CN103254699A - Coating suitable for PVC (Poly Vinyl Chloride) plastic-coated cloth - Google Patents
Coating suitable for PVC (Poly Vinyl Chloride) plastic-coated cloth Download PDFInfo
- Publication number
- CN103254699A CN103254699A CN2013101912433A CN201310191243A CN103254699A CN 103254699 A CN103254699 A CN 103254699A CN 2013101912433 A CN2013101912433 A CN 2013101912433A CN 201310191243 A CN201310191243 A CN 201310191243A CN 103254699 A CN103254699 A CN 103254699A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic
- pvc
- coating
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a coating suitable for PVC (Poly Vinyl Chloride) plastic-coated cloth. The coating comprises the following raw materials in parts by weight: 90-120 parts of PVC resin, 50-80 parts of epoxy butyl oleate, 3-6 parts of organic tin stabilizer, 2-6 parts of D-810 plasticizer, 5-10 parts of white oil, 1-3 parts of epoxidized fatty acid, 1.5-4.5 parts of magnesium hydrate flame retardant, 20-40 parts of paraffin, 30-45 parts of light calcium carbonate, 20-30 parts of talcum powder and 10-20 parts of organic pigment. The coating disclosed by the invention has the advantages that low-toxicity or nontoxic raw materials are selected, so that the produced PVC plastic-coated cloths are low in toxicity and more friendly to environment; inorganic flame retardant is utilized, so that the flame retardance and the smoke abatement performance are good; and environment-friendly plasticizer is utilized, so that the thermal stability is good; and a viscosity reducer is utilized, so that the produced plastic-coated cloth has smooth and clean surfaces and is more competitive in the market.
Description
Technical field
The present invention relates to a kind of coating of the PVC of being applicable to plastic-coated fabric.
Background technology
The PVC plastic-coated fabric is exactly to coat the glue that contains PVC at canvas cloth base, making its Paint Gloss and water resistance in surface is 100%, and its purposes is very extensive, as foreign trade, grain depot, oil field, harbour, tent, boring tower clothing, the Rail Highway transportation, canvas works such as storage, colliery, open depot.The PVC plastic-coated fabric has excellent mildew resistance, tangible water-repellancy, and good low-temperature pliability, the intensity height, pulling force is strong, and is slim and graceful relatively.
The PVC plastic-coated fabric of traditional coating prescription production has the following disadvantages: the stablizer that contains lead salt and cadmium soap constituents enters human body and environment by all means, is detrimental to health contaminate environment; The softening agent that contains the phthalate composition has reproduction and development toxicity, have in addition have carinogenicity, very big to human health damage; There are shortcomings such as degradation production toxicity is big, smog is big in organic fire-retardant; Bad, the easy adhesion of product surface feel, bright and clean inadequately.
Summary of the invention
The technical problem that solves: at the deficiencies in the prior art, the invention provides a kind of coating of the PVC of being applicable to plastic-coated fabric, the PVC plastic-coated fabric toxicity of production is little, any surface finish, environmental friendliness, more can satisfy market demand.
Technical scheme: the coating that the invention provides a kind of PVC of being applicable to plastic-coated fabric, it is made up of the raw material of following parts by weight: 90 ~ 120 parts of polyvinyl chloride resins, 50 ~ 80 parts of epoxyoleic acid butyl esters, 3 ~ 6 parts of organotin stabilizers, 2 ~ 6 parts in D-810 softening agent, 5 ~ 10 parts of white oils, 1 ~ 3 part of epoxidized fatty acid, 1.5 ~ 4.5 parts of flame retardant of magnesium hydroxide, 20 ~ 40 parts in paraffin, 30 ~ 45 parts of light calcium carbonates, 20 ~ 30 parts of talcum powder, 10～20 parts of pigment dyestuffs.
As preferred version, above-described a kind of coating that is applicable to the PVC plastic-coated fabric, it is made up of the raw material of following parts by weight: 100 ~ 110 parts of polyvinyl chloride resins; 60 ~ 70 parts of epoxyoleic acid butyl esters; 4 ~ 5 parts of organotin stabilizers; 3 ~ 5 parts in D-810 softening agent; 6 ~ 9 parts of white oils; 1.5 ~ 2 parts of epoxidized fatty acids; 2 ~ 3 parts of flame retardant of magnesium hydroxide; 25 ~ 35 parts in paraffin; 35 ~ 40 parts of light calcium carbonates; 25 ~ 30 parts of talcum powder; 15～20 parts of pigment dyestuffs.
Beneficial effect: (1) coating of the present invention is selected the little or nontoxic raw material of toxicity for use, little, the environmental protection more of PVC plastic-coated fabric toxicity of production; (2) coating of the present invention uses inorganic combustion inhibitor (flame retardant of magnesium hydroxide), and is fire-retardant all good, nonpoisonous and tasteless, with low cost with smoke elimination; (3) coating of the present invention has used environment-friendly plasticizer, and thermostable effect is good, and has used viscosity-depression agent, and the plastic-coated fabric any surface finish of producing has more the market competitiveness.
Embodiment
Mode below by embodiment further specifies this explanation, and therefore scope of the present invention is not confined to following embodiment.
Embodiment 1
With 90 parts of polyvinyl chloride resins, 50 parts of epoxyoleic acid butyl esters, 3 parts of organotin stabilizers, 2 parts of D-810 softening agent, 5 parts of white oils, 1 part of epoxidized fatty acid, 1.5 parts of flame retardant of magnesium hydroxide, 20 parts of paraffin, 30 parts of light calcium carbonates, 20 parts of talcum powder, 10 parts of pigment dyestuffs are stirred to homogeneous slurry, grind through three-roll grinder, the particulate matter in the slurries is ground namely get coating.
Embodiment 2
With 100 parts of polyvinyl chloride resins, 60 parts of epoxyoleic acid butyl esters, 4 parts of organotin stabilizers, 3 parts of D-810 softening agent, 7 parts of white oils, 2 parts of epoxidized fatty acids, 2 parts of flame retardant of magnesium hydroxide, 30 parts of paraffin, 35 parts of light calcium carbonates, 25 parts of talcum powder, 15 parts of pigment dyestuffs are stirred to homogeneous slurry, grind through three-roll grinder, the particulate matter in the slurries is ground namely get coating.
Product sticking power is greater than force of cohesion, breaking tenacity 〉=120N/cm
2, plasticization temperature 125-170 ℃, viscosity changes≤50%.
Embodiment 3
With 110 parts of polyvinyl chloride resins, 70 parts of epoxyoleic acid butyl esters, 5 parts of organotin stabilizers, 4 parts of D-810 softening agent, 8 parts of white oils, 2.5 parts of epoxidized fatty acids, 3 parts of flame retardant of magnesium hydroxide, 35 parts of paraffin, 35 parts of light calcium carbonates, 25 parts of talcum powder, 15 parts of pigment dyestuffs are stirred to homogeneous slurry, grind through three-roll grinder, the particulate matter in the slurries is ground namely get coating.
Embodiment 4
With 120 parts of polyvinyl chloride resins, 80 parts of epoxyoleic acid butyl esters, 6 parts of organotin stabilizers, 6 parts of D-810 softening agent, 10 parts of white oils, 3 parts of epoxidized fatty acids, 4.5 parts of flame retardant of magnesium hydroxide, 40 parts of paraffin, 45 parts of light calcium carbonates, 30 parts of talcum powder, 20 parts of pigment dyestuffs are stirred to homogeneous slurry, grind through three-roll grinder, the particulate matter in the slurries is ground namely get coating.
Claims (2)
1. coating that is applicable to the PVC plastic-coated fabric is characterized in that being made up of the raw material of following parts by weight:
90 ~ 120 parts of polyvinyl chloride resins;
50 ~ 80 parts of epoxyoleic acid butyl esters;
3 ~ 6 parts of organotin stabilizers;
2 ~ 6 parts in D-810 softening agent;
5 ~ 10 parts of white oils;
1 ~ 3 part of epoxidized fatty acid;
1.5 ~ 4.5 parts of flame retardant of magnesium hydroxide;
20 ~ 40 parts in paraffin;
30 ~ 45 parts of light calcium carbonates;
20 ~ 30 parts of talcum powder;
10～20 parts of pigment dyestuffs.
2. a kind of coating that is applicable to the PVC plastic-coated fabric according to claim 1 is characterized in that it is made up of the raw material of following parts by weight:
100 ~ 110 parts of polyvinyl chloride resins;
60 ~ 70 parts of epoxyoleic acid butyl esters;
4 ~ 5 parts of organotin stabilizers;
3 ~ 5 parts in D-810 softening agent;
6 ~ 9 parts of white oils;
1.5 ~ 2 parts of epoxidized fatty acids;
2 ~ 3 parts of flame retardant of magnesium hydroxide;
25 ~ 35 parts in paraffin;
35 ~ 40 parts of light calcium carbonates;
25 ~ 30 parts of talcum powder;
15～20 parts of pigment dyestuffs.