CN103174056A - 一种预油漆纸用水性涂料及制备工艺 - Google Patents
一种预油漆纸用水性涂料及制备工艺 Download PDFInfo
- Publication number
- CN103174056A CN103174056A CN2013101005101A CN201310100510A CN103174056A CN 103174056 A CN103174056 A CN 103174056A CN 2013101005101 A CN2013101005101 A CN 2013101005101A CN 201310100510 A CN201310100510 A CN 201310100510A CN 103174056 A CN103174056 A CN 103174056A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- add
- uniformly dispersed
- based paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种预油漆纸用水性涂料及制备工艺,包括以下组分:水性丙烯酸乳液、氨基树脂、去离子水、硅酮类基材润湿剂、非离子型表面活性剂、流平剂、消泡剂和催化剂,所述环氧树脂的制备工艺为带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液,接着加入氨基树脂,然后加入去离子水,分散均匀后,在中速搅拌下依次加入硅酮类基材润湿剂,非离子型表面活性剂以及流平剂,分散均匀后,在高速下加入消泡剂,分散均匀后,在低速下加入催化剂,分散均匀即可。本发明不含有机溶剂,并且能够克服由于涂料表面张力高,造成预油漆纸表面展布不开,以及大面积卷缩或缩孔等缺陷。
Description
技术领域
本发明涉及一种用于预油漆纸用的水性涂料及制备工艺。
背景技术
目前,预油漆纸的生产和消费量正在迅速增长,大量应用在木质人造板的表面装饰上,已成为木材行业表面装饰材料研究应用的一个热点。预油漆纸是高质量的装饰纸经印刷、水性树脂浸渍和涂料装饰等生产工艺加工而成的,这些工艺一般都是在一条生产线上完成的。按照预油漆纸生产工艺的特点,其表面涂饰的涂料要求在一定的烘烤温度下瞬间固化成膜,且漆膜的最终使用性能达到国家标准规定的要求。目前预油漆质采用的溶剂型涂料中有机溶剂含量常在40%以上,有的涂料在施工时的有机溶剂含量甚至高达80%~85%,这些挥发性有机化合物进入大气,造成环境的严重污染。而采用水性涂料时,由于涂料的表面张力高于预油漆纸的表面张力,预油漆纸表面常出现涂料展布不开、大面积卷缩或者形成大量缩孔的现象。
发明内容
本发明的目的在于解决现有技术存在的问题,从而提供一种不含有机溶剂并且能够克服涂料展布不开、大面积卷缩或缩孔等缺陷的预油漆纸用水性涂料及制备工艺。
本发明所解决的技术问题采用以下技术方案来实现:一种预油漆纸用的水性涂料,其特征在于:它由以下重量配比的原料配制而成:
水性丙烯酸乳液 45~50
氨基树脂 20~25
去离子水 8~12
硅酮类基材润湿剂 0.15~0.2
非离子型表面活性剂 0.2~0.25
流平剂 0.1~0.15
消泡剂 0.5~1
催化剂 0.2~0.5。
本发明所述的预油漆纸用的水性涂料制备工艺包括以下步骤:
第一步:在带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液,接着加入氨基树脂,然后加入去离子水,转速为1000~1200r/min,分散5~10min,确保其分散均匀;
第二步:在中速搅拌下依次加入硅酮类基材润湿剂,非离子型表面活性剂以及流平剂,搅拌速度控制在500~600r/min,每种助剂分散5~10min;
第三步:加入消泡剂,搅拌速度控制在1000~1200r/min,分散5~10min;
第四步:加入催化剂,搅拌速度为300~400r/min,分散均匀即可。
本发明预油漆纸用的水性涂料用水作为溶剂,不含有机溶剂;由于水的表面张力高,润湿基材的能力差,展布性不好,必须降低水与基材接触的表面张力,硅酮类基材润湿剂一般会在基材与涂料界面之间排布,朝向预油漆纸的界面定向排布,因此,可以降低预油漆纸与涂料液面之间的表面张力,增加涂料在预油漆纸上的扩展性和渗透力,这样可以解决预油漆纸表面产生缩孔和卷缩的现象。非离子型表面活性剂能在高剪切速率下使动态表面张力达到平衡,而且还有脱泡作用,没有层间附着力问题,有流动促进作用。
本发明提供的预油漆纸用水性涂料及制备工艺,具有不含有机溶剂,并且能够克服由于涂料表面张力高,造成预油漆纸表面展布不开,以及大面积卷缩或缩孔等缺陷。
具体实施方式
下面根据具体实例对本发明作进一步说明:
实施例1
在带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液45g,接着加入氨基树脂20g,然后加入去离子水8g,转速为1000 r/min,分散10min,分散均匀后,将搅拌器的速度控制在500r/min,加入硅酮类基材润湿剂0.15g,分散10min,分散均匀后,加入非离子型表面活性剂0.2g,分散10min,分散均匀后,加入流平剂0.1g,分散10min,分散均匀后,调节搅拌速度到1000r/min,加入消泡剂0.5g,分散10min,分散均匀后,调节搅拌速度到300r/min,加入催化剂0.2g,分散均匀即可。
实施例2
在带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液47g,接着加入氨基树脂23g,然后加入去离子水10g,转速为1100 r/min,分散8min,分散均匀后,将搅拌器的速度控制在550r/min,加入硅酮类基材润湿剂0.17g,分散8min,分散均匀后,加入非离子型表面活性剂0.23g,分散8min,分散均匀后,加入流平剂0.12g,分散8min,分散均匀后,调节搅拌速度到1100r/min,加入消泡剂0.8g,分散8min,分散均匀后,调节搅拌速度到350r/min,加入催化剂0.3g,分散均匀即可。
实施例3
在带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液50g,接着加入氨基树脂25g,然后加入去离子水12g,转速为1200 r/min,分散5min,分散均匀后,将搅拌器的速度控制在600r/min,加入硅酮类基材润湿剂0.2g,分散5min,分散均匀后,加入非离子型表面活性剂0.25g,分散5min,分散均匀后,加入流平剂0.15g,分散5min,分散均匀后,调节搅拌速度到1200r/min,加入消泡剂1g,分散5min,分散均匀后,调节搅拌速度到400r/min,加入催化剂0.5g,分散均匀即可。
以上显示和描述了本发明的基本原理和主要特征及本发明的优点,本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内,本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种预油漆纸用水性涂料,其特征在于:它由以下重量配比的原料配制而成:
水性丙烯酸乳液 45~50
氨基树脂 20~25
去离子水 8~12
硅酮类基材润湿剂 0.15~0.2
非离子型表面活性剂 0.2~0.25
流平剂 0.1~0.15
消泡剂 0.5~1
催化剂 0.2~0.5。
2.一种预油漆纸用水性涂料的制备工艺,其特征在于:包括以下步骤:
第一步:在带有高速搅拌器的干净不锈钢容器内,按照配方量先缓慢加入水性丙烯酸乳液,接着加入氨基树脂,然后加入去离子水,转速为1000~1200r/min,分散5~10min,确保其分散均匀;
第二步:在中速搅拌下依次加入硅酮类基材润湿剂,非离子型表面活性剂以及流平剂,搅拌速度控制在500~600r/min,每种助剂分散5~10min;
第三步:加入消泡剂,搅拌速度控制在1000~1200r/min,分散5~10min;
第四步:加入催化剂,搅拌速度为300~400r/min,分散均匀即可。