CN103242058A - 一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺及制成的蓄热制品 - Google Patents
一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺及制成的蓄热制品 Download PDFInfo
- Publication number
- CN103242058A CN103242058A CN2013101846249A CN201310184624A CN103242058A CN 103242058 A CN103242058 A CN 103242058A CN 2013101846249 A CN2013101846249 A CN 2013101846249A CN 201310184624 A CN201310184624 A CN 201310184624A CN 103242058 A CN103242058 A CN 103242058A
- Authority
- CN
- China
- Prior art keywords
- heat storage
- chromium slag
- storage medium
- friendly energy
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺及制成的蓄热制品,1)配料:取铬渣10~70Wt%,煤1~10Wt%,高铝矾土或三石10~70Wt%,硅镁微粉5~20Wt%,粘性土5~10Wt%;2)在球磨机混磨,得到用铬渣制成的高效环保节能蓄热介质原料。用铬渣制成的高效环保节能蓄热介质原料可制成蜂窝陶瓷,蓄热球,格子砖等蓄热制品。本发明具有如下的有益效果,一是铬渣与高铝矾土形成陶瓷基复合体蓄热制品,抗腐蚀性和阻止与氧化铁、氧化亚铁形成低共熔物,使用寿命长,热效率提高20%以上;二是在配料中加入了碳,在烧制过程中产生一氧化碳,一氧化碳的强还原性能,将有毒的六价铬还原成稳定无毒三价铬,实现对铬渣的解毒,消除了铬渣对环境的污染;三是使铬渣得到了利用,节约了资源,降低了蓄热制品的生产成本,有利于各种蓄能节能项目开发和运用,有益于节能环保。
Description
技术领域
本发明涉及一种对铬渣解毒制作高效无机盐/陶瓷基复合蓄热材料及制成的蓄热制品。
背景技术
铬盐产品是一些工业生产中不可缺少的原料,但在铬盐的生产过程中会产生有毒的铬渣很容易毒害生物,污染环境,虽然目前有一些治理方法,但都是用量少或者是成本高,而不能彻底解决问题;另一方面,全球面临能源资源的枯竭,利用蓄热制品将工业余能的回收利用,将太阳能、风能等各种可再生能源进行收集、蓄存和转换利用成为未来能源发展的方向,目前,蓄热制品用得最多的是蓄热球、格子砖、蜂窝陶瓷等,此类制品以高铝质的高铝矾土、三石(硅线石、红柱石、篮晶石)、莫来石为主材质,高铝质蓄热制品虽然蓄热密度大,但在实际使用中常常没有足够的时间空间来达到预想的蓄热密度,如:轧钢加热炉的冷热风切换时间一般只有30秒,而且,高铝质的蓄热制品在具有酸、碱等腐蚀性高温状态下,使用寿命很短,在存在大量氧化铁、氧化亚铁的高温状态下,蓄热制品极易形成低共熔物,降低制品的软熔温度。
发明内容
本发明的目的是提供一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺及制成的蓄热制品。
本发明的目的是通过如下方式实现的:一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺:
1)配料:取铬渣10~70Wt%,煤1~10Wt%,高铝矾土或三石10~70Wt%,硅镁微粉5~20Wt%,粘性土5~10Wt%;
2)在球磨机混磨,得到用铬渣制成的高效环保节能蓄热介质原料。
2、一种用铬渣制成的高效环保节能蓄热介质原料制成的蜂窝陶瓷:
1)将用铬渣制成的高效环保节能蓄热介质原料加水在捏合机捏合;
2)练泥;
3)陈腐;
4)压机压制成型;
5)干燥;
6)精整;
7)烧成。
3、一种用铬渣制成的高效环保节能蓄热介质原料制成的蓄热球:
1)将用铬渣制成的高效环保节能蓄热介质原料进行团球或压制成球;
2)干燥;
3)烧成。
4、一种用铬渣制成的高效环保节能蓄热介质原料制成的格子砖:
1)将用铬渣制成的高效环保节能蓄热介质原料压制成格子砖;
2)干燥;
3)烧成。
本发明具有如下的有益效果,一是铬渣与高铝矾土形成陶瓷基复合体蓄热制品,抗腐蚀性和阻止与氧化铁、氧化亚铁形成低共熔物,抗高温,耐氧化,抗化学腐蚀性好,热膨胀系数小,蓄热密度大,热效率提高20%以上,使用寿命长;二是在配料中加入了碳,在烧制过程中产生一氧化碳,一氧化碳的强还原性能,将有毒的六价铬还原成稳定无毒三价铬,实现对铬渣的解毒,消除了铬渣对环境的污染;三是使铬渣得到了利用,节约了资源,降低了蓄热制品的生产成本,有利于各种蓄能节能项目开发和运用,有益于节能环保。
附图说明
图1是本发明铬渣与三氧化二铝复合的成分和耐火度关联图。
具体实施方式
下面结合实施例对本发明做进一步说明:
实施例1
取铬渣10Wt%,煤1Wt%,高铝矾土70Wt%,硅镁微粉10Wt%,粘性土9Wt%;在球磨机混磨;制成一种用铬渣制成的高效环保节能蓄热介质原料,使用温度1700℃以上。
实施例2
取铬渣50Wt%,煤5Wt%,高铝矾土35Wt%,硅镁微粉5Wt%,粘性土5Wt%。在球磨机混磨;制成一种用铬渣制成的高效环保节能蓄热介质原料,使用温度1500℃以上。
实施例3
取铬渣70Wt%,煤7Wt%,三石12Wt%,硅镁微粉5Wt%,粘性土6Wt%。在球磨机混磨;制成一种用铬渣制成的高效环保节能蓄热介质原料,使用温度1300℃以上。
实施例4
一种用铬渣制成的高效环保节能蓄热介质原料制成的蜂窝陶瓷:
1)将用铬渣制成的高效环保节能蓄热介质原料加水在捏合机捏合;
2)练泥;
3)陈腐;
4)压机压制成型;
5)干燥;
6)精整;
7)烧成。
实施例5
一种用铬渣制成的高效环保节能蓄热介质原料制成的蓄热球:
1)将用铬渣制成的高效环保节能蓄热介质原料进行团球或压制成球;
2)干燥;
3)烧成。
实施例6
一种用铬渣制成的高效环保节能蓄热介质原料制成的格子砖:
1)将用铬渣制成的高效环保节能蓄热介质原料压制成格子砖;
2)干燥;
3)烧成。
Claims (4)
1.一种用铬渣制成的高效环保节能蓄热介质原料的生产工艺,其特征在于:
1)配料:取铬渣10~70Wt%,煤1~10Wt%,高铝矾土或三石10~70Wt%,硅镁微粉5~20Wt%,粘性土5~10Wt%;
2)在球磨机混磨,得到用铬渣制成的高效环保节能蓄热介质原料。
2.一种用铬渣制成的高效环保节能蓄热介质原料制成的蜂窝陶瓷:
1)将用铬渣制成的高效环保节能蓄热介质原料加水在捏合机捏合;
2)练泥;
3)陈腐;
4)压机压制成型;
5)干燥;
6)精整;
7)烧成。
3.一种用铬渣制成的高效环保节能蓄热介质原料制成的蓄热球:
1)将用铬渣制成的高效环保节能蓄热介质原料进行团球或压制成球;
2)干燥;
3)烧成。
4.一种用铬渣制成的高效环保节能蓄热介质原料制成的格子砖:
1)将用铬渣制成的高效环保节能蓄热介质原料压制成格子砖;
2)干燥;
3)烧成。