CN103165831B - 一种新型锂电池用铝塑膜 - Google Patents
一种新型锂电池用铝塑膜 Download PDFInfo
- Publication number
- CN103165831B CN103165831B CN201310104306.7A CN201310104306A CN103165831B CN 103165831 B CN103165831 B CN 103165831B CN 201310104306 A CN201310104306 A CN 201310104306A CN 103165831 B CN103165831 B CN 103165831B
- Authority
- CN
- China
- Prior art keywords
- aluminium foil
- layer
- middle aluminium
- chemical treatment
- maleic anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种新型锂电池用铝塑膜,包括保护层、化学处理层Ⅰ、中间铝箔、化学处理层Ⅱ和热封层,所述的化学处理层Ⅰ和化学处理层Ⅱ是采用铬盐、酸、氟化物的混合溶液对中间铝箔表面进行化学处理,在中间铝箔表面形成的致密金属氧化物膜层,将保护层、经化学处理过的中间铝箔和热封层通过热帖复合机一次成型热帖复合。本发明的铝塑膜具有易制作、成本低、性能好等优点。可用于锂离子电池芯的包装,具有高阻隔、易成型性、高热封、高耐电解液腐蚀等性能。
Description
技术领域
本发明涉及一种锂电池包装膜,特别是一种新型锂电池用铝塑膜。
背景技术
软包装锂离子电池以能量密度高、循环寿命长、自然放电率低等优良性能,发展迅速,并很快占领了电池行业的大部分市场。目前应用于软包装锂离子电池的铝塑膜包材主要由日方提供,复合方式一般为干式复合或者挤出复合,工艺非常复杂,成本较高。
发明内容
本发明要解决的技术问题是针对现有技术的不足,提出了一种成本低、制作工艺简单的新型锂电池用铝塑膜。
本发明要解决的技术问题是通过以下技术方案来实现的,一种新型锂电池用铝塑膜,其特点是:包括保护层、化学处理层Ⅰ、中间铝箔、化学处理层Ⅱ和热封层,
所述保护层为聚酰胺与马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯共挤流延制作而成,聚酰胺的用量占总质量的50%-70%,保护层厚度为15μm-30μm;
所述的化学处理层Ⅰ和化学处理层Ⅱ是采用铬盐、酸、氟化物的混合溶液对中间铝箔表面进行化学处理,在中间铝箔表面形成的致密金属氧化物膜层,厚度为0.2μm-1.2μm;所述的铬盐为重铬酸钾、氧化铬、重铬酸钠的一种或者任意两种混合,铬盐在混合溶液里的质量百分比浓度为0.2%-1.2%;所述的酸为盐酸、硫酸、磷酸的一种或者任意两种混合,酸在混合溶液里的质量百分比浓度为3%-15%;所述的氟化物为氟化铵、氟化钾、氟化钠的一种或者任意两种混合,氟化物在混合溶液里的质量百分比浓度为0.1%-1%;
所述中间铝箔层厚度为30μm-100μm;
所述热封层为马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯与聚丙烯或者聚乙烯共挤流延制作而成,马来酸酐聚丙烯或者马来酸酐聚乙烯的用量占总质量的20%-60%,厚度为20μm-100μm;
将保护层、经化学处理过的中间铝箔和热封层通过热帖复合机一次成型热帖复合,具体的:经化学处理过的中间铝箔预热至190—210℃,通过压辊将保护层和热封层同时贴复在经化学处理过的中间铝箔的内外表面,贴复时保护层和热封层的由马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯构成的热帖面朝向经化学处理过的中间铝箔,再经过一个保热烘箱收卷即得到新型锂电池用铝塑膜。
本发明与现有技术相比,包括保护层、中间铝箔和热封层,中间铝箔采用铬盐、酸、氟化物的混合溶液进行表面化学处理,在中间铝箔表面形成的致密金属氧化物膜层,通过热帖复合机将保护层、经化学处理过的中间铝箔和热封层一次成型热帖复合。本发明的铝塑膜具有易制作、成本低、性能好等优点。可用于锂离子电池芯的包装,具有高阻隔、易成型性、高热封、高耐电解液腐蚀等性能。
具体实施方式
一种新型锂电池用铝塑膜,包括保护层、化学处理层Ⅰ、中间铝箔、化学处理层Ⅱ和热封层,
所述保护层为聚酰胺与马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯共挤流延制作而成,聚酰胺的用量占总质量的50%-70%,可以与铝箔热贴复合,可以起到保护铝箔,具有抗冲击作用,可印刷。保护层厚度为15μm-30μm,该层可以在聚酰胺厂家制作,成本较低;保护层可以是聚酰胺与马来酸酐改性聚丙烯共挤流延制作而成,也可以是聚酰胺与马来酸酐改性聚乙烯共挤流延制作而成。
马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯制作在保护层的内表面,作为热帖面。作为热帖面的马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯的用量占保护层总质量的20%-60%。
所述的化学处理层Ⅰ和化学处理层Ⅱ是采用铬盐、酸、氟化物的混合溶液对中间铝箔表面进行化学处理,在中间铝箔表面形成的致密金属氧化物膜层,厚度为0.2μm-1.2μm;所述的铬盐为重铬酸钾、氧化铬、重铬酸钠的一种或者任意两种混合,铬盐在混合溶液里的质量百分比浓度为0.2%-1.2%;所述的酸为盐酸、硫酸、磷酸的一种或者任意两种混合,酸在混合溶液里的质量百分比浓度为3%-15%;所述的氟化物为氟化铵、氟化钾、氟化钠的一种或者任意两种混合,氟化物在混合溶液里的质量百分比浓度为0.1%-1%,上述混合溶液可以起到防止铝箔被锂电池电解液腐蚀的作用;
所述中间铝箔层为在铝箔厂购买,牌号8021或者8079,厚度为30μm-100μm;具有高阻隔、良好的成型性、遮光等性能。
所述热封层为马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯与聚丙烯或者聚乙烯共挤流延制作而成,马来酸酐聚丙烯或者马来酸酐聚乙烯的用量占总质量的20%-60%,可以与铝箔进行热贴复合,具有良好的自热封及与极耳热封性能。厚度为20μm-100μm可以在CPP厂家制作。所述热封层可以为马来酸酐改性聚丙烯与聚丙烯共挤流延制作、或者马来酸酐改性聚丙烯与聚乙烯共挤流延制作;也可以是马来酸酐改性聚乙烯与聚丙烯共挤流延制作或者是马来酸酐改性聚乙烯与聚乙烯共挤流延制作而成。
马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯制作在所述热封层的内表面,作为热帖面。作为热帖面的马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯的用量为热封层总质量的20%-60%。
将保护层、经化学处理过的中间铝箔和热封层通过热帖复合机一次成型热帖复合,具体的:经化学处理过的中间铝箔预热至190—210℃,通过压辊将保护层和热封层同时贴复在经化学处理过的中间铝箔的内外表面,贴复时保护层和热封层的由马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯构成的热帖面朝向经化学处理过的中间铝箔,再经过一个保热烘箱收卷即得到新型锂电池用铝塑膜。
Claims (1)
1.一种新型锂电池用铝塑膜,其特征在于:包括保护层、化学处理层Ⅰ、中间铝箔、化学处理层Ⅱ和热封层,
所述保护层为聚酰胺与马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯共挤流延制作而成,聚酰胺的用量占总质量的50%-70%,保护层厚度为15μm-30μm;
所述的化学处理层Ⅰ和化学处理层Ⅱ是采用铬盐、酸、氟化物的混合溶液对中间铝箔表面进行化学处理,在中间铝箔表面形成的致密金属氧化物膜层,厚度为0.2μm-1.2μm;所述的铬盐为重铬酸钾、重铬酸钠的一种或者两种混合,铬盐在混合溶液里的质量百分比浓度为0.2%-1.2%;所述的酸为盐酸、硫酸、磷酸的一种或者任意两种混合,酸在混合溶液里的质量百分比浓度为3%-15%;所述的氟化物为氟化铵、氟化钾、氟化钠的一种或者任意两种混合,氟化物在混合溶液里的质量百分比浓度为0.1%-1%;
所述中间铝箔层厚度为30μm-100μm;
所述热封层为马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯与聚丙烯或者聚乙烯共挤流延制作而成,马来酸酐聚丙烯或者马来酸酐聚乙烯的用量占总质量的20%-60%,厚度为20μm-100μm;
将保护层、经化学处理过的中间铝箔和热封层通过热帖复合机一次成型热帖复合,具体的:经化学处理过的中间铝箔预热至190—210℃,通过压辊将保护层和热封层同时贴复在经化学处理过的中间铝箔的内外表面,贴复时保护层和热封层的由马来酸酐改性聚丙烯或者马来酸酐改性聚乙烯构成的热帖面朝向经化学处理过的中间铝箔,再经过一个保热烘箱收卷即得到新型锂电池用铝塑膜。