CN103130447A - Environment-friendly powder interior wall coating - Google Patents
Environment-friendly powder interior wall coating Download PDFInfo
- Publication number
- CN103130447A CN103130447A CN2011103721395A CN201110372139A CN103130447A CN 103130447 A CN103130447 A CN 103130447A CN 2011103721395 A CN2011103721395 A CN 2011103721395A CN 201110372139 A CN201110372139 A CN 201110372139A CN 103130447 A CN103130447 A CN 103130447A
- Authority
- CN
- China
- Prior art keywords
- interior wall
- parts
- wall coating
- kaolin
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly powder interior wall coating which comprises the following components by weight: 12-14 parts of urushiol paint flake, 25-35 parts of rutile titanium dioxide, 40-55 parts of light calcium carbonate, 5-8 parts of kaolin, 4-10 parts of barium sulfate, and proper pigments. The preparation method comprises the following steps: respectively weighing urushiol paint flake, rutile titanium dioxide, light calcium carbonate, kaolin, and barium sulfate, mixing, stirring, packaging, and examining to be qualified to obtain the environment-friendly powder interior wall coating. When in use, users prepare a proper amount of cold water, and mix the product with the cold water immediately before use. After storage for 5-7 days, corrosion may occur to cause waste since no preservative, such as formaldehyde, is added. The environment-friendly powder interior wall coating is slow in drying, easy to construct, corrosion resistant, aging resistant, strong in adhesion, and durable. The product is nontoxic and harmless, is suitable for wide application in rooms and office places, is suitable for both continuous production and indirect production, and has very good popularization application value.
Description
One, technical field
The present invention relates to a kind of interior wall coating, specifically a kind of environmental protection powder interior wall coating.
Two, technical background
In prior art, the coating such as Chang Yifang porcelain, emulsion paint are as the important finishing material of mankind room, office space.Select more and more some nontoxic inorganic materials in constituent, as multi mineral materials such as light calcium carbonate, talcum powder, kaolin, barium sulfate.But what also have has more or less added some virose chemical assistants.The coating such as porcelain as imitative in some in house decorative material, emulsion paint add sanitas---formaldehyde and organic compound.Brushing material on the wall can discharge naked eyes and cannot see, and with the impalpable formaldehyde of hand and harmful poison gas thereof, human body is caused very major injury.
Three, summary of the invention
The purpose of this invention is to provide a kind of environmental protection powder interior wall coating, is several raw material classification such as rutile-type phthalein white powder, light calcium carbonate metering specifically, mixes, stirs packing.It is solvent that the user provides appropriate pure cold water, adds and fills out powder coating, stirs, and can use.Structure must not surpass 5 to the good products storage phase---and 7 days, because this product adding preservative agent---formaldehyde not, lest corrosion causes waste.
This product is used nontoxic raw material, takees good care of healthy fresh air, improves domestic environment.Superpower self-cleaning, be the optimal selection of decorated house, office space.
1, the objective of the invention is the environmental protection powder interior wall coating realized by following purpose, is to be made by the raw material of following weight proportioning:
Laccol coating agent which has to be dissolved in alcohol before use 12-14 part, rutile-type phthalein white powder 25-35 part, light calcium carbonate 40-55 part, kaolin 5-8 part, barium sulfate 4-10 part, appropriate pigment forms.
The preparation process of environmental protection powder interior wall coating is: the raw materials such as laccol coating agent which has to be dissolved in alcohol before use, rutile-type phthalein white powder, light calcium carbonate, kaolin, barium sulfate are measured respectively, mix, stir packing, be up to the standards, be the environmental protection powder interior wall coating.
2, the preferred weight ratio range of preparation environmental protection powder interior wall coating is:
Laccol coating agent which has to be dissolved in alcohol before use 10-13 part, rutile-type phthalein white powder 20-30 part, light calcium carbonate 32-45 part, kaolin 4-5 part, barium sulfate 3-4 part, pigment is appropriate.
3, the optimum weight ratio range of preparation environmental protection powder interior wall coating is: 10 parts, laccol coating agent which has to be dissolved in alcohol before use, 32 parts, rutile-type phthalein white powder, 45 parts of light calcium carbonates, 5 parts of kaolin, 8 parts, barium sulfate.
Four, in environmental protection powder interior wall coating of the present invention and prior art, emulsion paint commonly used is compared following outstanding advantage and creationary contribution is arranged:
1, have superpower self-cleaning, fresh air.
2, strong adhesion is durable in use.
3, cost is low, and is inexpensive.
4, existing with existing right, remove doubt.Do not what auxiliary agent with existing right purpose be now: other people know because the emulsion paint that has synthesized attaches? whether sanitas is arranged---more Nobody Knows for formaldehyde.Again how about harm in the future? it is on tenterhooks when these unknown numbers allow common people's decorated house.In order to solve these trouble and worry, creatively invented " environmental protection powder interior wall coating ".Take powder as main, cold water is solvent.Attach the powder of environmental protection powder interior wall coating, mix and blend is the environmental protection powder interior wall coating.These powder mostly are common, and as light calcium carbonate, talcum powder etc., masses know nontoxic certainly.Barium sulfate is medical perspective " barium meal ", and the masses are of common occurrence.Select these materials to allow exactly the user relieved.The user provides appropriate cold water for oneself, and whether existing have sanitas one formaldehyde with existing right, understood at a glance.It is better to see once than hear a hundred times, the true checking true and false, and guide look is just known.
Five, implementation principle:
Formula one:
Laccol coating agent which has to be dissolved in alcohol before use 12kg, rutile-type phthalein white powder 32kg, light calcium carbonate 46kg, kaolin 4kg, barium sulfate 6kg.
Formula two:
Laccol coating agent which has to be dissolved in alcohol before use 8kg, rutile-type phthalein white powder 33kg, light calcium carbonate 52kg, kaolin 3kg, barium sulfate 4kg.
Formula three:
Laccol coating agent which has to be dissolved in alcohol before use 10kg, rutile-type phthalein white powder 32kg, light calcium carbonate 45kg, kaolin 5kg, barium sulfate 8kg.
The production stage of environmental protection powder interior wall coating is: according to the formula requirement, establish a transfer roller, the classification metering mixes, stirs packing.With laccol coating agent which has to be dissolved in alcohol before use, rutile-type phthalein white powder, light calcium carbonate, kaolin, barium sulfate philosophy accurate-metering, mix and blend is up to the standards, and is the bucket sealing, the finished product warehouse-in.
Claims (3)
1. environmental protection powder interior wall coating is characterized in that it is to be made by the raw material of following weight proportioning:
Laccol coating agent which has to be dissolved in alcohol before use 12-14 part, rutile-type phthalein white powder 25-35 part, light calcium carbonate 40-55 part, kaolin 5-8 part, barium sulfate 4-10 part, suitably pigment forms.The preparation process of environmental protection powder interior wall coating is: with laccol coating agent which has to be dissolved in alcohol before use, rutile-type phthalein white powder, light calcium carbonate, kaolin, the metering of barium sulfate philosophy, the mix and blend packing is the environmental protection powder interior wall coating.
When using, this product provides appropriate pure cold water for oneself by the user, and existing with existing right.Because adding preservative agent---formaldehyde, lest corrode, do not cause waste.
2. environmental protection powder interior wall coating according to claim 1 is characterized in that it is to be made by the raw material of following weight proportioning:
Laccol coating agent which has to be dissolved in alcohol before use 10-13 part, rutile-type phthalein white powder 20-30 part, light calcium carbonate 32-45 part, kaolin 4-5 part, barium sulfate 3-4 part, pigment is appropriate.
3. environmental protection powder interior wall coating according to claim 1 is characterized in that it is to be made by the raw material of following weight proportioning:
10 parts, laccol coating agent which has to be dissolved in alcohol before use, 32 parts, rutile-type phthalein white powder, 45 parts of light calcium carbonates, 5 parts of kaolin, 8 parts, barium sulfate, pigment is appropriate.