CN109853077A - A kind of manufacturing method of antibiotic property artificial grass filaments - Google Patents
A kind of manufacturing method of antibiotic property artificial grass filaments Download PDFInfo
- Publication number
- CN109853077A CN109853077A CN201711244641.1A CN201711244641A CN109853077A CN 109853077 A CN109853077 A CN 109853077A CN 201711244641 A CN201711244641 A CN 201711244641A CN 109853077 A CN109853077 A CN 109853077A
- Authority
- CN
- China
- Prior art keywords
- artificial grass
- fillet
- antibacterial
- manufacturing
- grass filaments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacturing methods of antibiotic property artificial grass filaments.The following steps are included: the first step, antibacterial agent, auxiliary agent and basic resin are uniformly mixed, then by single screw extrusion machine extruding pelletization, antibacterial matrices are obtained；Second step, by antibacterial matrices, basic resin and functional material be blended, through twin-screw 250 DEG C at a temperature of melt, be squeezed into film；Above-mentioned film is cooled and solidified, is then cut into narrow strip by third step；Fillet is carried out length direction stretching, fillet is made to stretch 6 times or so by the 4th step；5th step is heat-treated the fillet after stretching with baking oven.Method of manufacturing technology of the invention is simple, by increasing antibacterial agent, so that artificial grass filaments have the function of antibiotic and sterilizing, can resist germ growth, can pre- anti-bacteria propagation and infection.
Description
Technical field
The present invention relates to a kind of artificial grass filaments more particularly to a kind of manufacturing methods of antibiotic property artificial grass filaments.
Background technique
Be easy to produce bacterium, virus after natural lawn ponding, child play out be easy to infection yellow grape bacillus,
Escherichia coli and fall ill.Chinampa is using lifeless plastics chemical fibre as raw material, using the Ecology grass of manual method manufacture
Level ground, it needs to consume unlike natural lawn the resources such as fertilizer, water necessary to growth, and maintenance is simple, and can satisfy complete
The movement of weather high intensity needs.Therefore, the restriction by environmental condition or other factors is inconvenient to be laid with really many
The place on lawn, especially sports ground, such as: hockey, baseball, football, tennis, golf sports center, frequent employment
Make lawn laying.Chinampa is not merely to meet movement needs, and ornamental value is also relatively strong.But current chinampa
It without antibacterial functions, is easy to infect bacterium after a period of use, has one to the people's health moved on chinampa
Fixed threat.
Summary of the invention
In view of the foregoing drawbacks, the purpose of the present invention is to provide one kind to have the function of antibiotic and sterilizing, can resist germ increasing
It is long, can pre- anti-bacteria propagation and infection a kind of antibiotic property artificial grass filaments manufacturing method.
Thus the technical scheme adopted by the invention is that:
The following steps are included:
Antibacterial agent, auxiliary agent and basic resin are uniformly mixed by the first step, then by single screw extrusion machine extruding pelletization, are obtained
Antibacterial matrices；
Second step, by antibacterial matrices, basic resin and functional material be blended, through twin-screw 250 DEG C at a temperature of melt, squeeze
It is pressed into film；
Above-mentioned film is cooled and solidified, is then cut into narrow strip by third step；
Fillet is carried out length direction stretching, fillet is made to stretch 6 times or so by the 4th step；
5th step is heat-treated the fillet after stretching with baking oven.
As a further improvement of the above technical scheme, the weight percent score of the antibacterial agent, auxiliary agent and basic resin
It Wei not 5-30%, 5-10%, 60-90%.
As a further improvement of the above technical scheme, the antibacterial agent is organic antibacterial agent or light catalase antibiotic finish
Agent.
As a further improvement of the above technical scheme, the functional material is stabilizer or antioxidant.
The invention has the advantages that
Method of manufacturing technology of the invention is simple, by increasing antibacterial agent, so that artificial grass filaments have the function of antibiotic and sterilizing, energy
Enough resist germ increase, can pre- anti-bacteria propagation and infection.
Specific embodiment
A kind of manufacturing method of antibiotic property artificial grass filaments, comprising the following steps:
Antibacterial agent, auxiliary agent and basic resin are uniformly mixed by the first step, then by single screw extrusion machine extruding pelletization, are obtained
Antibacterial matrices；
Second step, by antibacterial matrices, basic resin and functional material be blended, through twin-screw 250 DEG C at a temperature of melt, squeeze
It is pressed into film；
Above-mentioned film is cooled and solidified, is then cut into narrow strip by third step；
Fillet is carried out length direction stretching, fillet is made to stretch 6 times or so by the 4th step；
5th step is heat-treated the fillet after stretching with baking oven.
As a further improvement of the above technical scheme, the weight percent score of the antibacterial agent, auxiliary agent and basic resin
It Wei not 5-30%, 5-10%, 60-90%.
As a further improvement of the above technical scheme, the antibacterial agent is organic antibacterial agent or light catalase antibiotic finish
Agent.
As a further improvement of the above technical scheme, the functional material is stabilizer or antioxidant.
Above-mentioned specific embodiment cannot function as limiting the scope of the invention, for the technology people of the art
For member, any alternate modification to made by embodiment of the present invention or transformation are fallen within the scope of protection of the present invention.
Claims (4)
1. a kind of manufacturing method of antibiotic property artificial grass filaments, which comprises the following steps:
Antibacterial agent, auxiliary agent and basic resin are uniformly mixed by the first step, then by single screw extrusion machine extruding pelletization, are obtained
Antibacterial matrices；
Second step, by antibacterial matrices, basic resin and functional material be blended, through twin-screw 250 DEG C at a temperature of melt, squeeze
It is pressed into film；
Above-mentioned film is cooled and solidified, is then cut into narrow strip by third step；
Fillet is carried out length direction stretching, fillet is made to stretch 6 times or so by the 4th step；
5th step is heat-treated the fillet after stretching with baking oven.
2. a kind of manufacturing method of antibiotic property artificial grass filaments according to claim 1, which is characterized in that the antibacterial agent,
Auxiliary agent and the weight percent of basic resin are respectively 5-30%, 5-10%, 60-90%.
3. a kind of manufacturing method of antibiotic property artificial grass filaments according to claim 1, which is characterized in that the antibacterial agent is
Organic antibacterial agent or light catalase antibacterial finishing agent.
4. a kind of manufacturing method of antibiotic property artificial grass filaments according to claim 1, which is characterized in that the functionality material
Material is stabilizer or antioxidant.