CN103236285A - 一种环保导电浆料及其制备方法 - Google Patents

一种环保导电浆料及其制备方法 Download PDF

Info

Publication number
CN103236285A
CN103236285A CN2013101086289A CN201310108628A CN103236285A CN 103236285 A CN103236285 A CN 103236285A CN 2013101086289 A CN2013101086289 A CN 2013101086289A CN 201310108628 A CN201310108628 A CN 201310108628A CN 103236285 A CN103236285 A CN 103236285A
Authority
CN
China
Prior art keywords
parts
slurry
preparation
ethanol
environmental protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101086289A
Other languages
English (en)
Inventor
宋玉春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TOPUSEN BATTERY Co Ltd
Original Assignee
ANHUI TOPUSEN BATTERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TOPUSEN BATTERY Co Ltd filed Critical ANHUI TOPUSEN BATTERY Co Ltd
Priority to CN2013101086289A priority Critical patent/CN103236285A/zh
Publication of CN103236285A publication Critical patent/CN103236285A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保导电浆料及其制备方法，其组成原料的重量份为：导电铜粉35-40、饱和聚酯树脂4.5-5.5、四酚基乙烷四缩水甘油醚环氧树脂6.5-7.5、交联剂TAC 1.6-1.8、二甲基二氯硅烷2.5-3.0、烷基醇酰胺1.5-1.7、改性纳米碳7.5-8.5、疏水改性聚丙烯酸酯4-6、聚丙烯酰胺1.2-1.4、氮化铝粉5-7和乙醇24-28；本发明制备方法简单，操作方便，配方合理，以导电铜粉作为主料，乙醇作为有机溶剂，在配方中添加了改性纳米碳，增加了本发明浆料的导电性能，制得的导电浆料可广泛应用于薄膜开关、电路及电路板等生产中，而且导电浆料无有害物质，符合国家标准。

Description

一种环保导电浆料及其制备方法
技术领域
本发明涉及一种环保导电浆料及其制备方法，属于电子浆料领域。
背景技术
导电浆料主要应用于薄膜开关、挠性电路等方向，随着我国丝网印刷以及柔性线路板行业的崛起，薄膜软性线路用的导电浆料的研究和开发也越来越受到关注，在日本及西方发达国家在过去的二十年里对导电浆料已经有较深入的研究，并有产品以不同的商品名称应用于实际，在我国，导电浆料也已经逐步进入产业化阶段，而珠江三角洲大量的薄膜开关生产厂家，就是导电浆料庞大的客户群之一，目前，环保是全世界人民共同关注的话题，各个国家的各行各业也都越来越重视环保。
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提供一种环保导电浆料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
环保导电浆料，其组成原料的重量份为：导电铜粉35-40、饱和聚酯树脂4.5-5.5、四酚基乙烷四缩水甘油醚环氧树脂6.5-7.5、交联剂 TAC  1.6-1.8、二甲基二氯硅烷2.5-3.0、烷基醇酰胺1.5-1.7、改性纳米碳7.5-8.5、疏水改性聚丙烯酸酯4-6、聚丙烯酰胺1.2-1.4、氮化铝粉5-7和乙醇24-28。
环保导电浆料，其组成原料的重量份为：导电铜粉38、饱和聚酯树脂5.0、四酚基乙烷四缩水甘油醚环氧树脂7.0、交联剂 TAC  1.7、二甲基二氯硅烷2.8、烷基醇酰胺1.6、改性纳米碳8.0、疏水改性聚丙烯酸酯5、聚丙烯酰胺1.3、氮化铝粉6和乙醇26。
环保导电浆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，首先将饱和聚酯树脂、四酚基乙烷四缩水甘油醚环氧树脂和乙醇在温度50-55℃的条件下混合均匀，得到有机载体；
（2）在步骤（1）的有机载体中加入其它组成原料，加热至40-50℃，机械搅拌均匀；然后再在三辊研磨机上进行混合，研磨浆料粒度至8-15微米，即得成品。
所述的改性纳米碳的制备方法如下：将纳米碳浸泡于8-12%的醋酸溶液中，超声分散20-30分钟，然后加入聚苯胺继续分散10-15分钟，用量为纳米碳的1-2%，后加入过硫酸钾，用量为纳米碳的0.1-0.2%，反应10-15分钟，反应结束后用蒸馏水清洗过滤、干燥，得到改性纳米碳。
本发明的有益效果：
本发明制备方法简单，操作方便，配方合理，以导电铜粉作为主料，乙醇作为有机溶剂，在配方中添加了改性纳米碳，增加了本发明浆料的导电性能，制得的导电浆料可广泛应用于薄膜开关、电路及电路板等生产中，而且导电浆料无有害物质，符合国家标准。
具体实施方式
实施例1：环保导电浆料，其组成原料的重量份（kg）为：导电铜粉38、饱和聚酯树脂5.0、四酚基乙烷四缩水甘油醚环氧树脂7.0、交联剂 TAC  1.7、二甲基二氯硅烷2.8、烷基醇酰胺1.6、改性纳米碳8.0、疏水改性聚丙烯酸酯5、聚丙烯酰胺1.3、氮化铝粉6和乙醇26。
环保导电浆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，首先将饱和聚酯树脂、四酚基乙烷四缩水甘油醚环氧树脂和乙醇在温度52℃的条件下混合均匀，得到有机载体；
（2）在步骤（1）的有机载体中加入其它组成原料，加热至45℃，机械搅拌均匀；然后再在三辊研磨机上进行混合，研磨浆料粒度至8-15微米，即得成品。
所述的改性纳米碳的制备方法如下：将纳米碳浸泡于10%的醋酸溶液中，超声分散25分钟，然后加入聚苯胺继续分散12分钟，用量为纳米碳的1.5%，后加入过硫酸钾，用量为纳米碳的0.15%，反应12分钟，反应结束后用蒸馏水清洗过滤、干燥，得到改性纳米碳。
上述制得的环保导电浆料的性能数据：表面电阻为≤0.025Ω；2、屏蔽率＞76.5dB；3、附着力为4.6B；4、硬度为2.3H；5、烘干温度为58℃，只需21分钟，导电浆料的固含量在48-51%之间。

Claims (4)

1.一种环保导电浆料，其特征在于其组成原料的重量份为：导电铜粉35-40、饱和聚酯树脂4.5-5.5、四酚基乙烷四缩水甘油醚环氧树脂6.5-7.5、交联剂 TAC  1.6-1.8、二甲基二氯硅烷2.5-3.0、烷基醇酰胺1.5-1.7、改性纳米碳7.5-8.5、疏水改性聚丙烯酸酯4-6、聚丙烯酰胺1.2-1.4、氮化铝粉5-7和乙醇24-28。
2.根据权利要求1所述的环保导电浆料，其特征在于其组成原料的重量份为：导电铜粉38、饱和聚酯树脂5.0、四酚基乙烷四缩水甘油醚环氧树脂7.0、交联剂 TAC  1.7、二甲基二氯硅烷2.8、烷基醇酰胺1.6、改性纳米碳8.0、疏水改性聚丙烯酸酯5、聚丙烯酰胺1.3、氮化铝粉6和乙醇26。
3.一种如权利要求1所述的环保导电浆料的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，首先将饱和聚酯树脂、四酚基乙烷四缩水甘油醚环氧树脂和乙醇在温度50-55℃的条件下混合均匀，得到有机载体；
（2）在步骤（1）的有机载体中加入其它组成原料，加热至40-50℃，机械搅拌均匀；然后再在三辊研磨机上进行混合，研磨浆料粒度至8-15微米，即得成品。
4.根据权利要求1所述的环保导电浆料，其特征在于，所述的改性纳米碳的制备方法如下：将纳米碳浸泡于8-12%的醋酸溶液中，超声分散20-30分钟，然后加入聚苯胺继续分散10-15分钟，用量为纳米碳的1-2%，后加入过硫酸钾，用量为纳米碳的0.1-0.2%，反应10-15分钟，反应结束后用蒸馏水清洗过滤、干燥，得到改性纳米碳。
CN2013101086289A 2013-04-01 2013-04-01 一种环保导电浆料及其制备方法 Pending CN103236285A (zh)