CN103232199A - 全废渣粉煤灰小型空心砌块及其制备方法 - Google Patents

全废渣粉煤灰小型空心砌块及其制备方法 Download PDF

Info

Publication number
CN103232199A
CN103232199A CN2013101639643A CN201310163964A CN103232199A CN 103232199 A CN103232199 A CN 103232199A CN 2013101639643 A CN2013101639643 A CN 2013101639643A CN 201310163964 A CN201310163964 A CN 201310163964A CN 103232199 A CN103232199 A CN 103232199A
Authority
CN
China
Prior art keywords
fly ash
hollow block
small hollow
percent
ash small
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101639643A
Other languages
English (en)
Inventor
韦展艺
姜曙光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shihezi University
Original Assignee
Shihezi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shihezi University filed Critical Shihezi University
Priority to CN2013101639643A priority Critical patent/CN103232199A/zh
Publication of CN103232199A publication Critical patent/CN103232199A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种利用工业废渣作为原料并添加一定量外加剂制造的粉煤灰小型空心砌块，涉及建筑材料技术领域。全废渣粉煤灰小型空心砌块，其特征在于：由粉煤灰、电石渣、粉煤灰陶粒、柠檬酸渣作为原料及添加外加剂，经搅拌、消化、轮碾、成型、预养，最后经高温高压养护后制成。各组分的重量百分比为：粉煤灰30-60％，电石渣10-25％，粉煤灰陶粒20-30％，柠檬酸渣1-3％，外加剂1-2％。该发明的有益效果是所用主要原料全部为工业废渣，且生产出的砌块强度高、质量轻、保温隔热性好、节能利废、节省土地，可以使工业废渣实现减量化、资源化、循环化利用。用上述方案制造的粉煤灰空心砌块，经检测，各项技术指标均达到JC862-2000《粉煤灰小型空心砌块》标准的要求。

Description

全废渣粉煤灰小型空心砌块及其制备方法
技术领域：
本发明涉及一种利用工业废渣作为原料并添加一定量外加剂制造的粉煤灰小型空心砌块，属于建筑用墙体材料技术领域。
背景技术：
目前的燃煤发电厂的排放物为粉煤灰，是最大宗的工业固体废物之一，粉煤灰处理不当会造成环境污染。而在聚氯乙烯工业中，用电石法聚氯乙烯装置生产聚氯乙烯的过程中产生的电石废渣已经成为电石法生产的巨大障碍，粉煤灰、电石废渣、柠檬酸渣等工业废渣不但占用场地，而且污染环境，这些工业废渣如不能加以利用，将给环境带来极大的危害。因此，利用粉煤灰、电石废渣、柠檬酸渣为原料生产用于建筑业的粉煤灰小型空心砌块，是实现生产装置清洁化生产、资源高效循环利用及充分利用当地特有资源的举措。
发明内容：
本发明的目的在于利用工业废渣作为原材料，主要材料为粉煤灰，粉煤灰陶粒作为骨料，电石渣和柠檬酸渣作为胶结料，添加一定量外加剂制成一种适用于建筑墙体材料领域的粉煤灰小型空心砌块，从而替代粘土砖，节约了土地资源，减少了大气的粉尘污染，并使废弃物得以二次利用。
本发明的技术方案如下：一种全废渣粉煤灰小型空心砌块，由粉煤灰、电石渣、粉煤灰陶粒、柠檬酸渣及一定量外加剂为原料制成，主要原材料的配比为：
Figure BSA00000889485500011
上述外加剂包括水玻璃、硫酸钠和氢氧化钠的组合物，其中各组分占合成剂的重量百分比分别是：水玻璃25-45％、硫酸钠15-25％、氢氧化钠30-50％。
一种全废渣粉煤灰小型空心砌块的制备方法，首先按比例配料并将各种原料混合均匀，加水搅拌使含水率为10-13％，再将混合料消化、轮碾、成型、预养，最后经高温高压养护后制成蒸压粉煤灰砖，养护压力为1.0-1.2Mpa，养护温度为180-200℃，养护时间为10-12h。
用上述方案制造的粉煤灰空心砌块，经检测，各项技术指标均达到国家标准，且容重轻、强度好、成本低、隔热保温性能好、干燥收缩率小，适用于普通砌体结构及框架结构。
本发明的目的，是提供一种新的粉煤灰小型空心砌块的制备方法，其充分利用了粉煤灰的活性特点加大掺入量，利用蒸压养护促使小型空心砌块各原料间能够充分反应，提高强度等物理力学性能，同时促进工业废渣的有利循环利用，实现无害化生产。
具体实施方式：
下面结合实施例对本发明做进一步的描述：
实施例1：
配料：粉煤灰50％，电石渣23％，粉煤灰陶粒23％，柠檬酸渣2％，外加剂2％
制造工艺：将上述原料加水搅拌成含水率为12％的混合料，将混合料消化、轮碾、成型、预养，最后经高温高压养护后制成蒸压粉煤灰小型空心砌块，其养护压力为1.0Mpa，养护温度为180℃，养护时间为12h，制成390mm×190mm×190mm粉煤灰小型空心砌块。
经检测制得的蒸压粉煤灰砖的抗压强度等级大于MU7.5，能够经受15次冻融循环的抗冻要求，其他各项技术指标均达到JC862-2000《粉煤灰小型空心砌块》标准的要求。
实施例2：
配料：粉煤灰45％，电石渣22％，粉煤灰陶粒30％，柠檬酸渣2％，外加剂1％
制造工艺：将上述原料加水搅拌得含水率为12％的混合料，将混合料消化、轮碾、成型、预养，最后经高温高压养护后制成蒸压粉煤灰小型空心砌块，其养护压力为1.2Mpa，养护温度为200℃，养护时间为12h，制成390mm×190mm×190mm粉煤灰小型空心砌块。经检测两种配料制得的蒸压粉煤灰砖的抗压强度等级均大于MU7.5，能够经受15次冻融循环的抗冻要求，其他各项技术指标均达到JC862-2000《粉煤灰小型空心砌块》标准的要求。

Claims (3)

1.一种全废渣粉煤灰小型空心砌块，其特征在于：由粉煤灰、电石渣、粉煤灰陶粒、柠檬酸渣及外加剂作为原料制成，主要原材料的配比为： 
Figure FSA00000889485400011
。
2.如权利要求1所述的一种全废渣粉煤灰小型空心砌块的制备方法，作为轻集料的粉煤灰陶粒的做法为：仅以粉煤灰、电石渣、柠檬酸渣为原料经处理后蒸压养护而成；外加剂为水玻璃、硫酸钠利氢氧化钠混合的复合激发剂，其中各组分占合成剂的重量百分比分别是：水玻璃25-45％、硫酸钠15-25％、氢氧化钠30-50％。 
3.如权利要求1所述的一种全废渣粉煤灰小型空心砌块的制备方法，其特征在于：首先按比例配料并将各种原料混合均匀，加水搅拌使含水率为10-13％，再将混合料消化、轮碾、成型、预养，最后经高温高压养护后制成粉煤灰小型空心砌块，养护压力为1.0-1.2Mpa，养护温度为180-200℃，养护时间为10-12h。 
CN2013101639643A 2013-05-07 2013-05-07 全废渣粉煤灰小型空心砌块及其制备方法 Pending CN103232199A (zh)