现已经能大规模种植，发明人通过实验发现，仙人掌提取物加入涂料中，能够提高涂料的防辐射性能和防污能力。
紫茎泽兰为中国南方一种外来入侵植物，给农作物生产带来极大危害，发明人发现，仙人掌提取物可作为防污剂加入涂料中，增加涂料的防污性能。
发明内容
一种耐老化防辐射的聚酰亚胺涂料，该涂料由以下重量份数的物质组成：聚酰亚胺10-50份，纳米硅3-10份，聚硅氧烷10-20份，溶剂3-10份，阻燃剂2-8份，仙人掌提取物1-5份，紫茎泽兰提取物5-10份。
所述纳米硅为球形颗粒结构或纳米微孔结构，粒径大小为50-200nm。
所述溶剂为石油醚、乙醇、甲醇、丙二醇、甲酚酸、石脑油、樟脑油中的一种及一种以上。
所述阻燃剂为氢氧化镁、氢氧化铝、磷酸二氢铵、磷酸氢二胺、多聚磷酸铵、硼酸中的一种或一种以上。
所述仙人掌提取物的提取方法为：
首先将仙人掌晒干或者烘干，粉碎至粉末，加入溶剂I浸泡3-7天，过滤除去固体，采用减压蒸馏回收溶剂I，得到粘稠状液体，烘干该液体得到粉末状仙人掌提取物。
所述溶剂I为水、甲醇、乙醇、乙酸乙酯、石油醚、二甲醚、正己烷中的一种或一种以上。
所述紫茎泽兰提取物的提取方法为：
首先将紫茎泽兰晒干或者烘干，粉碎至粉末，加入溶剂II浸泡4-10天，过滤除去固体，采用减压蒸馏回收溶剂II，得到粘稠状液体，烘干该液体得到粉末状紫茎泽兰提取物。
所述溶剂II为甲醇、乙醇、石油醚、乙酸乙酯、正己烷、石油醚、二甲醚中的一种或一种以上。
本发明的有益效果：本发明采用聚酰亚胺作为涂料的主要成分，具有耐高温、绝缘性能好、耐辐射的优点，纳米硅的加入提高了涂料的耐磨性，防止涂料久用老化，聚硅氧烷的加入提高了涂料的隔热性能，阻燃剂的加入提高了涂料的防火性能，仙人掌提取物的加入进一步提高了涂料的防辐射性能，并且推高了防污性能，紫茎泽兰提取物的应用开发了一种有害杂草的利用途径，并且增强了涂料的防污性能。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1仙人掌提取物的提取
首先将仙人掌晒干或者烘干，粉碎至粉末，秤取粉末100g，加入300mL水中浸泡3天，过滤除去固体，采用减压蒸馏，得到粘稠状液体，烘干该液体得到粉末状仙人掌提取物。
实施例2仙人掌提取物的提取
首先将仙人掌晒干或者烘干，粉碎至粉末，秤取粉末100g，加入300mL石油醚中浸泡6天，过滤除去固体，采用减压蒸馏回收石油醚，得到粘稠状液体，烘干该液体得到粉末状仙人掌提取物。
实施例3紫茎泽兰提取物的提取
首先将紫茎泽兰晒干或者烘干，粉碎至粉末，秤取粉末100g，加入300mL乙醇浸泡5天，过滤除去固体，采用减压蒸馏回收乙醇，得到粘稠状液体，烘干该液体得到粉末状紫茎泽兰提取物。
实施例4紫茎泽兰提取物的提取
首先将紫茎泽兰晒干或者烘干，粉碎至粉末，秤取粉末100g，加入300mL石油醚浸泡7天，过滤除去固体，采用减压蒸馏回收石油醚，得到粘稠状液体，烘干该液体得到粉末状紫茎泽兰提取物。
实施例5
将聚酰亚胺10g，纳米硅3g，聚硅氧烷10g，石油醚3g，氢氧化镁2g，实施例1制备的仙人掌提取物1g，实施例3制备的紫茎泽兰提取物5g搅拌混合均匀制成涂料。
纳米硅为球形颗粒结构或纳米微孔结构，粒径大小为50nm。
实施例6
将聚酰亚胺30g，纳米硅5g，聚硅氧烷15g，丙二醇5g，磷酸氢二胺4g，实施例2制备的仙人掌提取物3g，实施例4制备的紫茎泽兰提取物6g搅拌混合均匀制成涂料。
纳米硅为球形颗粒结构或纳米微孔结构，粒径大小为100nm。
实施例7
将聚酰亚胺50g，纳米硅10g，聚硅氧烷20g，樟脑油10g，硼酸8g，实施例1制备的仙人掌提取物5g，实施例4制备的紫茎泽兰提取物10g搅拌混合均匀制成涂料。
纳米硅为球形颗粒结构或纳米微孔结构，粒径大小为200nm。
实施例8防污实验
将实施例5-7制备的涂料均匀涂到挂板上，挂板大小为30X30cm2，干燥后，入海水3m的环境下进行防污实验，检测是否有海洋生物粘附，粘附面价大于8％为失效。
入海一个月后无海洋生物粘附，3个月后平均粘附面积为0.1％，一年后平均粘附面价为1％，证明制备的涂料具有良好的防污性能。

Claims (8)

1.一种耐老化防腐的聚酰亚胺涂料，其特征在于，该涂料由以下重量份数的物质组成：聚酰亚胺10-50份，纳米硅3-10份，聚硅氧烷10-20份，溶剂3-10份，阻燃剂2-8份，仙人掌提取物1-5份，紫茎泽兰提取物5-10份。
2.根据权利要求1所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述纳米硅为球形颗粒结构或纳米微孔结构，粒径大小为50-200nm。
3.根据权利要求1所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述溶剂为石油醚、乙醇、甲醇、丙二醇、甲酚酸、石脑油、樟脑油中的一种及一种以上。
4.根据权利要求1所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述阻燃剂为氢氧化镁、氢氧化铝、磷酸二氢铵、磷酸氢二胺、多聚磷酸铵、硼酸中的一种或一种以上。
5.根据权利要求1所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述仙人掌提取物的提取方法为：
首先将仙人掌晒干或者烘干，粉碎至粉末，加入溶剂I浸泡3-7天，过滤除去固体，采用减压蒸馏回收溶剂I，得到粘稠状液体，烘干该液体得到粉末状仙人掌提取物。
6.根据权利要求5所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述溶剂I为水、甲醇、乙醇、乙酸乙酯、石油醚、二甲醚、正己烷中的一种或一种以上。
7.根据权利要求1所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述紫茎泽兰提取物的提取方法为：
首先将紫茎泽兰晒干或者烘干，粉碎至粉末，加入溶剂II浸泡4-10天，过滤除去固体，采用减压蒸馏回收溶剂II，得到粘稠状液体，烘干该液体得到粉末状紫茎泽兰提取物。
8.根据权利要求7所述一种耐老化防腐的聚酰亚胺涂料，其特征在于，所述溶剂II为甲醇、乙醇、石油醚、乙酸乙酯、正己烷、石油醚、二甲醚中的一种或一种以上。
CN201310208451.XA 2013-05-30 2013-05-30 一种耐老化防腐的聚酰亚胺涂料 Active CN103254761B (zh)