CN103131379B - 一种高弹高拉伸性的无影胶及其制备方法 - Google Patents
一种高弹高拉伸性的无影胶及其制备方法 Download PDFInfo
- Publication number
- CN103131379B CN103131379B CN201310088850.7A CN201310088850A CN103131379B CN 103131379 B CN103131379 B CN 103131379B CN 201310088850 A CN201310088850 A CN 201310088850A CN 103131379 B CN103131379 B CN 103131379B
- Authority
- CN
- China
- Prior art keywords
- preparation
- shadow glue
- glue
- elastic
- stretchability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提出了一种高弹高拉伸性的无影胶及其制备方法。它由以下重量百分比的原料制成:聚氨酯丙烯酸酯30-50%,2,4,6-三甲基苯甲酰基-二苯基氧化膦1-5%,1-羟基环己基苯基甲酮1-5%,甲基丙烯酸羟乙酯20-35%,丙烯酸异冰片酯20-35%,丙烯酸甲酯1-5%3-(2,3-环氧丙氧)丙基三甲氧基硅烷1-5%。与现有技术相比,本发明的有益效果是本发明的产品具有拉伸率高,耐候性好,粘结强度高的特点,使用寿命长,能吸收所粘结产品的应力,来解决粘结处的减震问题;而且本发明的UV胶属于软质地,不是现有UV胶的硬块状。
Description
技术领域
本发明涉及一种高弹高拉伸性的无影胶及其制备方法。
背景技术
无影胶又称UV胶、光敏胶、紫外光固化胶,无影胶是指必须通过紫外线光照射才能固化的一类胶粘剂,它可以作为粘接剂使用,也可作为油漆、涂料、油墨等的胶料使用。适用范围极广、塑料与各种材料的粘接都有极好的粘接效果;粘接强度高、破坏试验可达到塑料本体破裂效果几秒钟定位、一分钟达到最高强度、极大地提高了工作效率;固化后完全透明、产品长期不变黄、不白化;
对比传统的瞬干胶粘接、具有耐环测、不白化、柔韧性好等优点。但普遍的无影胶均不能解决拉伸率低,耐候性差等问题,会影响产品的粘结强度和使用寿命,更不能吸收所粘结产品的应力,来解决粘结处的减震问题。
发明内容
本发明提出了一种高弹高拉伸性的无影胶及其制备方法,解决了现有技术中的不足,具有拉伸率高,耐候性好,粘结强度高的特点,使用寿命长,能吸收所粘结产品的应力,来解决粘结处的减震问题。
本发明的技术方案是这样实现的:一种高弹高拉伸性的无影胶,它由以下重量百分比的原料制成:
进一步的,它由以下重量百分比的原料制成:
更进一步的,它由以下重量百分比的原料制成:
制备上述高弹高拉伸性的无影胶的制备方法,包括以下步骤:
(1)在搅拌机中加入聚氨酯丙烯酸酯,然后依次加入2,4,6-三甲基苯甲酰基-二苯基氧化膦、1-羟基环己基苯基甲酮、甲基丙烯酸羟乙酯,将搅拌机由静止运转至300-500转/min速的低转速,并逐渐加热至10℃-50℃,持续保持温度10℃-50℃10-15分钟,待溶液搅拌至半透明状;
(2)然后依次加入丙烯酸异冰片酯、丙烯酸甲酯,然后提高搅拌机转速至900-1000转/min,并继续提高反应温度到摄氏60℃-80℃,在高转速状态下30分钟后,然后缓慢加入3-(2,3-环氧丙氧)丙基三甲氧基硅烷继续搅拌,10-15分钟后,成胶。
与现有技术相比,本发明的有益效果是:本发明的产品具有拉伸率高,耐候性好,粘结强度高的特点,使用寿命长,能吸收所粘结产品的应力,来解决粘结处的减震问题;而且本发明的UV胶属于软质地,不是现有UV胶的硬块状:
(1)一般现有UV胶的拉伸率为5%作用,而本发明UV胶的拉伸率可以达到80-150%;
(2)一般现有UV胶的180度弯折度实验时,一般弯折七八次就断了,而本发明弯折七八次不会出现这样的情况。
具体实施方式
下面对本发明中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明的其中的几个实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1:一种高弹高拉伸性的无影胶,它由以下重量百分比的原料制成:
聚氨酯丙烯酸酯35%,2,4,6-三甲基苯甲酰基-二苯基氧化膦3%,1-羟基环己基苯基甲酮3%,甲基丙烯酸羟乙酯28%,丙烯酸异冰片酯28%,丙烯酸甲酯2%,3-(2,3-环氧丙氧)丙基三甲氧基硅烷1%。
生产2000kg本发明的无影胶具体使用的各原料的用量为:聚氨酯丙烯酸酯700kg,2,4,6-三甲基苯甲酰基-二苯基氧化膦60kg,1-羟基环己基苯基甲酮60kg,甲基丙烯酸羟乙酯560kg,丙烯酸异冰片酯560kg,丙烯酸甲酯40kg,3-(2,3-环氧丙氧)丙基三甲氧基硅烷20kg。
其制备方法为:
(1)在搅拌机中加入聚氨酯丙烯酸酯,然后依次加入2,4,6-三甲基苯甲酰基-二苯基氧化膦、1-羟基环己基苯基甲酮、甲基丙烯酸羟乙酯,将搅拌机由静止运转至300转/min速的低转速,并逐渐加热至摄氏30℃,5分钟左右达到,持续15分钟,待溶液搅拌至半透明状;
(2)依次加入丙烯酸异冰片酯、丙烯酸甲酯,然后提高搅拌机转速至900转/min,并继续提高反应温℃到摄氏70℃,一般15分钟左右达到温℃,在高转速状态下30分钟后,然后缓慢加入3-(2,3-环氧丙氧)丙基三甲氧基硅烷继续搅拌,12分钟后,成胶。
实施例2:一种高弹高拉伸性的无影胶,它由以下重量百分比的原料制成:
聚氨酯丙烯酸酯40%,2,4,6-三甲基苯甲酰基-二苯基氧化膦2%,1-羟基环己基苯基甲酮2%,甲基丙烯酸羟乙酯25%,丙烯酸异冰片酯25%,丙烯酸甲酯3%,3-(2,3-环氧丙氧)丙基三甲氧基硅烷3%。
生产2000kg本发明的无影胶具体使用的各原料的用量为:聚氨酯丙烯酸酯800kg,2,4,6-三甲基苯甲酰基-二苯基氧化膦40kg,1-羟基环己基苯基甲酮40kg,甲基丙烯酸羟乙酯500kg,丙烯酸异冰片酯500kg,丙烯酸甲酯60kg,3-(2,3-环氧丙氧)丙基三甲氧基硅烷60kg。
其制备方法为:
(1)在搅拌机中加入聚氨酯丙烯酸酯,然后依次加入2,4,6-三甲基苯甲酰基-二苯基氧化膦、1-羟基环己基苯基甲酮、甲基丙烯酸羟乙酯,将搅拌机由静止运转至400转/min速的低转速,并逐渐加热至摄氏45℃,5分钟左右达到,持续12分钟,待溶液搅拌至半透明状;
(2)依次加入丙烯酸异冰片酯、丙烯酸甲酯,然后提高搅拌机转速至1000转/min,并继续提高反应温℃到摄氏80℃,一般15分钟左右达到温℃,在高转速状态下30分钟后,然后缓慢加入3-(2,3-环氧丙氧)丙基三甲氧基硅烷继续搅拌,15分钟后,成胶。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种高弹高拉伸性的无影胶的制备方法,其特征在于:该高弹高拉伸性的无影胶由以下重量百分比的原料制成:
所述该高弹高拉伸性的无影胶制备方法如下:
(1)在搅拌机中加入聚氨酯丙烯酸酯,然后依次加入2,4,6-三甲基苯甲酰基-二苯基氧化膦、1-羟基环己基苯基甲酮、甲基丙烯酸羟乙酯,将搅拌机由静止运转至300-500转/min速的低转速,并逐渐加热至10℃-50℃,持续保持温度10℃-50℃10-15分钟,待溶液搅拌至半透明状;
(2)然后依次加入丙烯酸异冰片酯、丙烯酸甲酯,然后提高搅拌机转速至900-1000转/min,并继续提高反应温度到摄氏60℃-80℃,在高转速状态下30分钟后,然后缓慢加入3-(2,3-环氧丙氧)丙基三甲氧基硅烷继续搅拌,10-15分钟后,成胶。
2.根据权利要求1所述的一种高弹高拉伸性的无影胶的制备方法,其特征在于:该高弹高拉伸性的无影胶由以下重量百分比的原料制成:
3.根据权利要求2所述的一种高弹高拉伸性的无影胶的制备方法,其特征在于:该高弹高拉伸性的无影胶由以下重量百分比的原料制成: