CN103254769A - Production method of non-adhesive coating for substrate surfaces - Google Patents
Production method of non-adhesive coating for substrate surfaces Download PDFInfo
- Publication number
- CN103254769A CN103254769A CN2013102035566A CN201310203556A CN103254769A CN 103254769 A CN103254769 A CN 103254769A CN 2013102035566 A CN2013102035566 A CN 2013102035566A CN 201310203556 A CN201310203556 A CN 201310203556A CN 103254769 A CN103254769 A CN 103254769A
- Authority
- CN
- China
- Prior art keywords
- production method
- substrate surface
- dispersion
- nano
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production method of a non-adhesive coating for substrate surfaces. The production method is characterized by firstly preparing a solution A and a solution B respectively and mixing the solution A with the solution B when in use. The coating is applied to the substrate surfaces and endows the substrate surfaces with the properties such as non-adhesiveness, heat resistance, weather resistance, decoration property, wound resistance, solvent resistance, non-inflammability, release property, foreign matter adhesion prevention property and the like.
Description
Technical field
The present invention relates to a kind of production method of the non-sticky coating for the substrate surface application.
Background technology
The coating of existing base material for metal or nonmetallic surface, flame retardant resistance is low, resistance toxicity is poor, lack not viscosity.When they are applied to substrate surface, do not reach effect fire-retardant, that resistance is malicious, not sticking.
Summary of the invention
Order of the present invention is the production method that works out a kind of non-sticky coating for the substrate surface application.
What the present invention will solve is the existing coating that is used for the base material of metal or nonmetallic surface, and flame retardant resistance is low, resistance toxicity is poor, lack the not problem of viscosity.
Production method of the present invention is: after adding surface-modifying agent silicone oil 20-40g, colloidal silicon dioxide 15-20g, organoalkoxysilane (TEOS) 0.8-2 in siloxane polymer (MPSP) 8-12g, after dissolving about 30 minutes with ultrasonic wave, after adding interpolation diadust 2-4g, diadust granularity 5-100 g, nano dye dispersion liquid 20-40g, tosic acid (p-TSA) 0.1-0.3g, be mixed and disperseed about 20 minutes with ultrasonic dispersing machine again, and placed at normal temperatures 2 hours, the painted transparent ink powder of spray ink Printing that obtains 100g is viscous composition not.
Advantage of the present invention is: the present invention is applied to substrate surface, and viscosity, thermotolerance, weathering resistance, ornamental, anti-injury property, solvent resistance, uninflammability, release, foreign substances are not adhered to preventing property etc. to give substrate surface.
Embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
The production method of a kind of non-sticky coating for the substrate surface application of the present invention, in siloxane polymer (MPSP) 8-12g, add surface-modifying agent silicone oil 20-40g, colloidal silicon dioxide 15-20g, behind organoalkoxysilane (TEOS) 0.8-2, after dissolving about 30 minutes with ultrasonic wave, add and add diadust 2-4g, diadust granularity 5-100 g, nano dye dispersion liquid 20-40g, behind tosic acid (p-TSA) 0.1-0.3g, be mixed and disperseed about 20 minutes with ultrasonic dispersing machine again, and placed at normal temperatures 2 hours, the painted transparent ink powder of spray ink Printing that obtains 100g is viscous composition not.
The nano dye dispersion liquid be mineral dye add water or organic solvent in, disperse with the superfine dispersion machine, after the dispersion the nano inorganic dispersible pigment dispersion, the median size of this nano inorganic dispersible pigment dispersion is 5～300, and is best 5～80.Mineral dye comprises titanium dioxide, zinc oxide, cobalt monoxide, Ti nitride, Zr nitride.
A specific embodiment of the present invention is:
Add behind surface-modifying agent silicone oil 33g, colloidal silicon dioxide 18.5g, organoalkoxysilane (TEOS) 0.92g with the ultrasonic wave dissolving after 30 minutes in siloxane polymer (MPSP) 11.9g, mix equably after adding diamond 2.64g, nanometer blue pigments dispersion liquid 33g, tosic acid (p-TSA) 0.13g, disperseed 20 minutes with ultrasonic dispersing machine again, and placed at normal temperatures 2 hours, the transparent ink powder of spray ink Printing that produces 100g is viscous composition not.
Claims (3)
1. production method that is used for the non-sticky coating of substrate surface application, it is characterized in that in siloxane polymer (MPSP) 8-12g, adding surface-modifying agent silicone oil 20-40g, colloidal silicon dioxide 15-20g, behind organoalkoxysilane (TEOS) 0.8-2, after dissolving about 30 minutes with ultrasonic wave, add and add diadust 2-4g, diadust granularity 5-100 g, nano dye dispersion liquid 20-40g, behind tosic acid (p-TSA) 0.1-0.3g, be mixed and disperseed about 20 minutes with ultrasonic dispersing machine again, and placed at normal temperatures 2 hours, the painted transparent ink powder of spray ink Printing that obtains 100g is viscous composition not.
2. the production method of a kind of non-sticky coating for the substrate surface application according to claim 1, it is characterized in that the nano dye dispersion liquid be mineral dye add water or organic solvent in, disperse with the superfine dispersion machine, get the nano inorganic dispersible pigment dispersion after the dispersion, the median size of this nano inorganic dispersible pigment dispersion is 5～300, and is best 5～80.
3. the production method of a kind of non-sticky coating for the substrate surface application according to claim 1 is characterized in that mineral dye comprises titanium dioxide, zinc oxide, cobalt monoxide, Ti nitride, Zr nitride.