CN103194824A - Blending process for manufacturing silk fiber on basis of cotton spinning device - Google Patents
Blending process for manufacturing silk fiber on basis of cotton spinning device Download PDFInfo
- Publication number
- CN103194824A CN103194824A CN2013101190297A CN201310119029A CN103194824A CN 103194824 A CN103194824 A CN 103194824A CN 2013101190297 A CN2013101190297 A CN 2013101190297A CN 201310119029 A CN201310119029 A CN 201310119029A CN 103194824 A CN103194824 A CN 103194824A
- Authority
- CN
- China
- Prior art keywords
- silk fiber
- cotton
- silk
- fibre
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of textile engineering in a textile industry and particularly relates to silk fiber resource development and utilization. A blending process for manufacturing a silk fiber on the basis of a cotton spinning device is characterized in that first the silk fiber is made into 8-50mm in length, then the silk fiber and other natural fiber or/and chemical fibers undergo a blowing-carding process to be fully blended, a single axial flow blow speed in the blowing-carding process is 480-520rpm, R20300.5 cylinder card clothing is adopted, a needle height is 2.0mm, all-cotton card clothing is adopted, and a card sliver output speed is 125-135m/min. Due to the technical scheme, the problems in the prior art are solved by the blending process, the silk fiber blending process based on the cotton spinning device is provided and is suitable for blending silk and other fibers to prepare blended yarn, and the manufactured silk blended yarn is good in spinning yarn evenness.
Description
Technical field
The invention belongs to Textile Engineering field in the textile industry, more specifically say so silk fiber development of resources and utilization can be applicable to the preparation of cotton spinning apparatus silk fiber and blended yarn, are particularly suited for the blending of silk fiber and other fiber.
Background technology
Traditional cotton spinning apparatus is difficult to spin silk fiber, its difficult point is that silk fiber has light weight, smooth, filament length, so when the clear connection of comb operation griping cotton machine to silk fiber be easier to fast, vast scale, preferential suction, other fiber then slow relatively, ratio is low, be difficult to evenly mix silk and other fiber, each fibre fractionation and the quality percentage that are unfavorable for certainty ratio control blended yarn, the formation irregularity is big, influence web and be shaped, carded sliver cotton (silk) knot, undo sliver evenness and drafting, rove, spun yarn and bobbin take later process to prepare the performance of yarn.
And silk is poor through the fibre length regularity of processing, and by mm more than several mm to 130, the difference of length mainly supplies cocoon silk quilt processing and silk spinning and wool spinning before between 130mm.Cocoon silk quilt greatly reduces the purposes of silk.And for silk spinning raw material class height, and also useful silk spinning die and car tripe bourette are done cotton spinning low count yarn spinning in earlier stage.And adopt the fiber of length regularity difference like this, at tradition (staple fibre) cotton spinning apparatus, do not mention solution, drawing-off position intractable.
In addition, the patent No. is " based on the high ratio blended technology of a kind of ultrashort low-density fibre of cotton spinning apparatus " patent of 200710047756.1, in its technological process by some condition setting in opening picking, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn and the winding procedure being made this equipment be fit to high ratio blended processing to ultrashort low-density fibre, and can't be to the blending of silk fiber processing, particularly the characteristics to the smooth and filament length of silk fiber can't solve all the time.
Summary of the invention:
The present invention overcomes the problem that prior art exists, blending technology based on the cotton spinning apparatus silk fiber is provided, be suitable for silk and other fiber and carry out blending and prepare blended yarn, and the good novel blending technology of making silk fiber based on cotton spinning apparatus of the silk blended yarn that makes spinning bar evenness
Realize above-mentioned purpose, the present invention is in the following way: a kind of blending technology of making silk fiber based on cotton spinning apparatus, include the clear connection of comb, drafting, rove, spun yarn and winding procedure, the raw material of using in this technology are that silk fiber and other natural fabric are or/and chemical fibre, it is characterized in that: earlier the length of silk fiber is made 8-50mm, then silk fiber with other natural fabric or/and chemical fibre comb clearly the connection operation fully mix, wherein the ratio of silk fiber is 35-75%, other natural fabric is or/and chemical fibre is 65-25%, single axial stream blow speed in the described clear comb connection operation is 480-520rpm, adopt R2030 0.5 Bearded-needle knitted cloth, the high 2.0MM of pin, the cotton card clothing, cylinder to the cover plate 0.23mm that spaces, 0.20mm, 0.18mm, 0.18mm, 0.20mm, licker-in and cylinder are than 1:2.25, and carded sliver output speed reaches 125-135m/min.
By adopting such scheme, can effectively solve the problem of the blending resultant yarn difficulty of spinning silk fiber and other fiber, spin the resize ratio method by before the cotton platform binning processing and examination and reach mixed than requiring, improve workshop relative humidity raising fiber surface flatness and antistatic behaviour by clear comb connection humidifier, the clear comb connection of minimizing twines, hangs, blocks up the phenomenon generation.Wherein the length of silk fiber is made 8-50mm, well solved the oversize problem of silk fiber, the ratio of silk fiber is 35-75%, other natural fabric is or/and chemical fibre is 65-25%, limit the content of silk fiber by science, make the light weight and the smooth characteristics that spin and have silk that finally obtain, also can increase the characteristics of other fiber in addition, as cotton fiber, flax fibre, wool fibre, polyster fibre, it silk, model, viscose glue, it bamboo fibre, arranging fully at the characteristics of silk fiber of last above-mentioned these parameters draws through test of many times, makes cotton spinning apparatus to the blending of the silk fiber possibility that becomes.
The further setting of the present invention is: described raw material are silk fiber, other natural fabric and chemical fibre, described other natural fabric is cotton fiber, flax fibre, in the wool fibre one or more, described chemical fibre is polyster fibre, it silk, model, viscose glue, in it bamboo fibre one or more, described comb is made line density 1.33-1.67dtex with chemical fibre before joining operation clearly, fibre length 38mm, make silk fiber and garnetting its density suitable with chemical fibre density again, and silk fiber is carried out dewing makes its regain control 6---8%, workshop relative humidity is grasped 55%-65%, and the temperature control of the clear connection of comb operation is at 20-35 degree; Described mixing in doubling step include the head and and the end also, head and select the FA306A drawing frame for use wherein, 6 of drawing frames also close roller gauge: 8 * 16mm, not and adopt the FA322B drawing frame, 8 of drawing frame employings are also closed, roller gauge 10 * 11 * 16mm, this machine are equipped with the online detection evereven of Uster and prepare ripe, and described rove operation is selected the FA457 Speed frames for use, wherein the two ingot pressure of rove roller are 120 * 200 * 150 * 150N, roller gauge: 11 * 25 * 32mm, rove draw coefficient 87, and the angle gear in the rove operation is adjusted into 27 teeth, described spinning process is selected the DTM129 fine spining machine for use, wherein the spun yarn twist factor 359, front roller output speed 15.6m/min, PG1 42 * 54 rings, arrangement of steel wires circle BJM11/0, winding procedure selects for use Germany to grant the Lai Fu AC of company * 5 automatic winders, winder speed 1300m/min, electronic clearing device configuration Switzerland USTER, cotton knot sensitivity is+340%, short slub sensitivity+160%, length 2CM, long slubbing sensitivity+50%, details-50%, length 32CM; Coating in the described mixing in doubling step on the roller of drawing frame is made up of RC coating A and RC coating B, and usage ratio RC coating A:RC coating B is coated with into the roller surface after 1:6-8 mixes.
By adopting such scheme, utilize cotton spinning apparatus to produce the silk blended yarn, this method technology is reasonable, and flow process is simple, and yarn quality is good, the silk sense utilizes clearing and combing joined process flow by force, reduced rolling technology, shortened flow process, pressed at cotton platform and mix than meticulous binning, add the hybrid technique of many storehouses of supernatant comb connection mixed cotton, the composition mixing ratio is guaranteed; Carding step has still adopted cotton type card clothing, has only done adjustment at technological parameter, need not change special textile part and increase parts, reduces expenses, and card sliver quality is stable; Become the carded sliver, only need that at mixing in doubling step roller hardness and coating are done suitable adjustment and can obtain the good sliver of bar evenness; Utilize ripe can carry out in the revolving cup spinning, it is good to produce bar evenness, powerful high yarn; Utilize rove to carry out fasciated yarn spinning with long filament, Bao Xin is spun into spun yarn, also can carry out fasciated yarn spinning with staple fibre yarn, the parallel spun yarn that is spun into, and the match network spins and spins A, B yarn with the rove of other composition at spun yarn.
The specific embodiment:
Example 1 viscose and silk fiber and cotton fiber blending
Selecting its line density of viscose for use is 1.33dtex, length 38mm, and silk fiber length 40mm, the cotton fiber grade is 3 grades, length 29mm.
With viscose, silk fiber, cotton fiber is pressed mass ratio 55:35:10 at cotton platform binning, height and upper, middle and lower layer composition unanimity during binning.
Griping cotton machine adopts grabs the technology of hurrying up less, and it is little to grasp piece, is convenient to the rear portion and handles, and opener is FA113C, and blow speed 500rpm dirt bar device handle is regulated 2 positions, has adopted the FA028C cotton blender machine, improves mixed effect.
Clear comb connection preparation FA221E carding machine, mainly long from silk fiber length, with feed plate to the disconnected overcut fibre of comb between the licker-in, licker-in is to cylinder speed ratio 1:2.25, increase transfer effect, reduce cotton knot, Bearded-needle knitted cloth adopts the cotton type card clothing of 2030 0.5mm() the difficult cylinder that twines of short tooth, so spacing, grasps at 0.23mm by cylinder to cover plate, 0.20mm, 0.18mm, 0.18mm, 0.20mm, silk fiber is carried out dewing makes its regain control 6%, workshop relative humidity is grasped 55%, and the temperature control of the clear connection of comb operation is at 25 degree, and carded sliver output speed reaches 130m/min.
Mixing in doubling step: head is also selected FA306A for use, 6 of drawing frames also close, roller gauge: 8 * 16mm, not and adopt FA322B and 8 of strip adoptions and close, roller gauge 10 * 11 * 16mm, this machine is equipped with the online detection evereven of Uster and prepares ripe, coating in the described mixing in doubling step on the roller of drawing frame is made up of RC coating A and RC coating B, usage ratio RC coating A:RC coating B is coated with into the roller surface after 1:6 mixes, wherein RC coating A is the RC coating (A) that WUXI NO.2 RUBBER CO.,LTD produces, and RC coating B is the RC coating (B) that WUXI NO.2 RUBBER CO.,LTD produces.
The rove operation is selected the FA457 Speed frames for use, and wherein the two ingot pressure of rove roller are 120 * 200 * 150 * 150N, and roller gauge: 11 * 25 * 32mm, rove draw coefficient 87.
Spinning process selects for use the DTM129 fine spining machine to adopt the match network to spin, and wherein the spun yarn twist factor 359, front roller output speed 15.6m/min, PG1 42 * 54 rings, arrangement of steel wires circle BJM11/0, winding procedure select for use Germany to grant the Lai Fu AC of company * 5 automatic winders, winder speed 1300m/min, electronic clearing device configuration Switzerland USTER, cotton knot sensitivity is+340%, short slub sensitivity+160%, length 2CM, long slubbing sensitivity+50%, details-50%, length 32CM.To mistake and passage, periodically yarn defect, tieing yarn defect all can be set on request, make cheese.
Make the blended yarn performance according to above-mentioned technology and see Table 1.
The main performance of table 1 viscose and silk fiber and cotton fiber mixed yarn
| Sample | Unit | Sticking fine gray yarn specification requirement | Viscose and silk fiber and cotton fiber mixed yarn |
| Line density | Tex | 14~15 | 14.8 |
| Ultimate strength | CN | >160 | 210.5 |
| Fracture strength | CN/tex | >10.5 | 14.2 |
| The different coefficient of single intensity | CV% | Excellent＜11.5 | 9.0 |
| The weight coefficient of variation | CV% | Excellent＜2.5 | 2.4 |
| Deviation of weight | % | ±2.5 | +2.4 |
| Bar evenness | CV% | <15.0 | 12.7 |
Embodiment 2 viscoses and silk fiber and polyster fibre blended yarn
Selecting the viscose line density for use is 1.33dtex, length 38mm, silk fiber length 30mm, polyster fibre line density 1.56dtex, length 38mm.
Griping cotton machine adopts grabs the technology of hurrying up less, and it is little to grasp piece, is convenient to the rear portion and handles, and opener is FA113C, and blow speed 500rpm dirt bar device handle is regulated 2 positions, has adopted the FA028C cotton blender machine, improves mixed effect.
Clear comb connection preparation FA221E carding machine, mainly long from silk fiber length, with feed plate to the disconnected overcut fibre of comb between the licker-in, licker-in is to cylinder speed ratio 1:2.25, increase transfer effect, reduce cotton knot, Bearded-needle knitted cloth adopts the cotton type card clothing of 2030 0.5mm() the difficult cylinder that twines of short tooth, so spacing, grasps at 0.23mm by cylinder to cover plate, 0.20mm, 0.18mm, 0.18mm, 0.20mm, silk fiber is carried out dewing makes its regain control 6%, workshop relative humidity is grasped 60%, and the temperature control of the clear connection of comb operation is at 25 degree, and carded sliver output speed reaches 125m/min.
Mixing in doubling step: head is also selected FA306A for use, 6 of drawing frames also close, roller gauge: 8 * 16mm, not and adopt FA322B and 8 of strip adoptions and close, roller gauge 10 * 11 * 16mm, this machine is equipped with the online detection evereven of Uster and prepares ripe, coating in the described mixing in doubling step on the roller of drawing frame is made up of RC coating A and RC coating B, usage ratio RC coating A:RC coating B is coated with into the roller surface after 1:7 mixes, wherein RC coating A is the RC coating (A) that WUXI NO.2 RUBBER CO.,LTD produces, and RC coating B is the RC coating (B) that WUXI NO.2 RUBBER CO.,LTD produces.
The rove operation is selected the FA457 Speed frames for use, and wherein the two ingot pressure of rove roller are 120 * 200 * 150 * 150N, and roller gauge: 11 * 25 * 32mm, rove draw coefficient 87.
Spinning process selects for use the DTM129 fine spining machine to adopt the match network to spin, and wherein the spun yarn twist factor 359, front roller output speed 15.6m/min, PG1 42 * 54 rings, arrangement of steel wires circle BJM11/0, winding procedure select for use Germany to grant the Lai Fu AC of company * 5 automatic winders, winder speed 1300m/min, electronic clearing device configuration Switzerland USTER, cotton knot sensitivity is+340%, short slub sensitivity+160%, length 2CM, long slubbing sensitivity+50%, details-50%, length 32CM.To mistake and passage, periodically yarn defect, tieing yarn defect all can be set on request, make cheese.
Make the blended yarn performance according to above-mentioned technology and see Table 2.
The main performance of table 2 viscose and silk fiber and polyster fibre blended yarn
| Sample | Unit | Sticking fine gray yarn specification requirement | Viscose and silk fiber and polyster fibre blended yarn |
| Line density | Tex | 14~15 | 14.7 |
| Ultimate strength | CN | >160 | 250.7 |
| Fracture strength | CN/tex | >10.5 | 17.1 |
| The different coefficient of single intensity | CV% | Excellent＜11.5 | 10.4 |
| The weight coefficient of variation | CV% | Excellent＜2.5 | 2.3 |
| Deviation of weight | % | ±2.5 | +1.5 |
| Bar evenness | CV% | Excellent＜15.0 | 11.9 |
Example 1 and example 2 contrasts: implement 2 cottons that will implement in 1 and change terylene into, resize ratio 10%, and powerful rising 21%, bar evenness is better than implementing 1.
Embodiment 3 polyster fibres and silk fiber and cotton fiber and viscose and bamboo pulp viscose fiber blended yarn
Select polyster fibre line density 1.56dtex for use, length 38mm, silk fiber length 50mm; Viscose line density 1.33dtex, length 38mm, bamboo pulp viscose fiber line density 1.33dtex, length 38mm.With the sticking pine of silk fiber, the control of humidification regain is at 7% one-tenth bag, polyster fibre, silk fiber, cotton fiber, viscose, bamboo pulp viscose fiber are pressed mass ratio 30:35:15:10:10 binning on cotton platform, height and upper, middle and lower layer composition unanimity during binning.
Griping cotton machine adopts grabs the technology of hurrying up less, and it is little to grasp piece, is convenient to the rear portion and handles, and opener is FA113C, and blow speed 500rpm dirt bar device handle is regulated 2 positions, has adopted the FA028C cotton blender machine, improves mixed effect.
Clear comb connection preparation FA221E carding machine, mainly long from silk fiber length, with feed plate to the disconnected overcut fibre of comb between the licker-in, licker-in is to cylinder speed ratio 1:2.25, increase transfer effect, reduce cotton knot, Bearded-needle knitted cloth adopts the cotton type card clothing of 2030 0.5mm() the difficult cylinder that twines of short tooth, so spacing, grasps at 0.23mm by cylinder to cover plate, 0.20mm, 0.18mm, 0.18mm, 0.20mm, silk fiber is carried out dewing makes its regain control 7%, workshop relative humidity is grasped 65%, and the temperature control of the clear connection of comb operation is at 35 degree, and carded sliver output speed reaches 135m/min.
Mixing in doubling step: head is also selected FA306A for use, 6 of drawing frames also close, roller gauge: 8 * 16mm, not and adopt FA322B and 8 of strip adoptions and close, roller gauge 10 * 11 * 16mm, this machine is equipped with the online detection evereven of Uster and prepares ripe, coating in the described mixing in doubling step on the roller of drawing frame is made up of RC coating A and RC coating B, usage ratio RC coating A:RC coating B is coated with into the roller surface after 1:7 mixes, wherein RC coating A is the RC coating (A) that WUXI NO.2 RUBBER CO.,LTD produces, and RC coating B is the RC coating (B) that WUXI NO.2 RUBBER CO.,LTD produces.
The rove operation is selected the FA457 Speed frames for use, and wherein the two ingot pressure of rove roller are 120 * 200 * 150 * 150N, and roller gauge: 11 * 25 * 32mm, rove draw coefficient 87.
Spinning process selects for use the DTM129 fine spining machine to adopt the match network to spin, and wherein the spun yarn twist factor 359, front roller output speed 15.6m/min, PG1 42 * 54 rings, arrangement of steel wires circle BJM11/0, winding procedure select for use Germany to grant the Lai Fu AC of company * 5 automatic winders, winder speed 1300m/min, electronic clearing device configuration Switzerland USTER, cotton knot sensitivity is+340%, short slub sensitivity+160%, length 2CM, long slubbing sensitivity+50%, details-50%, length 32CM.To mistake and passage, periodically yarn defect, tieing yarn defect all can be set on request, make cheese.
Make mixed than seeing Table 3 for 30:35:15:10:10 polyster fibre, silk fiber, cotton fiber, viscose and bamboo pulp viscose fiber blended yarn performance according to above-mentioned technology.
The main performance of table 3 polyster fibre, silk fiber, cotton fiber, viscose and bamboo pulp viscose fiber blended yarn
| Sample | Unit | Polyster fibre, silk fiber, cotton fiber, viscose and bamboo pulp viscose fiber blended yarn |
| Line density | Tex | 14.6 |
| Ultimate strength | CN | 214.6 |
| Fracture strength | CN/tex | 14.6 |
| The different coefficient of single intensity | CV% | 10.4 |
| The weight coefficient of variation | CV% | 2.3 |
| Bar evenness | CV% | 15.01 |
Claims (4)
1. blending technology of making silk fiber based on cotton spinning apparatus, include the clear connection of comb, drafting, rove, spun yarn and winding procedure, the raw material of using in this technology are that silk fiber and other natural fabric are or/and chemical fibre, it is characterized in that: earlier the length of silk fiber is made 8-50mm, then silk fiber with other natural fabric or/and chemical fibre comb clearly the connection operation fully mix, wherein the ratio of silk fiber is 35-75%, other natural fabric is or/and chemical fibre is 65-25%, single axial stream blow speed in the described clear comb connection operation is 480-520rpm, adopt R2030 0.5 Bearded-needle knitted cloth, the high 2.0MM of pin, the cotton card clothing, cylinder to the cover plate 0.23mm that spaces, 0.20mm, 0.18mm, 0.18mm, 0.20mm licker-in and cylinder are than 1:2.25, carded sliver output speed reaches 125-135m/min.
2. the blending technology of making silk fiber based on cotton spinning apparatus according to claim 1, it is characterized in that: described raw material are silk fiber, other natural fabric and chemical fibre, described other natural fabric is cotton fiber, flax fibre, in the wool fibre one or more, described chemical fibre is polyster fibre, it silk, model, viscose glue, in it bamboo fibre one or more, described comb is made line density 1.33-1.67dtex with chemical fibre before joining operation clearly, fibre length 38mm, make silk fiber and garnetting its density suitable with chemical fibre density again, and silk fiber is carried out dewing makes its regain control 6---8%, workshop relative humidity is grasped 55%-65%, and the temperature control of the clear connection of comb operation is at 20-35 degree.
3. the blending technology of making silk fiber based on cotton spinning apparatus according to claim 1 and 2, it is characterized in that: described mixing in doubling step include the head and and the end also, wherein head and in 6 of drawing frames and closing, roller gauge: 8 * 16mm, 8 of also middle drawing frame employings are also closed, roller gauge 10 * 11 * 16mm, this machine is equipped with online detection evereven and prepares ripe, the two ingot pressure of the Speed frames rove roller of described rove operation are 120 * 200 * 150 * 150N, and roller gauge: 11 * 25 * 32mm, rove draw coefficient 87, angle gear in the rove operation is adjusted into 27 teeth, the spun yarn twist factor 359 of the fine spining machine of described spinning process, front roller output speed 15.6m/min, PG1 42 * 54 rings, arrangement of steel wires circle BJM11/0, the winder speed 1300m/min of the automatic winder of winding procedure, cotton knot sensitivity is+340%, short slub sensitivity+160%, length 2CM, long slubbing sensitivity+50%, details-50%, length 32CM.
4. the blending technology of making silk fiber based on cotton spinning apparatus according to claim 1 and 2, it is characterized in that: the coating in the described mixing in doubling step on the roller of drawing frame is made up of RC coating A and RC coating B, and usage ratio RC coating A:RC coating B is coated with into the roller surface after 1:6-8 mixes.