CN103183494B - 一种用建筑垃圾制得的环保生态砖 - Google Patents
一种用建筑垃圾制得的环保生态砖 Download PDFInfo
- Publication number
- CN103183494B CN103183494B CN201310154026.7A CN201310154026A CN103183494B CN 103183494 B CN103183494 B CN 103183494B CN 201310154026 A CN201310154026 A CN 201310154026A CN 103183494 B CN103183494 B CN 103183494B
- Authority
- CN
- China
- Prior art keywords
- parts
- flyash
- carbide slag
- building waste
- admixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种用建筑垃圾制得的环保生态砖,由下列重量份的原料制成:外加剂13-15份,粉煤灰或电石渣15-17份,建筑垃圾骨料40-42份,页岩石28-30份,其余均为水;其中:外加剂由重量份为硅酸盐水泥孰料65-72份、高炉渣20-22份、煤矸石10-24份、水琉璃1-1.5份的原料配制而成;粉煤灰或电石渣仅为粉煤灰,或者为由重量份为粉煤灰70-75份、电石渣25-30份的原料配制而成;建筑垃圾骨料由重量份为砖瓦35-38份、混凝土50-55份、废浆砂10-12份的原料配制而成的颗粒料;所述的外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成高强度产物。本发明密度小,抗冻融性好。
Description
技术领域
本发明涉及建筑用砖块,特别指一种用建筑垃圾制得的环保生态砖。
背景技术
随着我国城市建设的高速发展,有城市改造产生的拆除建筑垃圾数量十分巨大,每年达到数亿吨,绝大部分建筑垃圾未经任何处理,运到郊区或乡村,采用露天堆放或简易填埋的方式处理,占用了大量土地。同时在清运和堆放过程中移撒,粉尘和灰沙飞扬等问题造成严重的污染。随着我国对于保护耕地和环境的各相关法规的颁布和实施,如何处置建筑垃圾、粉煤灰、工业废渣等污染源已是摆在我们面前的一项迫切工作。
针对我国建筑垃圾的现状,利用我国现有的环保资源页岩石和自主研制的外加剂,通过先进的隧道窑加工即可生产一种建筑垃圾环保生态新型砖。
发明内容
本发明的目的是针对背景技术中存在的缺点和问题加以改进和创新,提供一种利用本地资源即用建筑垃圾制得的环保生态砖。
本发明由下列重量份的原料制成:
外加剂13-15份,粉煤灰或电石渣15-17份,建筑垃圾骨料40-42份,页岩石28-30份,其余均为水;其中:
外加剂由重量份为硅酸盐水泥孰料65-72份、高炉渣20-22份、煤矸石10-24份、水琉璃1-1.5份的原料配制而成;
粉煤灰或电石渣为粉煤灰,或者为由重量份为粉煤灰70-75份、电石渣25-30份的原料配制而成;
建筑垃圾骨料由重量份为砖瓦35-38份、混凝土50-55份、废浆砂10-12份的原料配制而成的颗粒料;
所述的外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的托贝莫来石等高强度产物。
本发明各原料的最佳用量重量份为:
外加剂13份,粉煤灰或电石渣17份,建筑垃圾骨料40份,页岩石30份,其余均为水;其中:
外加剂由重量份为硅酸盐水泥孰料70份、高炉渣21份、煤矸石17份、水琉璃1份的原料配制而成;
粉煤灰或电石渣为粉煤灰,或者为由重量份为粉煤灰72份、电石渣28份的原料配制而成;
建筑垃圾骨料由重量份为砖瓦36份、混凝土52份、废浆砂11份的原料配制而成的颗粒料;
所述的外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的托贝莫来石等高强度产物。
本发明的优点及有益效果:
本发明通过加入合理比例的天然环保的页岩石,在未加工的组份中稀释了粉煤灰中的一些不利的元素,再通过配制的外加剂对粉煤灰、建筑垃圾中的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生产具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的托贝莫来石等高强度产物,其强度超过国家标注值。在隧道窑初始燃烧后,利用粉煤灰的热含产生热量进行反应,大大节约了能源,减少了因加入传统燃料产生热量而产生的污染,是一种既生态又环保的新型砖;同时砖的密度小,抗冻融性好。
具体实施方式
本发明原料组分是根据砖的标准标号来确定的,一般外加剂加入量越高,强度越高。其中将粉煤灰进行分类最终加工成细度为96.8%(80#目通过率),堆积密度为640kg/m3。电石渣氧化钙含量为42-45%,含水量要控制在32%以内。
本发明页岩石加工后最大直径小于10mm,其中:
筛孔径mm | 10 | 5 | 2.5 | 1.25 | 0.63 | 0.315 | 0.16 | 小于0.16 |
累计筛余率% | 0 | 20 | 51 | 67 | 82 | 92 | 97 | 100 |
建筑垃圾含有砖瓦、混凝土和废浆砂,将砖瓦和废浆砂破碎研磨处理成颗粒直径小于5mm,细度模数小于2.47;将混凝土破碎研磨处理成颗粒直径小于5mm,细度模数小于2.52.
本发明制作过程中,采用25MPa的成型机,在先进的隧道窑中烧制即可。以碎建筑垃圾骨料生产的本发明环保生态砖平均抗压强度为11.2Mpa,碳化后强度为10.5Mpa,平均干燥收缩率为0.57%。
实施例1:
1、配料:
取65Kg硅酸盐水泥孰料、20Kg高炉渣、10Kg煤矸石和1Kg水琉璃制备成外加剂备用;
将粉煤灰粉碎加工备用;
取35Kg砖瓦、50Kg混凝土和10 Kg废浆砂粉碎制备成建筑垃圾骨料备用。
2、制砖:
将13Kg外加剂、15Kg粉煤灰、40Kg建筑垃圾骨料、28Kg页岩石和适量水混合送入隧道窑燃烧,再经成型机得成型砖块。其制作工艺流程为:外加剂的配置----建筑垃圾的分类----建筑垃圾、粉煤灰、电石渣的破碎研磨----骨料的均匀化处理----配方计量----搅拌处理----挤压成型----隧道窑烧结----堆码出厂。
制砖过程中,外加剂使粉煤灰的玻璃体活性激发,促进粉煤灰、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的高强度产物。
实施例2:
1、配料:
取72Kg硅酸盐水泥孰料、22Kg高炉渣、24Kg煤矸石和1.5Kg水琉璃制备成外加剂备用;
取75Kg粉煤灰、30Kg电石渣粉碎制备成粉煤灰或电石渣料备用;
取38Kg砖瓦、55Kg混凝土和12Kg废浆砂粉碎制备成建筑垃圾骨料备用。
2、制砖:
将15Kg外加剂、17Kg粉煤灰或电石渣料、42Kg建筑垃圾骨料、30Kg页岩石和适量水混合送入隧道窑燃烧,再经成型机得成型砖块。其制作工艺流程为:外加剂的配置----建筑垃圾的分类----建筑垃圾、粉煤灰、电石渣的破碎研磨----骨料的均匀化处理----配方计量----搅拌处理----挤压成型----隧道窑烧结----堆码出厂。
制砖过程中,外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的高强度产物。
实施例3:
1、配料:
取70Kg硅酸盐水泥孰料、21Kg高炉渣、17Kg煤矸石和1Kg水琉璃制备成外加剂备用;
将粉煤灰粉碎加工备用;
取36Kg砖瓦、52Kg混凝土和11Kg废浆砂粉碎制备成建筑垃圾骨料备用。
2、制砖:
将13Kg外加剂、17Kg粉煤灰、40Kg建筑垃圾骨料、30Kg页岩石和适量水混合送入隧道窑燃烧,再经成型机得成型砖块。其制作工艺流程为:外加剂的配置----建筑垃圾的分类----建筑垃圾、粉煤灰、电石渣的破碎研磨----骨料的均匀化处理----配方计量----搅拌处理----挤压成型----隧道窑烧结----堆码出厂。
制砖过程中,外加剂使粉煤灰的玻璃体活性激发,促进粉煤灰、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的高强度产物。
实施例4:
1、配料:
取68Kg硅酸盐水泥孰料、21Kg高炉渣、20Kg煤矸石和1.2Kg水琉璃制备成外加剂备用;
取70Kg粉煤灰、25Kg电石渣粉碎制备成粉煤灰或电石渣料备用;
取37Kg砖瓦、53Kg混凝土和11Kg废浆砂粉碎制备成建筑垃圾骨料备用。
2、制砖:
将14Kg外加剂、16Kg粉煤灰、41Kg建筑垃圾骨料、29Kg页岩石和适量水混合送入隧道窑燃烧,再经成型机得成型砖块。其制作工艺流程为:外加剂的配置----建筑垃圾的分类----建筑垃圾、粉煤灰、电石渣的破碎研磨----骨料的均匀化处理----配方计量----搅拌处理----挤压成型----隧道窑烧结----堆码出厂。
制砖过程中,外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的高强度产物。
本发明所述的实施例仅仅是对本发明的优选实施方式进行的描述,并非对本发明构思和范围进行限定,在不脱离本发明设计思想的前提下,本领域中工程技术人员对本发明的技术方案作出的各种变型和改进,均应落入本发明的保护范围,本发明请求保护的技术内容,已经全部记载在权利要求书中。
Claims (2)
1.一种用建筑垃圾制得的环保生态砖,其特征在于它由下列重量份的原料制成:
外加剂13-15份,粉煤灰或粉煤灰和电石渣的混合物15-17份,建筑垃圾骨料40-42份,页岩石28-30份,其余均为水;其中:
外加剂由重量份为硅酸盐水泥孰料65-72份、高炉渣20-22份、煤矸石10-24份、水琉璃1-1.5份的原料配制而成;
粉煤灰或粉煤灰和电石渣的混合物仅为粉煤灰,或者为由重量份为粉煤灰70-75份、电石渣25-30份的原料配制而成的混合物;
建筑垃圾骨料由重量份为砖瓦35-38份、混凝土50-55份、废浆砂10-12份的原料配制而成的颗粒料;
所述的外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的托贝莫来石等高强度产物。
2.根据权利要求1所述的用建筑垃圾制得的环保生态砖,其特征在于它由下列重量份的原料制成:
外加剂13份,粉煤灰或粉煤灰和电石渣的混合物17份,建筑垃圾骨料40份,页岩石30份,其余均为水;其中:
外加剂由重量份为硅酸盐水泥孰料70份、高炉渣21份、煤矸石17份、水琉璃1份的原料配制而成;
粉煤灰或粉煤灰和电石渣的混合物仅为粉煤灰,或者为由重量份为粉煤灰72份、电石渣28份的原料配制而成的混合物;
建筑垃圾骨料由重量份为砖瓦36份、混凝土52份、废浆砂11份的原料配制而成的颗粒料;
所述的外加剂使粉煤灰或电石渣的玻璃体活性激发,促进粉煤灰或电石渣、建筑垃圾骨料和页岩石中的Ca2+、SiO3 2+、Al3+在高温高压和水的作用下反应,生成具有凝胶性质的水合产物CSH和CAH,并转化成稳定的、分布均匀的托贝莫来石等高强度产物。