CN103160951A - Negative-ion-contained artificial grass fiber and preparation method thereof - Google Patents
Negative-ion-contained artificial grass fiber and preparation method thereof Download PDFInfo
- Publication number
- CN103160951A CN103160951A CN2013100918023A CN201310091802A CN103160951A CN 103160951 A CN103160951 A CN 103160951A CN 2013100918023 A CN2013100918023 A CN 2013100918023A CN 201310091802 A CN201310091802 A CN 201310091802A CN 103160951 A CN103160951 A CN 103160951A
- Authority
- CN
- China
- Prior art keywords
- negative
- ion
- artificial grass
- resin
- anion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a negative-ion-contained artificial grass fiber and a preparation method thereof. The negative-ion-contained artificial grass fiber consists of polypropylene (PP) resin, linear low density polyethylene (LLDPE) resin and negative ion master batch. The negative ion master batch consists of a series of accessory ingredients including ANION series of negative ion powders, an antioxidizer, an anti-ultraviolet agent, a coupling agent, a lubricating agent, a filling agent and pigment. The preparation method comprises the steps of uniformly mixing part of PP resin and all the accessory ingredients in a high-seed mixer, and preparing the mixture into the negative ion master batch by adopting a double-screw extruder; then uniformly mixing the rest PP resin, the LLDPE resin and the negative ion master batch in mixing equipment, then carrying out the processes of screw extrusion film formation, cutting and the like to prepare the negative-ion-contained artificial grass fiber which is the raw materials for preparing a lawn. The negative-ion-contained artificial grass fiber has the obvious effects of releasing negative ions with the concentration of 2000 per each cubic meter and more than 2000 per each cubic, purifying ambient air, effectively resisting bacteria and removing dust, and being beneficial to physical and psychological health of a human body.
Description
Technical field
The present invention relates to a kind of contain anion artificial grass fibre and preparation thereof.
Background technology
build the athletic ground with chinampa and have abroad the history of decades, along with the development of science and technology with sports, now by high-performance polyethylene, the acrylic resin fiber, uvioresistant anti-aging " amine " material interlayer and the chinampa that consists of fibrage according to the multiple auxiliary agent of needs apolegamy of different motion field function, can be the specialty, the asf motor personage creates very good athletic ground, it not only can be used for the tennis court, but also be used for laying the stadium of track and field runway, the ball park, the Rugby field, golf course, the swimming pool periphery, leisure place greenbelt and interior decoration etc., it is a kind of multi-functional material for paving sports field.
Yet cheap although now widely used chinampa can give aesthetic feeling, convenient management does not have the function of natural lawn anion releasing, and this has had a strong impact on the use field of chinampa.People are called airborne vitamin to anion, and it is born in the environment such as waterfall, seashore, dark woods meadow except richness, also can result from the natural minerals that excites molecule in air to produce anion.The negative-ion auxiliary agent that the present invention uses be with opal as main raw material, add simultaneously several functions material (as multiple nonmetallic materials such as iron oxide, aluminium oxide, titanium dioxide, medical stone, shells).Haze weather is to people's production, life and healthyly all impact, the main cause that produces is that in air, particulate contaminants increases, these particulate contaminants easily adsorb under the charge effect of negative aeroion, gathering, sedimentation, air is well purified, improve air quality.Contain the anion chinampa and can improve natural ecological environment, reduce the PM2.5 index, purify air, have clean air and dustproof function.
Summary of the invention
The present invention is directed to the weak point of existing chinampa, provide a kind of making to contain the raw material of anion chinampa---contain anion artificial grass fibre and preparation method thereof.
The present invention realizes by following processing step:
(1) choose the PP resin, the LLDPE resin is major ingredient, choosing ANION series negative ion powder, antioxidant, ultraviolet (UV) resistant agent, coupling agent, lubricant, filler and pigment is auxiliary agent.
(2) preparation negative-ion master batch: a part of PP resin and ANION series negative ion powder, antioxidant, ultraviolet (UV) resistant agent, coupling agent, lubricant, filler and pigment are mixed in high-speed mixer, mixed raw material is prepared into negative-ion master batch through double screw extruder, and dry through drying equipment.
(3) then all the other PP resins, LLDPE resin and negative-ion master batch are mixed in mixing device, through vacuum feeding, coat-hanger die extruder film extrusion, water-cooled, carry film, cut off into silk, hot drawing-off, HEAT SETTING, sub-wire, be wound into the step such as silk cylinder, make the anion artificial grass fibre.
Each composition weight proportion of described step (1) Raw is: 90.0～10.0 parts of PP resins; LLDPE10.0～90.0 part; 10.0～15.0 parts of ANION series negative ion powders; 0.05～0.2 part, antioxidant; 0.1～0.5 part of ultraviolet (UV) resistant agent; 1.0～4.0 parts of coupling agents; 1.0～4.0 parts of lubricants; 0.05～0.2 part of pigment.
In described step (1), the PP resin
MIBe 2～6g/min; LLDPE's
MIBe 0.5-2g/min.
In described step (1), ANION series negative ion powder is the natural minerals (〉=1250 order) that contains nano-pore, and after adding, the lawn anion releasing concentration of made is at 2000/cm
3Above.
In described step (1), antioxidant be antioxidant 1010,264 or DLTP in one or more mixture.
In described step (1), ultraviolet (UV) resistant agent is UV-NBC.
In described step (1), coupling agent is silane resin acceptor kh-550.
In described step (1), lubricant is one or more the mixture in calcium stearate or Tissuemat E.
In described step (1), filler is precipitated calcium carbonate.
In described step (1), pigment is the green PG-550 of cobalt titanium.
The present invention is the raw material of making chinampa, and the outstanding effect of anion artificial grass fibre that contains of made is:
Except having the uvioresistant long service life, beautifying the environment, can also increase airborne anion number, bacteriostat degerming is removed the pernicious gas peculiar smell, effectively cleaning ambient air; Eliminate the sportsman battle-weary with the leisure personage, improve mood, improve the health resistance against diseases, realized the equal environment of Sport ﹠ Casual in the open air as people, be of value to the human body physical and mental health; Contain lawn anion releasing concentration that the anion artificial grass fibre is made at 2000/cm
3Above.
The specific embodiment
Embodiment 1 outdoor sports type artificial grass fibre: 90.0 parts of PP resins, 10.0 parts of LLDPE; Negative-ion master batch: 10.0 parts of PP resins, 10.0 parts of ANION series negative ion powders, (1010) 0.2 parts, antioxidant, (264) 0.2 parts, antioxidant, 0.5 part of ultraviolet (UV) resistant agent, 1.0 parts of coupling agents; 1.0 parts of lubricants, 0.2 part of pigment.Contain by what above-mentioned technique made the 2000/cm of lawn anion releasing that the anion artificial grass fibre is made
3Above.
The indoor decoration type artificial grass fibre of embodiment 2: 80.0 parts of PP resins, 20.0 parts of LLDPE; Negative-ion master batch: 10.0 parts of PP resins, 15.0 parts of ANION series negative ion powders, antioxidant (1010) 0.05,0.1 part of anti-oxidant DLTP, 0.1 part of ultraviolet (UV) resistant agent, 4.0 parts of coupling agents, each 2.0 parts of two kinds of lubricants, 5 parts of fillers, 0.05 part of pigment.Contain by what above-mentioned technique made the 3000/cm of lawn anion releasing that the anion artificial grass fibre is made
3Above.
Claims (5)
1. one kind contains anion artificial grass fibre and preparation method, it is characterized in that by following processing step preparation:
(1) choose the PP resin, the LLDPE resin is major ingredient, choosing ANION series negative ion powder, antioxidant, ultraviolet (UV) resistant agent, coupling agent, lubricant, filler and pigment is auxiliary agent;
(2) preparation negative-ion master batch: a small part PP resin and auxiliary agent are mixed in high-speed mixer, be prepared into negative-ion master batch through double screw extruder, and dry through drying equipment;
(3) all the other PP resins, LLDPE resin and negative-ion master batch are mixed in mixing device, through vacuum feeding, coat-hanger die extruder film extrusion, water-cooled, carry film, cut off into silk, hot drawing-off, HEAT SETTING, sub-wire, be wound into the step such as silk cylinder, make the anion artificial grass fibre.
2. a kind of anion artificial grass fibre and preparation method of containing as claimed in claim 1, is characterized in that each composition weight proportion of described step (1) Raw is: 90.0～10.0 parts of PP resins; 10.0～90.0 parts of LLDPE; Each composition weight proportion of auxiliary agent is: 10.0～15.0 parts of ANION series negative ion powders; 0.05～0.2 part, antioxidant; 0.1～0.5 part of ultraviolet (UV) resistant agent; 1.0～4.0 parts of coupling agents; 1.0～4.0 parts of lubricants; 0.05～0.2 part of pigment.
3. a kind of preparation method who contains the anion artificial grass fibre as claimed in claim 1, is characterized in that in described step (1), the PP resin
MIBe 2-6g/min; LLDPE's
MIBe 0.5-2g/min.
4. a kind of anion artificial grass fibre and preparation method of containing as claimed in claim 1, it is characterized in that in described step (1), ANION series negative ion powder is the natural minerals (〉=1250 order) that contains nano-pore, and after adding, the lawn anion releasing concentration of made is at 2000/cm
3Above.
5. a kind of anion artificial grass fibre and preparation method of containing as claimed in claim 1, it is characterized in that in described step (1), antioxidant be antioxidant 1010,264 or DLTP in one or more mixture, ultraviolet (UV) resistant agent is UV-NBC, lubricant is one or more the mixture in calcium stearate or Tissuemat E, coupling agent is silane resin acceptor kh-550, and filler is precipitated calcium carbonate, and pigment is the green PG-550 of cobalt titanium.