CN103254718A - Floor paint - Google Patents
Floor paint Download PDFInfo
- Publication number
- CN103254718A CN103254718A CN2013102135719A CN201310213571A CN103254718A CN 103254718 A CN103254718 A CN 103254718A CN 2013102135719 A CN2013102135719 A CN 2013102135719A CN 201310213571 A CN201310213571 A CN 201310213571A CN 103254718 A CN103254718 A CN 103254718A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- floor paint
- dimethylbenzene
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses floor paint which is prepared from the following raw materials in parts by weight: 3-10 parts of illite clay, 30-40 parts of hydroxy acrylic resin, 25-35 parts of fatty acid alkyd resin, 10-20 parts of pigment, 9-13 parts of dimethylbenzene, 5-10 parts of butyl acetate, 0.1-0.5 part of dispersing agent, 0.1-0.5 part of leveling agent, 0.1-0.5 part of defoaming agent and 0.1-0.5 part of anti-settling agent. The floor paint disclosed by the invention has the advantages of high abrasion resistance, excellent transparency and good hardness.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of Floor paint.
Background technology
Hard floor paint is used for the floor coating of buildings flooring coating facing.Adopt hard floor paint facing cost low, upgrade convenient and good integrity from heavy and light, maintenance, thereby very popular.Wear resistance, hardness and transparency are three big key propertys of hard floor paint.How preparing wear resistance hard floor paint good, that hardness is big and transparency is good is in the hard floor paint preparation process, the problem that need take all factors into consideration.
Summary of the invention
The technical problem to be solved in the present invention provides the Floor paint that a kind of fastness to rubbing is strong, transparency is good, hardness is good.
For solving the problems of the technologies described above, the present invention by the following technical solutions:
A kind of Floor paint is made by the raw material of following weight part:
3～10 parts of illite/smectite mixed layer clays, 30～40 parts of Hydroxylated acrylic resins, 25～35 parts of fatty acid alcohol acid resins, 10～20 parts of pigment, 9～13 parts of dimethylbenzene, 5～10 parts of N-BUTYL ACETATEs, 0.1～0.5 part of dispersion agent, 0.1～0.5 part of flow agent, 0.1～0.5 part of defoamer, 0.1～0.5 part of anti-settling agent.
Preferred weight part of described raw material is:
4～8 parts of illite/smectite mixed layer clays, 32～37 parts of Hydroxylated acrylic resins, 27～33 parts of fatty acid alcohol acid resins, 13～19 parts of pigment, 10～12 parts of dimethylbenzene, 6～8 parts of N-BUTYL ACETATEs, 0.1～0.4 part of dispersion agent, 0.1～0.3 part of flow agent, 0.1～0.3 part of defoamer, 0.2～0.4 part of anti-settling agent.
Optimum weight part of described raw material is:
6 parts of illite/smectite mixed layer clays, 35 parts of Hydroxylated acrylic resins, 30 parts of fatty acid alcohol acid resins, 16 parts of pigment, 11 parts of dimethylbenzene, 7 parts of N-BUTYL ACETATEs, 0.3 part of dispersion agent, 0.2 part of flow agent, 0.1 part of defoamer, 0.3 part of anti-settling agent.
In the above-mentioned raw materials, preferably from the illite/smectite mixed layer clay of producing of Shangsi County, Guangxi, all the other select the art raw material commonly used for use to described illite/smectite mixed layer clay.
Described Floor paint is that 30～60min made through high speed dispersion after above-mentioned raw materials was mixed.During use, the using method of the common Floor paint of reference gets final product.
The beneficial effect of Floor paint of the present invention is: Floor paint of the present invention is heat-resisting, wear-resisting, acid and alkali-resistance, long service life.Can produce versicolor product according to user's needs, light transmission is good, and splendid decorative effect is arranged.Applied widely, can be widely used in wooden, marble, the indoor floor of concrete structure, the surface decoration of top ceiling and the external coating of top-grade furniture.
Embodiment
Be described further with embodiment below, but the present invention is not limited to these embodiment.
Embodiment 1
Floor paint, after the raw material mixing by following weight part, 30min makes through high speed dispersion:
6 parts of illite/smectite mixed layer clays, 35 parts of Hydroxylated acrylic resins, 30 parts of fatty acid alcohol acid resins, 16 parts of pigment, 11 parts of dimethylbenzene, 7 parts of N-BUTYL ACETATEs, 0.3 part of dispersion agent, 0.2 part of flow agent, 0.1 part of defoamer, 0.3 part of anti-settling agent.
Embodiment 2
Floor paint, after the raw material mixing by following weight part, 60min makes through high speed dispersion:
3 parts of illite/smectite mixed layer clays, 35 parts of Hydroxylated acrylic resins, 35 parts of fatty acid alcohol acid resins, 10 parts of pigment, 11 parts of dimethylbenzene, 9 parts of N-BUTYL ACETATEs, 0.2 part of dispersion agent, 0.4 part of flow agent, 0.5 part of defoamer, 0.1 part of anti-settling agent.
Embodiment 3
Floor paint, after the raw material mixing by following weight part, 40min makes through high speed dispersion:
10 parts of illite/smectite mixed layer clays, 30 parts of Hydroxylated acrylic resins, 30 parts of fatty acid alcohol acid resins, 20 parts of pigment, 9 parts of dimethylbenzene, 8 parts of N-BUTYL ACETATEs, 0.5 part of dispersion agent, 0.1 part of flow agent, 0.3 part of defoamer, 0.5 part of anti-settling agent.
Embodiment 4
Floor paint, after the raw material mixing by following weight part, 30min makes through high speed dispersion:
5 parts of illite/smectite mixed layer clays, 40 parts of Hydroxylated acrylic resins, 25 parts of fatty acid alcohol acid resins, 15 parts of pigment, 12 parts of dimethylbenzene, 5 parts of N-BUTYL ACETATEs, 0.3 part of dispersion agent, 0.5 part of flow agent, 0.1 part of defoamer, 0.3 part of anti-settling agent.
Claims (4)
1. a Floor paint is characterized in that, is made by the raw material of following weight part:
3～10 parts of illite/smectite mixed layer clays, 30～40 parts of Hydroxylated acrylic resins, 25～35 parts of fatty acid alcohol acid resins, 10～20 parts of pigment, 9～13 parts of dimethylbenzene, 5～10 parts of N-BUTYL ACETATEs, 0.1～0.5 part of dispersion agent, 0.1～0.5 part of flow agent, 0.1～0.5 part of defoamer, 0.1～0.5 part of anti-settling agent.
2. Floor paint according to claim 1 is characterized in that, the weight part of described raw material is:
4～8 parts of illite/smectite mixed layer clays, 32～37 parts of Hydroxylated acrylic resins, 27～33 parts of fatty acid alcohol acid resins, 13～19 parts of pigment, 10～12 parts of dimethylbenzene, 6～8 parts of N-BUTYL ACETATEs, 0.1～0.4 part of dispersion agent, 0.1～0.3 part of flow agent, 0.1～0.3 part of defoamer, 0.2～0.4 part of anti-settling agent.
3. Floor paint according to claim 1 is characterized in that, the weight part of described raw material is:
6 parts of illite/smectite mixed layer clays, 35 parts of Hydroxylated acrylic resins, 30 parts of fatty acid alcohol acid resins, 16 parts of pigment, 11 parts of dimethylbenzene, 7 parts of N-BUTYL ACETATEs, 0.3 part of dispersion agent, 0.2 part of flow agent, 0.1 part of defoamer, 0.3 part of anti-settling agent.
4. according to claim 1,2 or 3 described Floor paints, it is characterized in that: above-mentioned raw materials makes described Floor paint through high speed dispersion 30～60min after mixing.