CN103206060A - Calcium silicate decorative plate production method - Google Patents
Calcium silicate decorative plate production method Download PDFInfo
- Publication number
- CN103206060A CN103206060A CN2013101267848A CN201310126784A CN103206060A CN 103206060 A CN103206060 A CN 103206060A CN 2013101267848 A CN2013101267848 A CN 2013101267848A CN 201310126784 A CN201310126784 A CN 201310126784A CN 103206060 A CN103206060 A CN 103206060A
- Authority
- CN
- China
- Prior art keywords
- calcium silicate
- silicate board
- paint
- fluorine carbon
- priming paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a novel calcium silicate decorative plate production method, and aims to find a production method which can reduce the calcium silicate decorative plate production cost and improve production efficiency and production quality. The production method includes (1), performing thick sanding process on the surface of the calcium silicate; (2),performing roller painting sealing with water-proofing agent; (3), performing roller painting with UV (ultraviolet) putty, curing UV, and polishing and dedusting; (4), performing roller painting with UV undercoat, curing UV and polishing and dedusting; (5), performing shower coating with fluorocarbon undercoat and drying with infrared rays; (6), polishing and dedusting by a sander; and (7), performing shower coating with fluorocarbon finishing coat and drying with infrared rays. The calcium silicate decorative plate is made by shower coating technique, so that efficiency is greatly improved; no streaks are left on the surface of the film, so that the film is smooth, thin, and even and has mirror surface effect, and is free of environmental pollution.
Description
Technical field
The present invention relates to the calcium silicates decorative panel, be specifically related to a kind of new method of making the calcium silicates decorative panel.
Background technology
The calcium silicates decorative panel is to be substrate with the calcium silicate board, lays waterproofing materialss such as paint, coating on it and makes, and what have also is provided with insulation layer, fireprotection layer, decorative layer etc.The existing manufacture craft of calcium silicates decorative panel mostly is spraying coating process or roller coating technology, but spraying coating process efficient is low, and the unrestrained coating of spraying is difficult for recycle and reuse, and the aerosol that produces during spraying is siphoned away by exhausting system, cause the waste of raw material and the pollution of air, make cost than higher; And roller coating technology sometimes has very light streak, and paint film is smooth smooth inadequately.
Summary of the invention
At above-mentioned the deficiencies in the prior art, the purpose of this invention is to provide a kind of new method of making the calcium silicates decorative panel, in the hope of reducing production costs, enhance productivity and the quality of production.
For achieving the above object, the invention provides a kind of like this preparation method of calcium silicates decorative panel, it is characterized in that may further comprise the steps:
(1) fixed thick sanding is done on the calcium silicate board surface and handled, and mend flat with the atom ash hole that the calcium silicate board surface is bigger;
(2) at the smooth calcium silicate board surface roller coating sealing waterproof agent of above-mentioned processing, dry back is stand-by;
(3) at above-mentioned dried calcium silicate board surface roller coating UV putty, ultraviolet light polymerization, polishing dedusting;
(4) the calcium silicate board surface roller coating UV priming paint that obtains in step (3), ultraviolet light polymerization, polishing dedusting;
(5) calcium silicate board that step (4) is obtained is sent into curtain coater and is coated with fluorine carbon priming paint in the showering mode, again through 5~15 minutes levelling Duan Houyong infrared baking;
(6) calcium silicate board that obtains of step (5) is through the sander dedusting of polishing;
(7) calcium silicate board that step (6) is obtained is sent into curtain coater and is coated with fluorine carbon finishing paint in the showering mode, again through 5~15 minutes levelling Duan Houyong infrared baking.
Preferably, the thickness of described calcium silicate board is 5.5mm.
Preferably, described sealing waterproof agent is the epoxy mounting medium, described epoxy mounting medium is that the ratio of 4:1:1 mixes by 1825A, 1825B and 1825C according to mass ratio, described 1825A is that epoxy resin 40-50%, dimethylbenzene 40-45% and n-butanol 10-20% form by mass percent, described 1825B is that epoxy hardener 40-50%, dimethylbenzene 40-50% and n-butanol 10-20% form by mass percent, and described 1825C is that dimethylbenzene 50-60%, n-butanol 30-40% and methyl iso-butyl ketone (MIBK) 10-20% form by mass percent.
Preferably, before showering, described fluorine carbon priming paint adds the solidifying priming paint agent in advance and the priming paint thinner is allocated, and the mass ratio of fluorine carbon priming paint, solidifying priming paint agent and priming paint thinner is 7:1:4.
Preferably, the fluorine carbon priming paint after every square metre of calcium silicate board showering 100g allocates.
Preferably, before showering, described fluorine carbon finishing paint adds the finish paint curing compound in advance and the finish paint thinner is allocated, and the mass ratio of fluorine carbon finishing paint, finish paint curing compound and finish paint thinner is 6:1:3.
Preferably, the fluorine carbon finishing paint after every square metre of calcium silicate board showering 100g allocates.
Beneficial effect:
Compared with prior art, the present invention adopts leaching coating process to make the calcium silicates decorative panel, has improved efficient to a great extent, and coating surface do not have streak, and very smooth, paint film is thin and smooth and can accomplish mirror effect, and is free from environmental pollution.Compare with roller coat, the present invention can make coating surface not have streak and very smooth; Compare with spraying, the present invention can accomplish that raw material is recycling, and efficient is more much higher than spraying.By experiment with manufacturing process in practice confirm, the paint consumption that adopts method of the present invention to make the calcium silicates decorative panel of a 2440x1220mm size is every square metre of 100-120g, time spent 4-5 second, the paint consumption that adopts spraying coating process to make an onesize calcium silicates decorative panel then is every square metre of 150-200g, about 1 minute time spent.The cleaning difficulty of paint finishing is bigger in addition, waste time and energy very much, and the cleaning of curtain coater is fairly simple, and the face of cleaning is smaller, dismounting easily.
The specific embodiment
The present invention is described in further detail below in conjunction with specific embodiment, and following examples are explanation of the invention, and the present invention is not limited to following examples.
The preparation method of calcium silicates decorative panel provided by the invention may further comprise the steps:
(1) is that the surperficial sand milling of calcium silicate board of 5.5mm is smooth with thickness with 120 sand paper, and mends flat with the atom ash hole that the calcium silicate board surface is bigger;
(2) be the good sealing waterproof agent of proportional arrangement of 1825A:1825B:1825C=4:1:1 by mass ratio, roller coat is in the smooth calcium silicate board surface of above-mentioned sand milling again, and air drying is stand-by after 24 hours;
(3) at above-mentioned dried calcium silicate board surface roller coating UV putty, ultraviolet light polymerization, polishing dedusting;
(4) the calcium silicate board surface roller coating UV priming paint that obtains in step (3), ultraviolet light polymerization, polishing dedusting;
(5) be fluorine carbon priming paint in mass ratio: the solidifying priming paint agent: the ratio of priming paint thinner=7:1:4 prepares fluorine carbon priming paint in advance, the calcium silicate board that step (4) obtains is sent into curtain coater, every square metre of aforementioned fluorine carbon priming paint for preparing in advance of calcium silicate board showering 100g is again through sending into the oven dry of infrared baking line after 5~15 minutes the levelling section;
(6) calcium silicate board that obtains of step (5) is through the sander dedusting of polishing;
(7) be fluorine carbon finishing paint in mass ratio: the finish paint curing compound: the ratio of finish paint thinner=6:1:3 prepares fluorine carbon finishing paint in advance, the calcium silicate board that step (6) obtains is sent into curtain coater, every square metre of aforementioned fluorine carbon finishing paint for preparing in advance of calcium silicate board showering 100g, through sending into the oven dry of infrared baking line after 5~15 minutes the levelling section, get product after the oven dry again.
Claims (7)
1. the preparation method of a calcium silicates decorative panel is characterized in that may further comprise the steps:
(1) fixed thick sanding is done on the calcium silicate board surface and handled, and mend flat with the atom ash hole that the calcium silicate board surface is bigger;
(2) at the smooth calcium silicate board surface roller coating sealing waterproof agent of above-mentioned processing, dry back is stand-by;
(3) at above-mentioned dried calcium silicate board surface roller coating UV putty, ultraviolet light polymerization, polishing dedusting;
(4) the calcium silicate board surface roller coating UV priming paint that obtains in step (3), ultraviolet light polymerization, polishing dedusting;
(5) calcium silicate board that step (4) is obtained is sent into curtain coater and is coated with fluorine carbon priming paint in the showering mode, again through 5~15 minutes levelling Duan Houyong infrared baking;
(6) calcium silicate board that obtains of step (5) is through the sander dedusting of polishing;
(7) calcium silicate board that step (6) is obtained is sent into curtain coater and is coated with fluorine carbon finishing paint in the showering mode, again through 5~15 minutes levelling Duan Houyong infrared baking.
2. preparation method according to claim 1, it is characterized in that: the thickness of described calcium silicate board is 5.5mm.
3. preparation method according to claim 1, it is characterized in that: described sealing waterproof agent is the epoxy mounting medium, described epoxy mounting medium is by 1825A, 1825B and 1825C are that the ratio of 4:1:1 mixes according to mass ratio, described 1825A is epoxy resin 40-50% by mass percent, dimethylbenzene 40-45% and n-butanol 10-20% form, described 1825B is epoxy hardener 40-50% by mass percent, dimethylbenzene 40-50% and n-butanol 10-20% form, and described 1825C is dimethylbenzene 50-60% by mass percent, n-butanol 30-40% and methyl iso-butyl ketone (MIBK) 10-20% form.
4. preparation method according to claim 1, it is characterized in that: before showering, described fluorine carbon priming paint adds the solidifying priming paint agent in advance and the priming paint thinner is allocated, and the mass ratio of fluorine carbon priming paint, solidifying priming paint agent and priming paint thinner is 7:1:4.
5. preparation method according to claim 4 is characterized in that: the fluorine carbon priming paint after every square metre of calcium silicate board showering 100g allocates.
6. preparation method according to claim 1, it is characterized in that: before showering, described fluorine carbon finishing paint adds the finish paint curing compound in advance and the finish paint thinner is allocated, and the mass ratio of fluorine carbon finishing paint, finish paint curing compound and finish paint thinner is 6:1:3.
7. preparation method according to claim 6 is characterized in that: the fluorine carbon finishing paint after every square metre of calcium silicate board showering 100g allocates.