CN103230330A - Process for manufacturing black pottery cinerary casket - Google Patents
Process for manufacturing black pottery cinerary casket Download PDFInfo
- Publication number
- CN103230330A CN103230330A CN2013101437054A CN201310143705A CN103230330A CN 103230330 A CN103230330 A CN 103230330A CN 2013101437054 A CN2013101437054 A CN 2013101437054A CN 201310143705 A CN201310143705 A CN 201310143705A CN 103230330 A CN103230330 A CN 103230330A
- Authority
- CN
- China
- Prior art keywords
- manufacturing
- technology
- cinerary casket
- black pottery
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a process for manufacturing a black pottery cinerary casket. The process is characterized by including the following steps: A. carefully selecting sedimentary soil on an ancient riverbed of the Yellow river as a raw material; B. utilizing a ball mill to levigate the raw material and filtering the levigated raw material through a 70-mesh screen; C. dosing; D. vacuum pugging; E. throwing; F; conducting mud board pressing; G. mould blank printing; H. sealing gaps; I. reshaping; J. press polishing; K. carving; L. conducting bonding connection; M. twisting polishing; N. drying in the shade; and O. burning. The process solves the problem that a product is contracted and deformed in the manufacturing process and is broken in the burning process.
Description
Technical field
The present invention relates to a kind of technology of manufacturing the black pottery cinerary casket.
Background technology
In the face of the cinerary casket of unlike material on the market does not have pottery only, its main cause is that some defectives that the product of pottery exists at technical elements in manufacturing process are difficult to solve, as square-folded product more difficult having accomplished just.
Summary of the invention
For solving above-mentioned existing shortcoming, main purpose of the present invention is to provide a kind of technology of making black pottery cinerary casket of practicality, has solved contraction distortion that product occurs in manufacturing process and the fracture in the sintering procedure.
For reaching above-described purpose, a kind of technology of manufacturing the black pottery cinerary casket of the present invention is taked following technical scheme:
A kind of technology of manufacturing the black pottery cinerary casket is characterized in that it may further comprise the steps:
A: selected ancient riverbed of the Yellow River warp is as raw material;
B: utilize ball mill to filter by 70 orders raw material is levigate;
C: batching;
D: vacuum pugging;
E: throwing;
F: soil compressing plate;
G: mould hand-pressing;
H: close lightly seam;
I: shaping;
J: press polish;
K: engraving;
L: bonding;
M: rub light with the hands;
N: dry in the shade;
O: fire.
Described mould hand-pressing has certain thick and heavy sense after making formed product, is convenient to the engraving of some patterns.
Described engraving adopts the hand engraving technology.
Described bonding employing mud is bonding, and adhesive bond position, fired back becomes one, and has increased product strength.
Described drying in the shade in order to grasp the shrinkage rates coefficient better.
Described firing is the following preheatings of 200 degree, and 200 degree are to the intensifications at a slow speed of 500 degree, being rapidly heated and constantly holding interim insulating process of 500 to 900 degree.
Adopt as above the present invention of technical scheme, have following beneficial effect:
Contraction distortion that product occurs and fracture in the sintering procedure have been solved in manufacturing process.
The specific embodiment
To be described further by the present invention of embodiment below, the description of these embodiment is not that content of the present invention is done restriction.One skilled in the art will understand that to be equal to replacement to what content of the present invention was done, or corresponding the improvement, still belong within protection scope of the present invention.
Embodiment 1
Selected ancient riverbed of the Yellow River warp is as raw material; Utilize ball mill to filter by 70 orders raw material is levigate; Batching; Vacuum pugging; Throwing; Soil compressing plate; The mould hand-pressing has certain thick and heavy sense after making formed product, is convenient to the engraving of some patterns; Close lightly seam; Shaping; Press polish; Engraving adopts the hand engraving technology; Bonding, adopt traditional mud bonding, adhesive bond position, fired back becomes one, and has increased product strength; Rub light with the hands; Dry in the shade, in order to grasp the shrinkage rates coefficient better; Fire, the following preheating of 200 degree, 200 degree are to the intensifications at a slow speed of 500 degree, being rapidly heated and constantly holding interim insulating process of 500 to 900 degree.
Claims (6)
1. technology of manufacturing the black pottery cinerary casket is characterized in that it may further comprise the steps:
A: selected ancient riverbed of the Yellow River warp is as raw material;
B: utilize ball mill to filter by 70 orders raw material is levigate;
C: batching;
D: vacuum pugging;
E: throwing;
F: soil compressing plate;
G: mould hand-pressing;
H: close lightly seam;
I: shaping;
J: press polish;
K: engraving;
L: bonding;
M: rub light with the hands;
N: dry in the shade;
O: fire.
2. a kind of technology of manufacturing the black pottery cinerary casket according to claim 1 is characterized in that, described mould hand-pressing has certain thick and heavy sense after making formed product, is convenient to the engraving of some patterns.
3. a kind of technology of manufacturing the black pottery cinerary casket according to claim 1 is characterized in that, described engraving adopts the hand engraving technology.
4. a kind of technology of manufacturing the black pottery cinerary casket according to claim 1 is characterized in that, described bonding employing mud is bonding, and adhesive bond position, fired back becomes one, and has increased product strength.
5. a kind of technology of manufacturing the black pottery cinerary casket according to claim 1 is characterized in that, described drying in the shade in order to grasp the shrinkage rates coefficient better.
6. a kind of technology of manufacturing the black pottery cinerary casket according to claim 1 is characterized in that, described firing is the following preheatings of 200 degree, and 200 degree are to the intensifications at a slow speed of 500 degree, being rapidly heated and constantly holding interim insulating process of 500 to 900 degree.