CN103254666A - Production method of non-adhesive coating for substrate surfaces - Google Patents
Production method of non-adhesive coating for substrate surfaces Download PDFInfo
- Publication number
- CN103254666A CN103254666A CN2013102034972A CN201310203497A CN103254666A CN 103254666 A CN103254666 A CN 103254666A CN 2013102034972 A CN2013102034972 A CN 2013102034972A CN 201310203497 A CN201310203497 A CN 201310203497A CN 103254666 A CN103254666 A CN 103254666A
- Authority
- CN
- China
- Prior art keywords
- liquid
- production method
- substrate surface
- organoalkoxysilane
- sticky coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a non-adhesive coating for substrate surfaces. The production method is characterized by firstly preparing a solution A and a solution B respectively, and mixing the solution A with the solution B when in use. The coating is applied to the substrate surfaces and endows the substrate surfaces with the properties such as non-adhesiveness, heat resistance, weather resistance, decoration property, wound resistance, solvent resistance, non-inflammability, release property, foreign matter adhesion prevention property and the like.
Description
Technical field
The present invention relates to a kind of production method of the non-sticky coating for the substrate surface application.
Background technology
The coating of existing base material for metal or nonmetallic surface, flame retardant resistance is low, resistance toxicity is poor, lack not viscosity.When they are applied to substrate surface, do not reach effect fire-retardant, that resistance is malicious, not sticking.
Summary of the invention
Order of the present invention is the production method that works out a kind of non-sticky coating for the substrate surface application.
What the present invention will solve is the existing coating that is used for the base material of metal or nonmetallic surface, and flame retardant resistance is low, resistance toxicity is poor, lack the not problem of viscosity.
Production method of the present invention is: produce A liquid and B liquid at first respectively, A liquid preparation method is: add surface-modifying agent silicone oil 1-5g, methyl alcohol 8-15g, ethylene glycol monobutyl ether 1-2g, water 5-15g, phosphoric acid 0.01-0.05g, acetic acid 0.1-0.2g stirring in silicon sol 15-20g after, add diadust 1-4g, diadust granularity 5-100, dioxide peroxide 8-12g, short glass fiber 1-2g, calcium sulfate crystal whiskers 1-2g, mineral dye 10-30g again, after they are mixed, disperse with ultrasonic dispersing machine, get the A liquid of the about 80g of total amount; B liquid preparation method is: get organoalkoxysilane (MTMS) 15-25g, organoalkoxysilane (TEOS) 0.1-0.5g, surface-modifying agent silicone oil 0.1-0.8g, mix the back gets the about 20g of total amount with ultrasonic dispersing B liquid;
During use above-mentioned A liquid and B liquid are mixed,, placed at normal temperatures 2 hours, not viscous composition after about 60 minutes 30 ℃ of following ultrasonication.
Advantage of the present invention is: the present invention is applied to substrate surface, and viscosity, thermotolerance, weathering resistance, ornamental, anti-injury property, solvent resistance, uninflammability, release, foreign substances are not adhered to preventing property etc. to give substrate surface.
Embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
The production method of a kind of non-sticky coating for the substrate surface application of the present invention, produce A liquid and B liquid at first respectively, A liquid preparation method is: add surface-modifying agent silicone oil 1-5g in silicon sol 15-20g, methyl alcohol 8-15g, ethylene glycol monobutyl ether 1-2g, water 5-15g, phosphoric acid 0.01-0.05g, after acetic acid 0.1-0.2g stirs, add diadust 1-4g again, diadust granularity 5-100, dioxide peroxide 8-12g, short glass fiber 1-2g, calcium sulfate crystal whiskers 1-2g, mineral dye 10-30g, after they are mixed, disperse with ultrasonic dispersing machine, get the A liquid of the about 80g of total amount; B liquid preparation method is: get organoalkoxysilane (MTMS) 15-25g, organoalkoxysilane (TEOS) 0.1-0.5g, surface-modifying agent silicone oil 0.1-0.8g, mix the back gets the about 20g of total amount with ultrasonic dispersing B liquid;
During use above-mentioned A liquid and B liquid are mixed,, placed at normal temperatures 2 hours, not viscous composition after about 60 minutes 30 ℃ of following ultrasonication.
Mineral dye is one or two or more kinds combination in the titanium dioxide, zinc oxide, ferric oxide, cobalt monoxide, chromium sesquioxide of particle diameter 0.03～20.Thickness 0.1-1, the length 5-300 of whisker.
A specific embodiment of the present invention is:
After adding surface-modifying agent silicone oil 2.2g, methyl alcohol 10.7g, ethylene glycol monobutyl ether 1.6g, water (distilled water) 10.7g, phosphoric acid 0.05g, acetic acid 0.16g in the silicon sol 16.3g, under the state that stirs, after adding diadust 3.3g, dioxide peroxide 10.7g, short glass fiber 1.1g, calcium sulfate crystal whiskers 1.1g, white pigment 21.7g, mix equably, disperseed 40 minutes with ultrasonic dispersing machine afterwards, produce the A liquid of about 80g.
Organoalkoxysilane (MTMS) 19g, organoalkoxysilane (TEOS) 0.5g, surface-modifying agent silicone oil 0.4g are mixed the back produced about 20g in 10 minutes with ultrasonic dispersing B liquid.
During use above-mentioned A liquid and B liquid are mixed,, placed at normal temperatures 2 hours, not viscous composition after about 60 minutes 30 ℃ of following ultrasonication.
Claims (3)
1. production method that is used for the non-sticky coating of substrate surface application, its feature is in producing A liquid and B liquid at first respectively, A liquid preparation method is: add surface-modifying agent silicone oil 1-5g in silicon sol 15-20g, methyl alcohol 8-15g, ethylene glycol monobutyl ether 1-2g, water 5-15g, phosphoric acid 0.01-0.05g, after acetic acid 0.1-0.2g stirs, add diadust 1-4g again, diadust granularity 5-100, dioxide peroxide 8-12g, short glass fiber 1-2g, calcium sulfate crystal whiskers 1-2g, mineral dye 10-30g, after they are mixed, disperse with ultrasonic dispersing machine, get the A liquid of the about 80g of total amount; B liquid preparation method is: get organoalkoxysilane (MTMS) 15-25g, organoalkoxysilane (TEOS) 0.1-0.5g, surface-modifying agent silicone oil 0.1-0.8g, mix the back gets the about 20g of total amount with ultrasonic dispersing B liquid;
During use above-mentioned A liquid and B liquid are mixed,, placed at normal temperatures 2 hours, not viscous composition after about 60 minutes 30 ℃ of following ultrasonication.
2. the production method of the non-sticky coating for the substrate surface application according to claim 1 is characterized in that mineral dye is one or two or more kinds combination in the titanium dioxide, zinc oxide, ferric oxide, cobalt monoxide, chromium sesquioxide of particle diameter 0.03～20.
3. the production method of the non-sticky coating for the substrate surface application according to claim 1 is characterized in that thickness 0.1-1, the length 5-300 of whisker.