CN103173134B - 一种溶剂型氯丁橡胶胶黏剂 - Google Patents

一种溶剂型氯丁橡胶胶黏剂 Download PDF

Info

Publication number
CN103173134B
CN103173134B CN201310059998.8A CN201310059998A CN103173134B CN 103173134 B CN103173134 B CN 103173134B CN 201310059998 A CN201310059998 A CN 201310059998A CN 103173134 B CN103173134 B CN 103173134B
Authority
CN
China
Prior art keywords
parts
solvent
chloroprene rubber
good
trees ashes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310059998.8A
Other languages
English (en)
Other versions
CN103173134A (zh
Inventor
徐冉阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huibang paint Co., Ltd
Original Assignee
ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd filed Critical ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority to CN201310059998.8A priority Critical patent/CN103173134B/zh
Publication of CN103173134A publication Critical patent/CN103173134A/zh
Application granted granted Critical
Publication of CN103173134B publication Critical patent/CN103173134B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种溶剂型氯丁橡胶胶黏剂，由下列重量份的原料制成：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR12120-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、氯醇橡胶H4510-15、环氧树脂改性聚酰胺热熔胶5-8、氧化锌2-3等。本发明胶黏剂具有优良的耐热性，粘结强度高，耐水防潮，贮存稳定性好，环保性好，使用效果好且方便。

Description

一种溶剂型氯丁橡胶胶黏剂
技术领域
本发明涉及一种胶黏剂，具体涉及一种溶剂型氯丁橡胶胶黏剂。
背景技术
氯丁橡胶胶粘剂性能优异、价格低廉，对橡胶、钢铁、混凝土、木材、皮革、织物等材料均有良好的粘接力。氯丁胶黏剂特性是：初始粘力大、粘接强度高、耐久性好、胶层柔韧，弹性良好，耐冲击与振动，有较好的耐油、耐水、耐碱、耐酸、耐溶剂性能，对木材有较好的粘接性，使用方便，价格低廉，但其耐热性较差，耐寒性不佳，贮存稳定性差。为了克服传统的氯丁胶黏剂耐热性较差，耐寒性不佳，贮存稳定性差等缺点，通过改进配方，从而生产出一种新型溶剂型氯丁橡胶胶黏剂。
发明内容
本发明的目的是提供一种耐温性好、粘结强度高、贮存稳定性好的溶剂型氯丁橡胶胶黏剂。
 本发明采用的技术方案如下：
一种溶剂型氯丁橡胶胶黏剂，由下列重量份的原料制成：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、氯醇橡胶H45 10-15、环氧树脂改性聚酰胺热熔胶5-8、氧化锌2-3、纳米碳酸钙15-20、膨润土10-15、防老剂NBC1-2、防老剂MB 1-2、促进剂Na-22 1-2、促进剂DM 1-2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷2-3、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、抗氧剂1035 1-2、快压出炭黑N660 20-25、硬脂酸锌1-2、柠檬酸三乙酯5-8、乙酰柠檬酸三乙酯3-5、环氧硬脂酸辛酯5-8、改性树木灰烬1-2。
    所述的改性树木灰烬由以下步骤制得：先用10-15%盐酸浸泡树木灰烬3-4h，去离子水洗涤干净，再用10-12%氢氧化钠溶液浸泡3-4h，再用去离子水洗涤至中性，烘干，加入相当于树木灰烬重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%的活性氧化铝，高速1200-1500r/min搅拌1-2h，烘干，粉碎研磨成超细粉末即可。
     溶剂型氯丁橡胶胶黏剂的制备方法，包括以下步骤：
    （1）将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、氯醇橡胶H45、环氧树脂改性聚酰胺热熔胶混合，在100-120℃下反应1-2h；
（2）将其它物料与反应物混合，搅拌30-40min，得到成品，包装即可。
    本发明的有益效果：
本发明通过对树木灰烬进行改性，提高了其在在胶黏剂组分中的分散均匀性，从而可以明显改善制鞋用高性能用高性能胶黏剂的粘接强度和耐水性,并具有成本低,效果优良的特点。本发明胶黏剂具有优良的耐热化学性，粘结强度高，耐水防潮，贮存稳定性好，环保性好，使用效果好且方便。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例
一种溶剂型氯丁橡胶胶黏剂，由下列重量份的原料制成：苯乙烯115份、乙酸乙酯120份、氯丁橡胶CR121 24份、二甲苯18份、4,4’-二苯基甲烷二异氰酸酯1.5份、聚异丁烯10份、3-氨丙基三甲氧基硅烷3份、聚四氢呋喃醚二醇3份、SG-2型PVC树脂4份、二茂铁1.5份、氯醇橡胶H45 12份、环氧树脂改性聚酰胺热熔胶6份、氧化锌3份、纳米碳酸钙16份、膨润土12份、防老剂NBC1.6份、防老剂MB 1.5份、促进剂Na-22 1.5份、促进剂DM 1.6份、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷3份、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2份、抗氧剂1035 1.6份、快压出炭黑N660 22份、硬脂酸锌1.5份、柠檬酸三乙酯6份、乙酰柠檬酸三乙酯4份、环氧硬脂酸辛酯6份、改性树木灰烬2份。
其中，所述的改性树木灰烬由以下步骤制得：先用12%盐酸浸泡树木灰烬4h，去离子水洗涤干净，再用10%氢氧化钠溶液浸泡4h，再用去离子水洗涤至中性，烘干，加入相当于树木灰烬重量3%的月桂醇硫酸钠、2%的平平加O、3%的柠檬酸三丁酯、5%的活性氧化铝，高速1200-1500r/min搅拌1-2h，烘干，粉碎研磨成超细粉末即可。
     溶剂型氯丁橡胶胶黏剂的制备方法，包括以下步骤：
    （1）将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、氯醇橡胶H45、环氧树脂改性聚酰胺热熔胶混合，在105℃下反应2h；
（2）将其它物料与反应物混合，搅拌35min，得到成品，包装即可。
本实施例制得的胶黏剂的主要性能如下表1。
表1
Figure 2013100599988100002DEST_PATH_IMAGE002
耐水，在水中浸泡12个月，剥离强度下降5%。

Claims (2)

1.一种溶剂型氯丁橡胶胶黏剂，其特征在于，由下列重量份的原料制成：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4’-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、SG-2型PVC树脂3-5、二茂铁1-2、氯醇橡胶H45 10-15、环氧树脂改性聚酰胺热熔胶5-8、氧化锌2-3、纳米碳酸钙15-20、膨润土10-15、防老剂NBC1-2、防老剂MB 1-2、促进剂Na-22 1-2、促进剂DM 1-2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷2-3、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、抗氧剂1035 1-2、快压出炭黑N660 20-25、硬脂酸锌1-2、柠檬酸三乙酯5-8、乙酰柠檬酸三乙酯3-5、环氧硬脂酸辛酯5-8、改性树木灰烬1-2；
所述的改性树木灰烬由以下步骤制得：先用10-15%盐酸浸泡树木灰烬3-4h，去离子水洗涤干净，再用10-12%氢氧化钠溶液浸泡3-4h，再用去离子水洗涤至中性，烘干，加入相当于树木灰烬重量2-3%的月桂醇硫酸钠、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%的活性氧化铝，高速1200-1500r/min搅拌1-2h，烘干，粉碎研磨成超细粉末即可。 
2.一种如权利要求1所述的溶剂型氯丁橡胶胶黏剂的制备方法，其特征在于包括以下步骤：
    （1）将氯丁橡胶CR121 、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、SG-2型PVC树脂、二茂铁、氯醇橡胶H45、环氧树脂改性聚酰胺热熔胶混合，在100-120℃下反应1-2h；
（2）将其它物料与反应物混合，搅拌30-40min，得到成品，包装即可。
CN201310059998.8A 2013-02-26 2013-02-26 一种溶剂型氯丁橡胶胶黏剂 Active CN103173134B (zh)