CN103122104A - High-temperature-resistant antibacterial foamed plastic - Google Patents
High-temperature-resistant antibacterial foamed plastic Download PDFInfo
- Publication number
- CN103122104A CN103122104A CN 201110368202 CN201110368202A CN103122104A CN 103122104 A CN103122104 A CN 103122104A CN 201110368202 CN201110368202 CN 201110368202 CN 201110368202 A CN201110368202 A CN 201110368202A CN 103122104 A CN103122104 A CN 103122104A
- Authority
- CN
- China
- Prior art keywords
- temperature resistant
- resistant antibacterial
- porous plastics
- antibacterial porous
- plastics according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of antibacterial foamed plastic and discloses high-temperature-resistant antibacterial foamed plastic which is contains, by content, 82-90% of matrix, 2-5% of foaming agent, 0.7-1.1% of fire retardant, 0.1-0.5% of antioxidant, 3-6% of flexibilizer, 0.8-1.2% of dispersant, 8-10% of antibacterial agent and 1-2% of other auxiliaries. Raw materials of components are easy to get and low in price, tourmaline can release anions which can adjust ion balance of human bodies, relax body and mind, activate cells, improve self-healing rate, inhibit oxidation of bodies, eradicate odors and the like; silver ions have functions of radiation protection, sterilization and disinfection; and nano silicon dioxide and nano titanium dioxide can emit infrared rays to function in healthcare.
Description
Technical field
The present invention relates to a kind of high-temperature resistant antibacterial porous plastics, belong to the antibiotic plastic technical field.
Background technology
The foam thermal insulation plastics are widely used on buildings, no matter are on metope or floor, because its thermal conductivity is low, so can make the temperature of interior of building keep cool in summer and warm in winter.Along with the widespread use of plastic prod, people are also more and more higher to the performance requriements of plastic prod.Negative ion is a kind of electronegative gaseous ion in air, negative ion can not only be facilitated the physiological activity of human body synthetic and vitamin storage, reinforcement and human activin, activity on human body and other life has very important impact, therefore is called as " air VITAMIN ".Negative ion can make brokenly the factor such as the acidity, oxidation, active oxygen, lactic acid of ring life entity health reduce gradually, and the metabolism of activating cells tissue gives that life entity is inner creates good environment, brings up the health of health.Thereby strengthen restorer and the natural healing ability of life entity self, and then overcome disease.Be no lack of high temperature resistant and antibiotic porous plastics in present plastic prod, but just be used for heat-insulating property, can not meet the people's needs.
Summary of the invention
The defective that exists in view of prior art a kind ofly can be emitted the high-temperature resistant antibacterial porous plastics that negative ion has nourishing function thereby the purpose of this invention is to provide.
For achieving the above object, the technology used in the present invention solution is: a kind of high-temperature resistant antibacterial porous plastics, include matrix, whipping agent, fire retardant, oxidation inhibitor, toughner, dispersion agent, antiseptic-germicide and other auxiliary agents, wherein the content of each composition is: matrix 82 ~ 90%, whipping agent 2 ~ 5%, fire retardant 0.7 ~ 1.1%, oxidation inhibitor 0.1 ~ 0.5%, toughner 3 ~ 6%, dispersion agent 0.8 ~ 1.2%, antiseptic-germicide 8 ~ 10%, other auxiliary agents 1 ~ 2%.
Described matrix is a kind of in polystyrene, urethane, resol.
Described whipping agent is a kind of in sodium lauryl sulphate, polyoxyethylenated alcohol sodium sulfate.
Described fire retardant is selected a kind of in magnesium hydroxide in inorganic combustion inhibitor, aluminium hydroxide.
Described oxidation inhibitor is at least a in three grades of butyl of 2,6--4-methylphenol, two (three grades of butyl of 3,5--4-hydroxy phenyl) thioether, four (β-(three grades of butyl of 3,5--4-hydroxy phenyl) propionic acid) pentaerythritol ester.
Described toughner is acrylic polymer.
Described dispersion agent is aliphatic amide type.
Described antiseptic-germicide is the mixture of tourmalinite, nano titanium oxide, Silver Nitrate, and proportioning is tourmalinite: nano titanium oxide: Silver Nitrate=5:4:3.
In the present invention, the raw material of each component is easy to get, and low price, tourmalinite can the little electric current of permanent generation, and the current capacity of this electric current and human nerve seemingly can play and impel blood circulation, effect smoothly, tourmalinite can also anion releasing in addition, these negative ions can the balance the body ionic equilibrium, and body and mind loosens, active cells, improve a lot of effects such as self-healing rate, and can suppress the oxidation of health and the effect that eliminates the unusual smell; Silver ions has the function of radioprotective sterilization and disinfection; Nano silicon, nano titanium oxide can radiate its nourishing function of infrared rays.
Embodiment
A kind of high-temperature resistant antibacterial porous plastics, include matrix, whipping agent, fire retardant, oxidation inhibitor, toughner, dispersion agent, antiseptic-germicide and other auxiliary agents, wherein the content of each composition is: matrix 82 ~ 90%, whipping agent 2 ~ 5%, fire retardant 0.7 ~ 1.1%, oxidation inhibitor 0.1 ~ 0.5%, toughner 3 ~ 6%, dispersion agent 0.8 ~ 1.2%, antiseptic-germicide 8 ~ 10%, other auxiliary agents 1 ~ 2%.
Described matrix is a kind of in polystyrene, urethane, resol.
Described whipping agent is a kind of in sodium lauryl sulphate, polyoxyethylenated alcohol sodium sulfate.
Described fire retardant is selected a kind of in magnesium hydroxide in inorganic combustion inhibitor, aluminium hydroxide.
Described oxidation inhibitor is at least a in three grades of butyl of 2,6--4-methylphenol, two (three grades of butyl of 3,5--4-hydroxy phenyl) thioether, four (β-(three grades of butyl of 3,5--4-hydroxy phenyl) propionic acid) pentaerythritol ester.
Described toughner is acrylic polymer.
Described dispersion agent is aliphatic amide type.
Described antiseptic-germicide is the mixture of tourmalinite, nano titanium oxide, Silver Nitrate, and proportioning is tourmalinite: nano titanium oxide: Silver Nitrate=5:4:3.
Claims (8)
1. high-temperature resistant antibacterial porous plastics, it is characterized in that including matrix, whipping agent, fire retardant, oxidation inhibitor, toughner, dispersion agent, antiseptic-germicide and other auxiliary agents, wherein the content of each composition is: matrix 82 ~ 90%, whipping agent 2 ~ 5%, fire retardant 0.7 ~ 1.1%, oxidation inhibitor 0.1 ~ 0.5%, toughner 3 ~ 6%, dispersion agent 0.8 ~ 1.2%, antiseptic-germicide 8 ~ 10%, other auxiliary agents 1 ~ 2%.
2. a kind of high-temperature resistant antibacterial porous plastics according to claim 1 is characterized in that described matrix is a kind of in polystyrene, urethane, resol.
3. a kind of high-temperature resistant antibacterial porous plastics according to claim 1 is characterized in that described whipping agent is a kind of in sodium lauryl sulphate, polyoxyethylenated alcohol sodium sulfate.
4. a kind of high-temperature resistant antibacterial porous plastics according to claim 1 is characterized in that described fire retardant selects a kind of in magnesium hydroxide in inorganic combustion inhibitor, aluminium hydroxide.
5. a kind of high-temperature resistant antibacterial porous plastics according to claim 1, it is characterized in that described oxidation inhibitor is 2, three grades of butyl of 6--4-methylphenol, two (3, three grades of butyl of 5--4-hydroxy phenyl) at least a in thioether, four (β-(three grades of butyl of 3,5--4-hydroxy phenyl) propionic acid) pentaerythritol ester.
6. a kind of high-temperature resistant antibacterial porous plastics according to claim 1, is characterized in that described toughner is acrylic polymer.
7. a kind of high-temperature resistant antibacterial porous plastics according to claim 1, is characterized in that described dispersion agent is aliphatic amide type.
8. a kind of high-temperature resistant antibacterial porous plastics according to claim 1, is characterized in that described antiseptic-germicide is the mixture of tourmalinite, nano titanium oxide, Silver Nitrate, and proportioning is tourmalinite: nano titanium oxide: Silver Nitrate=5:4:3.