CN103171073B - 一种温度可调水解塑料薄膜生产工艺 - Google Patents
一种温度可调水解塑料薄膜生产工艺 Download PDFInfo
- Publication number
- CN103171073B CN103171073B CN201310093440.1A CN201310093440A CN103171073B CN 103171073 B CN103171073 B CN 103171073B CN 201310093440 A CN201310093440 A CN 201310093440A CN 103171073 B CN103171073 B CN 103171073B
- Authority
- CN
- China
- Prior art keywords
- temperature
- production process
- glue
- powdery solid
- pure water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种温度可调水解塑料薄膜生产工艺,其特征是将粉状固体原料质量百分比为98—99%的PVA、0.1—0.3%的对羟基苯甲酸乙酯、0.2—0.8%的水杨酸纳、0.08—0.2%的助剂混合均匀后,按粉状固体原料重量占纯净水的重量的20—30%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,制取薄膜。本发明由于实现了在常温(25℃)不溶,高于30℃才溶解,从而提高了水解塑料薄膜的应用价值和应用领域。
Description
技术领域
本发明涉及一种塑料薄膜生产工艺,尤其涉及一种温度可调水解塑料薄膜生产工艺。
背景技术
水溶性塑料薄膜是一种水溶性的可降解的新颖的绿色包装材料,在欧美、日本等国被广泛用于各种产品的包装,例如服装出口、农药、化肥、颜料、染料、清洁剂、水处理剂、矿物添加剂、洗涤剂、混凝土添加剂等。具有环保易溶、安全无毒、耐油耐腐、防止静电、弹性抗拉、随意包装、计量准确、热封性强、透气阻氧、印刷清晰、高度防伪的特点。现有的利用PVA制取的水溶性薄膜稳定性、成膜性差,不能调节水解温度,通常情况下在常温下就水解,从而严重影响了水溶性薄膜的应用和生产。
发明内容
本发明的目的是提供一种温度可调水解塑料薄膜生产工艺,通过该工艺制备的水解塑料薄膜实现常温不水解,且水解温度可调。
本发明采用的技术方案是:
一种温度可调水解塑料薄膜生产工艺,将粉状固体原料质量百分比为98—99%的PVA、0.1—0.3%的对羟基苯甲酸乙酯、0.2—0.8%的水杨酸纳、余量为助剂混合均匀后,按粉状固体原料重量占纯净水的重量的20—30%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,制取薄膜。
进一步的,当将胶液涂布在流延机上,在未固化的流延塑料层还在滚筒上时,再用6000—10000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为0.5—1.5S,然后制取薄膜。
所述助剂占粉状固体原料的质量百分比构成为:甘油0.02—0.04%,碳酸铵0.08—0.2%,月桂酸0.001—0.005%。
本发明将粉状固体原料质量百分比为98—99%的PVA、0.1—0.3%的对羟基苯甲酸乙酯、0.2—0.8%的水杨酸纳、0.08—0.2%的助剂混合均匀后,按粉状固体原料重量占纯净水的重量的20—30%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,制取薄膜。
作为进一步的改进,当胶液在涂布在流延机上后,可以在未固化的流延塑料层还在滚筒上时,再用6000—10000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为0.5—1.5S,然后制取薄膜。
本发明的水溶性塑料薄膜具有在不同水温条件下水解的功能,且在常温下不溶解。通过调控对羟基苯甲酸乙酯的在质量百分比0.1—0.3%范围内的加入量,可以实现水解温度30—60℃的温度调控,本配方制成的水溶性塑料薄膜水解后的产物为C、H、O,对环境无污染。
本发明同时用6000—10000伏的电压对滚筒上的未固化的流延塑料层进行电击,调节其塑料膜内的分子层结构疏松程度、分子键接合力,电击电压越高,塑料膜内的分子层结构越疏松,从而实现塑料薄膜的不同水解温度,即30—60℃的温度调控。
本发明由于实现了在常温(25℃)不溶,高于30℃才溶解,从而提高了水解塑料薄膜的应用价值和应用领域。
具体实施方式
下述实施例仅是用于对本发明方案的说明。
实施例1
将粉状固体原料质量百分比为98%的PVA、0.3%的对羟基苯甲酸乙酯、0.8%的水杨酸纳,0.02%的甘油、0.2%的碳酸铵,0.005%的月桂酸混合均匀后,按粉状固体原料重量占纯净水的重量的20%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,在未固化的流延塑料层还在滚筒上时,再用6000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为0.5S,然后制取薄膜。
实施例2
将粉状固体原料质量百分比为98.5%的PVA、0.2%的对羟基苯甲酸乙酯、0.4%的水杨酸纳,0.03%的甘油、0.13%的碳酸铵、0.003%的月桂酸混合均匀后,按粉状固体原料重量占纯净水的重量的25%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,制取薄膜。
实施例3
将粉状固体原料质量百分比为99%的PVA、0.1%的对羟基苯甲酸乙酯、0.2%的水杨酸纳,0.02%的甘油,0.08%的碳酸铵,0.001%的月桂酸混合均匀后,按粉状固体原料重量占纯净水的重量的30%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,在未固化的流延塑料层还在滚筒上时,再用10000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为1.5S,然后制取薄膜。
实施例4
将粉状固体原料质量百分比为98.5%的PVA、0.2%的对羟基苯甲酸乙酯、0.4%的水杨酸纳,0.03%的甘油、0.13%的碳酸铵、0.003%的月桂酸混合均匀后,按粉状固体原料重量占纯净水的重量的25%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,在未固化的流延塑料层还在滚筒上时,再用8000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为1S,然后制取薄膜。
本发明配方制成的水溶性塑料薄膜具有在不同水温条件下水解的功能,且在常温下不溶解。通过调控对羟基苯甲酸乙酯的在质量百分比0.1—0.3%范围内的加入量,可以实现水解温度30—60℃的温度调控,本配方制成的水溶性塑料薄膜水解后的产物为C、H、O,对环境无污染,对羟基苯甲酸乙酯加入量与水解塑料薄膜水解温度和时间的关系如下表所示:
本发明同时用6000—10000伏的电压对滚筒上的未固化的流延塑料层进行电击,调节其塑料膜内的分子层结构疏松程度、分子键接合力,电击电压越高,塑料膜内的分子层结构越疏松,从而实现塑料薄膜的不同水解温度,即30—60℃的温度调控。电击电压与水解塑料薄膜水解温度和时间的关系如下表所示:
本发明由于实现了在常温(25℃)不溶,高于30℃才溶解,从而提高了水解塑料薄膜的应用价值和应用领域。
Claims (3)
1.一种温度可调水解塑料薄膜生产工艺,其特征是将粉状固体原料质量百分比为98—99%的PVA、0.1—0.3%的对羟基苯甲酸乙酯、0.2—0.8%的水杨酸纳、余量为助剂混合均匀后,按粉状固体原料重量占纯净水的重量的20—30%比例加入纯净水制成胶液,然后将胶液涂布在流延机上,制取薄膜。
2.根据权利要求1所述的一种温度可调水解塑料薄膜生产工艺,其特征是当将胶液涂布在流延机上,在未固化的流延塑料层还在滚筒上时,再用6000—10000伏的电压对滚筒上的未固化的流延塑料层进行电击,电击时间为0.5—1.5S,然后制取薄膜。
3.根据权利要求2所述的一种温度可调水解塑料薄膜生产工艺,其特征是所述助剂占粉状固体原料的质量百分比构成为:甘油0.02—0.04%,碳酸铵0.08—0.2%,月桂酸0.001—0.005%。