CN103213348A - 一种三银低辐射镀膜玻璃 - Google Patents

一种三银低辐射镀膜玻璃 Download PDF

Info

Publication number
CN103213348A
CN103213348A CN2013101482967A CN201310148296A CN103213348A CN 103213348 A CN103213348 A CN 103213348A CN 2013101482967 A CN2013101482967 A CN 2013101482967A CN 201310148296 A CN201310148296 A CN 201310148296A CN 103213348 A CN103213348 A CN 103213348A
Authority
CN
China
Prior art keywords
layer
low
glass
znsno
coated glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101482967A
Other languages
English (en)
Inventor
郑民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JUYE YAOHUA GLASS TECHNOLOGY Co Ltd
Original Assignee
JUYE YAOHUA GLASS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JUYE YAOHUA GLASS TECHNOLOGY Co Ltd filed Critical JUYE YAOHUA GLASS TECHNOLOGY Co Ltd
Priority to CN2013101482967A priority Critical patent/CN103213348A/zh
Publication of CN103213348A publication Critical patent/CN103213348A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种三银低辐射玻璃，包括玻璃基片和金属膜层，其特征在于，在所述玻璃基片上镀有14层以纳米计算的各金属膜层，所述金属膜层从内到外依次为Si3N4层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、Si3N4层。本发明能更有效的提高节能的同时在提供不同种类的透光率的基础上，同时大幅度的降低了辐射率，还有效的解决了银层氧化问题，和膜层抗划伤问题，适合推广应用。

Description

一种三银低辐射镀膜玻璃
技术领域
本发明属于玻璃技术领域，涉及一种三银低辐射镀膜玻璃。
背景技术
现代建筑上使用的玻璃再也不是仅仅提供遮风挡雨和采光意义下的单纯玻璃了。自从LOW-E(低辐射)玻璃诞生以来，其发展迅猛，传播广泛，技术上更是逐步提升，升级换代。这一方面是现代建筑对能耗节约的需求驱动，更是人们节能，环保，低碳生活意识的提升所致。
但是，如我们要做好建筑的节能，首选就需要了解节能玻璃的性能和发展趋势，玻璃的节能，技术上需要从减低玻璃的表面热辐射，降低玻璃对流传热进行研究。LOW-E玻璃有单银，双银和三银之分，从目前材料的发展来看，LOW-E玻璃中节能最强悍的产品无疑是三银LOW-E玻璃了。
三银LOW-E玻璃之所以被称为终极节能玻璃，是因为三银LOW-E玻璃具有光谱选择特性，其特有的镀膜能将不受欢迎的红外线，紫外线同人们需要的可见光加以区分，结果导致太阳辐射热量和褪色防护的终极性能。一方面将人眼可见的光线最大限度的放进来，另一方面又最大限度的将携带能量最多的近中红外热能阻隔出去。由于其具有极低的表面辐射率E值，对远红外的热能反射也非常高，保温隔热能力都是节能玻璃中最好的。因此，三银LOW-E镀膜玻璃制作技术，成为了目前较为迫切的生产需求。
发明内容
为了克服现有镀膜玻璃技术中的一些缺陷，解决上述技术问题，本发明提供一种三银低辐射玻璃，在玻璃基片上从内而外的镀了14层膜，能更有效的提高节能的同时提供高低不同种类的透光率，还有效的解决了银层氧化问题。
其技术方案如下：
一种三银低辐射玻璃，包括玻璃基片和金属膜层，在所述玻璃基片上镀有14层以纳米计算的各金属膜层，所述金属膜层从内到外依次为Si3N4层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、Si3N4层。
本发明的有益效果：1、本发明三银低辐射玻璃辐射率低可以达到0.03已经趋近于0，所以称之为终极节能产品，而目前单银辐射值在0.15；
2、本发明三银低辐射玻璃在提高可见光透过率高的基础上，同时还降低了遮阳系数，例如，在透过率在达到71的情况下，遮阳系数仍然可以低至0.3；
3、本发明三银低辐射玻璃多层膜颜色均匀性好；
4、本发明三银低辐射玻璃性能稳定，光学指标、三银LOW-E的红外热能透过仅仅是不到5％，是普通LOW-E的八分之一；
5、本发明三银低辐射玻璃抗氧化能力强，耐磨性高，保存时间长，可实现异地加工，产品的有效时间保持在半年以上。
具体实施方式
下面结合具体实施例对本发明的技术方案作进一步详细地说明。
在更进一步改进改善了基片的清洗质量，及设备密封性使其达到真空10-6以上的基础上，通过中频磁控溅射对不同腔室内充入不同工作气体的流量对不同靶材进行溅射，达到其特有的功能，具体如下：在玻璃基片的复合面上由内到外依次相邻地复合有十四个膜层，第一膜层即最内层为Si3N4层，其强大的附着力保证了膜层的牢固性，第二膜层为ZnO层，第三膜层为Ag层，第四膜层为NiCr层，第五膜层为ZnSnO层，第六膜层为ZnO层，第七膜层为AG层，第八膜层为NiCr层，第九膜层为ZnSnO层，第十膜层为ZnO层，第十一膜层为Ag层，第十二膜层为NiCr层，第十三膜层为ZnSnO层，第十四层膜层即最外层为Si3N4层，一般金属膜层厚度在10nm左右，可根据透过率的要求增加或减少金属层的厚度，而氧化物膜层厚度在40～60nm之间，而且氧化物膜层厚度还可以控制玻璃的色调。顶层采用了硬度很高的氮化硅作为保护膜，大大加强了薄膜的抗磨、抗氧化的能力。一组单银、双银和三银生产产品比较具体请见表1。
表1
Figure BSA00000884656100021
以上所述，仅为本发明较佳的具体实施方式，本发明的保护范围不限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可显而易见地得到的技术方案的简单变化或等效替换均落入本发明的保护范围内。

Claims (1)

1.一种三银低辐射玻璃，包括玻璃基片和金属膜层，其特征在于，在所述玻璃基片上镀有14层以纳米计算的各金属膜层，所述金属膜层从内到外依次为Si3N4层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、ZnO层、Ag层、NiCr层、ZnSnO层、Si3N4层。
CN2013101482967A 2013-04-26 2013-04-26 一种三银低辐射镀膜玻璃 Pending CN103213348A (zh)