CN103173096A - 一种盛装白酒用金属容器内壁涂料及其制备方法 - Google Patents
一种盛装白酒用金属容器内壁涂料及其制备方法 Download PDFInfo
- Publication number
- CN103173096A CN103173096A CN2013100753891A CN201310075389A CN103173096A CN 103173096 A CN103173096 A CN 103173096A CN 2013100753891 A CN2013100753891 A CN 2013100753891A CN 201310075389 A CN201310075389 A CN 201310075389A CN 103173096 A CN103173096 A CN 103173096A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- weight part
- raw material
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种盛装白酒用金属容器内壁涂料，它是由甲乙两组分按3-5:1的重量比组成，其中所述的甲组份是由下述重量份的原料组成：E-20环氧树脂60-70、二甲苯20-25、醋酸乙酯5-8、三聚磷酸铝8-10、改性复合填料4-6、氨水4-5、氢氧化铝3-5、纳米氧化锌3-5、聚二甲基硅氧烷1-2、草木灰1-2、聚丙烯酸丁酯2-4、二乙胺1-2、2，6-二叔丁基对甲酚1-2、三聚磷酸钠1-2、抗氧剂DLTP0.8-1、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷0.8-1、聚乙二醇0.6-1；本发明的漆膜具有优异的附着力、交联程度高、硬度、耐醇性好，增加的改性复合填料，进一步增强了漆膜的机械物理性能和稳定性。
Description
技术领域
本发明主要涉及一种内壁涂料，尤其涉及一种盛装白酒用金属容器内壁涂料。
背景技术
传统生产的盛装白酒用金属容器内壁涂料，漆膜性能不稳定，导致涂层的硬度、防腐性差，有的甚至会出现锈斑等不良现象。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种盛装白酒用金属容器内壁涂料。
本发明是通过以下技术方案实现的：
一种盛装白酒用金属容器内壁涂料，它是由甲乙两组分按3-5:1的重量比组成，其中所述的甲组份是由下述重量份的原料组成：
E-20环氧树脂60-70、二甲苯20-25、醋酸乙酯5-8、三聚磷酸铝8-10、改性复合填料4-6、氨水4-5、氢氧化铝3-5、纳米氧化锌3-5、聚二甲基硅氧烷1-2、草木灰1-2、聚丙烯酸丁酯2-4、二乙胺1-2、2，6- 二叔丁基对甲酚1-2、三聚磷酸钠1-2、抗氧剂DLTP0.8-1、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷0.8-1、聚乙二醇0.6-1；
所述的改性复合填料是由下述重量份的原料组成：
纳米二氧化硅80-90、氢氧化钙30-40、硬脂酸30-40、失水山梨醇单油酸酯5-7、脂肪醇聚氧乙烯醚2-3、月桂醇硫酸钠1-2、过氧化二异丙苯2-3、液体石蜡1-2、邻苯二甲酸二辛酯1-2、1,2-双(三乙氧基硅基)乙烷0.8-1、3-缩水甘油醚氧基丙基三甲氧基硅烷0.6-0.8、水适量；
所述的改性复合填料的制备方法包括以下步骤：
（1）将上述重量份的氢氧化钙加入到等质量的水中，再加入上述重量份的1,2-双(三乙氧基硅基)乙烷，在90-110℃下搅拌加热20-30分钟；
（2）将上述重量份的硬脂酸加热到60-70℃，加入上述重量份的失水山梨醇单油酸酯、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，升高温度至于80-85℃，恒温搅拌1-2小时，在搅拌条件下缓慢添加入上述混合液，添加完毕后继续搅拌1-2小时，得料A；
（3）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与料A混合，加入剩余各原料，高速1500-2000转/分搅拌20-30分钟，烘干，即得所述改性复合填料；
所述的乙组份是由下述重量份的原料混合组成：
650聚酰胺固化剂20-40、二甲苯10-20、丁醇10-20。
一种盛装白酒用金属容器内壁涂料的制备方法，包括以下步骤：
所述的甲组份的制备方法包括以下步骤：
（1）将上述重量份的E-20环氧树脂、二甲苯、醋酸乙酯、氨水混合加入到备料锅中，在300-400rpm下低速搅拌15-20分钟；
（2）依次加入上述重量份的三聚磷酸铝、改性复合填料、氢氧化铝、纳米氧化锌、聚乙二醇、聚二甲基硅氧烷、草木灰、三聚磷酸钠，在1200-1300rpm下高速分散20-30分钟；
（3）将上述分散后的浆料进行研磨，细度为5-15um，加入剩余各原料，在500-700rpm下低速搅拌10-15分钟，即得所述甲组份；
所述的乙组份的制备方法为：
将各原料混合，在500-700rpm下低速搅拌20-30分钟，即得所述乙组份。
本发明的优点是：
本发明的漆膜具有优异的附着力、交联程度高、硬度、耐醇性好，增加的改性复合填料，进一步增强了漆膜的机械物理性能和稳定性。
具体实施方式
实施例1
一种盛装白酒用金属容器内壁涂料，它是由甲乙两组分按5:1的重量比组成，其中所述的甲组份是由下述重量份(公斤)的原料组成：
E-20环氧树脂70、二甲苯25、醋酸乙酯8、三聚磷酸铝10、改性复合填料6、氨水5、氢氧化铝5、纳米氧化锌5、聚二甲基硅氧烷2、草木灰2、聚丙烯酸丁酯4、二乙胺2、2，6- 二叔丁基对甲酚2、三聚磷酸钠2、抗氧剂DLTP0.8、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷0.8、聚乙二醇0.6；
所述的改性复合填料是由下述重量份的原料组成：
纳米二氧化硅90、氢氧化钙40、硬脂酸40、失水山梨醇单油酸酯7、脂肪醇聚氧乙烯醚3、月桂醇硫酸钠2、过氧化二异丙苯3、液体石蜡2、邻苯二甲酸二辛酯2、1,2-双(三乙氧基硅基)乙烷0.8、3-缩水甘油醚氧基丙基三甲氧基硅烷0.8、水适量；
所述的改性复合填料的制备方法包括以下步骤：
（1）将上述重量份的氢氧化钙加入到等质量的水中，再加入上述重量份的1,2-双(三乙氧基硅基)乙烷，在110℃下搅拌加热30分钟；
（2）将上述重量份的硬脂酸加热到70℃，加入上述重量份的失水山梨醇单油酸酯、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，升高温度至于85℃，恒温搅拌2小时，在搅拌条件下缓慢添加入上述混合液，添加完毕后继续搅拌2小时，得料A；
（3）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与料A混合，加入剩余各原料，高速2000转/分搅拌20-30分钟，烘干，即得所述改性复合填料；
所述的乙组份是由下述重量份的原料混合组成：
650聚酰胺固化剂40、二甲苯20、丁醇20。
一种盛装白酒用金属容器内壁涂料的制备方法，包括以下步骤：
所述的甲组份的制备方法包括以下步骤：
（1）将上述重量份的E-20环氧树脂、二甲苯、醋酸乙酯、氨水混合加入到备料锅中，在400rpm下低速搅拌20分钟；
（2）依次加入上述重量份的三聚磷酸铝、改性复合填料、氢氧化铝、纳米氧化锌、聚乙二醇、聚二甲基硅氧烷、草木灰、三聚磷酸钠，在1300rpm下高速分散30分钟；
（3）将上述分散后的浆料进行研磨，细度为15um，加入剩余各原料，在700rpm下低速搅拌15分钟，即得所述甲组份；
所述的乙组份的制备方法为：
将各原料混合，在700rpm下低速搅拌30分钟，即得所述乙组份。
漆膜性能测试：
用本发明涂布于马口铁，马口铁尺寸：5cm x 94.7cm、表面积804.95 x 2 = 1609.90平方厘米；浸泡在浓度为50%的乙醇溶液中，常温下放置，试验时间为60天，将马口铁取出后，漆膜表面无变化，马口铁无生锈现象，按照国家标准对漆膜进行测试，附着力为1级、冲击性50cm、柔韧性1mm。
Claims (2)
1.一种盛装白酒用金属容器内壁涂料，其特征在于它是由甲乙两组分按3-5:1的重量比组成，其中所述的甲组份是由下述重量份的原料组成：
E-20环氧树脂60-70、二甲苯20-25、醋酸乙酯5-8、三聚磷酸铝8-10、改性复合填料4-6、氨水4-5、氢氧化铝3-5、纳米氧化锌3-5、聚二甲基硅氧烷1-2、草木灰1-2、聚丙烯酸丁酯2-4、二乙胺1-2、2，6- 二叔丁基对甲酚1-2、三聚磷酸钠1-2、抗氧剂DLTP0.8-1、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷0.8-1、聚乙二醇0.6-1；
所述的改性复合填料是由下述重量份的原料组成：
纳米二氧化硅80-90、氢氧化钙30-40、硬脂酸30-40、失水山梨醇单油酸酯5-7、脂肪醇聚氧乙烯醚2-3、月桂醇硫酸钠1-2、过氧化二异丙苯2-3、液体石蜡1-2、邻苯二甲酸二辛酯1-2、1,2-双(三乙氧基硅基)乙烷0.8-1、3-缩水甘油醚氧基丙基三甲氧基硅烷0.6-0.8、水适量；
所述的改性复合填料的制备方法包括以下步骤：
（1）将上述重量份的氢氧化钙加入到等质量的水中，再加入上述重量份的1,2-双(三乙氧基硅基)乙烷，在90-110℃下搅拌加热20-30分钟；
（2）将上述重量份的硬脂酸加热到60-70℃，加入上述重量份的失水山梨醇单油酸酯、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，升高温度至于80-85℃，恒温搅拌1-2小时，在搅拌条件下缓慢添加入上述混合液，添加完毕后继续搅拌1-2小时，得料A；
（3）将上述重量份的纳米二氧化硅颗粒分散到水中，得到含纳米二氧化硅的悬浮液，与料A混合，加入剩余各原料，高速1500-2000转/分搅拌20-30分钟，烘干，即得所述改性复合填料；
所述的乙组份是由下述重量份的原料混合组成：
650聚酰胺固化剂20-40、二甲苯10-20、丁醇10-20。
2.一种如权利要求1所述的盛装白酒用金属容器内壁涂料的制备方法，其特征在于包括以下步骤：
所述的甲组份的制备方法包括以下步骤：
（1）将上述重量份的E-20环氧树脂、二甲苯、醋酸乙酯、氨水混合加入到备料锅中，在300-400rpm下低速搅拌15-20分钟；
（2）依次加入上述重量份的三聚磷酸铝、改性复合填料、氢氧化铝、纳米氧化锌、聚乙二醇、聚二甲基硅氧烷、草木灰、三聚磷酸钠，在1200-1300rpm下高速分散20-30分钟；
（3）将上述分散后的浆料进行研磨，细度为5-15um，加入剩余各原料，在500-700rpm下低速搅拌10-15分钟，即得所述甲组份；
所述的乙组份的制备方法为：
将各原料混合，在500-700rpm下低速搅拌20-30分钟，即得所述乙组份。