CN104403426A - Nonslip paint - Google Patents
Nonslip paint Download PDFInfo
- Publication number
- CN104403426A CN104403426A CN201410741559.XA CN201410741559A CN104403426A CN 104403426 A CN104403426 A CN 104403426A CN 201410741559 A CN201410741559 A CN 201410741559A CN 104403426 A CN104403426 A CN 104403426A
- Authority
- CN
- China
- Prior art keywords
- percent
- parts
- nonslip
- paint
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nonslip paint. The nonslip paint comprises the following raw materials by weight percent: 25 to 30 percent of an elastic polyurethane emulsion, 20 to 40 percent of a modified ammonium polyphosphate flame retardant, 2 to 5 percent of titanium dioxide, 3 to 4 percent of barium sulphate, 3 to 6 percent of coarse whiting, 2 to 85 percent of fillers, 10 to 20 percent of water, and 20 to 30 percent of a waterborne additive. By adopting the mode, the nonslip paint has good water resistance, adhesive force and stable chemical property after forming a film, meanwhile does not obstruct the flame retardant property of the whole flame retardant system under the condition that coating is heated. In terms of the using effect, the nonslip paint has good elongation property, high tensile strength and high color retaining capacity.
Description
Technical field
The present invention relates to building coating field, particularly a kind of skid-resistant coating.
Background technology
The one anti-skidding building materials that slip when skid-resistant coating is used for various public place, the deck, ground, workshop, family, garden etc. of ship prevent from walking.Its advantage is that sticking power is good, coarse and can be effectively anti-skidding, can adapt to, different places because of ground, different object and adopt different anti-skidding building materials.But the environmental-protecting performance of some anti-slip material is bad, on environment unfriendly and impact building attractive in appearance.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of skid-resistant coating, solves skid-resistant coating brushing weak effect, problem not environmentally.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of skid-resistant coating, its composition of raw materials is made up of the material of following masses percentage composition:
Gum Rosin 25 ~ 30 parts;
Butyl latex 40 ~ 60 parts;
Nano-oxide particles toughener 6 ~ 12 parts;
Aliphatic firming agent 12 ~ 16 parts;
6 ~ 12 parts, sodium sulfate;
Talcum powder 2 ~ 6 parts;
Carbon black 3 ~ 6 parts;
Thickening material 1 ~ 5 part.
The invention has the beneficial effects as follows: provide a kind of skid-resistant coating, this skid-resistant coating is while the non-skid property ensureing coating, and the performances such as the sticking power of described coating, weathering resistance, wear resistance and resistance to elevated temperatures are all very excellent.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention 1 comprises: a kind of skid-resistant coating, and its composition of raw materials is made up of the material of following masses percentage composition:
Gum Rosin 25 parts;
Butyl latex 40 parts;
Nano-oxide particles toughener 6 parts;
Aliphatic firming agent 12 parts;
6 parts, sodium sulfate;
Talcum powder 2 parts;
Carbon black 3 parts;
Thickening material 1 part.
The embodiment of the present invention 2 comprises: a kind of skid-resistant coating, and its composition of raw materials is made up of the material of following masses percentage composition:
Gum Rosin 26 parts;
Butyl latex 50 parts;
Nano-oxide particles toughener 8 parts;
Aliphatic firming agent 14 parts;
10 parts, sodium sulfate;
Talcum powder 4 parts;
Carbon black 5 parts;
Thickening material 3 parts.
The embodiment of the present invention 3 comprises: a kind of skid-resistant coating, and its composition of raw materials is made up of the material of following masses percentage composition:
Gum Rosin 30 parts;
Butyl latex 60 parts;
Nano-oxide particles toughener 12 parts;
Aliphatic firming agent 16 parts;
12 parts, sodium sulfate;
Talcum powder 6 parts;
Carbon black 6 parts;
Thickening material 5 parts.
Above-described embodiment is only for illustrating technical conceive of the present invention and feature; its object is to person skilled in the art can be understood content of the present invention and be implemented; can not limit the scope of the invention with this; all equivalences done according to spirit of the present invention change or modify, and all should be encompassed in protection scope of the present invention.
Claims (1)
1. a skid-resistant coating, is characterized in that: its composition of raw materials is made up of the material of following masses percentage composition:
Gum Rosin 25 ~ 30 parts;
Butyl latex 40 ~ 60 parts;
Nano-oxide particles toughener 6 ~ 12 parts;
Aliphatic firming agent 12 ~ 16 parts;
6 ~ 12 parts, sodium sulfate;
Talcum powder 2 ~ 6 parts;
Carbon black 3 ~ 6 parts;
Thickening material 1 ~ 5 part.